Article
Microstructure and Some Properties of Aluminum-Silicon Matrix Composites Reinforced by Alumina or Chromia
التركيب المجهري وبعض الخصائص للمواد المتراكبة نوع الالمنيوم- سليكون المقواة بأوكسيدالايتريوم او أوكسيد الالومينا

Author: Ahmed A. Moosa احمد علي موسى
Journal: Al-Khwarizmi Engineering Journal مجلة الخوارزمي الهندسية ISSN: 18181171 23120789 Year: 2010 Volume: 6 Issue: 1 Pages: 57-68
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

In this work, yttrium oxide particles (powder) reinforced AL-Si matrix composites (Y2O3/Al-Si) and Chromium oxide particles reinforced AL-Si matrix composites (Cr2O3/AL-Si) were prepared by direct squeeze casting. The volume percentages of yttrium oxide used are (4, 8.1, 12.1, 16.1 vol %) and the volume percentages of the chromium oxide particles used are (3.1, 6.3, 9.4, 12.5 vol. %). The parameters affecting the preparation of Y2O3/Al-Si and Cr2O3/AL-Si composites by direct squeeze casting process were studied. The molten Al-Si alloy with yttrium oxide particles or with chromium oxide particles was stirred again using an electrical stirrer at speed 500 rpm and the molten alloy was poured into the squeeze die cavity. The pouring temperature that used for all castings is (700)˚C. The required squeeze pressure, 53 MPa, was then applied for 30 seconds at a delay time of 5. The die temp is (200˚C). The Y2O3/Al-Si composites and Cr2O3/Al-Si composites produced by squeeze casting have more microstructure refinement, higher hardness and lower wear rate than the unreinforced alloy.

تم دراسة تحضير مادة متراكبة ذات اساس من سبيكة الالمنيوم- سليكون مقواة بدقائق اوكسيد الكروم (الالمنيوم- سليكون/ اوكسيد الكروم ) و دقائق اوكسيد الايتريوم (الالمنيوم- سليكون/ اوكسيد الايتريوم ) بطريقة السباكة بالعصر المباشر. تم اضافة كسور حجمية مختلفة من دقائق اوكسيد الكروم3.1, 6.3 , 9.4, 12.5 vol %) ) وكذلك اضافة كسور حجمية مختلفة من اوكسيد الايتريوم(4, 8.1, 12.1, 16.1 vol %) . اجريت عملية خلط منصهر سبيكة الالمنيوم- سليكون/ اوكسيد الايتريوم او منصهر سبيكة الالمنيوم- سليكون/ اوكسيد الكروم باستخدام خلاط كهربائي وبسرعة 500 دورة /دقيقة . تم استعمال المتغيرات مثل ضغط العصر (53MPa)، درجة حرارة الصب (700˚C)، زمن الكبس (30sec.) وزمن التريث (5sec.). ودرجة حرارة القالب(200˚C ) .تم فحص البنية المجهرية للمواد المتراكبة ،الصلادة ومعدل البلى . اظهرت النتائج حصول تنعيم في البنية المجهرية في السبائك المقواة مقارنة مع السبيكة غير المقواة . كما اظهرت النتائج زيادة في الصلادة وانخفاض في معدل البلى في السبائك المقواة مقارنة مع السبيكة غير المقواة .


Article
Effect of Magnesium Addition on Corrosion Resistance of Aluminum -17%Silicon Alloy
تأثير أضافة المغنيسيوم على مقاومة االتآكل لسبيكة المينيوم – سيليكون 17%

Authors: Muna Khethier Abbass منى خضير عباس --- Khairia Salman Hassan خيرية سلمان حسن --- Kayser Aziz Ameen قيصر عزيز أمين
Journal: Al-Khwarizmi Engineering Journal مجلة الخوارزمي الهندسية ISSN: 18181171 23120789 Year: 2016 Volume: 12 Issue: 4 Pages: 50-58
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

The electrochemical behavior of Al-17%Si alloy is investigated in 3.5wt% NaCl solution. Many alloys with addition of the different wt% magnesium metal of 1wt%, 2%, 3wt% ,4.5wt% ,and 9wt% were prepared by gravity die casting . The microstructures of prepared alloys were examined by optical and SEM microscopes. Corrosion behavior was investigated by using potentiostat instrument under static potentials test and corrosion current was recorded to determine corrosion resistance of all prepared samples. It was found that the addition of Mg metal improves the corrosion resistance of Al-17%Si alloy in 3.5%NaCl solution. The alloy containing 1%Mg shows less corrosion rate than the others while the alloys containing 4.5%Mg, 9%Mg content have the better pitting corrosion resistance than other alloys.

