Article
STUDY THE EFFECT OF ADDING DIFFERENT RATIOS OF IRON AND ALUMINUM OXIDES ON THE COMPRESSIVE STRENGTH AND THE SOFTENING TEMPERATURE OF A LOW-DENSITY POLYETHYLENE
دراسة تاثير اضافة نسب مختلفة من اكاسيد الحديد و الالمنيوم على مقاومة الانضغاط ودرجة حرارة الليونة للبولي اثيلين واطئ الكثافة

Loading...
Loading...
Abstract

This research aims to study the effect of adding Iron Oxide Fe2O3 and Aluminum Oxide Al2O3 on mechanical properties of Low Density Polyethylene (LDPE), where various weight percentages of the oxides of (1%, 3%, 5%, 7%, and 10%) were used.To investigate the effect of adding oxides on the mechanical properties of (LDPE), Compression test was performed and the ultimate compression test was determined, then the softening point was measured. From the results reached it was concluded that the best compression strength was recorded at 7% addition of Iron Oxide, while for the Aluminum Oxide the highest compression strength was recorded at 5%. Also it was found that the relationship was directly proportional between softening point and oxide percentage. It was noticed that the adding of the oxides up to 10% results in decreasing of the formability during compression.

يهدف هذا البحث الى دراسة تاثير اضافة اوكسيد الحديد واوكسيد الالمنيوم على الخواص الميكانيكية للبولي اثيلين، حيث استخدمت نسب وزنية مختلفة من الاكاسيد وهي(1%,3%,5%,7%,10%).لتقييم مدى تاثير الاكاسيد المظافة على الخواص الميكانيكية تم اجراء اختبار الانضغاط وتحديد اجهاد الانضغاط الاقصى ومن ثم قياس نقطة الليونة. ومن خلال النتائج التي تم التوصل اليها تبين ان افضل مقاومة انضغاط كانت عند اضافة اوكسيد الحديد بنسبة 7% ، اما بالنسبة لاوكسيد الالمنيوم فكانت افضل قيمة مقاومة انضغاط عند اضافة 5%. كذلك تبين ان العلاقة كانت طردية مابين زيادة النسب المضافة ونقطة الليونة. وقد لوحظ ان اضافة اوكسيد الحديد واوكسيد الالمنيوم لغاية 10% ادت الى انخفاض في قابلية التشكيل اثناء الانضغاط.


Article
الموصلية الكهربائية لراتنج البولي أثلين المقوى بدقائق السليكا

Author: سعد محمد حمزة
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2015 Volume: 23 Issue: 1 Pages: 84-87
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

Electrical conductivity of low density polyethylene resin reinforced by variety weight fracture (1%,2%,3%,4%,5%) from silica particles with (8µm) grain particles has been studied in this paper before and after reinforcement . The experimental results obtained through measurement of resistivity by (Keithly electrometer type (616 ºC)) and then converted to conductivity show that decreased electrical conductivity of resin after adding silica particles, where the electrical conducting was decreased from 5 ×10-14 (ohm.cm)-1 before adding silica to 8.7 ×10-17 (ohm.cm)-1 after addition (5%) from silica at (40ºC).

الموصلية الكهربائية لراتنج البولي أثلين واطئ الكثافة المقوى بكسر وزني متنوع(1%،2%،3%،4% ،5%) من دقائق السليكا بحجم حبيبي (8µm) تم دراستها في هذا البحث قبل وبعد التقوية . النتائج العملية التي تم الحصول عليها من خلال قياس المقاومية بواسطة Keithly electrometer type (616 ºC))) وتحويلها بعد ذلك إلى الموصلية ، أظهرت إنخفاض الموصلية الكهربائية للراتنج بعد إضافة دقائق السليكا ، حيث إنخفض معدل التوصيل الكهربائي من 5 ×10-14 (ohm.cm)-1 قبل إضافة السليكا إلى 8.7 ×10-17 (ohm.cm)-1 بعد إضافة (5%) من السليكا عند درجة حرارة (40 ºC).


