دراسة تأثير اوكسيد التيتانيوم على مقاومة التآكل والتآكل –تعرية للبولي ستايرين

اسراء علي حسين

Journal of University of Babylon مجلة جامعة بابل
ISSN: 19920652 23128135 Year: 2013 Volume: 21 Issue: 3 Pages: 1080-1089
Publisher: Babylon University جامعة بابل

Abstract

In this research , some sample from polystyrene with TiO2 as a filler in different weight percent (5,10,15,20,25,30)% have been prepared. Samples produced by (Hot press)method. Corrosion test has been done using simple immersion test in different period of time as (2,4,6,12,24) hours and the immersion done in different solution (distilled water, 0.9% NaCl and 3.5 %NaCl) also erosion – corrosion have been done in different period of time (10,20,30,40,50)min. Hardness test has been don and results show that the corrosion resistance increased for both test with increasing the TiO2 percentage addition and hardness increase with increasing TiO2 weight percentage.

في هذا البحث تم تحضير عدة عينات من البولي ستايرين وتم إضافة اوكسيد التيتانيوم TiO2 بنسب وزنيه مختلفة تراوحت بين 5, 10 , 15 , 20 , 25 , 30) )% ، حيث تم الحصول على العينات عن طريق الكبس الساخن ( Hot pressing) ثم تم اجراء اختبار التاكل بواسطة الغمر البسيط لكل العينات وبأزمان مختلفة (2,4,6,12,24) ساعة ، حيث تم الغمر في محاليل مختلفة وهي (الماء المقطر ، NaCl %0.9، NaCl %3.5) وأيضا تم أجراء اختبار تأكل التعرية ( erosion-corrosion) لازمان مختلفة تراوحت بين (10,20,30,40,50) دقيقة. وكذلك اجري اختبار الصلادة للعينات قبل الغمر بالمحاليل اظهرت النتائج أن مقاومة التآكل تزداد بزيادة النسبة الوزنية TiO2 بالنسبة للتآكل بالغمر البسيط والتآكل بالتعرية بنسبة 98% كما اوضحت النتائج زيادة الصلادة مع زيادة النسبة الوزنية لاوكسيد التيتانيوم TiO2