Flammability action of tires material after adding flame inhibitor

فعل قابلية الإشتعال لمادة الإطارات بعد إضافة مثبط للهب

Abbass Hashim عباس هاشم --- Mohammad H. Al- Maamori محمد حمزة المعموري --- Haider K.Ammash حيدر كاظم عماش --- Ali I.Al-Mosawi علي إبراهيم الموسوي

Baghdad Science Journal مجلة بغداد للعلوم
ISSN: 20788665 24117986 Year: 2013 Volume: 10 Issue: 3عدد خاص بموتمر الكيمياء Pages: 1057-1061
Publisher: Baghdad University جامعة بغداد

Abstract

Magnesium hydroxide was used as flame inhibitor to increased flame resistance for tires .Magnesium hydroxide was adding with (5%,10%) weight percents to rubber master batch of tire and then exposed the resulting material to a flame generated from gas torch with (10 mm) exposure distance . Method of measuring the surface temperature opposite to the flame was used to determine the heat transferred through tire material. The results were obtained shows enhanced flame resistance for tire by added magnesium hydroxide and this resistance increased by increasing hydroxide Percentage .

إستخدم هيدروكسيد المغنيسيوم كمثبط لهب لزيادة مقاومة اللهب للإطارات . هيدروكسيد المغنيسيوم تم إضافته بنسب وزنية (5% ،10%) للخلطة المطاطية للإطار ثم تم تعريض المادة الناتجة إلى لهب متولد من شعلة غازية وبمسافة تعرض(10 mm) . إستخدمت طريقة قياس درجة حرارة السطح المعاكس للهب لحساب الحرارة المنتقلة خلال مادة الإطار . النتائج التي تم الحصول عليها أوضحت تحسن مقاومة اللهب للإطار عند إضافة هيدروكسيد المغنيسيوم وتزداد المقاومة مع زيادة نسبة الهيدروكسيد المضافة .

Keywords

Flame action --- Magnesium Hydroxide --- Tires material.