Article
دراسة تأثير إضافة مسحوق قشور الرز على الخواص الميكانيكية لبوليمر البولي اثيلين واطئ الكثافة

Author: ناظم عبد الجليل عبد الله ، أحمد جاسم محمد ، *إبراهيم كاظم إبراهيم ، **فائز جمعة محمد
Journal: Albahir journal مجلة الباهر ISSN: 23125721 Year: 2017 Volume: 6 Issue: 11+12 Pages: 79-89
Publisher: Shiite Endowment ديوان الوقف الشيعي

Loading...
Loading...
Abstract

This research used polyethylene with low density )low Density Polyethylene( as the basis ofmaterial and product by the General Company for Petrochemical Industries )Basra-Iraq( in the formof powder. This polymer produced in )2012(, as function of the percentages of rice husk powder atthe particular size (≤ 250 μm) were investigated through several variables, such as Young's modules,strength, and elongation. The obtained results appeared that the added husk rice powder to reducethe spaces between the polymer chains, which reflects the high ability of the polymer against theapplied stress, and a high degree of homogeneity between the host polymer and the added fillers, andthis increase will give further property that increases the hardness of the prepared specimens which)12.6( MPa at the percentage is )5%(, and the result also indicate a lowered in young's modules atthe percentage (10%), which reflects the increase in the ductile of the polymer grafted with and thewide range of the application for this polymer. The results also appear that the highest point of theproportional limits is )155 N( at the percentage )25%(.

تم في هذا البحث دراسة الخواص الميكانيكية لبوليمر الاثيلين واطئ الكثافةوالمنتج من قبل الشركة العامة لصناعات البتروكيمياوية )بصرة-عراق( على شكل Polyethyleneمسحوق حيث كان إنتاج هذه المادة البوليمرية في عام ) 2012 ( كداله للنسبة الوزنية لمسحوق قشورالرز عند حجم دقائق هذا المسحوق مساو الى) 250 ) مایكرو متر. إذ تمت دراسة عدة متغيرات مثلالاستطالة وقوه الشد عند الوهن والقطع ومعامل يونك، وبينت النتائج المستحصله إن مسحوققشور الرز المضاف يعمل على تقليل الفراغات بين السلاسل البوليمريه مما يعكس إمكانية البوليمرالعالية بتحمل الإجهاد المسلط عليه وتكون درجة التجانس عالية بين كل من البوليمر والحشوات ،وان زيادة نسبة المالئات تضفي زيادة صفة الصلابة على النماذج المحضرة عند النسبة المئوية ) 5%( حيث)% وبينت النتائج أيضا انخفاض معامل يونك مع نسبه المضاف ) 10 ،MPa ) كانت قيمة هي ) 12.6مما يعكس مرونة البوليمر المطعم بقشور الرز وتوسع مدى التطبيقات لهذا البوليمر ،وكانت أعلى قيمة.)% للنسبة الوزنية ) 25 )N لحد التناسب ) 155


Article
Effect of high and low density polyethylene on some mechanical properties of concrete
تأثير البولي ايثيلين ذو الكثافة المرتفعة و المنخفضة على بعض الخواص الميكانيكية للخرسانة

Authors: Nada Mahdi Algalawi ندى مهدي الجيلاوي --- Hadel Ibraheem Ahmad هديل ابراهيم احمد
Journal: Journal of Engineering مجلة الهندسة ISSN: 17264073 25203339 Year: 2014 Volume: 20 Issue: 8 Pages: 20-33
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

The increasing use of plastics in various aspects of modern life resulted in the availability of enormous amount of wastes, including a negative effect on the environment and humans. So it is necessary to find solutions to deal with these wastes and ensure to use them as solutions to use in concrete mix . In this research the production of concrete containing high and low density polyethylene has been used by (5, 10, 15)% as a replacement of part of the volume of sand, so as to obtain concrete good compressive strength as well as other benefits such as improved possibility of pumping concrete and reduce the loss of concrete for workability polymer is a material that is non-absorbable of water . It is also intended to dispose of these wastes positively to achieve benefits to the environment and humans alike .

ان تزايد استخدام اللدائن البلاستيكية في مختلف جوانب الحياة العصرية اسفر عن توفر كم هائل من مخلفاتها وبما يؤثر بشكل سلبي على البيئة و الانسان . لذا كان لابد من ايجاد حلول لمعالجة هذه المخلفات وبما يضمن الاستفادة منها وكأحد هذه الحلول محاولة استخدامها الخلطة الخرسانية . تم في هذا البحث استخدام الفحوصات المختبرية لإنتاج خرسانة حاوية على مثروم البولي ايثيلين ذو الكثافة المرتفعة و المنخفضة وقد استخدم بمقدار (5 ، 10 ، 15) % كنسبة استبدال جزئي من حجم الرمل وذلك للحصول على خرسانة اخف وزناً وذات مقاومة انضغاط جيدة فضلاً عن فوائد اخرى مثل تحسين امكانية ضخ الخرسانة وتقليل سرعة فقدان الخرسانة لقابلية تشغيلها كون ان هذا البوليمر مادة غير قابلة لامتصاص الماء والاستفادة ايضاً من هذه المخلفات الضارة بشكل ايجابي يحقق فوائد للبيئة و الانسان على حد سواء .