Samples prepared by using carbon black as a filler material and phenolic resin as a binder. The samples were pressed in a (3) cm diameter cylindrical die to (250)MPa and treated thermally within temperature range of (600-1000)oC for two and three hours. Physical properties tests were performed, like density, porosity, and X-ray tests. Moreover vicker microhardness and electric resistivity tests were done. From the results, it can be concluded that density was increased while porosity was decreased gradually with increasing temperature and treating time. In microhardness test, it found that more temperature and treating time cause more hardness. Finally the resistivity was decreased in steps with temperature and treating time. It can be concluded that these variables may increase the graphitizing degree, and minimizing in interplanar distance for samples comparing with ideal one, when these variables may increased.

في هذا البحث تم تحضير عينات من أسود الكاربون و صمغ الفينول فورمالدهايد كمادة رابطة بعد كبس المزيج في قالب اسطواني بقطر (3) سم وبضغط مقداره MPa(250)، جرت معالجة العينات حراريا بمدى من درجات الحرارة (600-1000) درجة مئوية ولفترة ساعتين وثلاثة ساعات. تم دراسة الخصائص الفيزيائية للعينات من كثافة ومسامية وفحص الاشعة السينية, اضافة الى ذلك تم فحص صلادة فيكر للعينات . كما تم بيان تأثير التغير في قيمة المقاومية الكهربائية والخصائص التركيبية بدلالة المتغيرين درجة الحرارة وزمن المعالجة . من نتائج الفحص تم استنتاج ان الكثافة تزداد يصاحبها نقصان في المسامية بزيادة درجة الحرارة وزمن المعالجة, أضافة الى زيادة صلادة العينات مع هذين المتغيرين. اما في فحص المقاومية , فقد وجد انها تقل تدريجيا ّمع درجة الحرارة وزمن المعالجة. وهذا يدل على ان هذين المتغيرين تزداد بهما درجة الكرفتة , وتناقص الفرق في المسافات البينية للعينات مقارنة بالعينات المثالية بزيادة هذين المتغيرين .

Thermal fragmentation --- Infusible --- Heat treatment