Comparison Between the Effect of Silica Fume and Wood Ash Used for the Production of High Performance Mortar
المقارنة بین تاثیر أبخرة السیلكا ورماد فحم الخشب المستخدمین لإنتاج مونة الاسمنت عالیة الأداء

Author: Eethar Thanon Dawood ایثار ذنون داؤد
Journal: AL-MANSOUR JOURNAL مجلة المنصور ISSN: 18196489 Year: 2013 Issue: 20 Pages: 43-49
Publisher: Private Mansour college كلية المنصور الاهلية

Loading...
Loading...
Abstract

This paper presents a comparison between the use of silica fume and wood ashfor High Performance Mortar (HPM). The different percentages used for each of thesilica fume and wood ash are: 6, 8, 10, 12 and 16%. The experimental testsincluded density, compressive strength and flexural strength. The results illustratethat the use of silica fume increases the density, whereas the wood ash decreasesthe density of HPM. Besides, the inclusion of Silica fume (10 % as a partialreplacement of cement) and wood ash at the same level of replacement gives thebest properties of the HPM. In other words, the compressive strength and flexuralstrength have been enhanced by the inclusion of silica fume and wood ash.

ھذه الدراسة تھدف إلى مقارنة بین استخدام أبخرة السیلكا ورماد فحم الخشب لإنتاج مونة الأسمنت عالیة الأداء. تمت ھذه,%14 ,%12 ,%10 ,%8 ,% الدراسة باستخدام نسب مختلفة من أبخرة السیلكا ورماد الفحم حیث كانت النسب كالأتي: 6%16 . تم فحص نماذج مونة الأسمنت لكل من الكثافة ومقاومة الانضغاط ومقاومة الانحناء. النتائج بینت ان استخدامابخرة السیلكا سوف یزید من كثافة مونة الاسمنت عالیة الأداء في حین ان استخدام رماد الفحم یعمل على تقلیل الكثافة.بالإضافة إلى ذلك فان استبدال 10 % من أبخرة السیلكا أو رماد الفحم أعطت أفضل أداء لمونة الأسمنت وخاصة بالنسبةلمقاومتي الانضغاط الانحناء.


Article
Modification of Soil Used in Core of Earth Dams
تحسين خواص التربة المستخدمة في لب السد الترابي

Authors: Hassan A. Omran حسن علي عمران --- Noura B. Ibraheem نورة باسم ابراهيم
Journal: Iraqi Journal of Civil Engineering المجلة العراقية للهندسة المدنية ISSN: 19927428 Year: 2018 Volume: 12 Issue: 2 Pages: 40-46
Publisher: University of Anbar جامعة الانبار

Loading...
Loading...
Abstract

The earth-fill dams are simple structures which are able to prevent the sliding and overturning because of their self-weight. Due to lack of suitable clay materials, the dams may be designed as zoned core which is composed of three vertical zones contains central impermeable core and two permeable shells on their two sides of the core. Impervious core is used in zoned earth dam to reduce the quantity of seepage through the body of the dam and to relief part of risk of piping and erosion in the downstream side. This study aims to study the soil properties that is used as a core of earth dam through a series of laboratory experiments that were carried out a several soil samples mixed with both lime and silica fume, in order to stabilize the soil. The process of stabilization aims to increase the soil strength and reducing its permeability and compressibility. Test results show that adding lime and silica fume to the soil decreases the permeability of soil with different cases of study, the percentage of decreases in case of standard compaction about (21%-90%) while in modified compaction test the permeability decreases in range (41.7%-91.3%). Also the unconfined compressive strength of the soil increasing significantly in both cases of compaction which were standard and modified. When add the materials, these values were increased in range (76%-90%) for samples from standard compaction test, while it being (0.21%-42%) in modified compaction test.

