Article
Some properties of light weight concrete containing carbon fiber

Authors: Aly AL- Attar --- Israa.Y.Al- Hyally --- Shakir A. AL-Mishhadani
Journal: Iraqi Journal of Civil Engineering المجلة العراقية للهندسة المدنية ISSN: 19927428 Year: 2009 Volume: 6 Issue: 1 Pages: 46-58
Publisher: University of Anbar جامعة الانبار

Loading...
Loading...
Abstract

Abstract:-
This investigation studies the mechanical characteristics of carbon fiber reinforced
light weight aggregate concrete, containing different percentages of fiber. The effect of
using high range water reducing agent (SP) with 8% silica fume (SF) and 8% high
reactivity Metakaolin (HRM), as a partial replacement by weight of cement, on the
behavior of (LWA) concrete is also studied.
This investigation was carried out using several tests. These tests were workability fresh
and hardened density, compressive strength, splitting tensile strength and modulus of
rupture. Tests were performed for specimens at ages of (7,28,60,90 and 180) days . The
test results indicated that the inclusion of carbon fiber to the light weight concrete mix did
not affect the compressive strength significantly, while the splitting tensile strength and
the modulus of rupture were improved significantly. The addition of silica fume and
metakaolin improves the compressive, splitting tensile , and modulus of rupture strengths
of carbon fiber light weight concrete. The average improvement was about (26.5%, 71%
and 73 %) respectively for carbon fiber LWA concrete containing silica fume and (28%,
72% and 75%) respectively for carbon fiber LWA concrete containing high reactivity
metakaolin.

يتضمن هذا البحث دراسة الخواص الميكانيكية للخرسانة الخفيفة الوزن المسلحة بنسب مختلفة من الياف الكاربون.كما تم دراسة تأثير الملدن المتفوق مع % 8 من ابخرة السليكا او % 8 من الميتاكاوؤلين العالي الفعالية (كتعويضجزئي من وزن السمنت) على سلوك الخرسانة الخفيفة الوزن الحاوية على الياف الكاربون. تم اعتماد عدةفحوصات لاجراء هذا البحث وهي فحوصات قابلية التشغيل والكثافة للخرسانة الطر ية والمتصلبة ومقاومة180, 90, 60, 28 )يوم . , الانضغاط ومقاومة الانشطار ومعاير الكسر. وتمت الفحوصات بعد اعمارمعالجة ( 7بينت نتائج الفحص بان وضع الياف الكاربون مع الخرسانة الخفيفة الوزن لم يؤثر على مقاومة انضغاط الخرسانةبشكل واضح, الا ان مقاومة الانشطار ومعاير الكسر قد تحسنت بشكل مهم . ان اضافة ابخرة السليكاوالميتاكاوؤلين مع الخرسانة الخفيفة الوزن الحاوية على الياف الكاربون قد حسنت من الخواص الميكانيكية لها., %71,% وان معدل التحسن في مقاومة الانضغاط ومعاير الكسر ومقاومة الانشطار كان حوالي ( 26.5%73 )على التوالي للخرسانة الخفيفة الوزن المسلحة بالالياف والحاوية على ابخرة السليكا وان نسب التحسن75 %)على التوالي للحرسانة الخفيفة الوزن المسلحة بالالياف والحاوية على الميتاكاؤولين . ,%72,% كانت( 2

Keywords


Article
Utility of Non Destructive Tests to Assess the Compressive Strength of High Performance Concrete
إمكانية تقييم مقاومة الانضغاط للخرسانة عالية الاداء باستخدام الفحوصات اللاإتلافية

Authors: Sura F. Al-Khafaji --- Waleed A. Al-Qaisi --- Shakir A. Al-Mishhadani
Journal: AL-NAHRAIN JOURNAL FOR ENGINEERING SCIENCES مجلة النهرين للعلوم الهندسية ISSN: 25219154 / eISSN 25219162 Year: 2008 Volume: 11 Issue: 3 Pages: 552-559
Publisher: Al-Nahrain University جامعة النهرين

Loading...
Loading...
Abstract

In this study, high performance concrete mixes were produced by using high range water reducing agent(Glenium 51) and also by using 10% silica fume or 10% high reactivity metakaolin as a partial replacement by weight of cement. Three cement contents (350, 450, and 550) kg/m3 were used through this study. A total of 330 (100 mm) cubes, 66 (150×300 mm) cylinders, and 132 (100×100×400 mm) prisms were cast and cured to the required age of test. Compressive strength, rebound number, ultrasonic pulse velocity and dynamic modulus of elasticity were investigated for all mixes at 7, 28, 90, and 120 days age. Results of the destructive test of compressive strength and non–destructive tests (hammer, ultrasonic pulse velocity, and dynamic modulus) are statistically analyzed by using SPSS Ver.15 software to study the possibility of assessing the compressive strength of high performance concrete by using non–destructive tests. Simple and multiple linear regression analysis of the obtained results leads to the proposed statistical models for evaluating the compressive strength by using one or two or three of the above non–destructive tests. Analysis of variance (ANOVA) and t–test was also used to investigate the adequacy of the statistical models. The statistical models were subjected to adequacy checks at a selected level of significance of 5%.

تم في هذه الدراسة انتاج خلطات خرسانية عالية الاداء باستخدام مضاف مقلل للماء بدرجة متفوقة وكذلك باستخدام ابخرة السليكا المكثفة بنسبة ۱۰% او الميتاكاؤولين عالي الفعالية بنسبة ۱٠% كتعويض عن جزء من وزن السمنت ، كما و تم استخدام ثلاث محتويات من السمنت (۳٥۰،٤٥٠ و٥٥٠) كغم/م۳. تم صب و تهيئة ۳۳۰ مكعب بابعاد (۱٠۰ملم) ، ۱۳۲ موشور بابعاد (۱٠۰×۱٠۰×٤۰۰ملم) و٦٦ اسطوانة بابعاد (۱٥۰×۳۰۰ملم) و قد عولجت جميعها بالماء لغاية عمر الفحص المطلوب.اجريت فحوصات مقاومة الانضغاط ، رقم الارتداد، سرعة الموجات فوق الصوتية، معامل المرونة الديناميكي باعمار ۷،۲٨،٩٠،۱۲٠يوم. تم تحليل نتائج الفحص الإتلافي ( مقاومة الانضغاط ) والفحوصات اللاإتلافية (رقم الارتداد ،سرعة الموجات فوق الصوتية ، معامل المرونة الديناميكي) احصائياً باستخدام برنامج SPSS Ver.15 لدراسة امكانية تقييم مقاومة الانضغاط للخرسانة عالية الاداء باستخدام الفحوصات اللاإتلافية. التحليل الانحداري البسيط والمتعدد الخطي للنتائج المستحصلة ادى الى النماذج الاحصائية المقترحة لتقييم مقاومة الانضغاط باستخدام فحص واحد او فحصين او ثلاثة من الفحوصات اللاإتلافية. كذلك تم استخدام تحليل التباين ((ANOVA و(t–test) لتحري كفاءة النماذج الاحصائية.