Article
Study the Efffect of Adding Cu on Some Mechanical and Structural Properties of the Ag-Sn Alloy
دراسة تأثير إضافة النحاس على بعض الخصائص التركيبية والميكانيكية لسبيكة فضة-قصدير

Authors: Mohammed Obaid Kadhim --- Hassan Juma Abd --- Huda Khailed Hameed
Journal: Iraqi Journal of Science and Technology المجلة العراقية للعلوم والتكنولوجيا ISSN: 18136893 Year: 2013 Volume: 4 Issue: 3 Pages: 134-141
Publisher: Ministry of science and technology وزارة العلوم والتكنولوجيا

Loading...
Loading...
Abstract

In this Research, four high-copper amalgam alloys have been prepared by melting at 1050oC in an inert atmosphere, with copper content ranging from (14 to 26wt. %). Heat treatment processes were carried out to increase phases homogeneity and to reduce residual stresses, then, the alloys were mixed with mercury with a ratio of (1:1.2). Several structural measurements were carried out such as x-ray diffraction and microstructure analysis and some mechanical tests such as micro-hardness and compressive strength. X-ray diffraction results show that the amalgams and amalgams alloys have a variety of phases which depends on the copper content in the alloys. On the other hand, results of micro-hardness and compressive strength show that there is a linear increment in the mechanical properties with increasing copper in the amalgam, the results of D (Cu 26%) amalgam was comparable to those measured for the commercial amalgam of ANA that have high mechanical properties.

حضرت أربع سبائك ملغم عالية النحاس بصهرها عند درجة حرارة 1050oC في أجواء خاملة. وقد تراوحت نسب النحاس في السبائك بين (14~26wt.%) , تم إجراء معالجات حرارية لتحسين التجانس الطوري في السبائك وإزالة الإجهادات، أُجريت عملية الملغمة بخلط السبائك مع الزئبق بنسبة (1:1.2) ,أُجري عدد من القياسات التركيبية مثل تحليلات حيود الأشعة السينية وتحليلات البنية الدقيقة وبعض الخواص الميكانيكية المهمة مثل الصلادة ومقاومة الأنضغاط. وبينت تحليلات حيود الأشعة السينية وجود عدد من الأطوار الرئيسية في السبائك والملاغم تعتمد نسبها وتوزيعها على محتوى النحاس في السبيكة. بينما أظهرت نتائج قياسات الصلادة ومقاومة الانضغاط حصول زيادة خطية في الخصائص الميكانيكية مع زيادة النحاس في الملاغم. وكانت نتائج الملغم D (%26 Cu) مقاربة للقيم المقاسة للملغم التجاري ANA والذي يمتلك خصائص ميكانيكية عالية


Article
Fatigue Test of Coated Mild Steel with Nickel and Aluminum
فحص الكلال للصلب الطري المطلي بالنيكل والألمنيوم

Authors: Moyad A. Mohammad مؤيد عبد لله محمد --- Nawal E. Matti نوال ايشوع متي
Journal: Rafidain journal of science مجلة علوم الرافدين ISSN: 16089391 Year: 2013 Volume: 24 Issue: 1A Pages: 84-97
Publisher: Mosul University جامعة الموصل

Loading...
Loading...
Abstract

In this research, we try to study the fatigue resistance of coated mild steel 1020 AISI. The alloy was coated with Al in single process using pack cementation technique and Ni using electrodeposition technique. Both processes were also used for coating the same alloy (double layer coating). The fatigue resistance of these coating was compared with the base alloy and with those subjected to a heat treatment at the same conditions of time and temperature. The aim of this study was to understand the effect of the temperature and coating type on the fatigue life. The results obtained, based on XRD, Fatigue test, optical microstructure and hardness measurement, that the temperature of heat treatment played the major rule of fatigue life reduction. This can be attributed to the phase transformation of α­ ferrite steel to pearlite ( ferrite + cementite). The results also showed that the coating types have a very important effect on fatigue life. The coatings performed at high temperature (aluminizing) revealed a negative effect on the fatigue life. This is due to the formation of a new brittle and less ductility of Fe-Al phase on the alloy surface. The electrodeposition of Ni leads to a positive effect which is due to an improvement in surface conditions of the alloys via filling the voids or other defects which are present at the surface. The double layer coating (Ni-Al) applied to some specimens shows some improvement in fatigue resistance, in comparison with a single aluminized specimen. This was attributed to the formation of multiphase layer consisting of Fe-Al and Ni-Al intermetallic compound.

