Table of content

Al-Nahrain Journal of Science

مجلة النهرين للعلوم

ISSN: (print)26635453,(online)26635461
Publisher: Al-Nahrain University
Faculty: Science
Language: Arabic and English

This journal is Open Access

About

ANJS(Al-Nahrain Journal of Science) has been published by College of Science since 1996. This Journal consists of the latest researches in both English and Arabic Languages within the Specializations of the scientific departments in the College.

Loading...
Contact info

Al-Nahrain Journal of Science
P.O. Box: 64055, Al-Jadriah, Baghdad, Iraq .
Email: alnahrain-sci@hotmail.com
Webmaster Email: webmaster@jnus.org

Table of content: 2016 volume:19 issue:4

Article
Fabrication of Laser Detectors using Ge wafer Doped with Sb

Loading...
Loading...
Abstract

Germanium antimony (Ge:Sb) thin films have been fabricated by thermal evaporation system deposition at atmospheric pressure between (5.8x10-6 to 7.5x10-6) mbar. The (Ge:Sb) thin films then exposure to Nd:YAG laser with 1064μm wavelength at different energy densities (100,200) mj/cm2. XRD analysis show that Germanium antimony thin films are polycrystalline and the full width at half maximum (FWHM) increase as laser energy densities increases. Photocurrent and quantum efficiency of the detector increases as the laser energy densities increases.في هذه الد ا رسة، حضرت أغشيه الجرمانيوم المشوبة بالانتموني في منظومة الترسيب التبخير الح ا رري عند ضغط 6-01 ( ملي بار. عرضت الاغشية ×5.8-6-01× جوي ) 8.5 لليزر نيدميوم ياك ذي الطول الموجي 0161 نانو متر عند . كثافة طاقات ليزرية مختلفة ) 011 و 011 ( ملي جول/سم 0 اظهرت النتائج تحليل حيود الاشعة السينية ان الاغشية جميعها متعددة التبلور. ان زيادة طاقة الليزر تودي الى زيادة .FWHM ان تيار والكفاءة الكمية للكاشف يزداد بزيادة كثافة طاقة الليزر.

Keywords

Germanium --- Antimony --- thin films --- Nd:YAG laser


Article
Synthesis and Characterization of Some Anti-bacterial Active Transition Metal Complexes of N'-[2-(2-Phenyl hydrazinyl) Phenyl] Benzothiohydrazide

Authors: Shaymaa H. Naji --- Falih H. Musa
Pages: 8-15
Loading...
Loading...
Abstract

The ligand N'-[2-(2-Phenyl hydrazinyl) Phenyl] benzothiohydrazide (L) has been prepared from the reaction of ortho amino hydrazo benzene with phenyl isothiocyanate in mole ratio (1:1) and characterized by elemental analysis (C,H,N), H1, 13C-NMR, IR and Uv-Vis Spectroscopic methods . The complexes of the bivalent ions (Co (II), Ni (II), Cu (II), Cd (II) and Hg (II)) have been prepared and characterized. The structural diagnosis were established by IR, Uv- Visible spectrum, conductivities, atomic absorption and magnetic susceptibility. Chloride ion content was also evaluated by (Mohr method) .The suggested geometry of the complexes were octahedral around the metal ion with the (N,N,S) ligand coordinated in tridentate mode. , Kf, max for the complexes were estimated too.  for Co- complex was calculated. In addition biological activity of the ligand and complexes against two selected types of bacteria were also examined. Some of the complexes exhibited a good anti bacterial activities -2 تفنيم تييم) ا رنييتيم (ت -2 -'N ،)L تم تتحضميرتالليكانم)ت فنيمم (توننيواييييمم) ا رت ا نيمم)تامميتتياومم تايرويااينيييمم) ا رنيوننييتامم ت تويايم ت )L فنيم تاينيوماييتيميانيبتيونيمو ت 1:1 .تتم تتشم يصت ت يمممنتالمممرنييتالنممميي ت ،)N,H,C التحليممم تالممم)ري)تلل نا مممرت الاغنا ييم ،تاعشم تتحممبتالحام ا ر تياعشمم تفمي)تالونييمم ي –ت الارئيممم .تكاممماتتممم تتحضممميرتيتشممم يصتا قممم)ابت اممم تو ممم ت ت.)Hg تي Cd ت،Cu ت،Ni ت،Co ايينابتال نا مرتالونائيم تالتكماف ت تاعشمم تتحممبت ،)N,H,C ايممت )ابتتقنيممابتتحليمم تال نا ممرت الحامممممم ا ر ،تاعشمممممم تفممممممي)تالونييمممممم ي –تالارئيمممممم ،تالتي مممممميلي ت الكهروائي ،تاعات ا ي تالذريم تيالحيايمي تالاغنا ييمي تكاماتتم ت حيمماستنيممو تالكليريمم)تي يممتنتنتامميتالتحاليمم تايتالا قمم)ابتلهممات تو ومم ت )L شمك توامان تاليم ي تحمي تايمييتاليلمنتام تالليكانم)ت تلهمذاتالا قم)ابت max ت،Kf, ت، تيتم تتح)يم)ترمي ت )S,N,N اليميت تلا قم)تالكيولمب.تكاماتتامبت) ا ريم تالي اليم ت  ير)تت تحياستريا ت الواييلي يم تلليكانم)تيا ق)اتموتضم)تنميوييتاميتالوكتريماتالانت وم ،ت حيممأت رهممربتالنتممائنتلهممذاتالا قمم)ابتراوليمم تاتيايتمموتولممتترتمم ت الأنياعتالانت و تايتالوكتريا.


Article
Design and Implementation of PCV Device Based on Arduino Board

Loading...
Loading...
Abstract

There are many methods which can be used to determine packed red blood cells volume (PCV) value. Some of them are direct and another are indirect methods. However using of the manual ruler to evaluate PCV is the easiest and more economic method which is commonly used as a direct way to determine PCV but with probability of personal errors and plasma trapped. In our search, we have been designed and implemented electronic circuit which is depended on Arduino board to evaluate PCV. The new measuring device is consisted of red light (600nm) emitters or diodes to benefit of specified absorbance of this light by erythrocytes (red blood cells) in comparison with lowest absorbance of red light by blood plasma. Then, the transmitted light is received by photocell and photocell's signal is processed by Arduino board. The difference of light intensity between incident and transmitted light after it passes through centrifuged blood sample makes PCV evaluation method reliable on. Seventeen diodes and photocells which are included in this device make determination process of erythrocytes volume to total blood volume easiest and more accurate. Finally using of programmable Arduino board 2560 mega (with determined mathematical equations which are stored in Arduino memory) to calculate and screen PCV and Hb (hemoglobin) values, it makes analysis of PCV blood reliable and simple treatment.هناك العديد من الطرق المباشرة وغير المباشرة لقياس النسبة الحجمية لكريات الدم الحم ا رء نسبة الى حجم نموذج الدم الكلي, ولكن تبقى طريقة المسطرة اليدوية هي الاسهل والاقل كلفة على الرغم من احتمالية للخطا البشري. في بحثنا هذا عمدنا الى تصميم وتنفيذ دائرة الكترونية لمعالجة (mega 2560)Arduino تسنخدم المسيطر الدقيق الاشارة وقياس حجم كريات الدم الحم ا رء المضغوطه. الفرق بين الشدة العالية للشعاع المنبعث من بلازما الدم )الجزء الشفاف من نموذج الدم بعد فصله بأستخدام الطرد المركزي بسرعة 01111 دورة بالدقيقة( مقارنة مع الشدة الواطئة جدا للشعاع المنبعث من الجزء الاحمر الغامق )المتكون من كريات الدم الحم ا رء المضغوطة( بعد امتصاص نسبة عالية منه بوساطة كريات الدم, يجعل النتائج المستحصلة بهذه الطريقة بلامكان الاعتماد عليه. جهاز القياس الجديد يتكون من خمسة عشر من بواعث الضوء الاحمر )بحدود طول موجي 011 نانومتر(على احد جانبي الانبوب الشعري وذلك للاستفادة من الامكانية الانتقائية العالية لامتصاص هذا الضوء بوساطة خلايا كريات الدم الحم ا رء المضغوطة مقارنة بأقل مقدار من الامتصاصية للضوء بذات الطول الموجي بوساطة بلازما الدم. هذا الضوء المنبعث )غير الممتص( سيتم استقباله بوساطة الخلايا الضوئية على الجانب الاخر من الانبوب الشعري لنموذج الدم ومن ثم فان الاشارة الناتجة من تحسس 2560 بما Arduino board هذا الضوء ستعالج ببرنامج ياذن ببدا قياس أرتفاع كريات الدم المضغوطة الى الحجم باستخدام المعادلات Hb و PCV الكلي ومن ثم قياس قيمة ذات العلاقة المخ زنه في الذاكرة واستع ا رض هذه النتائج على وعرضها بطريقة سهلة وسريعة


