Structure and Optical Properties of ZnCdO Thin Films Prepared by Spray Pyrolysis

Jabbar H. Khlaief

Al-Nahrain Journal of Science مجلة النهرين للعلوم
ISSN: (print)26635453,(online)26635461 Year: 2016 Volume: 19 Issue: 3 Pages: 77-86
Publisher: Al-Nahrain University جامعة النهرين

Abstract

ZnCdO films were compounded by spray pyrolysis on glass substrates at temperature of 250Co, using solution of zinc acetate and cadmium acetate salts with various additions concentrations of Zn (25, 50, 75)%. Structure and optical properties have been analyzed using XRD and UV-Vis spectroscopy. XRD analysis premiered that thin films were of polycrystalline nature with face centered cubic structure. The crystallinity increases when the Zn additions increases. Film additions with 75% Zn has minimum value of dislocation density and strain which confirm the improved crystallinity of the film. The optical results featured the transparency of the ZnCdO films is greater than 80% in the visible region, and we found when the concentration of Zn additions increase the optical band gap increasing from (2.49 to 2.9eV).

اغشية اوكسيد الكادميوم-الزنك تم تحضيرها بطريقة الرش الكيميائي الحراري على قواعد من الزجاج وبدرجة حرارة 250 درجة مئوية، باستخدام محاليل لاملاح الكادميوم والزنك وبنسب اضافة مختلفة لمادة الزنك (%25,50,75). الخصائص التركيبية والبصرية تم تحليلها باستخدام حيود الاشعة السينية ومطياف الاشعة المرئية – فوق البنفسجية. واظهرت نتائج حيود الاشعة السينية أن الاغشية الرقيقة ذات طبيعة متعددة التبلوروبتركيب الوجه المركزي المكعب. وبينت نتائج النفاذية البصرية بأن اغشية اوكسيد الكادميوم زنك ذات نفاذية عالية اكبر من 80% للمنطقة المرئية. وقد وجدنا عند زيادة تركيز اضافة الزنك ان فجوة الطاقة تزداد من (2.49 الى 2.9 الكترون فولت).

Keywords

ZnCdO --- thin film --- spray pyrolysis --- optical and structural properties