تعتبر السدود الترابية من ابسط المنشأت الهيدروليكية التي تعتمد على وزنها لمقاومة الانزلاق والانقلاب.ويمكن اعتماد تصميم السدود الترابية على أساس تقسيمها الى أجزاء محددة عندما تكون التربة الطينية ذات النفاذية القليلة, حيث يمكن ان يقسم جسم الى ثلاثة اجزاء هي الجزء المركزي غير نفاذ الذي يمثل اللب, وجزئين نفاذين على جانبي اللب الطيني.التجارب المختبرية التي تم اجراءها على عدة نماذج للتربة الطينية الممزوجة بمادتي مسحوق السيليكا (silica-fume) والجص (lime) لغرض تحسين خصائص التربة المستخدمة والمتمثلة بزيادة المقاومة وتقليل النفاذية والانضغاطية. بينت نتائج البحث ان خلط التربة الطينية مع مادتي مسحوق السيليكا (silica-fume) والجص (lime) يؤدي الى تقليل نفاذية التربة في مختلف الحالات التي تم دراستها, نسبة التناقص في حالة الرص القياسي تتتراوح بين (21%-90%) بينما نسبة هذا التناقص تتتراوح بين (41,7%-91,3%) في حالة الرص المعدل.كذلك مقاومة الانضغاط الغير محصور ازدادت في حالتي الرص القياسي والرص المعدل عند إضافة المادة هذه القيم ازدات تقريبا بمقدار (76%-90%) بالنسبة للرص القياسي بينما تصبح (0.21%-42%) بالنسية للرص المعدل.

Keywords

Earth dam --- core --- soil modification --- lime --- silica fume


Article
Effect of Materials and Stabilizers Type on the Strength of Base Layer
تأثير نوع المواد والمضافات على قوة طبقة الأساس

Loading...
Loading...
Abstract

Pavement is defined as multiple layers system and the strength of each layer is reflected on the pavement as whole. Two type of materials used as base layer, conventional granular materials and reclaimed concrete aggregate (RCA) materials. This study presents test results and discusses the effect of lime-silica fume on strength of base layer as stabilizer. Also, a comparison is made between the changes that occur in treated base layer and untreated base layer. Combination of lime - silica fume is used as stabilizer with (1, 3, 5, 7) % and also cement stabilizer is used with (0.5, 1.5) %. Comparison between treated and untreated base layer is made in terms of strength. The material of base layer is conventional base material taken from Al-Nibaee quarry. Samples with three replicates of each possible combination are performed. A total of (68) samples is prepared and subjected to compressive strength test. The obtained results indicate an increase in the strength of base material by factor of increment about (2.56) when Reclaimed Concrete Aggregate (RCA) is used. Also, at (5%) lime -silica fume stabilizer, the factor of increment increases in the strength by about (42.248) more than the untreated samples.

يعرف التبليط كنظام متعدد الطبقات وقوة كل طبقة تؤثر على ألتبليط ككل. نوعان من المواد استخدمت كطبقة أساس٬ مواد الركام التقليدية والركام المعاد تدويره من الخرسانة الكونكريتية. تقدم هذه الدراسة نتائج الاختبار، ويناقش تأثير النورة - غبار السيليكا على قوة طبقة الأساس كمثبت. أيضا، يتم إجراء مقارنة بين التغيرات التي تحدث في طبقة الأساس المثبتة وغير المثبتة. كل من النورة – غبار السيليكا أستخدمت كمثبتات بالنسب (7٬5٬3٬1) ٪ وكذلك تم استخدام الأسمنت كمثبت بالنسب (0,5 1,5٬)٪. يتم المقارنة بين طبقة الأساس المعالجة وغير المعالجة من حيث القوة. المواد المستعملة كطبقة الأساس هي المادة الأساسية التقليدية التي أخذت من مقلع النباعي. تم تحضير نماذج بمعدل ثلاثة لكل نسبة قدر الامكان. (68) المجموع الكلي للنماذج التي أعدت لفحص قوة الانضغاط. النتائج المستحصلة أظهرت زيادة في قوة طبقة ألاساس بواسطة عامل الازدياد بمقدار (2,56) عند استخدام ركام الكونكريت المعاد تدويره. كذلك مثبت النورة - غبار السيليكا بنسبة (5%)، عامل الازدياد في القوة ازداد بحوالي(42,248) أكثر من العينة الغير المثبتة.


