تأثير اضافة الكروم على الصفات الميكانيكية للمادة المركبة ذات الاساس شبه المعدني (NiAl-Al2O3)

Loading...
Loading...
Abstract

In this investigation NiAl-based composites containing a dispersion of Al2O3 particles are prepared by sintering technique at 1350°C for 90 min. in an argon atmosphere. Intermetallic compound NiAl was prepared from a mixture of nickel and aluminum powders by using reactive sintering technique at 600°C for 12 Hrs. in an argon atmosphere. To improve the ductility of NiAl three weight percents of Cr (3.5, 4, 4.5 wt %) were added to the composite (NiAl-Al2O3). Series of experiments showed that: -adding of (Al2O3) to (NiAl) leads to increase its compressive strength and its hardness but with a decrease in its ductility;-adding Cr to the intrmetallic composite (NiAl-Al2O3) leads to increase its compressive strength and its hardness with an ability to improve its ductility. An addition of (4.5 wt% Cr) to the composite containing (10wt%Al2O3) led to improve the compressive strength by (25%), hardness by (9%) and ductility by (94%) in comparison with that containing no Cr.

في البحث الحالي تم تحضير المادة المركبة ذات الأساس من ألومينايد النيكل NiAl والمقواة بدقائق أوكسيد الألمنيوم Al2O3 بواسطة تقنية التلبيد عند درجة حرارة 1350°C لمدة ساعة ونصف تحت جو من غاز الآركون وقد حضر المركب شبه المعدني NiAl بواسطة التلبيد التفاعلي لمسحوقي السبك الرئيسيين النيكل والألمنيوم عند درجة حرارة 600°C لمدة 12 ساعة. اضيفت ثلاث نسب وزنية من الكروم هي (3.5,4,4.5wt%) إلى المركب ( (NiAl.اظهرت الاختبارات بان إضافة نسب من اوكسيد الالمنيوم إلى ألومينايد النيكل NiAl تؤدي إلى زيادة مقاومة الانضغاط والصلادة ولكن مع انخفاض في المطيلية، وان إضافة الكروم إلى المادة المركبة (NiAl-Al2O3) تؤثر باتجاه زيادة مقاومتها للانضغاط وزيادة صلادتها مع امكانية الحصول على مطيلية اعلى.ان افضل النتائج التي تم الحصول عليها كانت عند اضافة كروم نسبة (4.5wt%)الى المادة المركبة(90NiAl-10Al2O3) حيث ازدادت مقاومة الانضغاط بنسبة(25%%) والصلادة بنسبة (9%) والمطيلية بنسبة (94%) بالمقارنة مع قيمها للمادة الخالية من الكروم.


Article
Studying the Effect of Corrosive Liquids on Pipes Properties of Unplastizied Polyvinyl Chloride (UPVC) Which is Used in Sewage Purpose
دراسة تأثير المحاليل الآكالة على خصائص أنابيب البولي كلورايد الفاينيل الجسيء (UPVC) المستخدمة في الصرف الصحي

Author: Ahmad Star Ali احمد ستار عيل
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2012 Volume: 30 Issue: 15 Pages: 329-340
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

The current study concerns with studying some mechanical and physical properties of different samples taken from Unplasticized Polyvinyl Chloride (UPVC) pipes used in sewage purpose. Impact strength, compressive strength, shore-D hardness, and diffusion coefficient also were calculated for the samples immersed in different solutions (Wastewater, HCl-0.5N, and Tape water) for four months. Results showed that the mechanical properties of samples were affected by solutions and reduced by (3 – 5)% for impact strength and (10%) for compressive strength. Values for diffusion coefficient (D) were calculated, itwas found that (HCl-0.5N) had a higher value, followed by wastewater then tape water. No cracks were observed, and there were no changes in sample’s dimensions after immersion in solutions.

تم في هذا البحث دراسة بعض الخصائص الميكانيكية و الفيزيائية لنماذج مختلفة من المحاليل على نماذج مقطعة من انابيب الماء و الصرف الصحي المصنعة من البولي كلوريد الفاينيل الجسيء (UPVC). اذ تم حساب متانة الصدمة والصلادة و كذلك متانة الانضغاط للنماذج قبل و بعد غمرها في محاليل من ماء المجاريو ماء الحنفية و المحلول الحامضي (0.5 N). كذلك تم حساب معامل الانتشار بعد غمرها في المحاليل السابقة و لمدة أربعة اشهر. وقد أظهرت النتائج تأثر الخصائص الميكانيكية بعد غمرها في المحاليل و بنسب قليلة بعد انتهاء فترة اربعة اشهر حيث انخفضت بنسبة (3 – 5)% بالنسبة لمتانة الصدمة و كذلك (10)% بالنسبة لمتانة الانضغاط. اما معامل الانتشار فكانت نسبة التغير فيه واضحة.


