The Combined Action of Zeolite and Chlorinated Rubber as Flame Retardants for Epoxy Resin

التأثير التآزري للزيولايت والمطاط المكلور كمثبطات لهب لراتنج الايبوكسي

L.M.Hadi* لقاء محمد هادي* --- J.R .Ugal جليل رهيف عكال

Baghdad Science Journal مجلة بغداد للعلوم
ISSN: 20788665 24117986 Year: 2013 Volume: 10 Issue: 3عدد خاص بموتمر الكيمياء Pages: 561-568
Publisher: Baghdad University جامعة بغداد

Abstract

In this work , the effect of chlorinated rubber (additive I), zeolite 3A with chlorinated rubber (additive II), zeolite 4A with chlorinated rubber (additiveIII), and zeolite 5A with chlorinated rubber (additive IV), on flammability for epoxy resin studied, in the weight ratios of (2, 4, 7,10 & 12%) by preparing films of (130x130x3) mm in diameters, three standard test methods used to measure the flame retardation which are ; ASTM : D-2863 , ASTM : D-635 & ASTM : D-3014. Results obtained from these tests indicated that all of them are effective and the additive IV has the highest efficiency as a flame retardant.

في هذا العمل, تم أستخدام المطاط المكلور (مضاف I) ، زيولايت نوع 3A مع المطاط المكلور (مضاف II) ، زيولايت نوع 4A مع المطاط المكلور (مضاف III) و زيولايت نوع 5A مع المطاط المكلور (مضاف IV)وبنسب مختلفة10,7,4,2)و 12)% بوصفها مضافات لتثبيط لهوبية وزيادة مقاومة اشتعال راتنج الايبوكسيتم تحضير شرائح بابعاد (3×130×130) ملم. واستخدمت ثلاث طرق قياسية لاختبار تثبيط اللهوبية وهي : الطريقة القياسية ASTM : D-2863 ، الطريقة القياسية ASTM : D-635 والطريقة القياسية ASTM : D-3014 ان النتائج التي تم الحصول عليها تشير الى ان جميع المضافات فعالة وأن المضاف IV يمتلك كفاءة اعلى في تثبيت لهوبية راتنج الايبوكسي.

Keywords

Key word : Polymers --- Epoxy resin --- Flame retardant --- Flammability --- Additives --- Composite materials .