Dielectric Properties of Iraqi Clay; Effect of Alumina Content

تأثير المحتوى الألومني على خصائص العزل الكهربائي للأطيان العراقية

. Qasid Abdul Sattar قاصد عبد الستار --- Talib Saloom Hamadi طالب سلوم حمادي

AL-NAHRAIN JOURNAL FOR ENGINEERING SCIENCES مجلة النهرين للعلوم الهندسية
ISSN: 25219154 / eISSN 25219162 Year: 2009 Volume: 12 Issue: 2 Pages: 147-150
Publisher: Al-Nahrain University جامعة النهرين

Abstract

In order to investigate the alumina effect on the low frequency dielectric constant of fire clay manufacture from Iraqi clay. Fire clay products have been powder pressed with different alumina content ,sintered ,then dielectric constant and dielectric loss( tan δ) has been measured at low frequencies which extend from 30 kHz to 100kHz.There is a significant difference in their properties were observed between samples made with different alumina content added to the fire clay product where these differences were measured as a function of alumina content. This confirm that the insulating properties of the fire specimen from the electrical view point was affected by the crystallization of mullite and cristobolite .

للتحقق من تأثير الألومينا على ثابت العزل الكهربائي لمدى الترددات الواطئة للمنتج الناري المصنوع من الأطيان العراقية حيث تم تشكيل تلك النماذج التي تحتوي على نسب ألومينا مختلفة (20%,15%,10%,5%) ومعاملتها حراريا ثم قياس ثابت العزل والفقدان العزلي لمديات التردد الواطئة (100kHz-30kHz) . حيث لوحظ وجود تحسن في خواص تلك النماذج (الفيزيائية والعزلية)بسبب زيادة محتوى الألومينا المضافة الى نماذج الطين الناري . وقد أعتمد في هذا البحث التغير في ثابت العزل الكهربائي كدالة لتغير محتوى الألومينا وهذا مايؤكد تأثر خاصية العزل الكهربائي من وجهة النظر الكهربائية بظهور كل من المولايت والكرستوبولايت كأطوار في تلك النماذج مما يجعل سلوكها كعازل مقترن بسلوك تلك الاطوار والتي عادة ما تتصف بثابت عزل منخفض .

Keywords

dielectric constant --- alumina --- fire clay --- mullite.