Article
Preparation of Edible Film from Fish Skin Gelatin and Study its Physical and Mechanical Properties
تحضیر أغشیة قابلة للأكل من الجیلاتین المستخلص من جلد سمك المزلك ودراسة صفاته الفیزیائیة والمیكانیكیة Brachirus orientalis

Loading...
Loading...
Abstract

Edible film with 2,3,4% gelatin extracted from skin of Brachirus orientalisand (20,30,40)% glycerol was prepared; it was easy to be removed from the melding,the film were fine texture and the transparent of the film was lowered and it has takencolor of oil, it is thickness ranged 0.012 to 0.026 ml. the penetration of water vapor offilm increased with increase percentage of gelatin and glycerol it rang from 2.13 to 9.12gMmM2 .h. kpa Pascal, the percentage of water solubility was increase from 20.55% to41.92%. the results showed increased in tensile strength of film with the increase ofgelatin percentage and decrease with increase of glycerol whereas percentage elongationof films as increase with increased of gelatin and glycerol percentage form 2.45% to22.95%.

Brachirus الخلاصة: حضرت أغشیة بنسب ( 4,3,2 ) من الجیلاتین المستخلص من جلد سمك المزلكمع الكلیسیرول بتراكیز 20 % و 30 %و 40 %من وزن الجیلاتینوتمیزت الاغشیة بسهولة ازالتها من orientalisالقالب و اكتسابها القوام المناسب واللون الشفاف وتراوح سمكها من 0.012 الى 0.026 ملم. ودرست صفاتهاالفیزیائیة والمیكانیكیةوازدادت نفاذیة الأغشیةلبخار الماء بزیادة نسبة الجیلاتین وتركیز الكلیسیرول أذ تراوحت من4% جیلاتین كما ارتفعت ذوبانیة الأغشیة - 2.13 الى 9.12 غم .ملم/م 2 .ساعة كیلو باسكال عند نسبة 2من 20.55 % الى 41.92 %.أما مقاومة شدها ارتفعت مع زیادة نسبة الجیلاتین وانخفضت بزیادة تركیزالكلیسیرول في حین زادت نسبة استطالتها حتى القطع عند زیادة كل من الجیلاتین و الكلیسیرول من 2.45 % الى


Article
Effect of Water Proof Admixture on Hardened Concrete
تأثير المضاف المانع للرطوبة على الخرسانة المتصلبة

Authors: Asmaa Mahdi Ali --- Gheed Basil Hameed
Journal: journal of the college of basic education مجلة كلية التربية الاساسية ISSN: 18157467(print) 27068536(online) Year: 2012 Volume: 18 Issue: 73 Pages: 49-67
Publisher: Al-Mustansyriah University الجامعة المستنصرية

Loading...
Loading...
Abstract

Admixtures improve the compressive strength of concrete. This study shows the using of water proof admixture on hardened concrete (40MPa) when the samples Water curing condition is used and the age at testing are 7, 28 and 90 days to evaluate the mechanical properties such as compressive strength, splitting tensile strength and flexure strength and 28 days and are exposed to temperature (100°C and 500°C) at samples in 28 days. In this study the compressive strength decreases by about (33.03 %) and increases by about (29.95%) at (7 and 90) days respectively. They study shows that the compressive strength decreases by about (0.96% and 19.12 %) at 100°C and 500°C respectively while the tensile strength decreases by about (2.06% and 19.38%) at 100°C and 500°C respectively, and the flexural strength decreases by about (3.01% and 21.07%) at 100°C and 500°C respectively. All the above results are compared with cubes tested at room temperature (25 °C).