Article
Study the Molar Ratio of the Reaction between Thalassemia s Drug (Deferoxamine) with Iron Over loud

Authors: Amer Hasan Abdullah
Pages: 21-25
Loading...
Loading...
Abstract

Iron-Deferoxamine complex have been synthesized in vitro by the reaction of deferoxamine (which are use as therapeutic agent for removing iron overload from the bodies of thalassemia patients) with Fe(II) salt in aqueous medium. The geometry of the prepared complex as well as the mode of bonding were determined through FTIR, UV-Vis, mass spectral studies, metal content, and molar conductance. These studies revealed octahedral geometry for the complex with the general formula [FeII (DEF)]Cl2. Complex formation via molar ratio method and variation continuous method in aqueous solution have been also investigated and results were consistent to those found in the solid complexes with a ratio of (M:L) as (1 : 1). Conditional formation constant could also be calculated for [FeII (DEF)]Cl2 as 2.0 × 103. The effect of time on the formation of Iron – Deferoxamine complex has been also studied. This study showed that each 1×10-3M of deferoxamine needs 2.5 – 3 hrs to remove 1×10-3M of Iron (II) by formation coordination complex.تم تحضير معقد )ديفيروكسامين الحديد( خارج النظام – الحياتي من تفاعل الديفيروكسامين والمستخدم كمادة علاجية تعمل على إ ا زلة الحديد ال ا زئد من أجسام مرضى الثلاسيما مع ملح الحديد في وسط مائي. طبيعة التاصر والشكل الهندسي للمعقد تم تحديد من خلال استخدام تقنية الأشعة تحت الحم ا رء البعيدة ومطايف فوق البنفسجية المرئية ود ا رسة – طيف الكتلة ومحتوى المعقد من عنصر الحديد) III ) ودراسة التوصيلة المولارية وكشفت الد ا رسة إن شكل المعقد هو ثماني السطوح وان الصيغة العامة للمعقد هو [[FeII (DEF)]CI2 تكون المعقد بطريقة النسب المولارية وطريقة النسب المتغي ة ر تم التحقق منها في الوسط المائي وكانت النتائج متطابقة مع الحالة الصلبة للمعقد كذلك وكانت النسب بين الايون المركزي والليكند ) L: M ) ( يمثل ) 1:1 وثابت التكوين المقاس للمعقد [[FeII (DEF )]CI2 هي 2.0 × 103 وقت تكوين المعقد ديفروكسامين الحديد تم – د ا رسته أيضا وأظهرت الد ا رسة إن كل 1×10-3 مولاري من ديفروكسامين تحتاج 3-2,5 ساعة لإ ا زلة 1×10-3 مولاري من الحديد ) II ( عن طريق المعقد ألتناسقي.

Keywords


Article
DFT Based Simulations Study for Comparative Prediction of Reactivity and Stability of Thiadiazoles

Authors: Zeyad Fadhil --- Anwar Hussein
Pages: 26-31
Loading...
Loading...
Abstract

HOMO and LUMO energies and thermodynamics of a set of thiadiazoles have been evaluated based on Density Functional Theory (DFT) at B3LYP level of theory at 6-31G* in the Gaussian program. The results of HOMO density of frontier orbitals indicate that thiadiaoles, sequence of donor ability is in the order, 2-methyl-1,3,4-thiadiazole > 2,5-dimethyl-1,3,4-thiadiazole > 5-methyl-1,3,4-thiadiazol-2-amine > 1,3,4-thiadiazol-2-amine > 1,3,4-thiadiazole-2,5-diamine. The electron charge density allowed to find out different molecular properties such us the electrostatic potential and the dipole moment, which were finally subject to a comparison leading to a good match obtained between studied molecules. The intramolecular charge transfer has also been confirmed by an HOMO-LUMO analysis.طاقات أعلى مدار جزيئي مشغول وطاقات أدنى مدار جزيئي غير مشغول والتي يرمز له اختصا ا ر HOMO و LUMO للمدا ا رت الجزيئية من حيث شغلها بالإلكترونات لمجموعة من الثايوديازولات تم تقيمها بالاعتماد على نظرية دالة الحالة Density Functional Theory (DFT) باستخدام المستوى B3LYP level of theory at 6-31G* باستخدام برنامج كاوسين Gaussian program . نتائج ال HOMO و LUMO للجزيئات المدروسة اعتمادا علة قابلية هبة الالكترونات والاستق ا ررية بالترتيب التالي . 2-methyl-1,3,4-thiadiazole > 2,5-dimethyl-1,3,4-thiadiazole > 5-methyl-1,3,4-thiadiazol-2-amine > 1,3,4-thiadiazol-2-amine > 1,3,4-thiadiazole-2,5-diamine. . ان كثافة شحنة الإلكترون سمحت بمعرفة الخصائص الجزيئية المختلفة مثل ثنائي القطب وغيرها من الدوال والتي كانت في النهاية حققت معرفة تامة لنا لعلاقات الجزيئات المدروسة وتاثير المجاميع المعوضة والتي شملتها الد ا رسة

Keywords

Thiadiazole --- DFT --- HOMO --- LUMO


Article
Evaluation of Ligand Competitive Ability for Binding in Mixed Ligand Complex

