تحضير فلز الخارصين من محلول كبريتات الخارصين بالأسلوب الكهروكيميائي

جميل يوسف عبد الرضا

KUFA JOURNAL OF ENGINEERING مجلة الكوفة الهندسية
ISSN: 25230018 Year: 2012 Volume: 3 Issue: 2 Pages: 1-9
Publisher: University of Kufa جامعة الكوفة

Abstract

Experimental result are presented for the preparation of zinc metal from Zinc Sulphate solution using electrochemical process.Laboratory cell which equipped with lead anode and aluminum cathode, was designed and utilized to obtain experimental result which was necessary for proceeding of the designated objective of this work. In the present experiment about 121 gm.-Zn / L solution was electrolyzed batch-wise at a current density rang 0.03-0.1 Amp./cm2 at a temperature of 40 to 45 ◦C. The effect of electrolytes concentration and the final concentration of zinc ions and sulphuric acid formed were also tested.The current efficiency of about 92% was obtained for 75% zinc ions conversion, at optimum condition mainly current density of 0.08 Amp./cm2 ,temperature of about 40 ◦C. The above current efficiency is similar to that reported in related studies.

أشتمل البحث أستحصال النتائج العملية لتحضير معدن الخارصين باستخدام الأسلوب الكهروكيميائي .تم استخدام خلية تحلل كهربائي مختبريه تحوي على قطب أنود من الرصاص وقطب كاثود من الألمنيوم لأجراء التجارب اللازمة لإنجاز هذا البحث ، في هذه التجارب تم استخدام محلول من كبريتات الخارصين بتركيز خارصين بحدود 121 gm-Zn / L وبأسلوب الوجبات وبكثافة تيار بالمدى cm2/0.03 – 0.1 Amp. وبدرجة حرارة 40-45 ◦C ،وتم أيضا دراسة تأثير تركيز المحلول الابتدائي والتركيز النهائي للمحلول. كفاءة تيار بمقدار 92% تم الحصول عليها وبنسبة استخلاص للخارصين من المحلول الابتدائي بمقدار 75% باعتماد كثافة تيار بمقدار 0.08 Amp. / cm2 ودرجة حرارة بحدود 40 ◦C وكفاءة التيار هذه مشابهة إلى ما مثبت في المصادر العلمية ذات العلاقة .

Keywords

Electro wining of metals --- Economic grounds --- Carbon reduction of the oxide --- Electrolytic reduction --- Cathodic reaction --- Current efficiencies