تستخدم المضافات لتقليل كمية الماء المضافة و زيادة مقاومة الانضغاط، حيث تم استخدام مضافات "Water reducing" للخرسانة ذات مقاومة انضغاط مقدارها (40 نت/مم2). تم صب50 نماذج مكعبة بأبعاد (150X150)مم لفحص مقاومة الانضغاط بعمر (7، 28و 90) يوم لكل عمر وقد تم تعريض هذه النماذج بعمر 28 يوم الى درجات حرارة (100 م° و 500م°)، ثم مقارنتها مع النماذج التي تم فحصها بدرجة حرارة الغرفة (25 م°) وكذلك صب 50 نماذج اسطوانية بأبعاد (150X300) مم لفحص مقاومة الشد الانشطاري وصب 50 نماذج موشورية بأبعاد (100X100X500) مم لفحص مقاومة الانحناء بعمر 28 يوم و تعريضها إلى درجات حرارة (100م° و 500م°)، ثم مقارنتها مع النماذج التي تم فحصها بدرجة حرارة الغرفة (25 م°) ، لوحظ أن مقاومة الانضغاط تقل بمقدار ( 33,03 % ) بعمر 7 ايام و تزداد بمقدار (29,95 %) بعمر 90يوم عند مقارنتها مع النماذج بعمر 28 يوم. عند تعرض النماذج الى درجة حرارة (100 م° و 400م° ) لوحظ أن مقاومة الانضغاط تقل بمقدار(0,96% و 19,12% ) على التوالي بينما تقل مقاومة الشد الانشطاري بمقدار ( 2,06% و19,38 %) و مقاومة الانحناء تقل بمقدار (3,01 % و 21,07%) عند التعرض الى درجة حرارة (100 م° و 400م° ) على التوالي


Article
The Effect Of Phoenix Dactylifera L. Pinnae Reinforcement On The Mechanical And Thermal Properties Of Polymer Composite

Authors: Adil I. Khadim --- Dhefaf H.Badrri --- Zainab S. Abdul-Ridha
Journal: journal of the college of basic education مجلة كلية التربية الاساسية ISSN: 18157467(print) 27068536(online) Year: 2019 Volume: 25 Issue: 104 / علمي Pages: 339-351
Publisher: Al-Mustansyriah University الجامعة المستنصرية

Loading...
Loading...
Abstract

Phoenix dactylifera l. pinnae (the green leaves of dates palm) were used as natural reinforcing (strengthening) fibers to improve the mechanical properties of polyester as a matrix material, the fibers of the green leaves of dates palm were used in two lengths, 10 and 20mm with five rates of 0, 2.5, 5, 10, and 20% , where the reinforcing with the leaves fibers increases the hardness strength from 76.5 to be about 86.55 , the Impact value raised from about 0.313 to 0.461 , in addition to that the flexural strength from 2.66 to be about 55 , and the thermal conductivity increases from 2.54


Article
Design Chart of Concrete Containing Recycled Coarse Aggregate
مخطط تصميمي للخرسانة الحاوية على ركام خشن معاد استخدامه

Loading...
Loading...
Abstract

The re-use of the demolished parts of buildings is considered as an important factor of conserving natural sources and minimizing its consumption, this may be taken as a good development pattern, which leads to compatibility between economical savings and an environmental and social consideration.Development in this sense not only aims at improving production but also takes into account the abiding by the production rules in considering the available sources, its cost, and its overall effect on environmental and social values. To carry out this research work a number of concrete mixes were prepared using different ratios the specimen then tested the outcome of the crushed concrete specimens were then used as coarse aggregate to constitute new concrete mixes of similar ratios for studying the mechanical properties of those new mixes and comparing then with the original mixes.The results indicated clearly the possibilities of using recycled destroyed concrete as aggregates also the results showed a reduction in the compressive strength and an increase in tensile strength. Finally a mix design procedure is given foe the future design of any mix using crushed recycled concrete as an aggregate.

الخلاصةإن أعادة استخدام مخلفات البناء ثانية يعتبر من النقاط المهمة من اجل الحفاظ على المصادر الطبيعية والتقليل من استنزافها وهذا نمط من انماط التنمية المستدامة والتي تعرف على انها نمط جديد من التنمية يسعى الى التوفيق بين النجاعة أو المردود الاقتصادي من جهة والاعتبارات الاجتماعية والبيئية من جهة ثانية فالتنمية في هذا الإطار لا تهدف فقط إلى رفع الإنتاج بل تعمل على مراعاة شروط هذا الإنتاج من حيث قيمة وآهمية الموارد المستعملة فيه وما تخلفه هذه التنمية من انعكاسات على البيئة، وذلك من حيث القيمة الاجتماعية في مجال القطاعات التنموية. مما تقدم ,ولاجراء الدراسة ذات العلاقة تم صب عدة خلطات خرسانية وبنسب مختلفة لايجاد بعض الخواص الميكانيكية لها وبعد فحص نماذجها يتم استخدامها كركام خشن في تكوين خلطة خرسانية جديدة وبنفس نسب المواد ودراسة خواصها الميكانيكية ومقارنتها مع نتائج الخلطة الأولية. من نتائج الفحوصات تبين انه يمكن استخدام الخرسانة المهشمة والمدمرة مرة اخرى كركام خشن في عملية البناء وصب خلطات جديدة، كما تبين ان مقاومة الخرسانة الجديدة للأنضغاط أقل مقارنة بالخلطات الاصلية لكن مقاومتها للشد اعلى، وبالاستفادة من النتائج التي تم الحصول عليها تم عمل مخطط يمكن من خلاله تصميم اي خلطة خرسانية حاوية على خرسانة مهشمة كركام خشن وبمقاس أقصى(25mm).