Article
Strength of Concrete Using Different Types of Additives
مقاومة الخرسانة المنتجة باستخدام أنواع مختلفة من المواد المضافة

Author: Ali Hussain Ali علي حسين علي
Journal: Journal of Engineering and Sustainable Development مجلة الهندسة والتنمية المستدامة ISSN: 25200917 Year: 2011 Volume: 15 Issue: 4 Pages: 30-48
Publisher: Al-Mustansyriah University الجامعة المستنصرية

Loading...
Loading...
Abstract

In this investigation, conventional concrete mixes (as a reference mixes) and concretemixes produced with (5, 10, and 20)% of cement replacement by silica fume, crushed glass and crushed nucleate additives respectively, these mixes were used in preparing (144) concrete specimens. Laboratory test results in dictated that:

a)There was a significant increase (17.6 to 88.5 and 8.8 to 25.8) % in the compressive strength of concretes produced with silica fume and crushed glass additives respectively, while a significant reduction (29.6 to 62.6)% in the compressive strength was recorded using concrete mixes with crushed nucleate.
b)there lation ships between the 7-day(fc,7)and:the28day(fc,28)compressive strength areas follows
- [fc,28 = 1.701 fc,7] for (reference mix);
- [fc,28 = (1.590 to 1.931) fc,7] for silica fume mixes;
- [fc,28 = (1.660 to 1.813) fc,7] for crushed glass mixes;
- [fc,28 = (1.521 to 1.796) fc,7] for crushed nucleate mixes.
c)percentages of increasing in both flexural and splitting tensile strengths, as compared with conventional concrete, are as follows:
- for silica fume mixes: (26.92 to 48.72 and 44.44 to 72.22)% respectively;
- for crushed glass mixes: (46.15 to 71.79 and 11.11 to 36.11)% respectively.
On the other hand, crushed nucleate mixes recorded a drop in both flexural and splitting tensile strengths (5.41 to 34.48 and 28.57 to 71.43)% respectively.
d)Finally, the research included also deriving different relationships between compressive, flexural and tensile strengths of concretes produced using silica fume and crushed glass additives.

في هذا البحث، تم انتاج خلطات خرسانية عادية (كخلطات مرجعية) وخلطات خرسانية اخرى باحلال نسب ( 5، 10 ،20 )% بدلا من الاسمنت البورتلاندي بغبار السيليكا، الزجاج المطحون، و نوى التمر المطحون على التوالي، وهذه الخلطات استعملت في تهيئة (144) نموذج خرساني. نتائج الفحوصات المختبرية بينت ما يلي: أ‌.تسجيل زيادة معتبرة في مقاومة انضغاط الخرسانة ( 17.6 to 88.5و 8.8 to 25.8)% المنتجة بغبار السيليكا و الزجاج المطحون على التوالي، بينما الخرسانة المنتجة بنوى التمر المطحون قد سجلت نقصان في مقاومة الانضغاط بمقدار يتراوح بين (29.6 to 62.6)%. ب‌.العلاقة بين مقاومة الانضغاط بعمر7 و28 يوم كانت كما يلي: - الخلطة المرجعية [fc,28 = 1.701 fc,7]، -الخلطات الخرسانية بغبارالسيليكا [fc,28 = (1.590 to 1.931) fc,7]، -الخلطات الخرسانية بالزجاج المطحون [fc,28 = (1.660 to 1.813) fc,7]، -الخلطات الخرسانية بنوى التمر المطحون [fc,28 = (1.521 to 1.796) fc,7]. ‌ج.نسب الزيادة في كل من مقاومة الشد والتكسير، مقارنة مع الخلطات المرجعية، وكما يلي: -الخلطات الخرسانية بغبارالسيليكا (44.44 to 72.22 & 26.92 to 48.72) على التوالي، -الخلطات الخرسانية بالزجاج المطحون (11.11 to 36.11 & 46.15 to 71.79)% على التوالي. -و من ناحية اخرى، تم تسجيل هبوط في مقاومات الشد والتكسير للخلطات الخرسانية بنوى التمر المطحون بمقدار (28.57 to 71.43 & 5.41 to 34.48)% على التوالي. ‌د.واخيرا، تضمن البحث اشتقاق علاقات رياضية بين مقاومة الانضغاط ومقاومة الشد من جهة ومقاومة الانضغاط ومقاومة التكسير من جهة اخرى للخلطات الخرسانية المنتجة بغبار السيليكا والزجاج المكسر.