Authors: Salah Aldin Jassim
Pages: 32-40
Loading...
Loading...
Abstract

In this work, several attempts were carried out to evaluate the formation of mixed ligand complex from 1-10 phenanthroline (phen.) and dimethylglyoxime (DMG) with zinc ion. Complex formation tested using both FTIR and1H NMR techniques supported by density functional theory calculations (DFT) to investigate the mulliken charges of both free ligands and their corresponding mixed ligand complex to determine the competitive ability of each ligand toward zinc ion and to study the possibility of the synthesis of mixed ligand complex. Results obtained show that 1-10 phen. ligand binds stronger than DMG. Octahedral geometry of the complex was observed involves 2:1 mole ratio of L:M in addition to 2 mole of chloride ion.في هذا البحث تم اج ا رء العديد من المحاولات لتحضير معقدات الخارصين مع خلائط الليكاندات المكونة من 1-10 phenanthroline (phen.) و dimethylglyoxime (DMG) لتقييم القدرة التنافسية لهذه الليكاندات للارتباط مع الايون الفلزي وفحص امكانية تكوين هذا المعقد باستخدام تقنيات FTIR و H1 NMR ومدعمة بالحسابات النظرية وبطريقة نظرية دوال الكثافة (DFT) لتحديد قيم mulliken charges لكل من الليكاندات بشكلها المنفرد وعند خلطها في معقد الخارصين وبالتالي د ا رسة قوة ارتباطها ومدى امكانية تحضير المعقدات المختلطة. النتائج المستحصلة من هذا البحث ان الليكاند 1-10 phen ارتبط بشكل اقوى بكثير من الليكاند DMG وحصيلة الشكل الهندسي لهذا المعقد تثبت مقدار وقوة التنافس بين هذه الليكاندات تجاه ايون الخارصين حيث ارتبط المعقد من خلال مولين من 1-10 phen مع الزنك وبوجود مولين من ايون الكلوريد.


Article
Synthesis and Characterization of New Complexes Fe(II), Co(II) and Ni(II) Ions with Azo Ligand Derived from 4-Aminoantipyrene

Loading...
Loading...
Abstract

The ligand (4-(7-hydroxy-4-methylcoumarin-8-ylazo)-1-phenyl-2,3-dimethyl pyrazol-5-one 4-yl) derived from 4-aminoantipyrine and 7-hydroxy-4-methyl coumarin. The synthesized ligand was characterized by 13C, 1HNMR, FT.IR and UV-Vis spectra. Complexes of Fe(II), Co(II) and Ni(II) with the ligand were prepared in aqueous methanol with a (1:2) M:L ratio. The prepared complexes have been characterized by using flame atomic absorption, FT.IR, UV-Vis spectra as well as magnetic susceptibility and conductivity measurements. On the basis of physicochemical data octahedral geometries were attributed for the complexes.هيدروكسي 4 مثيل كيومارين - - - - ( حضر الليكند ) 4 – - - - - - - - 8 ايل ازو( 1 فنيل 2,3 ثنائي مثيل بايروزول 5 - - - - - اون 4 ايل( من 7 هيدروسي 4 ميثل كومارين و 4 امينو انتي بارين و شخص الليكاند المحضر بواسطة اطياف الرنين النووي المغناطيسي و الاشعة تحت الحم ا رء و فوق البنفسجية المرئية. حضرت معقدات الحديد و الكوبلت و – النيكل الثنائية الشحنة مع الليكاند في وسط الميثانول وبنسبة فلز: ليكاند (2:1) ، شخصت المعقدات المحضرة باستخدام اطياف الاشعة تحت الحم ا رء و فوق البنفسجية المرئية و – تقنية الامتصاص الذري، فضلا عن قياسات الحساسية المغناطيسية و الت وصيلية الكهربائية و من النتائج المحصول عليها تم اقت ا رح الشكل الثماني السطوح للمعقدات المحضرة.


Article
Geochemical Characteristics and Modeling of Conventional Petroleum System of Majnoon Oil Field, South Iraq

Loading...
Loading...
Abstract

Organic geochemical analysis and model set–up to simulate the genetic relationships among 18 crude oil samples recovered from different formations and various oil fields within Amara city South Iraq, with depths approximately begin from 2167 to 4430 m, ages of marine carbonates sourced from Middle Jurassic age (Sargelu Formation) according to geochemical similarities appointed previously for this period. The levels of maturation are relatively varied for each sample from low to moderate, MJ-1, MJ-18 (Hartha Formation), MJ-3, MJ-10 (Mishrif Formation), MJ-9 (Nahr Umr Formation), MJ-15 (ZubairFormation), MJ-2, MJ-19(Nahr Umr Formation MJ- 10,MJ-11(Zubair Formation) MJ-3 (Nahr Umr Formation), Mj-3 (Sulaiy Formation), MJ-12 (two samples) Sulaiy Formation MJ-11, MJ-2 (Nahr Umr Formation), MJ-2 (Zubair Formation), MJ-11 (Sulaiy Formation )of Amara city Oil fields. These samples suggest the ages and paleoenvironments of their source rocks. The samples were collected from Upper Jurassic to Cretaceous reservoirs of 18 developed oil fields where about 15 billion barrels of recoverable oil have been reserved. The oil density varies in rather wide range, between 12.2 and 39.2 API. Twelve oil samples are ˂25 API referring to heavy oil and only oil samples attained defiantly from 25 to 35API are medium oil. Canonial Variables (CV) range attain to (- 1.89 to – 3.99) of waxy oil. According to the Tissot and Welte’s classification (1984), most of the oils can be classified as ‘‘high sulfur’’ oils/indicate that these samples are of marine origin. Stable Carbon Isotope Composition C15+ Saturate and Aromatic is relatively approximate values giving good supporting evidences for the same family which is Middle Jurassic Age (sourced from Sargelu Formation), generated within the sedimentation of the bituminous calcareous shale and Limestone in Mesopotamian basin. This basin consider as one of the most formative, potential and promising basin in the Middle East according to the typical petroleum system elements. This family was generated by marine carbonate - intrashelf sub basin source rocks, occurring in Jurassic – Cretaceous – Neogene reservoir rocks of Mesopotamian basin which are geochemically similar to the extracts from Middle –Upper Jurassic age (Sargelu Formations), yielding the majority of petroleum oil and gas fields in north and south Iraq. Petroleum system modeling in one dimension (1-D Petro Mod) was performed using Petro Mod basin modeling software which developed by Integrated Exploration System (IES) to demonstrate burial thermal history hydrocarbon generation and expulsion for Majnoon oil field so that 1-D Petro Mod was applied to Nine wells (Mj-2, Mj-3, Mj-4, Mj-8, Mj-9, Mj-11, Mj-12, Mj-15, and Mj-19) following the procedure of Pitman et al 2004.تحاليل الجيوكيماء العضوية وبناء موديلات تحاكي العلاقات الاحيائية بين ثمانية عشر من نماذج النفط الخام المستخلصة من تكاوين جبولوجية متعددة ومن حقول نفطية ضمن مدينة العمارة جنوب الع ا رق وبأعماق تقريبية تبدأ من 2167 - 4430 م, ومن اعمار لصخور كاربونية بحرية تعود للعصر الجو ا رسي المتوسط حسب التشابه الجيوكميائي مع صخور تلك الفترة والمحددة في د ا رسات سابقة. ان مستوى النضج يختلف بشكل نسبي لكل عينة من الواطئ الى المتوسط بئر مجنون - 1 ومجنون- 18 )تكوين الهارثة( وبئر مجنون- 3 ومجنون- 10 )تكوين مشرف( ومجنون- 9 )تكوين نهر عمر( ومجنون - 15 ))تكوين الزبير( وبئريي مجنون- 2 و 19 )تكوين نهر عمر( ومجنون- 10 و 11 )تكوين الزبير( ومجنون 3 تكوين نهر عمر ومجنون - - 3 )تكوين السلي ( ومجنون- 11 ومجنون- 2 )تكوين نهر عمر( ومجنون - 2 )تكوين الزبير( ومجنون- 11 )تكوين السلي( من حقول النفط في مدينة العمارة. هذه النماذج توحي بالاعمار والبيئة الترسيبية القديمة للصخور المصدرية. تم جمع النماذج من مكامن الجو ا رسي الاعلى الى العصر الطباشيري لثمانية عشر بئرتم تط ويرها حيث تحوي على احتياطي نفطي يقارب 15 بليون برميل قابل للاستخ ا رج. كثافة النفط API لها مديات اختلاف واسعة تت ا رح ما بين 12,2 , 39 API . اثنا عشر منها اقل من 25 درجة مما تشير الى نفط ثقيل وفقط هناك نموذج تت ا روح فيه الاي بي اي ما بين 25 الى 35 درجة ويعتبر من النفوط الوسط اوالمعتدلة. Canonical Variable (C.V) بلغ ) 1.89- الى 3.99 (. من النفط الشمعي. بالاستناد الى تصنيف تيسوت وفلته ) 1984 ( معظم النفوط يمكن ان تصنف عالية الكبريت مما يدل على انها من اصل بحري. مكون نظير الكاربون المستقر المشبع والاروماتي تكون ذات قيم متقاربة وتعطي قادت الى اعطاء دلائل جيدة على كونها من عائلة موحدة والمتمثلة بالعصر الجو ا رسي المتوسط )والي يمثله كصخور مصدرية جيدة هو تكوين ساركلو( المتولد من ترسبات حجر السجيل الجيري البتيوميني مع حجر الجيري حوض ال ا رفدين. ان هذا الحوض يعتبر واحدا من اكثر الاحواض الرسوبية تمي ا ز ومولدا وواعدا لتوليد النفط في الشرق الاوسط حسب توافر عناصر اجمالي Ahmed Askar Al Ahmed 65 النظام النفطي النموذجي. ان هذه العائلة تولدت بفعل ترسب الكاربونيت البحري لصخور ساحلية متداخلة لأشباه احواض كونت مكامن من الفت ا رت العصر الجو ا رسي الطباشيري والى – العصر الحديث ال Neogene في حوض وادي ال ا رفدين والذي يشابه من الناحية الجيوكيميائية للنفط المستخلص من عصر الجو ا رسي المتوسط والاعلى اولمتمثل بتكوين ساركلو والناوكليكان والذي يولد معظم نفط الع ا رق. موديل النظام النفطي ذو الاتجاه الواحد تم انجازه باستخدام نظام Petro Mod والمطور من نظام الاستكشاف المتكامل ) IES ( والذي يظهر بوضوح تاريخ الدفن الح ا رري وتكوين الهيدروكاربونات لحقول مجنون Mj-2,3,4,8,9,11,12,15,19 بالاستناد الى ما اتبعته Pitman واخرون 200