Article
تأثير إضافة الألومينا على قيم الصلادة ومقاومة البلى لسبيكة Mg-Al

Author: عقيل علي ناظم العطار
Journal: KUFA JOURNAL OF ENGINEERING مجلة الكوفة الهندسية ISSN: 25230018 Year: 2010 Volume: 2 Issue: 1 Pages: 33-43
Publisher: University of Kufa جامعة الكوفة

Loading...
Loading...
Abstract

Magnesium-Aluminum alloys considered specially Mg-6Al very important alloys in engineering applications, but this alloys have weakly wear resistance and low hardness, therefore, addition some materials such as (Al2O3) at (3%-4%-5%) weight percentage to improve the hardness and wear resistance. In this present research Mg-6Al was prepare as a master alloy then recast this alloy after adding (Al2O3) under argon gas in electrical furnace, then study the effect of this addition on the hardness and wear resistance of the master alloy.

تعتبر سبائك المغنيسيوم - ألمنيوم من السبائك ذات التطبيقات الهندسية الواسعة وخصوصاً سبيكة Mg-6Al ولكن هذه السبائك تعاني من ضعف مقاومة البلى وذات صلادة منخفضة، لذلك تم اللجوء الى إضافة بعض المواد الى هذه السبيكة لزيادة الصلادة ومقاومة البلى ومن هذه المواد هي الألومينا. وفي هذا البحث نعمل على تحضير سبيكة Mg-6Al كسبيكة أساسية، ثم نحاول إعادة سبك هذه السبيكة وإضافة الألومينا إليها، وأجريت هذه العملية باستخدام فرن كهربائي وفي وسط حاوي على غاز خامل (Argon) لحماية السبيكة من التأكسد أثناء عملية الصهر. ونسلط الضوء على تأثير إضافة الألومينا وبنسب إضافة مختلفة (3%-4%-5%) على الصلادة ومقاومة البلى لسبيكة Mg-6Al وكذلك على التركيب ألمجهري للسبيكة.وتبين من خلال إجراء فحوص التركيب ألمجهري، الصلادة، مقاومة البلى وحيود الأشعة السينية، أنه بزيادة نسبة إضافة الألومينا الى السبيكة تزداد مقومة البلى وكذلك تزداد الصلادة، ويعود هذا التأثر نتيجة إلى ترسب الألومينا على الحدود البلورية لطور β-Mg17-Al12 وكذلك ترسبها في أرضية السبيكة (طور α-Mg).


Article
A STUDY OF MECHANICAL PROPERTIES OF (AL-CU-MG) ALLOYS REINFORCED BY SILICON CARBIDE AND GRAPHITE PARTICULATES
د ا رسة الخواص الميكانيكية لسبيكة (ألمنيوم- نحاس- مغنسيوم) المقواة بدقائق كاربيد السيلكون والك ا رفيت

Author: Jameel Habeeb Ghazi جميل حبيب غازي
Journal: Iraqi journal of mechanical and material engineering المجلة العراقية للهندسة الميكانيكية وهندسة المواد ISSN: 20761819 Year: 2011 Volume: 11 Issue: 4 Pages: 775-783
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

AbstractThis work deals with the preparing of composite materials based on aluminum alloy (2024)and reinforcement materials particles of silicon carbide and graphite powder . Silicon carbide are(3,5,7 wt%) , whereas the proportion of the graphite was certified at (3wt%) . All samplesadopted in this work are prepared by stir casting.The results have shown an increasing in mechanical properties such as ultimate tensile strength ,Yield strength , Hardness and compressive strength at the expense of ductility for compositematerial with increasing reinforcement materials content.