في هذا البحث تم دراسة السلوك الكهروكيمياوي لسبيكة (Al- 17%Si) في محلول (3.5 wt% NaCl)، وذلك باضافة معدن المغنيسيوم للسبائك وبنسب مختلفة (1wt%, 2wt%, 3wt%, 4.5wt%, 9wt%) حيث تم تحضير السبائك بواسطة قوالب الصب بالجاذبية.وقد تم استعمال المجهر الضوئي والمجهر الالكتروني الماسح لفحص التركيب المجهري للسبائك. وتم بحث اسلوب التآكل بواسطة استعمال جهاز المجهاد الساكن (Potentiostat) وتحت اختبار الجهد الساكن وتم تسجيل تيار التأكل وحساب مقاومة التأكل لكل النماذج المحضرة. وقد لوحظ انه عند اضافة معدن المغنيسيوم يزيد من مقاومة التأكل في سبائك (Al-17%Si) في محلول (3.5% NaCl). ولوحظ ايضاً ان السبائك الحاوية على (1% Mg) اظهرت اقل معدل تآكل من السبائك الاخرى بينما كانت السبائك الحاوية على (9% Mg, 4.5% Mg) تمتلك افضل مقاومة للتاكل النقري من باقي السبائك.


Article
Effect of Lanthanum Addition on the Microstructure ofMg-4Al Alloy
تاثير اضافة معدن اللنثانيوم على خصائص سبيكة المغنسيوم - 4% المنيوم

Author: Ahmed A. Moosa احمد علي موسى
Journal: Al-Khwarizmi Engineering Journal مجلة الخوارزمي الهندسية ISSN: 18181171 23120789 Year: 2011 Volume: 7 Issue: 2 Pages: 75-82
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

This research was to determine the effect of rare earth metal (REM) on the as-cast microstructure of Mg-4Al alloy.
The rare earth metal used here is Lanthanum to produce Mg-4Al-1.5La alloy. The microstructure was characterized by
optical microscopy. The phases of this alloy were identified by X-ray diffraction. The microstructure of Mg-4Al
consists of α-Mg and grain boundaries with precipitated phase particles. With the addition of Lanthanum, three distinct
phases were identified in the X-ray diffraction patterns of the as cast Mg-4Al-1.5La: Mg, Al11La3, Al4La. The Mg17Al12
phase was not detected. The addition of Lanthanium increases the hardness and decrease the wear rate of Mg-4Al.

يهدف هذا البحث الى دراسة تاثير اضافة عناصر الارض النادرة على سبائك (Mg-4Al) والحيلولة دون اكسـدة المغنيسيوم أو احتراقه وأنتاج سبيكة (Mg-4Al-1.5 La).كما تضمن البحث الفحوصات المجهرية وفحص الأشعة السينية لمعرفة الأطوار الناتجة في سبيكة ( (Mg-4Al-1.5 La. أظهرت النتائج أن سبيكة ((Mg-4Al تحتوي على الطور ( α- Mg) مع وجود ترسبات على الحدود البلورية .اما الاطوار في سبيكة ( (Mg-4Al-1.5 La فهي . Mg, Al11La3, Al4La مع عدم ظهور الطور Mg17Al11 . ان اضافة اللنثانيوم يؤدي الى زيادة الصلادة وانخفاض معدل البلى


Article
Effect of Sintering Time for Aluminum / Stainless Steel Composite on Mechanical Properties
تأثير زمن التلبيد لمركب الألمنيوم / الصلب اللامصديء على الخواص الميكانيكية

Author: Saheb Mohammed Mahdi صاحب محمد مهدي
Journal: Journal of Engineering and Sustainable Development مجلة الهندسة والتنمية المستدامة ISSN: 25200917 Year: 2013 Volume: 17 Issue: 1 Pages: 154-161
Publisher: Al-Mustansyriah University الجامعة المستنصرية