Article
A Quantum Circuit for Three Quantum Bits to Produce Quantum Entanglement States (ML- Quadripartite)

Authors: Mezher B. Saleh --- Loay E. George
Pages: 66-70
Loading...
Loading...
Abstract

In this research, a quantum system consists of three qubits is considered; it has eight states (ǀ000˃, ǀ001˃, ǀ010˃, ǀ011˃, ǀ100˃, ǀ101˃, ǀ110˃ and ǀ111˃). Each of these states is passed through a quantum circuit made of a sequence of quantum gates. The circuit applies X- gate on the first qubit from the left, then using CNOT-gate on the first and second qubits and using the Hadamard-gate on the first qubit. Finally, Hadamard–gate is applied on the third qubit. When the state ǀ000˃ is passed as input through the proposed quantum circuit then the output includes four entanglement states; for the other input states the output will be another non-repeatable entanglement states. So, for using all states in quantum circuit the result will be eight equations each one consists of four entanglement states; which called ML- Quadripartite.في هذا البحث، نظام كمي يتكون من ثلاثة كيوبتات. (ǀ000˃, ǀ001˃, ǀ010˃, ǀ011˃, لديها ثماني حالات كل من هذه الحالات .)ǀ100˃, ǀ101˃, ǀ110˃ ǀ111˃ يتم تمريرها من خلال دائرة كمية مصنوعة من سلسلة من على الكيوبت الاول X البوابات الكمية. الدائرة تطبق بوابة على الكيوبتين الأول CNOT من اليسار، ثم استخدام بوابة والثاني ومن ثم نستخدم بوابة هادمرد على الكيوبت الأول. وأخي ا ر، يتم تطبيق بوابة هادمرد على الكيوبت الثالث. عندما كمدخل عبر الدائرة الكمية المقترحة ǀ000˃ يتم تمرير الحالة يتضمن الإخ ا رج أربع حالات متشابكة. بالنسبة لحالات الإدخال الأخرى فان الاخ ا رج سيكون حالات تشابك اخرى غير مكررة. لذلك، عند استخدام جميع الحالات في دائرة الكم فان النتيجة ستكون ثمانية معادلات تتكون كل واحدة من أربع الرباعية. -ML حالات التشابك، التي سميت


Article
Structural and the Optical Properties of Graphene Prepared by Electrochemical Exfoliation Technique

Loading...
Loading...
Abstract

In this research, graphene suspension was prepared by electrochemical exfoliation of graphite electrodes immersed in aqueous solution which contains sulfuric acid, nitric acid and distilled water (H2SO4/HNO3/H2O). DC biases of 10 V have been applied and the graphene foam was deposited on glass slide. The structural and optical properties of graphene was characterized via X-ray diffraction (XRD), scanning electron microscope (SEM), energy dispersive spectroscopy (EDS), optical microscopy (OP) and Uv-Vis spectroscopy respectively. The XRD pattern shows crystalline structure of graphene with sharp peak at 26.59o corresponds to an interlayer distance of 0.334 nm of (002) orientation which matching with the interlayer distance of normal graphite. The SEM of graphene was showed that thin layered graphene structures with wrinkled shapes. The compositions of graphene consist of carbon and oxygen with atomic percentages 82.75% and 12.01%, respectively. The absorbance spectra using UV-VIS was exibited the graphene suspension and graphene film have two transitions included π-π* and n- π* respectively.في هذا البحث, تم تحضير عالق الك ا رفين بواسطة التقشير الكهروكيمياوية لأقطاب الج ا رفيت المغمورة في محلول مائي لحامض الكبريتيك وحامض النتريك وماء مقطر ( H2SO4/HNO3/H2O (. تم تسليط فرق جهد من نوع انحياز DC بقيمة 10 V و تم ترسيب رغوة الك ا رفين على لوح الزجاج. الخصائص التركيبية والبصرية للك ا رفين شخصت عن طريق حيود الاشعة السينية) (XRD والمجهر الالكتروني الماسح ) SEM ( ومطياف المشتت للطاقة ) EDS ( والمجهر الضوئي) (OP ومطياف الضوئي بالمنطقة الفوق البنفسجية والمرئية Vis) - (Uv على التوالي. اظهر نموذج حيود الاشعة Journal of Al-Nahrain University Vol.19 (4), December, 2016, pp.71-77 Science 77 السينية للتركيب البلوري للك ا رفين قمة حادة عند 26.59o والتي تقابل مسافة بين المستويات تساوي 0.334 nm بتجاه (002) تتوافق مع المسافة بين المستويات للج ا رفيت الطبيعي. اظهر فحص SEM لت ا ركيب الك ا رفين بانه متكون من طبقات قليلة مع وجود اشكال متجعدة. البنية التركيبية للك ا رفين تتكون من كاربون واكسجين بنسب ذرية 82.75 % و 12.01 % على التوالي. اظهرت اطياف الامتصاص بواسطة Uv-Vis لعالق الك ا رفين وغشاء الك ا رفين يمتلك انتقالين تضمنت π-π * و n- π * على التوالي.


