Fire retardancy characteristics of polymeric composite materials

صفات تثبيط اللهب للمواد المركبة البوليميرية

Naser A.Alwash نصر عبد الأمير علوش --- Ali J.Salaman علي جاهل سلمان --- Mustafa A. Rijab مصطفى أحمد رجب** --- Ali I .Al-Mosawi علي إبراهيم الموسوي

Baghdad Science Journal مجلة بغداد للعلوم
ISSN: 20788665 24117986 Year: 2013 Volume: 10 Issue: 3عدد خاص بموتمر الكيمياء Pages: 828-831
Publisher: Baghdad University جامعة بغداد

Abstract

Fire retardancy characteristics of polymeric composite material reinforced by fibers using coating by a fire retardant layer represent antimony tetroxide was studied. A coating layer (4mm) thickness from antimony tetroxide was used as a surface layer to react and prevent spread of flame on surface of epoxy resin reinforced by carbon – Kevlar fibers and exposed this coating layer to direct flame generated from oxyacetylene flame with different exposure distances (10,15,20mm) and study how it can protect the substrate . The experimental results showed that a great increment in thermal resistance and flame retardancy after coating by antimony tetroxide as well as rising flame resistance increased exposure distances to flame. .

الخلاصة :صفات تثبيط اللهب لمادة مركبة بوليمرية مقواة بالألياف بإستخدام الطلاء بطبقة مثبط لهب متمثلة برابع أوكسيد الأنتيمون قد تم دراستها . تم إستخدام طبقة طلاء بسمك (4mm) من رابع أوكسيد الأنتيمون كطبقة طلاء سطحية لمقاومة ومنع إنتشار اللهب على سطح راتنج الإيبوكسي المقوى بألياف الكربون - كيفلار ، وتعريض هذه الطبقة للهب مباشر الناتج متولد من شعلة أوكسي أستيلينية مع مسافات تعرض مختلفة (mm10،15،20) ودراسة كيف تستطيع حماية الطبقة التحية. أظهرت النتائج العملية زيادة كبيرة في المقاومة الحرارية وتثبيط اللهب بعد طلاء برابع أوكسيد الأنتيمون وكذلك إرتفاع مقاومة اللهب مع زيادة مسافات التعرض .

Keywords

Keywords: Fire Retardancy --- Composite Material --- Inorganic retardants