Loading...
Loading...
Abstract

The effect of sintering time on mechanical properties of two powder composition containing 25 wt% and 12.5 wt% 316L Austenitic Stainless Steel and the balance is Aluminum has been studied, at two sintering temperatures 500 and 530 Co for sintering time (30,60,90,120,180) minutes. Results of compression tests showed that compression strength and yield strength increase with sintering time, reaches a maximum value and then decreases gradually, for both compositions and sintering temperatures used. Hardness showed a similar relation with sintering time for both compositions and sintering temperatures, microstructure of the sintered parts showed a two phase structure, one phase was identified using XRD technique as FeAl3 , the other phase is Al matrix.

تم في هذا البحث دراسة تأثير زمن التلبيد على الخواص الميكانيكية لخليط مشكل بطريقة متالورجيا المساحيق ، يتكون من 25% و 12.5% وزناً صلب لامصديء نوع (316L) والباقي معدن الألمنيوم ، عند درجتي حرارة تحميص هي 500 و 530 oم لزمن تلبيد (180,120,90,60,30) دقيقة. بينت نتائج اختبارات الضغط ان مقاومة الضغط ومقاومة الخضوع ازدادت مع زيادة زمن التلبيد ، حتى قيمة قصوى ثم تنخفض تدريجياً .لكل من الخليط المعدني ولدرجتي حرارة التلبيد المستخدمة. وقد اظهر اختبار الصلادة نفس التصرف وايضا لكل من تركيب الخليط المعدني ولدرجتي حرارة التلبيد.ان التركيب ألمجهري للعينات التي جرى لها تلبيد أظهرت وجود طورين ، حيث تم تحديد احد الطورين باستخدام حيود أشعة X وكان عبارة عن) (FeAl3 وكان الطور الأخر هو الأساس معدن الألمنيوم .


Article
Effect of Cryogenic Treatment on the Properties of Low Carbon A858 Steel

Authors: Murtadha Qasim Idan AL-kinani --- Abbas A. Hussein
Journal: Journal of Engineering مجلة الهندسة ISSN: 17264073 25203339 Year: 2012 Volume: 18 Issue: 7 Pages: 837-843
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

This study is concerned with the effect of Deep Cryogenic Treatment (DCT) at liquid nitrogen temperature (-196 oC) on the mechanical properties and performance of low carbon steel (A858).The tests specimens were divided in to two groups, the first group was subjected to the conventional heat treatment of normalizing, and the second group was also normalized then subjected to (DCT).The results have shown that after (DCT), the Hardness, Tensile properties and the impact energy absorbed were all slightly increased. However the fatigue test showed some positive improvement in fatigue limit by 20(N/mm2), and the volume wear rates at different loads were significantly decreased after (DCT). The changes in microstructure due to (DCT) were clearly noticeable, the grain boundaries were no longer visible, and the Pearlite isles globalization was obvious.

هذه الدراسة تتركز على تأثير المعاملة الزمهريرية العميقة عند درجة حرارة النتروجين المسال والبالغة (-196oC) على الخواص الميكانيكية وخواص الأداء للفولاذ منخفض الكربون A858.عينات الاختبار قسمت إلى مجموعتين استنادا إلى ما قبل وما بعد المعاملة الزمهريرية , المجموعة الأولى تضمنت المعاملة الحرارية التقليدية للفولاذ وهي التطبيع, والمجموعة الثانية تضمنت المعاملة الزمهريرية ما بعد معاملة التطبيع. أن العينات في المجموعة الثانية تم تم مقارنته نتائج الخواص الميكانيكية الناتجة بالمعاملة الزمهريرية العميقة مع تلك التي لم تتم معاملتها بهذه الطريقة. أن الاختبارات الميكانيكية تضمنت اختبارات الصلادة, الشد والصدمة بينما اختبارات الأداء تمثلت باختبارات الكلال والبلى.اظهرت نتائج الاختبارات بعد أجراء المعاملة الزمهريرية العميقة , زيادة قليلة في قيم الصلادة وخواص الشد (جهد الخضوع, المفاومة القصوى , الاستطالة النسبية) وطاقة الصدم.أختبار الكلال أظهر تحسينات ايجابية في قيم حد الكلال ما بعد المعاملة الزمهريرية , حيث انها ازدادت بمقدار20 ن/ملم2. وبالنسبة لمعدل البلى ألحجمي عند أحمال مختلفة فقد أنخفض بعد المعاملة الزمهريرية بنسبة كبيرة , مما يعني ان المعاملة الزمهريرية العميقة تحسن مفاومة البلي للفولاذ منخفض الكربون.التغيرات في البنية المجهرية نتيجة المعاملة الزمهريرية كانت واضحة لهذا الفولاذ, حيث ان الحدود البلورية لم تظهر وحدث تكتل للبيرلايت بشكل واضح .