Article
Effect of Electrodes Separation in DC Plasma Sputtering on Morphology of Silver Coated Samples

Authors: Khalid A. Yahya --- Ban F. Rasheed
Pages: 78-85
Loading...
Loading...
Abstract

In this work, the effect of the electrodes separation on plasma parameters and morphology properties for coated glass samples by silver metal using low voltage DC discharge plasma sputtering source. At fixed argon gas pressure 0.2 mbar and discharge currents Id(20,30,40,50 and 60)mA, for different electrodes separation d (3,4,4.5,5,6)cm was studied. The plasma sputtering source consists of a cylindrical chamber including two circular electrodes made from stainless steel. The cathode electrode is carrying the silver metal as a target and permanent magnet, while a glass sample coater is placed on the anode electrode. The plasma parameters: temperature of electron(Te) and ion density(ni) were determined by using cylindrical single Langmuir probe. Also, the surface morphology for the coater samples were studied by atomic force microscope (AFM). The results of this work shown that a linear increases in ions density and an exponential decreasing in electron temperature for different electrodes separation. Furthermore, the relationship between the average grain diameter and average grain height as a function of electrodes separation are nonlinear. The minimum average grain diameter is (90 nm) at d=4 cm for Id=40 mA and minimum average grain height is (5.5 nm) at the same electrodes separation and discharge current. When the temperature of electron increased, the values of average grain diameter increased while the values of average grain height decreased.تم في هذا العمل, د ا رسة تأثير المسافة بين القطبين على معلمات البلازما وخصائص اشكال سطح النموذج المطلي بالفضة باستعمال مصدر للترذيذ البلازمي للتفريغ عند الفولتيات الواطئة المستمرة في الترذيذ البلازمي بضغط غاز الاركون الثابت ) 0.2 ( ملي بار لتيا ا رت التفريغ ( 20,30,40,50,60 ( ملي امبير لعدة مسافات بين القطبين ( 3,4,4.5,5,6 ( سم. يتكون مصدر الترذيذ البلازمي من حجرة اسطوانية تحتوي على قطبين دائرين مصنوعين من مادة الستنلس ستيل. قطب الكاثود يحمل مادة الهدف والمغناطيس الثابت بينما يوضع النموذج الزجاجي لطلائه على قطب الانود. عوامل البلازما, درجة ح ا ررة الالكترون وكثافة الايونات تم تحديد باستعمال مجس لانكمور الاسطواني المنفرد وايضا درست خصائص اشكال سطوح النماذج المطلية بواسطة مجهر القوة الذرية. أوضحت نتائج هذا البحث زيادة خطية في كثافة الايونات ونقصان بدالة أسية في درجة ح ا ررة الالكترون بزيادة المسافة بين القطبين. كما ان العلاقة بين معدل قطر الحبيبة وارتفاعها كدالة غير خطية للمسافة بين القطبين. اقل معدل قطر الحبيبة وارتفاعها هو ) 90 ( نانومتر عند المسافة (4) سم وبتيار تفريغ ) 40 ( ملي امبير, واقل معدل ارتفاع الحبيبة هو ( (5.5 نانومتر بنفس المسافة بين القطبين وتيار التفريغ. عند زيادة درجة ح ا ررة الالكترون فان قيم معدل قطر الحبيبة يزداد ويقل ارتفاعها.


Article
Nucleon Momentum Distributions and Elastic Electron Scattering form Factors for 54Fe, 56Fe and 58Fe Isotopes

Authors: Ahmed N. Abdullah
Pages: 86-93
Loading...
Loading...
Abstract

The nucleon momentum distributions and elastic electron scattering form factors of the ground state for some 1f-2p shell nuclei, such as 54Fe, 56Fe and 58Fe isotopes, have been studied utilizing the Coherent Density Fluctuation Model formulated by means of the fluctuation function (weight function). The fluctuation function has been connected to the nucleon density distribution of the nuclei and obtained from the theory and experiment. The feature of the long-tail behavior at high momentum region of the nucleon momentum distributions has been determined by both the theoretical and experimental fluctuation functions. The calculated elastic electron scattering form factors for considered isotopes are in a good agreement with those of experimental data throughout all values of momentum transfer q.تم حساب توزيعات زخم النيكليون ) NMD ( للحالة الارضية وعوامل التشكل للاستطارة الالكترونية المرنة لبعض النوى الواقعة ضمن القشرة النووية 1f-2p مثل نظائر الحديد 54Fe ، 56Fe و 58Fe وفقا لانموذج تموج الكثافة المت ا ربط الذي يعبر عنه بدلالة دالة التموج (| ( )| ) . لقد تم التعبير عن دالة التموج بدلالة توزيعات كثافة النيكليون وتم حسابها من النتائج النظرية والعملية. تميزت نتائج توزيعات زخم النيكليون )المستندة على دالة التموج النظرية والعملية( بخاصية الذيل الطويل عند قيم الزخوم العالية. أظهرت هذه الد ا رسة بان النتائج النظرية لعوامل التشكل للاستطارة الالكترونية المرنة لنظائر الحديد 54Fe ، 56Fe و 58Fe والمحسوبة بأنموذج التموج المتشاكه تتفق مع النتائج العملية ولكل قيم الزخم المنتقل.


Article
Bonding Behavior of Brazing Al2O3 / ZrO2 Composite to Kovar Alloy

Authors: Thamir A. Jumah
Pages: 94-102
Loading...
Loading...
Abstract

The production of a reliable joint between alumina composite and kovar alloy by brazing technique using an active filler foil consist of (Ag 70%wt., Cu 28%wt., and Ti 2%wt.). Decontamination processes were achieved over all research specimens. Wetting and bonding behavior were attempted at different condition. Active filler is well brazed with the kovar alloy where the Young angle is (33), while poor wettable achievement appear on the ceramics surfaces where the values of Young angle are between (70 ) to (80 ). Good bonding obtained with the assembly of (K / 2a / AZ15) where the optimum bonding strength obtained is (90 Mpa), and the fracture occurred from the ceramic and ceramic – filler interface. New structural phases are established at the interlayer of bonded area when subjected to the XRD technique. The new phases enhancement the bonding strength of the kovar bonded alumina composite. The fractured area was subjected to the test of SEM technique then notice the active filler was diffused into alumina composite. This phenomenon gives indicate that the reliable joint was due to the diffusivity of active filler into alumina composite and then enhanced the joint strength.يتضمن مشروع البحث تصنيع مفصل لحام متين بين مت ا ركب الالومينا وسبيكة الكوفار باستخدام تقنية لحام المونة المكونة من 07 % فضة و 82 % نحاس و 8% تيتانيوم. اجريت عمليات ا ا زلة الملوثات عن سطوح المواد المزمع لحامها وتهيئتها لعملية الربط. تم اختبار عملية التبليل والربط بين المواد باستخدام ظروف عمل مختلفة؟. تبين ان الحشوة الفعالة لها قابلية تبليل جيدة لسبيكة الكوفار حيث حصلنا على ا زوية يونك مقدارها 33 درجة بينما اظهرت الحشوة المالئة قابلة تبليل واطئة نوعا ما لكافة سطوح الس ا رميك وكانت قيمة ا زوية يونك تت ا روح بين 07 درجة و 27 درجة. ان افضل مقاومة ربط حصلنا عليها ) 07 ميكا باسكال( عند استخدام المجمع اللحامي المتكون من سبيكة الكوفار وحشوة مالئة ومت ا ركب الالومينا الذي يحتوي على 51 % زركونيا. لوحظ كذلك ان المفصل اللحامي قد كسر اثناء فحصه من منطقة السي ا رميك وايضا من المنطقة البينية بين السي ا رميك والحشوة الفعالة. عند فحص منطقة اللحام بوساطة منظومة حيود الاشعة السينية تبين وج ود اطوار جديدة ضمن البنية التركيبية للمفصل اللحامي وهو ما يعزز متانة الربط التي حصلت بين مت ا ركب الالومينا وسبيكة الكوفار. اجريت فحوصات بوساطة المجهر الالكتروني فتبين وجود انتشار لمكونات الحشوة الفعالة داخل المنطقة السحية لمت ا ركب الالومينا وهذا بدوره قد عزز الربط المحكم بين المواد المت ا ربطة.


