Improvement the efficiency of SnO2/n-Si detector by engraving method using a CNC machine

تحسين كفاءة كاشف SnO2/n-Si بأسلوب الحفر باستعمال ماكينة CNC

Wlla M. Mohammed ولاء محفوظ محمد

Iraqi Journal of Physics المجلة العراقية للفيزياء
ISSN: 20704003 Year: 2019 Volume: 17 Issue: 41 Pages: 51-57
Publisher: Baghdad University جامعة بغداد

Abstract

Tin oxide was deposited by using vacuum thermal method on silicon wafer engraved by Computer Numerical Controlled (CNC) Machine. The inscription was engraved by diamond-made brine. Deep 0.05 mm in the form of concentric squares. Electrical results in the dark were shown high value of forward current and the high value of the detection factor from 6.42 before engraving to 10.41 after engraving. (I-V) characters in illumination with powers (50, 100, 150, 200, 250) mW/cm2 show Improved properties of the detector, Especially at power (150, 200, 250) mW/cm2. Response improved in rise time from 2.4 µs to 0.72 µs and time of inactivity improved 515.2 µs to 44.2 µs. Sensitivity angle increased at zone from 40o to 65o.

تم في هذا البحث ترسيب أوكسيد القصدير على قواعد من السليكون المحفور بواسطة ماكينة مسيطر عليها رقمياً بالحاسبة الالكترونية CNC. تمت عملية الحفر بعمق 0.05 mm على شكل مربعات بواسطة برينة من الألماس. الخواص الكهربائية في الظلام بينت زيادة في قيمة التيار الامامي بالنسبة للتيار العكسي مع ارتفاع في قيمة عامل الكشفية من 6.42 قبل الحفر الى 10.4. اما الخواص الكهربائية عند الاضائة بقدرات (50, 100, 150, 200, 250) mW/cm2 فبينت زيادة في قيمة الكشفية وخصوصاً عند القدرات(150, 200, 250) mW/cm2. زمن الاستجابة لنهوض الإشارة تحسن من 2.4 µs الى 0.72 µs وتحسن زمن الخمود من 515.2 µs الى 44.2 µs. اما بالنسبة الى زاوية التحسس للكاشف فبينت النتائج الى زيادة ملحوظة في المنطقة المحصورة بين 40o الى65o .

Keywords

Tin oxide --- CNC machine --- diamond-made brine.