الموصلية الكهربائية لراتنج البولي أثلين المقوى بدقائق السليكا

Author: سعد محمد حمزة
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2015 Volume: 23 Issue: 1 Pages: 84-87
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

Electrical conductivity of low density polyethylene resin reinforced by variety weight fracture (1%,2%,3%,4%,5%) from silica particles with (8µm) grain particles has been studied in this paper before and after reinforcement . The experimental results obtained through measurement of resistivity by (Keithly electrometer type (616 ºC)) and then converted to conductivity show that decreased electrical conductivity of resin after adding silica particles, where the electrical conducting was decreased from 5 ×10-14 (ohm.cm)-1 before adding silica to 8.7 ×10-17 (ohm.cm)-1 after addition (5%) from silica at (40ºC).

الموصلية الكهربائية لراتنج البولي أثلين واطئ الكثافة المقوى بكسر وزني متنوع(1%،2%،3%،4% ،5%) من دقائق السليكا بحجم حبيبي (8µm) تم دراستها في هذا البحث قبل وبعد التقوية . النتائج العملية التي تم الحصول عليها من خلال قياس المقاومية بواسطة Keithly electrometer type (616 ºC))) وتحويلها بعد ذلك إلى الموصلية ، أظهرت إنخفاض الموصلية الكهربائية للراتنج بعد إضافة دقائق السليكا ، حيث إنخفض معدل التوصيل الكهربائي من 5 ×10-14 (ohm.cm)-1 قبل إضافة السليكا إلى 8.7 ×10-17 (ohm.cm)-1 بعد إضافة (5%) من السليكا عند درجة حرارة (40 ºC).

Listing 1 - 1 of 1
Sort by
Narrow your search

Resource type

article (1)


Language

Arabic (1)


Year
From To Submit

2015 (1)