STUDY THE EFFECT OF ADDING DIFFERENT RATIOS OF IRON AND ALUMINUM OXIDES ON THE COMPRESSIVE STRENGTH AND THE SOFTENING TEMPERATURE OF A LOW-DENSITY POLYETHYLENE
دراسة تاثير اضافة نسب مختلفة من اكاسيد الحديد و الالمنيوم على مقاومة الانضغاط ودرجة حرارة الليونة للبولي اثيلين واطئ الكثافة

Loading...
Loading...
Abstract

This research aims to study the effect of adding Iron Oxide Fe2O3 and Aluminum Oxide Al2O3 on mechanical properties of Low Density Polyethylene (LDPE), where various weight percentages of the oxides of (1%, 3%, 5%, 7%, and 10%) were used.To investigate the effect of adding oxides on the mechanical properties of (LDPE), Compression test was performed and the ultimate compression test was determined, then the softening point was measured. From the results reached it was concluded that the best compression strength was recorded at 7% addition of Iron Oxide, while for the Aluminum Oxide the highest compression strength was recorded at 5%. Also it was found that the relationship was directly proportional between softening point and oxide percentage. It was noticed that the adding of the oxides up to 10% results in decreasing of the formability during compression.

يهدف هذا البحث الى دراسة تاثير اضافة اوكسيد الحديد واوكسيد الالمنيوم على الخواص الميكانيكية للبولي اثيلين، حيث استخدمت نسب وزنية مختلفة من الاكاسيد وهي(1%,3%,5%,7%,10%).لتقييم مدى تاثير الاكاسيد المظافة على الخواص الميكانيكية تم اجراء اختبار الانضغاط وتحديد اجهاد الانضغاط الاقصى ومن ثم قياس نقطة الليونة. ومن خلال النتائج التي تم التوصل اليها تبين ان افضل مقاومة انضغاط كانت عند اضافة اوكسيد الحديد بنسبة 7% ، اما بالنسبة لاوكسيد الالمنيوم فكانت افضل قيمة مقاومة انضغاط عند اضافة 5%. كذلك تبين ان العلاقة كانت طردية مابين زيادة النسب المضافة ونقطة الليونة. وقد لوحظ ان اضافة اوكسيد الحديد واوكسيد الالمنيوم لغاية 10% ادت الى انخفاض في قابلية التشكيل اثناء الانضغاط.


Article
Investigation of Physical Properties of Polymeric Nanocomposite Material Used in Structural Applications
الاستقصاء عن الخصائص الفيزيائية للمواد المتراكبة النانوية البوليمرية المستخدمة في التطبيقات الهيكلية

Authors: Sihama Issa Salih سهامه عيسى صالح --- Wleed Bdaiwi Salih وليد بديوي صالح --- Salam Obaid Abdulghani سلام عبيد عبد الغني
Journal: Diyala Journal For Pure Science مجلة ديالى للعلوم الصرفة ISSN: 83732222 25189255 Year: 2017 Volume: 13 Issue: 1 - part 2 Pages: 60-71
Publisher: Diyala University جامعة ديالى

Loading...
Loading...
Abstract

In the current research were prepared composite materials, from thermoplastic polymer (PMMA) as a matrix materials by used the hand lay-out technique. The composite material was prepared from two sets of composites materials the first set consists of a poly methyl Methacrylate (PMMA) resin as matrix material reinforced by nanoparticle of aluminum Oxide (Al2O3) with average size (53.60) nm once and the second group is composed of poly methyl Methacrylate resin reinforced by nanoparticle of Magnesium Oxide (MgO) with average size (52.54) nm. The research includes the study of the influence of the selected volumetric fraction ratios of (0.5, 1, 1.5%) for the reinforce materials, on the properties of the prepared composite materials. Number of physical tests which included (density, Thermal Conductivity, specific heat and thermal diffusivity, and DSC) . which all test were done at room temperature. Result of the work shows that the values of Thermal Conductivity, Specific Gravity, Tg and Tm) increase with the increase of volume fraction of nanoparticle for both groups of polymeric Nano composites material. Whereas decreased the specific heat values with the increase of volume fraction of nanoparticle for both groups of polymeric Nano composites material Moreover the poly methyl Methacrylate Nano composite material reinforced with nanoparticle of aluminum Oxide possesses physical properties higher than those of Article composites reinforced with nanoparticle of Magnesium Oxide .

اجرية في البحث تحضیر مواد متراكبة ذات أساس مادة مطاوعة للحرارة بطريقة الصب الیدوي وقد حضرت مجموعتین من المواد المتراكبة النانوية المجموعة الأولى تتكون من راتنج البولي مثیل میثا اكريلیت (PMMA) كمادة أساس مدعمة بدقائق أوكسید الألمنیوم النانوية (Al2O3) ذات معدل حجم حبیبي (53,60 nm) نانو متر مرة والمجموعة الثانیة تتكون من راتنج البولي مثیل میثا اكريلیت (PMMA) كمادة أساس مدعمة بدقائق أوكسید المغنیسیوم النانوية (MgO) ذات معدل حجم حبیبي (52,54 nm). تضمن البحث دراسة تأثیر الكسر الحجمي المختار (0.5 ، 1 ، 1.5)% لدقائق مادتا التقوية على خصائص المواد المتراكبة المحضرة . وقد أجريت مجموعة من الإختبارات الفیزيائیة المتمثلة بالكثافة والتوصیلیة الحرارية والإنتشارية الحرارية والحرارة النوعیة والمسعر الماسح التفاضلي و المجهر الألكتروني الماسح ) ، وجمیع هذه الإختبارات تم إجراؤها عند درجة حرارة الغرفة . وقد أظهرت نتائج البحث إن قیم (التوصیلیة الحرارية والإنتشارية الحرارية والكثافة) تزداد مع زيادة الكسر الحجمي لدقائق مادتي التقوية في المادة المتراكبة . بینما قلت قیم (الحرارة النوعیة) مع زيادة الكسر الحجمي لدقائق مادتي التقوية .. وإن البولي مثیل میثا اكريلیت (PMMA) المدعم بدقائق أوكسید الألمنیوم النانوي يمتلك خصائص فیزيائیة أعلى من مثیلاتیها للمادة المتراكبة المدعمة بدقائق أوكسید المغنیسیوم النانويه كما بینت الدراسة زيادة درجة حرارة التحول الزجاج مع زيادة الكسر الحجمي لمادتي التقوية .