Article
The Effect of the Addition of Natural Rubber to (U-PTE) Resin on some Mechanical Properties
تاثیر اضافة المطاط الطبیعي لراتنج الالكاید على بعض الخواص المیكانیكیة

Author: Wafaa Mahdi Salih وفاء مھدي صالح
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2014 Volume: 32 Issue: 9 Part (A) Engineering Pages: 304-310
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

In this research polymer was prepared from Alkyd resin (U-PTE) with ratio 100% the and natural rubber with ratio 30%. The mixing process was performed by hand lay-up method. Some mechanical properties were studied in this work which included (flexural bending, shear stress, Impact test (charpy method) . the results showed that the addition of natural rubber to (u-pte) resin with this ratio leads to become the brittle behavior and decrease in the shear stress increase the ability of material to impact because the blend materials become elastic .the flexural strength increase of blend two times comparing with its value of pure resin while the result of shear stress value of blend showed decreasing with ratio(43%) but the impact value of blend increased with ratio (20%) with it value before the blending.

تم في هذا البحث دراسة تأثير اضافة نسبة 30% من المطاط الطبيعي لمادة بوليمرية (راتنج الالكايد ) وتمت مقارنتها بالنتائج لاختباري متانة الانحناء واجهاد القص واختبار الصدمة بطريقة جاربي في الحالتين لنفس المادة البوليمرية النقية (بدون اضافة ) وقد تم الخلط باستخدام طريقة القولبة اليدوية ، حيث وجد إن إضافة هذا النوع من المطاط الى راتنج الألكايد بهذه النسبة يؤدي ان يصبح السلوك اقرب الى السلوك المطيليى وكذلك ان اضافة المطاط خفض من قيمة اجهاد القص وازدادت قابلية المادة الى تحمل الصدمات بسبب تحول الخليط من مادة هشه الى مادة مرنة ذو معامل مرونة أقل ومتانة أعلى ومطيلية اعلى . وسجلت قيم متانة الانحناء للخليط زيادة الضعف عن قيمتها للراتنج بمفرده وأظهرت نتائج اجهاد القص انخفاضا مقداره (43%) في حين قيمة الصدمة ازدادت بمقدار (20%) مقارنة بقيمتها الأصلية قبل الخلط.


Article
The Effects of Wet Etching of Glass Fibers and Polyamide Fibers on The Bending and Impact Properties of The Resulting Composite Materials
تأثير التحفير الرطب لالياف الزجاج والياف البولي اميد على خواص الانحناء والصدم للمواد المركبة الناتجة

Author: ذوالفقار كريم الابراهيمي
Journal: Iraqi journal of mechanical and material engineering المجلة العراقية للهندسة الميكانيكية وهندسة المواد ISSN: 20761819 Year: 2009 Volume: 9 Issue: 2 Pages: 265-278
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

Improving the bonding strength can be achieved by surface treatment of fibers . Etching is one of the methods of this treatment , in this investigation wet etching of E-glass fibers and polyamide fibers carried out by using (H2O + NaOH) solution to get pits on their surface to increase the surface roughness . Group of tests was carried out to study the effect of this treatment on the mechanical (bending and impact) properties of a material composed of unsaturated polyester reinforced by (10 % wt) of etched glass fibers and Etched polyamide fibers . Also Calculation of the weight loss and executing of microscopic photo .The results show :- Increase of the bending strength of etched glass fibers reinforced composite materials with a maximum percentage of (301 %) compared with samples reinforced with untreated fibers . This maximum percentage was found when the fibers are treated at (25 oC) for (1 % NaOH) and (3 hr) .- Increase of the bending strength of etched polyamide fibers reinforced composite materials with a maximum percentage of (155 %) compared with samples reinforced with untreated fibers . This maximum percentage was found when the fibers are treated at (25 oC) for (1.5 % NaOH) and (3 hr) .- Increase of the impact strength of etched glass fibers reinforced composite materials with a maximum percentage of (270 %) compared with samples reinforced with untreated fibers . This maximum percentage was found when the fibers are treated at (25 oC) for (1 % NaOH) and (3 hr) .- Increase of the impact strength of etched polyamide fibers reinforced composite materials with a maximum percentage of (232 %) compared with samples reinforced with untreated fibers . This maximum percentage was found when the fibers are treated at (25 oC) for (0.5 % NaOH) and (5 hr) .- Increase of the weight loss of polyamide fibers than weigth loss of glass fibers .

يتم تحسين مقاومة الربط بالمعاملة السطحية للالياف . التحفير (Etching) احد اساليب هذه المعاملة حيث تم في البحث الحالي التحفير الرطب لالياف زجاج نوع (E-glass) والياف بولي اميد باستخدام محلول (H2O+NaOH) للحصول على حفر تزيد من الخشونة السطحية . اجريت مجموعة من الاختبارات لدراسة تأثير التحفير على الخواص الميكانيكية (انحناء وصدم) للمادة المركبة ذات اساس من البولي استر غير المشبع المقواة ب(10 % wt) الياف زجاج محفرة والياف بولي اميد محفرة . كذلك تم حساب الفقدان بالوزن واجراء تصوير مجهري . اظهرت نتائج الاختبارات ارتفاع مقاومة كسر الانحناء لعينات المواد المركبة المقواة بالياف زجاج محفرة بنسبة اقصاها (301 %) عند المعالجة في درجة حرارة (25 oC) وبتركيز (1 % NaOH) ولمدة (3 hr) , ارتفاع مقاومة كسر الانحناء لعينات المواد المركبة المقواة بالياف بولي اميد محفرة بنسبة اقصاها (155 %) عند المعالجة في درجة حرارة (25 oC) وبتركيز (1.5 % NaOH) ولمدة (3 hr) . كما اظهرت نتائج الاختبارات ارتفاع مقاومة الصدم لعينات المواد المركبة المقواة بالياف زجاج محفرة بنسبة اقصاها (270 %) عند المعالجة في درجة حرارة (25 oC) وبتركيز (1 % NaOH) ولمدة (3 hr) , ارتفاع مقاومة الصدم لعينات المواد المركبة المقواة بالياف بولي اميد محفرة بنسبة اقصاها (232 %) عند المعالجة في درجة حرارة (25 oC) وبتركيز (0.5 % NaOH) ولمدة (5 hr) . كذلك اظهرت النتائج ارتفاع نسبة الفقدان بالوزن لالياف البولي اميد اكثر من نسبة الفقدان بالوزن لالياف الزجاج .