Studying the effect of Different wt % AL2O3 Nanoparticles of 2024Al Alloy / AL2O3 Composites on Mechanical Properties
دراسة تاثير النسب الوزنية المختلفة للمادة النانوية في المركبات النانوية على المواصفات الميكانيكية

Loading...
Loading...
Abstract

The nanocompsite of alumina (Al2O3) produced a number of beneficial effects in alloys. There is increasing in resistance of materials to surface related failures , such as the mechanical properties , fatigue and stress corrosion cracking .The experimental results observed that the adding of reinforced nanomaterials type Al2O3 enhanced the HB hardness, UTS, 0.2 YS and ductility of 2014 Al/Al2O3 nano composites . the analysis of experiments, indicated that The maximum enhancement was observed at 0.4 wt.% Al2O3. The ultimate improvement percentage were 15.78% HB hardness, 18.1% (UTS), 12.86% (0.2 YS) and 25.71% ductility. These enhancements in the above properties maybe to high dislocation density resulting in good bounding between Al2O3 and metal matrix.

المواد المركبة النانوية بواسطة الالومنيا Al2O3، اعطى عدد من التاثيرات الايجابية في السبائك، التأثيرات هذه في زيادة مقاومة المواد على السطح المتعلقة بالفشل مثال على ذلك المواصفات الميكانيكية، الكلال والتشقق نتيجة التاكل الاجهادي. اوظحت النتائج العملية ان اضافة المادة المقواة نوع تحسن صلادة برينل، اجهاد الشد الأعظم، اجهاد الخضوع عند 0.2% والمطيلية الى2024Al/ Al2O3. التحليلات اوضحت ان أعظم تحسن تمت ملاحظته عند 0.4% نسبة وزنية الى الالومينا. حيث كان اعظم تحسن 15.87% لصلادة برينيل، 18.1% لاجهاد الشد الأعظم، 21.86% لإجهاد الخضوع و 25.71% للمطيلية. هذا التحسن في المواصفات اعلاه نتيجة الى الكثافة العالية للانخلاعات مؤدية الى تماسك جيد بين الالومينا والمعدن الأساس.

Listing 1 - 1 of 1
Sort by
Narrow your search

Resource type

article (1)


Language

Arabic and English (1)


Year
From To Submit

2018 (1)