Article
Preparation and Characterization of PSi/Si Electrochemically Formed as Photodetectors

Authors: Doaa S. Jbaier
Pages: 103-112
Loading...
Loading...
Abstract

Porous silicon were constructed electrochemically with various form ationtimes (5, 10, 15 and 20) min with current density 20mA/cm2 on p-type silicon. The influence of formation time on the structural and morphological properties have been presented by using SEM and optical microscopy. The SEM analysis was showed that the porous silicon layer has a uniform structure and this structure varied with increasing the etching time. The optical microscope was carried out to study the thickness, the pore diameter and etching rate of porous silicon layer, we have found the porous silicon thicknessis accretion with excess the formation time and pores diameter increased also. The etching rate was found to increase from 1.25 to 1.53 μm/min. The electrical properties of PSi samples which represented by I-V characterization under dark show that when the etching time increased the current which pass through the layer of porous silicon decreased because of increasing the resistivity of PSi surface. From I-V charecteristics PSi layer show a good rectification and high responsivity for visible and near IR region.السيليكون المسامي تم تحضيره بالطريقة الكهروكيميائية وبأزمان تحضير ) 5 و 01 و 05 و 01 ( دقيقة وبكثافة تيار 01 ملي امبير/سم 0 على السيليكون نوع P . تأثير زمن التشعيع على الخصائص التركبيبية والطبوغ ا رفية درست باستخدام المجهر الالكتروني الماسح والمجهر الضوئي. أظهرت نتائج المجهر الالكتروني الماسح ان السيليكون المسامي الناتج ذو شكل منتظم وطبيعة الشكل تتغير بتغير زمن التشعيع. المجهر الضوئي تم استخدامه لد ا رسة سمك السطح، قطر المسام بالاضافة الى معدل التاكلفي طبقة السيليكون وجدنا أن سمك السيليكون المسامي يزداد بزيادة زمن التشعيع بالاضافة الى قطر المسام يزداد كذلك بزيادة زمن التشعيع. معدل التاكل وجد انه يزداد من 0.05 الى 0.51 مايكرون/دقيقة. الخصائص الكهربائية لعينات السيليكون المسامي والمتمثلة بخصائص تيار جهد تحت - الظلام بينت ان عند زيادة زمن التشعيع يقل التيار المار خلال طبقة السيليكون المسامي بسبب زيادة مقاومة سطح السيليكون المسامي. من خصائص تيار جهد لسطح – السيليكون المسامي تبين انه يظهر تقويم جيد واستجابية عالية عند المنطقة المرئية وتحت الحم ا رء الق ريبة .


Article
Molecular Characterization and Genetic Variability of Trichoderma Harzianum Isolates by Using PCR-RAPD Markers

Authors: Alaa Mohsen Al-Araji
Pages: 113-121
Loading...
Loading...
Abstract

The PCR-based technique of randomly amplified polymorphic DNA (RAPD) was used to characterize and assess the genetic relatedness of eight Trichoderma harzianum isolates. Genomic DNA of each species was extracted at a final concentration of 400 - 600 μg / 2-3 g of wet mycelium and at a purity of 1.6-1.8. Each DNA sample was amplified with each of 15 primers and the products were resolved electrophoretic ally on 1.2% agarose gel, stained with ethidium bromide and photographed under UV. Six primers failed to support amplification while the remaining nine primers produced a total of 128 main bands (11-20 per primer) across the eight isolates. Of these bands, 120 (9-19 per primer) were polymorphic. The least efficient primer was OPY-19 (8.59), while the most efficient one was OP-B14 (15.63%). Primer OP-Y19 had the lowest (7.5%) discriminatory power while primer OP-B14 had the highest (15.8%). RAPD analysis fingerprinted six of the eight isolates through unique bands with one or more of the 9 primers. Cluster analysis based on the genetic distances split the eight isolates into two major group genotypes.استعملت تقنية RAPD المعتمدة على تفاعل PCR للتوصيف الجزيئي وتقييم العلاقة الو ا رثية لثمان عزلات من الفطر Trichoderma harzianum . وجرى استخلاص الدنا من كل عزلة وبتركيز نهائي قدره 044 044 مايكروغ ا رم لكل 3 2 غم من الغزل الفطري - – الرطب وبنقاوة 6.1 6.0 . وجرى مضاعفة كل عينة من – عينات الدنا بواسطة 61 بادئا واظهرت النتائج بالترحيل كهربائيا خلال هلام الاكاروز ذي التركيز 6.2 % والمصبغ بالمادة المتألقة بروميد الايثيديوم والتصوير تحت الاشعة فوق البنفسجية U.V.) (. أخفقت ست بادئات في دعم عملية التضاعف لاي دنا مجيني بينما انتجت البادئات التسعة المتبقية ما مجموعه 128 حزمة دنا رئيسية )بمعدل 6 1 - 20 لكل بادئ( للعزلات الفطرية الثمانية. ومن هذه الحزم كانت 624 حزمة متباينة )بمعدل 69 9 لكل بادئ(. وكان اقل - البادئات كفاءة في اسناد التضاعف هو البادئ OPY-19 )بكفاءة 8.59 %(، بينما الاكثر كفاءة كان OP-B14 )بكفاءة 15.63 %(. البادئ OP-Y19 حقق اقل قوة تمييزية ) 7.5 %( بينما البادئ OP-B14 حقق اعلى قوة تمييزية ) 15.8 %(. ساعدت تقنية RAPD من تحديد البصمة الو ا رثية لستة عزلات من الثماني عزلات المدروسة من خلال ظهور حزمة مؤشرة فريدة حين مضاعفة الدنا من كل عزلة من هذه العزلات مع واحد او اكثر من البوادئ التسعة اعلاه. التحليل العنقودي للمسافات الو ا رثية للعزلات الثمانية قسمها الى مجموعتين رئيسيتين من الطرز العرقية.


