Study of Some Mechanical and Physical Pproperties for Epoxy Rreinforced by Ffibers
دراسة بعض الخصائص الميكانيكية والفيزيائية للإيبوكسي المدعم بالألياف

Author: Hayat K.Hameed حياة خلف حميد
Journal: Ibn Al-Haitham Journal For Pure And Applied Science مجلة ابن الهيثم للعلوم الصرفة والتطبيقية ISSN: 16094042 Year: 2014 Volume: 27 Issue: 2 Pages: 136-143
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

In this research, we prepared a hybrid composite material of polymeric matrix hand cast method, composite material has been attended from epoxy resin EP as matrix materials reinforced woven roving fiber jute is constant volume fraction (13%), PVC fibers and woven glass fiber with different fraction on the properties of prepared composite materials to PVC fiber and glass fiber, some of mechanical tests were done at room temperature (impact test and banding test). Result shows that the values of (modulus bending elastic and fracture toughness) increase fraction of fiber with the increase of PVC, E-glass, there include (thermal conductivity and dielectric constant). Also experimental result indicated that the (thermal conductivity and dielectric constant) increase with the increase of fiber volume fraction.

تم في هذا البحث تحضير مواد متراكبة هجينة ذات أساس بوليمري بطريقة الصب اليدوي، حضرت المواد المتراكبة من راتنج الإيبوكسي EPمادة أساس مدعمة بألياف الجوت الحصيرية كسر حجمي ثابت (13%)، وألياف PVC والألياف الزجاجية الحصيرية بكسور حجمية مختلفة. وتضمن البحث دراسة تأثير الكسور الحجمية(7%, 12%, 17%) لألياف PVC وألياف الزجاج في خصائص المواد المتراكبة المحضرة، أجريت بعض الاختبارات الميكانيكية عند درجة حرارة الغرفة (اختبار الصدمة، اختبار الانحناء) وأظهرت النتائج أن قيمة (معامل مرونة الانحناء ومتانة الكسر) تزداد مع زيادة الكسر الحجمي للألياف، وكذلك أجريت مجموعة من الاختبارات الفيزيائية (اختبار الموصلية الحرارية واختبار ثابت العزل)، وأظهرت نتائج البحث أن عند زيادة الكسر الحجمي تزداد الموصلية الحرارية وثابت العزل الكهربا


Article
Study of Mechanical and Thermal Behavior for Epoxy Reinforced by Fibers
دراسة السلوك الميكانيكي والحراري لمادة الإيبوكسي المدعم بالألياف

Author: Hayat K. Hameed حياة خلف حميد
Journal: Ibn Al-Haitham Journal For Pure And Applied Science مجلة ابن الهيثم للعلوم الصرفة والتطبيقية ISSN: 16094042 Year: 2015 Volume: 28 Issue: 1 Pages: 321-330
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

In this study, epoxy was used as a matrix for composite materials, with E-glass fiber, jute and PVC fiber which was woven roving fiber, as reinforcement with volume fraction (Vf= 30%). There are two of prepared types of epoxy non reinforced, epoxy reinforced with E-glass, jute and PVC fibers including study of mechanical tests (Impact test, Bending test) different temperature and thermal conductivity and calculating the temperatures coefficient at different temperature. Results show that elastic modulus at rate values decrease to the increase of temperature and the impact strength, impact energy and thermal conductivity increase with increase temperature.

استعمل في هذه الدراسة راتنج الايبوكسي كمادة أساسية للمواد المتراكبة، وتم استعمال ألياف الزجاج وألياف الجوت وألياف PVC بصورة حصيرة محاكة كمواد مدعمة وبكسر حجمي مقداره 30%، إذ تم تحضير نوعين من الايبوكسي غير المدعم والايبوكسي المدعم بألياف الجوت والزجاج وPVC، وتضمنت الدراسة بعض الاختبارات الميكانيكية التي شملت (Bending Test, Impact Test)ببدرجات حرارية مختلفة، كما تم إجراء اختبار الموصلية الحرارية لحساب معامل التوصيل الحراري في درجات حرارية مختلفة. وأظهرت النتائج أن قيم معامل المرونة تقل بزيادة درجات الحرارة، وتزداد كل من طاقة الكسر ومتانة الكسر والموصلية الحرارية بزيادة درجات الحرارة.


Article
Evaluation of Mechanical Strength of Epoxy Polymer Concrete Reinforcement with Different Types of Fibers
قياس المقاومة الميكانيكية للايبوكسي بوليمر كونكريت مدعمة بانواع مختلفة من الالياف

Loading...
Loading...
Abstract

Polymer composite materials were prepared by mixing epoxy resin with sand particles in three different grain size (150-300 ), (300-600 ) and (600- 1200) μm . The weight of epoxy was 15%, 20%, 25% and 30% of the total weight. Compression strength and flexural strength tests were carried out for the prepared samples .The percentages of epoxy resin at 20% wt and 25% wt showed best mechanical properties for all grain sizes .These percentages were adopted to fill the void between particles sand which have two different size ranges (150-600) μm and {(150-300) & (600-1200)} μm respectively to obtain more dense material. The results showed that the strength of polymer composite at 20% resin is higher than 25% resin. The sample which has maximum value for compression strength and flexural strength was reinforced with fibers (glass, polypropylene and alucobond waste) by weight 1% and 1.5% respectively of the weight of epoxy resin.

