Article
Study of Dry Sliding Wear Behavior of Al-12%Si alloy Produced By Squeeze Casting
دراسة سلوك البلى الأنزلاقي الجاف لسبيكة الألمنيوم-12 %سليكون المنتجة يطريقة السباكة بالعصر

Loading...
Loading...
Abstract

The present research deals with study of the effect of applied casting pressure at constant pouring and die preheating temperatures on the microstructure and dry sliding wear behavior of the squeeze cast Al-12%Si alloy was investigated. A pin-on-disc tests were conducted at varying loads from 5 to 20 N and a sliding speed of 2.7m/sec for a constant sliding time of 20min. The results showed that a refinement in the microstructure with increasing the squeeze pressure. The results showed that the wear rates and coefficient of friction ( μ ) of the squeeze cast samples are lower than that of the gravity die cast sample. The results also showed that the density of the specimens decreased with application of a 7.5 MPa applied pressure, but it increased steadily for higher pressures up to 53 MPa. Increasing the squeeze pressure resulted in increasing the hardness and decreasing the wear rate. These results were explained based on the densification mechanism brought about by the application of pressure during solidification.

يتناول هذا البحث دراسة تاثير ضغط السباكة المسلط عند درجات حرارة صب وتسخين مسبق لقالب الصب ثابتة على التركيب المجهري وسلوك البلى الأنزلاثي الجاف لسبيكة الالمنيوم –12% سليكون المنتجة بطريقة السباكة بالعصر. وأجريت أختبارات البلى من نوع المسمار على القرص عند أحمال متغيرة من 5 -20 نيوتن وسرعة أنزلاق 2.7 متر/ثانية ولفترة زمنية ثابتة 20.دقيقة. واظهرت النتائج حصول تنعيم في البنية المجهرية مع زيادة ضغط السباكة. اظهرت النتائج أن معدلات البلى ومعامل الأحتكاك ( μ ) للنماذج المنتجة بطريقة السباكة بالعصرأقل مما هو عليه في حالة النموذج المنتج يطريقة السباكة بالجاذبية. واظهرت النتائج ايضا بان كثافة العينات قد قلت عند تطبيق ضغط مسلط مقداره (7.5MPa), لكنها قد زادت بصورة ثابتة عند تسليط ضغوط اعلى الى حد (53MPa). ان زيادة ضغط السباكة ادت الى زيادة الصلادة وتقليل معدل البلى. ان هذه النتائج قد تم تفسيرها بالاعتماد على الية زيادة الكثافة الناتجة بواسطة تطبيق الضغط اثناء التجمد.


Article
EFFECT OF SINTERING TEMPERATURE ON PHYSICAL PROPERTIES AND CORROSION BEHAVIOR OF COMPACT (AL-4.5%CU- 1.5%MG) ALLOY
دراسة تأثير درجة حرارة التلبيد عل الخواص الفيزياوية والسلوك التاكلي لمكبوسة من سبيكة ( ألمنيوم-4.5% نحاس –1.5% مغنيسيوم)

Loading...
Loading...
Abstract

This work aims to study the effect of sintering temperatures on physical properties (density and porosity) and corrosion behavior of compact(Al-4.5%Cu-1.5%Mg) alloy in 3.5% NaCl solution at room temperature using cyclic polarization method. Powder technology was used to prepare this alloy by mechanical mixing of Al, Cu and Mg powders in a ball mill for 6 hours to ensure a homogenous distribution of powders in the mixture. Mixed powder was compacted by using single action pressing at (450 MPa) then followed directly by sintering process at different temperatures (520,540,560,580 and 600ºC) for one hour in vacuum furnace under the effect of inert gas condition. Density ,porosity and microhardness measurements were performed to find the best sintering temperature. Tafel extrapolation method and cyclic polarization tests were conducted for all sintered samples. It was shown that the highest density and micro hardness were at sintering temperature 560ºC. It was found that the pitting corrosion resistance enhances with increasing sintering temperature up to 560ºC and afterword it drops again at higher temperatures (580 and 600ºC).

يهدف هذا البحث الى دراسة تأثير درجة حرارة التلبيد على الخواص الفيزياوية (الكثافة والمسامية) والسلوك التاكلي لسبيكة مكبوسة من ( ألمنيوم –4.5% نحاس-1.5% مغنيسيوم) في محلول 3.5% كلوريد الصوديوم في درجة حرارة الغرفة بطريقة الاستقطاب الحلقي ( الدوري ) باستخدام جهاز المجهاد الساكن . حيث تم خلط المساحيق من الألمنيوم ,النحاس ،المغنيسيوم بواسطة طاحونة الكرات لمدة 6 ساعات للحصول على مسحوق متجانس. تم كبس الخليط بعدها بضغط أحادي الاتجاه تحت ضغط (450MPa ) بواسطة مكبس هيدروليكي . لبدت المكبوسات بدرجات حرارة مختلفة ولمدة ساعة واحدة لكل درجة حرارية في فرن كهربائي مفرغ (في جو غاز الاركون). تم قياس الكثافة والمسامية والصلادة الدقيقة للعينات وكذلك اجري فحص التآكل بطريقة تافل للاستقطاب والاستقطاب الدوري للعينات. لوحظ أن أعلى كثافة حقيقية وصلادة مجهرية كانت عند درجة تلبيد (560 ºC). وكذلك لوحظ ان مقاومة التآكل النقري للسبيكة الملبدة تتحسن مع زيادة درجة حرارة التلبيد إلى حد (560ºC) ثم تنخفض بعد ذلك عند الدرجات الحرارية الأعلى منها .


Article
Studying the Effect of Thermal Shock on Stress Intensity Factor Using FEM
دراسة تأثير الصدمة الحرارية على معامل شدة الاجهاد بأستعمال طريقة العناصر المحددة

Loading...
Loading...
Abstract

This research concerns with studying the effect of sudden increment in temperature or thermal shock effect on Stress Intensity Factor generated at crackregion. The Mechanical Stress Intensity Factor (MSIF) was computed using FiniteElement Method technique with the aid of ANSYS software as well as a theoreticalmethods. The percent of error as a comparison between these results was about(3.18%). Elements used for thermal analysis were plane77, then by using switchelement technique from thermal to structural so, elements would be plane82 forstructural analysis. A comparison between this value and the values of Thermal StressIntensity Factor (TSIF) which is generated due to thermal stresses in case of applyinga thermal load (thermal shock) had been adopted to know the importance of thiseffect. So, a coupled field method with the same program, had been used to calculatethese values with estimation effect of heat transfer method. The results proved that foran instant temperature difference the effect of steady-state heat transfer method wasmore than the transient method. Also TSIF for low temperature difference, mayexceed the value of MSIF in case of (100 MPa) statical structural applied load withoutconsidering the temperature effects.