Article
Effect of Toxoplasmosis on Lipid Profile and Thyroid Hormones in Aborted Women

Authors: Maisam Balasim Al-Khamesi
Pages: 122-126
Loading...
Loading...
Abstract

This study addressed the effect of toxoplasmosis on levels of thyroid hormones (Triiodothyronine [T3], Thyroxine [T4] and Thyroid Stimulating Hormone [TSH], and lipid profile such as (Cholesterol, Triglycerides, High-Density Lipoprotein [HDL], Low-Density Lipoprotein [LDL] and very Low -Density Lipoprotein [vLDL] in 100 samples which included 80 aborted women, who had positive test for toxoplasmosis and 20 samples act as control group during the period from August 2015 to January 2016 which were taken from Al-Yarmouk Teaching Hospital in Baghdad City. Infected and control women had similar age that ranged between (17-47) years old. Serum samples were collected and tested by ELISA technique, lipid profile tests were performed by using commercial kits, in addition to measured thyroid hormones by using the Mini Vidus apparatus. The results revealed chronic infection [IgG] recorded the highest percentage (68.75%) and the acute infection [IgM] showed the lowest percentage (31.25%). There were significant decrease in the total cholesterol, Triglycerides, LDL and vLDL (110.96±1.55, 30.93±0.56, 41.38 ±1.55 & 6.40 ±0.18 mg/dl respectively) compared with control group (200.05 ±5.83, 56.05 ±1.98, 142.85±2.05 & 36.90±1.24 mg/dl respectively). On the other hand, a significant increase in HDL, T3 and TSH was recorded (64.51±1.27 mg/dl, 12.74 ±0.53 and 11.64±0.58 mlU/L respectively) compared with control group (53.45±1.57 mg/dl, 1.49 ±0.16 & 2.29 ±0.25 mlU/L respectively). A significant decline in T4 was estimated (2.81±0.12 mlU/L) compared with control group (8.35±0.80 mlU/L). So, we concluded that the Toxoplasma gondii had important role in changes of lipid profile levels & thyroid hormones in infected womenتناولت الد ا رسة تأثير الأصابة بداء المقوسات الكوندية على مستويات هرمونات الغدة الدرقية ) T3 و T4 و TSH ) اضافة الى فحص مستويات الدهون مثل )الكولستيرول، الدهون الثلاثية، HDL ، LDL ، vLDL ( ل 011 عينة حيث تضمنت 01 عينة لنساء مجهضات والتي اعطت نتيجة موجبة للمرض و 01 عينة عدت مجموعة سيطرة للفترة الممتدة من شهر آب 0102 ولغاية شهر كانون الثاني 0102 ، حيث جمعت من مستشفى اليرموك التعليمي في مدينة بغداد. كان لدى المجموعتين من النساء اعمار متشابهة حيث ت ا روحت بين ) 71 01 ( سنة. جمعت العينات وتم فحصها - بأستخدام تقنية ال) ELISA ( ، وفحص مستويات الدهون بأستخدام عدد فحص تجارية، اضافة الى قياس هرمونات الغدد الدرقية بأستخدام جهاز Mini-Vidas . كشفت النتائج ان الأصابة المزمنة IgG مثلت النسبة الأكبر) 20.12 %( والأصابة الحادة IgM مثلت النسبة الأقل %50.02 (. لوحظ وجود نقص معنوي لمستويات ( الكولستيرول والدهون الثلاثية و LDL و vLDL 0.22 و ± 1.22 و 70.50 ± 0.22±001.12 و 51.15 ( 1.00±2.71 mg/dl ( على التوالي مقارنة بمجموعة 0.10 و ± 2.05 و 22.12 ± السيطرة ) 011.12 0.07± 0.12±070.02 و 52.11 mg/dl ( على التوالي. من جانب اخر لوحظ وجود زيادة معنوية بقيمة ال HDL و T3 و TSH 0.01±27.20( mg/dl 1.25 و ± و 00.17 1.20±00.27 mlU/L ( مقارنة مع مجموعة السيطرة 0.21±25.72( mg/dl 1.02± 1.02 و 0.01 ± و 0.71 mlU/L (. كما بينت الد ا رسة هبوط معنوي بمستوى الهرمون T4 1.00±0.00( mlU/L ( مقارنة مع مجموعة السيطرة 1.01±0.52( mlU/L .) يمكننا الأستنتاج بأن طفيلي التوكسوبلازما Toxoplasma gondii له دور مهم في تغي ا رت مستويات الدهون في الدم اضافة الى تغي ا رت في هرمونات الغدة الدرقية في النساء المصابات بالمرض.


Article
Evaluation the Suitability of Saliva for DNA Profiling Analysis in Comparative with Blood Samples

Authors: Dhuha Salim Namaa
Pages: 127-134
Loading...
Loading...
Abstract

Collection, preservation and analysis of body fluids are important aspect of forensic science. Isolated DNA from saliva has become an attractive alternative to the use of blood-derived DNA in performance characteristics. The objectives of this study were to determine the suitability of saliva for DNA profiling analysis and compare blood and saliva as biological source in the performance characteristics. Saliva and buccal swab (as the reference source of genomic DNA) samples were collected from 7 healthy volunteers. The saliva samples were taken with different volumes (100, 200, 300, 400) μl of whole saliva. On the other hand, blood and saliva samples were collected from 25 healthy volunteers in a comparative study. Extraction of DNA was done by Phenol Chloroform method. The results showed difference in the mean DNA concentration which was quantified by using Real-Time PCR from various volumes of saliva samples (100, 200, 300, 400) μl recording (1.23, 2.21, 3.40, 8.24) ng / μl respectively. The mean allele’s percentage of 15 STR loci that appeared in profile of different volumes mentioned above were (73.3, 83.7, 89.5, 99.04)% respectively. The mean DNA concentration and the purity from saliva and blood samples were measured by using nonadrop spectrophotometer recording (10.736, 51.164) ng/ μl (1.64, 1.72) respectively. It is concluded that, saliva samples can be taken at different volumes in the field of criminal research instead of the traditional a way of taking blood samples.يعد جمع وحفظ وتحليل سوائل الجسم جانبا مهما في العلم الجنائي، حيث أصبح الحامض النووي ال ا ريبوزي منقصوص الاوكسجين )الدنا( المعزول من اللعاب بديلا جيدا عن الدم في الد ا رسات الجينية ويستخدم الآن على نطاق واسع في العديد من التطبيقات. الهدف من هذه الد ا رسة اولا، هو تحديد مدى ملائمة اللعاب لاستخلاص الحامض النووي و إمكانية استخدامه لتضخيم المؤش ا رت الجسمية الخاصة بتحديد التتابعات الو ا رثية الجنائية بالاعتماد على اخذ مسحة فموية باعتبارها المصدر الرئيسي للمقارنة. ثانيا، المقارنة بين الدم واللعاب كمصدر بايولوجي من حيث خصائص الأداء )جمع العينة، حفظ العينة ...الخ(. تم جمع عينات من المسحة الفموية واللعاب من 7 متطوعين، العينات أخذت بأحجام مختلفة من اللعاب من كل متطوع Dhuha Salim Namaa 134 044,044,044,044 ( ميكرولتر وبالتالي فإن العدد ( النهائي للعينات التي استخدمت في هذه الد ا رسة 02 عينة، كذلك تم جمع عينات من الدم واللعاب من 02 متطوعا كد ا رسة لمقارنة الخصائص. استخلصت العينات بالاعتماد على طريقة الفينول الكلوروفورم. أظهرت النتائج وجود فرق في ت ا ركيز الحامض النووي المستخلص عند الحصول على نتائج الحامض النووي الكمي باستخدام تقنية Real time - PCR بااحجام مختلفة لعينات اللعاب ،044( 200 ، 300 ،0.00 ، 044 ( ميكرولتر ) 0.00 ، 2.00 ( نانوغ ا رم/ ميكرولتر على التوالي، كذلك في ،0.04 نتائج تضخم المؤش ا رت الجسمية الخاصة بتحديد التتابعات الو ا رثية الجنائية باستخدام جهاز التحليل الو ا رثي حيث ظهرت ، نتائج النسبة المئوية لعينات اللعاب باحجام مختلفة ) 70.0 40 ...(٪ على التوالي في 02 موقع. تم ، 2..2 ،20.7 تقييم الحامض النووي وفق التركيز والنقاوة وامكانية استخدامه لاغ ا رض التحليلات الو ا رثية بالنسبة لعينات الدم واللعاب حيث تم قياسها باستخدام جهاز الطيف المرئي ) (Nano drop )0.10 ، 04.701 ( نانوغ ا رم/ ميكرولتر ) 0.70 ،20.010( على التوالي. ويستنتج من هذه الد ا رسة امكانية استخدام اللعاب في مجال البحث الجنائي وامكانية الحصول على الهوية الو ا رثية باحجام مختلفة من عينات اللعاب، بالاضافة الى امكانية الاستغناء عن اخذ عينات من الدم واستبدالها بعينات اللعاب. الكلمات المفتاحية: اللعاب، الدم، الحامض النووي، المؤش ا رت الجسمية الخاصة بتحديد التتابعات الو ا رثية الجنائية.