Article
Structural Behavior Of Self-Compacting Concrete Reinforced T-Beams

Authors: Mohammed M. Salman محمد مصلح سلمان --- Mohammed M. Rasheed --- Yahya S. Khudhair kingconger2000@yahoo.com
Journal: Journal of Engineering and Sustainable Development مجلة الهندسة والتنمية المستدامة ISSN: 25200917 Year: 2013 Volume: 17 Issue: 1 Pages: 284-299
Publisher: Al-Mustansyriah University الجامعة المستنصرية

Loading...
Loading...
Abstract

The study is concerned with the structural behavior of (12) reinforced T-shaped cross-section beams made of self-compacting concrete under flexural with two types of fibers (polypropylene and steel fibers). Compression and tensile strengths, deflection, ductility and cracking behavior are considered. Experimental results are compared with these evaluated based on the (ACI 318 – 08). The variables studied are reinforcing ratio (%ρ) (between %4.4907 - %6.0434) using different sizes of reinforcing steel bars (Ф25mm, Ф20mm, Ф16mm, Ф12mm, Ф6mm, Ф4mm, and Ф6mm wire mesh), in addition to two fibers, [polypropylene (RHEO-FIBERS®) and steel fibers (FIBERFORCE®) at a rate of [(1kg/m3) & (0.5%)], respectively. The tested T-Beams were categorized into three groups, each group includes (4) T-Beams of different steel ratios (ρ %). In Group (G1), polypropylene fibers were used. In Group (G2), steel fibers were used. The reference group (G3) is with the same reinforcement ratios as in the previous two groups. It was concluded that using polypropylene fibers (RHEO-FIBERS®)in addition to (1kg/m3) in self-compacting concrete (SCC) improves the cracking control, ductility by (Δμd = 0.5846 – 4.0514). However, fibers have minor effect on the deflection behavior of T-Beams. On the other hand, when steel fibers type (FIBERFORCE® steel fibers) of a volume rate of (Vf = 0.5% of concrete volume Vc) are used in combination with self-compacting concrete, affects the flexural behavior of T-Beams (reducing deflection, increasing ultimate loads' by (11.02% - 16.80%) and improving the ductility by (Δμd = 4.9232 – 12.1238), but it has a minor effect on reducing the crack width.

