The Optical Properties of GaAs Thin films Prepared by Flash Evaporation Technique

الخصائص البصرية لغشاء زرنيخات الكاليوم المحضرة بطريقة التبخير الفراغي الوميضي

Rasha A. Abdullah رشا عبد الله عباس1

Tikrit Journal of Pure Science مجلة تكريت للعلوم الصرفة
ISSN: 18131662 Year: 2008 Volume: 13 Issue: 2 Pages: 138-140
Publisher: Tikrit University جامعة تكريت

Abstract

A polycrystalline GaAs thin films have prepared by flash evaporation on glass substrate with Thickness ~ 1 µm and substrate temperature (Ts) of about 423 K under vacuum of about 10-5 mbar. The thin films heat treated at different annealing temperatures 423, 473, 523, 573 K. The optical measurements showed that GaAs has direct energy band gap, and the absorption coefficient decreases with increasing the annealing temperatures. The increasing of annealing temperature shifts the peak of transmittance spectrum toward the shorter wavelengths (higher energies) compared with the as-deposited thin film.

تم تحضير أغشية زرنيخات الكاليوم متعددة البلورات بسمك ~ 1 مايكرومتر على أرضيات زجاجية بواسطة تقنية التبخير ألوميضي في فراغ حوالي 10-5 ملي بار وبدرجة حرارة أرضية 423 مطلقة, حيث تم معاملتها حراريا بدرجات تلدين مختلفة 423, 473, 523 و573 مطلقة.أظهرت دراسة القياسات البصرية بأن اغشية زرنيخات الكاليوم تمتلك فجوة طاقة مباشرة و التي تزداد مع زيادة درجة حرارة التلدين. ان معامل الامتصاص يقل بزيادة درجات حرارة التلدين, و تزحف قمة طيف النفاذية نحو الاطوال الموجية القصيرة (الطاقات العالية) بزيادة درجة حرارة التلدين مقارنة مع النموذج غير الملدن.