حضرت مادة متراكبة بوليمرية بخلط راتنج الايوكسي مع الرمل لثلاثة احجام حبيبية مختلفة هي (150-300) و(600-300) و (600-1200) مايكرون . وزن الايبوكسي كان 15% ,20% ,25% ,30% ,من الوزن الكلي . فحصي مقاومة الانضغاط ومقاومة الانحناء اجري على العينات المحضرة. النسب الوزنية لراتنج الايبوكسي عند20 % و25% اظهرت افضل الخصائص الميكانيكية لكل الاحجام الحبيبية . اعتمدت هذه النسب لملئ الفراغات بين حبيبات الرمل التي تمتلك حجمين مختلفين(150-600) و}(150-300) &(600-1200){ μmعلى التوالي للحصول على مادة ذات كثافة اكبر. اظهرت النتائج بأن مقاومة المتراكبات البوليمرية عند النسبة20% كانت اعلى من تلك عند 25% . العينات التي تمتلك اعلى قيمة لمقاومة الانضغاط والانحناء دعمت بالألياف (ألياف الزجاج ,ألياف البوليبروبلين ,ألياف مخلفات الاليكوبوند) بنسب 1% و1.5% من وزن راتنج الايبوكسي .


Article
Electrical Insulation Breakdown Strength and Thermal Conductivity of Different Blended Nanocomposites of New Epoxy Resins
قوة انهيار العزل الكهربائي والتوصيل الحراري لمختلف السبائك النانوية المتراكبة لراتنج الايبوكسي الجديد

Loading...
Loading...
Abstract

This research studies the development and synthesis of blended nanocomposites filled with Titanium dioxide (TiO2). Blended nanocomposites based on unsaturated polyester resin (UPR) and epoxy resins were synthesized by reactive blending. The optimum quantity from nano partical of titanium dioxide was selected and different weight proportions 1%, 3%, 5%, and 7% ratios of new epoxy are blended with UPR resin. The dielectric breakdown strength and thermal conductivity properties of the blended nanocomposites were compared with those of the basis material (UPR and 3% TiO2).The results show good compatibility epoxy resins with the UPR resin on blending, dielectric breakdown strength values are higher while thermal conductivity values of blends nanocomposites are significantly lower compared to that of the(UPR and 3% TiO2), semi-interpenetrating UPR/Epoxy blends (semi-IPNs) for one type of new epoxy [P2]was prepared and noticed the blend nanocomposites show higher dielectric breakdown strength than the semi- IPNs (UPR/Epoxy) at low loading of new epoxies but the thermal conductivity is a higher than the semi- IPNs UPR/Epoxy at all loading. Thermogravimetric analysis (TGA) was employed to study the thermal properties of the blended nanocomposites.

يكشف هذا البحث عن تحضيروتطوير عشرة مخاليط متراكبة ومليئة بجسيمات نانويه وهي ثاني أوكسيد التيتانيوم (TiO2). تم تحضير شبكات البوليمر المتراكبة النانويه على أساس راتنج البوليستر غير المشبعة (UPR) وراتنجات ايبوكسي جديدة مختلفه عن طريق مزج فعال .أذ تم اختيار النسبه المثلى من الجسيمات النانويه لثاني أوكسيد التيتانيوم (3%) وهي نسبة مختارة من نتائج مزجها بنسب مختلفة مع راتنج البولي استر غير مشبع. ومن ثم مزجت النسبة المثلى (3%) من(TiO2) مع بولي استرالغير مشبع مع نسب مختلفه من مركبات الايبوكسي الجديدة 1 ٪ , 3٪ , 5٪ و 7٪ من وزن راتنج البولي استر غير مشبع. وتمت مقارنة خصائص قوة انهيار العزل الكهربائي والتوصيل الحراري للمتراكبات النانويه المقساة مع تلك المواد الأساس (UPR و 3٪ TiO2). تظهر الاولى قوة انهيار العزل الكهربائي اعلى في حين التوصيل الحراري هي اقل وكما تم تحضيرمخاليط لاحد تراكيب الايبوكسي رقم ( 2) وبالنسب المذكورة نفسها (UPR و (Epoxy و مقارنتها مع مخلوط المتراكبة النانويه لوحظه ان قوة انهيار العزل الكهربائي للمخلوط المتراكبة النانويه هو الاعلى عند نسب التحميل الواطئة للإيبوكسي رزن وكما اظهرت التوصيلية الحرارية عالية مقارنة بما اظهرته مخاليط من ( UPR Epoxy/) .اجري التحليل الحراري الوزني (TGA) لدراسة الخواص الحرارية للمخاليط المتراكبة النانويه .