أن هذا البحث يهدف ألى دراسة السلوك الأنشائي للعتبات الخرسانية ذات المقاطع بشكل حرف (T) بعدد (12 عتب) والمسلحة بنوعين من الألياف (ألياف البوليمر وألياف الحديد) , وأن دراسة هذا البحث تتضمن برنامج عملي شامل ، مع الأخذ بنظر الأعتبار تأثير أضافة هذين النوعين من الألياف (ألياف البوليبروبيلين وألياف الحديد) على سلوك الخرسانة الذاتية الرص كتأثيرها مثلا على (مقاومة الأنضغاط , ومقاومة الشد , ومقدار الهطول , وتحسين المطيلية ، بالأضافة ألى نمط وعرض التشقق الذي ممكن أن يظهر في الخرسانة الذاتية الرص) ومقارنة النتائج المستحصلة عمليا مع النتائج المحسوبة تخمينيا طبقا للمدونة الأمريكية المرقمة ACI 318) لسنة (2008) , وكل هذا تم دراسته خلال هذا البحث العملي . المتغيرات التي تم دراستها خلال البحث هي نسبة التسليح (ρ%) حيث تم أخذها بنسب تتراوح مابين (4.4907% - 6.0434%) وذلك بأستخدام أقطار مختلفة من قضبان حديد التسليح هي (25 ملم , 20ملم , 16ملم , 12ملم , 6 ملم , 4 ملم , شبكة بقطر 6 ملم) , بالأضافة ألى ذلك أنه تم أستخدام ألياف البوليبروبيلين من نوع (RHEO-FIBER®) بمعدل أضافة مقداره (1كغم / م3) , وألياف الحديد من نوع (FIBERFORCE®) بنسبة أضافة مقدارها (%0.5) كنسبة حجمية من الحجم الكلي للخرسانة الذاتية الرص . كل العتبات ذات المقاطع بشكل حرف (T) تم توزيعها على ثلاث مجاميع , كل مجموعة أستخدم فيها أربع نسب من التسليح بأقطار مختلفة من حديد التسليح , وهذه النسب تم تكرارها على المجاميع الثلاثة مع أستخدام ألياف البوليبروبيلين من نوع(RHEO-FIBERS®) في خلطة الخرسانة الذاتية الرص لعتبات المجموعة الأولى , بينما تم أستخدام ألياف الحديد من النوع (FIBERFORCE®) في خلطة الخرسانة الذاتية الرص لعتبات المجموعة الثانية , أما المجموعة الثالثة فقد تم صبها بدون أستخدام أي نوع من الألياف لكونها المجموعة التي سوف يتم المقارنة معها . وقد أظهرت النتائج العملية لهذا البحث أنه بأضافة ألياف البوليبروبيلين من النوع أعلاه وبنسبة أضافة مقدارها (1كغم / م3) مع الخرسانة الذاتية الرص تؤثر بدرجة كبيرة على تحسين السيطرة على التشققات التي يمكن أن تحصل للخرسانة وتعمل على تقليلها , وكذلك تحسين عامل المطيلية بمقدار يتراوح مابين [التغير بالمطيلية (Δμd) = 2.0356 ألى 4.3515]، بينما يكون تأثيرها على تقليل مقادير الهطول للعتبات الخرسنية الذاتية الرص قليلا . لكن عندما يتم أستخدام ألياف الحديد من النوع (FIBERFORCE®) وبنسبة أضافة حجمية مقدارها (0.5% من الحجم الكلي للخرسانة الذاتية الرص) تظهر تأثيرا كبيرا على تقليل مقادير الهطول وزيادة مقدار الحمل الأقصى لفشل العتب الخرساني بمقادير عالية تتراوح مابين (11.78% ألى 18.42%) مع تحسين عامل المطيلية بمقدار يتراوح مابين [التغر بالمطيلية (Δμd) = 4.9232 ألى 12.1238], ولكنها تكون ذات تأثير قليل على تقليل عرض التشققات التي تظهر على العتبات الخرسانية الذاتية الرص ذات المقاطع بشكل حرف (T).الكلمات الدالة: الخرسانة الذاتية الرص؛ العتب ذو المقطع بشكل (T)؛ ألياف الحديد؛ ألياف البوليمر (البوليبروبيلين)؛ الملدنات المتفوقة؛ مسحوق السيليكا الفعال (مادة بوزولانية ذات خواص أسمنتية)؛ مسحوق حجر النورة الكلسي؛ السلوك المرن؛ سلوك التشقق؛ الهطول؛ عامل المطيلية.

Listing 1 - 5 of 5
Sort by
Narrow your search

Resource type

article (5)


Language

Arabic and English (5)


Year
From To Submit

2018 (1)

2014 (1)

2013 (2)

2011 (1)