Keywords

saliva --- blood --- genomic DNA --- STR


Article
Biochemical Changes in Hepatic Function of Petrol Station Attendants in Basrah

Loading...
Loading...
Abstract

Previous studies on human and animals demonstrated that many of chemicals components of petroleum can affect the liver function. The present study investigated and evaluated the hepatotoxic effects of petroleum fumes and the changes in liver biochemical functions resulted from exposure to petrol and their derivatives by measuring the changes of liver enzymes and total serum bilirubin in 18 petrol workers station attendant in Basrah, Iraq. A corresponding 18healthy subjects were used as controls. Biochemical analyses on the serum samples were done after samples collection. Results are time exposure dependent. Our results showed the presence of a significant increase in the level of Glutamic-pyruvic transaminase (GOT), Glutamic-oxaloacetic transaminase (GPT), Alkaline phosphatase ALP and they related to the time of exposure to petroleum products especially for 3-6 years, and for 6-10 years, p value was p≤ 0.01, p≤ 0.001 respectively. Total serum bilirubin TSB for those workers which were exposed to petrol from six to ten years were also showed a significantly higher than the control. These effects may be directly related to time of exposure. The study suggests that long term inhalation of petrol fumes is associated with adverse effect on liver function.اشارت العديد من الد ا رسات السابقة التي اجريت على الانسان والحيوانات المختبرية بعد التعرض الى مشتقات البترول الى التاثي ا رت المحتملة على وضائف الكبد. الد ا رسة الحالية شملت ) 81 ( شخص من العاملين في محطات البترول في محافظة البصرة وشملت ايضا ) 81 ( شخص سليم غير معرض لتلك المشتقات النفطية. في الد ا رسة الحالية تم د ا رسة تاثير استنشاق مشتقات البترول على وضائف الكبد. أظهرت نتائج الد ا رسة وجود ارتفاع معنوي ملحوظ في تركيز انزيمات وضائف الكبد ومستوي البلروبين الكلي. هذه التغي ا رت في مستوى انزيمات الكبد وكذلك مستوى البلروبين الكلي قد ترتبط ارتباط مباشر بالفترة الزمنية لتعرض العاملين في محطات تعبئة الوقود للمشتقات النفطية خاصة بعد فترة 6 3 سنوات و 81 6 سنوات حيث اظهرت فروق معنوية - - كبيرة لقيمة الاحتمالية p≤0.01, p≤0.001 . في حين اظهرت نتائج الد ا رسة ان المستوى الكلي للبروتين يتاثر بعد التعرض لفترة 81 6 سنوات عند مقارنة النتائج بمجموعة - السيطرة. نتائج الد ا رسة تقترح ان التغيير في وضائف الكبد ومستوى البروتين الكلي ترتبط مع التعرض طويل الامد لاستنشاق مشتقات البترول.

Keywords

Liver function --- GOT --- GPT --- ALP --- TSB --- Petrol station


Article
In Vitro and In Vivo Tests of the Cidal Effects of Certain Agents for Hydatid Protoscolices

Authors: Dhilal Mahdi Al-Muathen
Pages: 139-142
Loading...
Loading...
Abstract

Cysts from the liver of hydatidosis infected sheep were obtained from a local abattoir, live protoscolices were prepared by using of Kreb's Ringer solution plus Hydatid Cyst Fluid (4:1) and exposed to selected protoscolicidal agents (Mebendazole 5%, Cetrimide 0.15%, and Formaline 2%) in vitro, survival times of protoscolices in the presence of chemicals was used as a criterion of protoscolicidal agents activity by using eosin stain. After treatment it was concluded that all the treated protoscolices of the study were completely killed with Mebendazole 5% and Cetrimide 0.15% at 5 minutes of exposure, while Formaline 2% did not cause complete killing even at 15 min of exposure. furthermore the results of in vivo part of this study showed that all the treated scolices in vitro part were completely killed and did not cause hydatidosis up to 90 days post infection in laboratory albino mice.جمعت الرؤيسات الأولية للأكياس العدرية من الخ ا رف المصابين بطفيلي المشوكة الحبيبية Echinococcus granulosus من المجازر المحلية. و حضرت في الزجاج بأستخدام وسط محلول كريبس رينكر + سائل الكيس العدري 4:1 ( لغرض معاملتها بمواد قاتلة للرؤيسات الأولية هي ( )الميبيندازول 5%, السترمايد 5145 %, الفورمالين 2%(. و قد أستخدم وقت البقاء للرؤيسات الأولية بوجود المواد الكيميائية المستخدمة كوسيلة لمعرفة فعالية هذه المواد بأستخدام صبغة الأيوسين. و قد أستنتج في هذه الد ا رسة أن كل من الميبندازول 5% و السسترمايد 5145 % هو مادة قاتلة جيدة للرؤيسات الأولية خلال فترة تعرض 5 دقائق, أضافة الى ذلك فأن الفورمالين 2% قد سبب قتل كامل للرؤيسات الأولية في 41 دقيقة. كما و أظهرت الد ا رسة داخل الجسم الحي ان كل الرؤيسات المعاملة بالمواد القاتلة لها المستعملة في الجزء المختبري قد قتلت بصورة كاملة و لم تسبب أحداث أصابة بالأكياس المائية حتى بعد تسعين يوم من أحداث الأصابة في الفئ ا رن المختبرية.


Article
Compactness of Fuzzy Cone Metric Spaces

Authors: Fadhel S. Fadhel --- Amer A. Abdullah
Pages: 143-150
Loading...
Loading...
Abstract

Cone metric spaces may be considered as a generalization of determinist metric spaces or fuzzy metric spaces. In this paper, we will construct fuzzy cone metric space using different approaches, which is based on the definition of fuzzy points, and then study different types of compact subsets of such spaces, as well as, the relationship among them.النظام المتري الكون يعتبر تعميم للنظام المتري العادي وكذلك للنظام المتري الضبابي. في هذا البحث سوف نقدم النظام المتري الضبابي المخروطي بواسطة تعريف النقاط الضبابية, وكذالك سندرس عدة انواع من الت ا رص لهذا الفضاء, وكذالك د ا رسة العلاقات بينهم.

Table of content: volume:19 issue:4