Article
Effect of Friction Stir Processing (FSP) to the Mechanical Properties of 7075-T73 Aluminum Alloys Plates Welded by Friction Stir Welding
تأثير معالجة للحام الاحتكاكي للمزج (FSP) على الخواص الميكانيكية لسبائك الألمنيوم من نوع 7075-T73 الملحومة بواسطة اللحام الاحتكاكي للمزج

Authors: Kadhim Kamail Resan كاظم كامل رسن --- Ayad Murad Takhakh اياد مراد طخاخ --- Ali Abed Salman علي عبد سلمان
Journal: Journal of Engineering and Sustainable Development مجلة الهندسة والتنمية المستدامة ISSN: 25200917 Year: 2014 Volume: 18 Issue: 5 Pages: 45-60
Publisher: Al-Mustansyriah University الجامعة المستنصرية

Loading...
Loading...
Abstract

Friction stir processing is a new method of changing the properties of a metal through intense, localized plastic deformation ,this process mixes the material without changing the phase (by melting or otherwise) and creates a microstructure with fine, equiaxedgrains , It is used to improve the microstructural properties of metals. In this paper , the enhancement of mechanical properties of friction stir welding specimens at variable rotation speeds (1500,1700 and 1900 rpm ) with constant feed speed(40mm/min) for 7075-T73 aluminum alloy is studied by using the friction stir processing method at the same variable rotation speed and feed speed in order to transform a heterogeneous microstructure to a more homogeneous, refined microstructure.The best results of the weld gained at the parameter 40 mm/min weld speed and 1700RPM rotation speed for the friction stir welding (FSW) and friction stir processing (FSP) where the efficiency reaches to 83.7% for FSW and 92.99% for FSP of the ultimate tensile strength of the parent metal.

تعتبر طريقة معالجة المزج الاحتكاكي من الطرق الحديثة لتحسين خصائص المعادن في هذه العملية يتم مزج المواد دون اي تغيير في الأطوار (عن طريق انصهار أو غير ذلك) و يتم استخدام تلك الطريقة لتحسين خصائص البنية ألمجهريه للمعادن. في هذه الدراسة ، تم قياس الخواص الميكانيكية لعينات لحام المزج بالاحتكاك بسرعات متغيرة ( 1500،1700 و 1900 دورة في الدقيقة ) مع سرعة تغذية مقدارها ( 40ملم / دقيقة) لسبائك الألمنيوم من نوع 7075-T73 و من ثم تم استخدام طريقة المعالجة بالمزج الاحتكاكي لنفس سرع الدوران وسرعة تغذية المستخدمة في اللحام بالاحتكاك من أجل تحويل البنية ألمجهريه إلى بنية مجهريه أكثر تجانسا.و كانت أفضل نتائج لخط اللحام عند سرعة خطية مقدارها 40 مم / دقيقة و سرعة دوران 1700دورة / دقيقة بالنسبة للحام المزج بالاحتكاك وكذلك عند المعالجة بالمزج بالاحتكاك حيث كانت الكفاءة لـ 83.7 ٪ و 92.99 ٪ على التوالي و قد تم حساب الكفاءة اعتمادا على أقصى مقاومة شد للمعدن الأساسي.

Listing 1 - 6 of 6
Sort by
Narrow your search

Resource type

article (6)


Language

Arabic and English (6)


Year
From To Submit

2016 (1)

2014 (1)

2013 (1)

2012 (1)

2011 (1)

More...