تم في هذا البحث دراسة مقاومة الكلال لسبيكة الصلب الطري ( Mild Steel) المطلية بطلاءات منفردة هما الألمنيوم (بتقنية السمنتة) مع النيكل بطريقة الترسيب الكهربائي إضافة إلى طلاءات مزدوجة هي النيكل والألمنيوم كلاهما معا. تم مقارنة النتائج البحثية بالسبيكة الأساس قبل وبعد معاملتها حراريا بشروط الزمن ودرجات الحرارة نفسها وذلك لمعرفة مدى تأثير كلًٍّ من درجة الحرارة و نوعية الطلاء على عمر الكلال.أثبتت نتائج البحث العلمي بالاعتماد على نتائج الأشعة السينية، فحص الكلال، الفحص ألمجهري، قياس الصلادة بأن درجة الحرارة تلعب الدور الأهم في تناقص عمر الكلال، كما أثبتت النتائج العملية أن لنوع الطلاء تأثيرا" مهما على عمر الكلال حيث الطلاء الذي ينجز في درجات حرارية عالية مثل الطلاء بالألمنيوم (الالمنة) له تأثير سلبي على عمر الكلال، في حين إن الطلاء بالترسيب الكهربائي مثل الطلاء بالنيكل يكون له تأثير ايجابي إذ يحسنَ من حالة سطح السبيكة عن طريق ملء الفجوات أو العيوب الأخرى المتواجدة على السطح. أما الطلاء المزدوج (نيكل-ألمنيوم) فقد اظهر تحسنا" لمقاومة الكلال مقارنة بالألمنيوم المنفرد بسبب اشتراك الحديد-ألمنيوم ونيكل-ألمنيوم في تكوين طبقة الطلاء.


Article
Evaluation Of Future Performance of Northern Fatha Storage System
دراسة تأثير الضغط المسلط على البنية المجهرية والكثافة الحقيقية لسبيكة المنيوم 380 باستخدام السباكة بالعصر

Author: د. فاروق منصور مهدي د. نجيب سلمان عبطان سعد رمضان احمد
Journal: Tikrit Journal of Engineering Sciences مجلة تكريت للعلوم الهندسية ISSN: 1813162X 23127589 Year: 2013 Volume: 20 Issue: 4 Pages: 11-17
Publisher: Tikrit University جامعة تكريت

Loading...
Loading...
Abstract

This present study shows ,the effect of applying pressure at rang(10-84) MPa using squeeze casting process to improve the microstructure and actual density of Alumium alloy A380 was studied .From fig(5) its clear that ,the microstructure of prepare casting samples consist of two phases hard eutectic (Al-Si) and Primary α-Al.The effect of applying pressure leads to increase the surface fraction percentage of eutectic phase at (68-84) MPa, but the eutectic percentage was decreased at the same range the actual density was increased at (10,17,84)MP

تم في هذا البحث دراسة تاثير الضغط المسلط ضمن المدى (10-84) ميكاباسكال خلال عملية السباكة بالعصر المباشر على البنية المجهرية والكثافة الحقيقية لسبيكة المنيوم 380 من الخردة , تبين من خلال البنية المجهرية ان البنية تتكون من طورين هما طور اليوتكتك الصلد وطور الالمنيوم الاولي وكذلك وجدنا من خلال علاقة الضغط المسلط وكسر المساحة لطور اليوتكتك ان نسبة كسر المساحة تزداد عند الضغوط (68,84) ميكاباسكال بينما قلت هذه النسبة عند الضغوط (10,17,34) ميكاباسكال . ومن خلال دراسة العلاقة بين الضغط المسلط بمدياته الخمسة والكثافة الحقيقية نلاحظ زيادة الكثافة بزيادة الضغط المسلط (10-17) ميكاباسكال وكذلك عند الضغط (84) ميكاباسكال.