Fulltext

Reduction of Wear Effect for Copper- Silicon Alloy by Laser Treatment

تقليل تأثير البلى لسبيكة النحاس- سليكون بواسطة المعاملة بالليزر

Sajid H.Alwan ساجد علوان

Al-Nisour Journal for Medical Sciences مجلة النسور للعلوم الطبية
ISSN: 26640562 26640554 Year: 2019 Volume: 1 Issue: 1 Pages: 22-29
Publisher: Al-Nisour University College كلية النسور الجامعة

Abstract

Copper- silicon alloy was prepared by CNC machining into disc shapes with diameter 18mm and thickness of 3mm using CNC machine to obtain more accuracy dimensions .Grinding and polishing process were carried out for all samples, and conducted to Nd-YAG laser treatment. Laser conditions involved laser fluency of 500mJ, wavelength of 1064nm, and different number of laser pulses (20, 40 and 60 pulses). The samples were subjected to wear system measurements before and after laser treatment to calculate the wear rate with different situations. The results revealed that the wear rate was reduced by 15% after laser treatment.

تم تحضير سبيكة النحاس – سيليكون بواسطة التشغيل بمكائن CNC على شكل قرص بقطر 18 ملم وبسمك 3 ملم . استعمال مكائن CNC لغرض الحصول على دقة ابعاد اكبر . عمليات التنعيم والتلميع اجريتلكل النماذج وتم تعريضها الى المعاملة بليزر Nd-YAG . عوامل الليزر كانت بطاقة 500mJ وبطول موجي 1064nm وبعدد مختلف من النبضات الليزرية ( 20 ، 40 ، 60 نبضة ) . تم فحص البلى بواسطة نظومة قياس البلى قبل وبعد المعاملة لغرض حساب معدل البلى . اظهرت النتائج ان معدل البلى انخفض بمقدار 15% بعد المعاملة الليزرية

Keywords

copper-silicon alloy --- laser treatment --- wear rate