(AA تناول البحث الحالي تحضير مواد مركبة ذات أساس معدني من سبيكة الألمنيوم ( 2024ومواد تقوية مشتركة من دقائق كاربيد السيلكون ومسحوق الك ا رفيت، إذ كانت النسب الوزنيةلكاربيد السيلكون (% 3,5,7 ) بينما ثبتت نسبة الك ا رفيت الوزنية عند (% 3)، وحضرت النماذج بطريقة.(Stir Casting) بالمزج السباكةًوقد أظهرت النتائج زيادة في مقاومة الشد القصوى ومقاومة الخضوع والصلادة ومقاومة الانضغاط علىحساب نقصان المطيلية للمادة المركبة مع زيادة النسب الوزنية لدقائق التقوية مقارنةً مع السبيكة الأساس


Article
USING OF REINFORCING BY CARBON FIBERS TO IMPROVEMENT MECHANICAL PROPERTIES OF UNSATURATED POLYESTER RESIN
إستخدام التقوية بألياف الكاربون لتحسين الخواص الميكانيكية لراتنج البولي أستر غير المشبع

Author: علي جاهل سلمان
Journal: AL-TAQANI مجلة التقني ISSN: 1818653X Year: 2012 Volume: 25 Issue: 3 Pages: A1-A6
Publisher: Foundation of technical education هيئة التعليم التقني

Loading...
Loading...
Abstract

Studying the effect of reinforcement by carbon fibers as woven roving (°90-°0) with density (1.95 Kgm3) on mechanical properties of unsaturated polyester resin after reinforcing it by different percentage of fibers (20%, 40%,60%) and these properties included : impact strength , tensile strength , compression strength , flexural strength , and hardness . the Mechanical properties were carried out for unsaturated polyester resin before and after reinforcement by fibers, and studied the effect on the above mechanical properties as illustrated in the diagrams between mechanical properties and reinforcing percentage .


Article
STUDY EFFECT OF ALTERNATIVE MOVEMENT ON RATE OF DRY AND WET WEAR AND ON THE MICROSTRUCTURE OF STRUCTURAL STEEL TYPE (A36ASTM)
د ا رسة تأثیر الحركة الترددیة على معدل البلى الجاف و الرطب والبنیة المجهریة للفولاذ (A 36 ASTM ) الإنشائي نوع

Author: Mohammed Abdulateef Ahmed Al-Khazraji محمد عبد اللطیف أحمد
Journal: DIYALA JOURNAL OF ENGINEERING SCIENCES مجلة ديالى للعلوم الهندسية ISSN: 19998716/26166909 Year: 2013 Volume: 6 Issue: 1 Pages: 24-36
Publisher: Diyala University جامعة ديالى

Loading...
Loading...
Abstract

ABSTRACT:- This research aimed to study the deference between the dry and wetwear was applied on structural steel A 36 ASTM, in the beginning the samples were preparedby cutting, grinding and polishing then these samples were applied in the wear set under twopart, one under dry wear and second under wet wear (in corrosive media in this case seawater), weight loss was measured to know the deference between two cases. Theexperimental work tests were done using special device which was locally designed andmanufactured .The results showed the wet wear experience loss in weight more than the drywear because of the stress corrosion.

الخلالاصةA یهدف هذا البحث الى دراسة البلیان الناتج من جهاز البلیان الترددي والبنیة المجهریة لعینات من الفولاذ الإنشائي36 ، حیث تم تحضیر العینات من خلال التقطیع والتنعیم والصقل العینات و إخضاع العینات الى جهاز بلى ذو ASTMحركة ترددیة أفقیة تم تصمیمه وتصنیعه محلیا"لهذا الغرض. ویتم أستخدام هذا الجهاز في حالتین الأولى بوضع العیناتتحت تأثیر الجهاز بدون مؤثر آخر أي بلى جاف، والثانیة بوضع العینات في وسط أكال مكون من ماء البحر وتحتتأثیر إجهاد البلى الترددي أي البلى الرطب، وتم بعد ذلك دراسة الفرق بین الحالتین وبیان سبب حدوث الاختلاف بینالوضعین. وتبین أنه یزداد نقصان الوزن ومعدل البلى في كلا الحالتین نتیجة السحق أثناء الاحتكاك وتكسر الروابطالبلوریة بین الكاربیدات الضعیفة و المتكونة نتیجة الحرارة المتولدة أثناء البلى وهذا ما أتضح في صور البنى المجهریة ،ولكن تكون زیادة نقصان الوزن مع البلى الرطب أكثر بسبب وجود عامل أخر مؤثر على نقصان الوزن ومعدل البلى وهوالتآكل ألإجهادي في الوسط الأكال والذي یزداد مع زیادة أجهاد البلى.

Listing 1 - 10 of 42 << page
of 5
>>
Sort by
Narrow your search

Resource type

article (42)


Language

Arabic (42)


Year
From To Submit

2019 (3)

2018 (1)

2017 (8)

2016 (2)

2015 (5)

More...