Article
THE EFFECT OF CURING CONDITION ON COMPRESSIVE STRENGTH IN HIGH STRENGTH CONCRETE
تأثير طريقة ألإنضاج على مقاومة الانضغاط في الخرسانة عالية المقاومة

Author: Ali H. Hameed علي حسين حميد
Journal: DIYALA JOURNAL OF ENGINEERING SCIENCES مجلة ديالى للعلوم الهندسية ISSN: 19998716/26166909 Year: 2009 Volume: 2 Issue: 1 Pages: 35-48
Publisher: Diyala University جامعة ديالى

Loading...
Loading...
Abstract

The paper shows the effect of curing condition on compressive strength in high strength concrete in three cases (Group A(moist curing in water for 7 days followed by air curing ) ,Group B(curing until the age test in water) and Group C(curing at high temperature 60ºC±2ºC for six days ) and two types of specimen of cubes (150 x150 and 100 x 100) used in the test age (7,28and 90 day) respectively in four mix proportion (Mix No.1(40 Mpa ,Mix No. 2(fcu 60 Mpa) ,Mix No. 3 (fcu 70 Mpa) and Mix No. 4 (fcu 80 Mpa) ). Results demonstrate that, in general, concrete specimens moist cured until testing ages (Group B) give compressive strength greater than specimens moist cured for 7 days in water then followed by air – drying (Group A). The percentage of increase in strength is (5 and12%) for mix No.3 and 6% for mix No.4, as compared with 3% for mix No.1 and (2 and4%) for mix No.2. When the curing temperature (group C ) increases, the compressive strength increases at different ratios ,the percentage of increase in compressive strength at 7,28 and 90 days for mix No.1 , mixes No.2 and 3 are (20,15 and 14% ), ( 7,11 and 5% ) and (13,12 and 5% ) respectively, while mix No4. shows an increase of 4 and 10% in compressive strength at 7 and 28 days where there is a reduction in the strength at 90 days by about 2%. Generally, as the size of specimen decreases, the effect of temperature curing (group C)on the compressive strength increases.

أن البحث المقدم يبين تأثير ثلاثة طرق للإنضاج (مجموعة A, مجموعة B , مجموعة C ) على مقاومة الانضغاط في لخرسانة ذات مقاومة عالية باستخدام نوعين من نماذج الفحوصات للمكعب (150 *150 ملم و 100*100 ملم ) فحصت بأعمار (7 ,28 و 90 يوم )بالتتابع لأربع خلطات (خلطة رقم 1 , خلطة رقم 2 , خلطة رقم 3 وخلطة رقم 4 ). النتائج المقدمة بشكل عام لنماذج (المجموعة B ) المرطبة لغاية الفحص أعطت أعلى مقاومة مقارنتا (بالمجموعة ِA ) المرطبة لعمر 7 أيام وإتمام الإنضاج بالهواء . معدل الزيادة (5-12%)للخلطة رقم 3 و6%للخلطة رقم 4 مقارنتا مع 3%للخلطة رقم 1 و(2-4) للخلطة رقم 2 . بزيادة الإنضاج الحراري (المجموعة C) مقاومة الانضغاط تزداد لمختلف النسب ومعدل الزيادات في مقاومة الانضغاط للأعمار(7 ,28 و90 يوم )للخلطة رقم1 والخلطة رقم 2 والخلطة رقم 3 هي (20 ,15 و 14 %)(7 ,11 و5 %)(13 ,12 و5 %) بالتتابع. بينما معدل الزيادة في مقاومة الانضغاط للخلطة رقم 4 (4و10 %) لعمر 7 و28 يوم وأعطت تقصان في المقاومة بعمر 90 يوم مقداره 2%.بشكل عام عندما يقل حجم النموذج تأثير الإنضاج بزيادة درجات الحرارة (المجموعة C)يزيد مقاومة الانضغاط .


Article
Some Mechanical Properties of Dental Stone Specimens after Disinfections by 70% Hospital Sprit
بعض الخواص الميكانيكية لعينات حجرية الأسنان بعد التطهير بنسبة 70٪ من كحول المستشفى

Author: Amera Kamal
Journal: Zanco Journal of Medical Sciences مجلة زانكو للعلوم الطبية ISSN: 19955588/19955596 Year: 2009 Volume: 13 Issue: 1 Pages: 49-54
Publisher: Hawler Medical Univeristy جامعة هولير الطبية

Loading...
Loading...
Abstract

Background and objectives: The transmission of oral pathogens to impression and subsequently on to gypsum casts had been demonstrated. The aim of the study to investigate the effect of disinfections of type III dental stone casts by spraying and immersion in 70% hospital sprit (ethanol) on the compressive strength and surface roughness at two different time intervals (24 and 48) hours.Materials and methods: Forty eight cylindrical stone specimens (12 for each group), were prepared for compressive strength and surface roughness testing. Six specimens of each group were tested after (24) hours and the other six after (48) hours.Results: The study showed no significant differences in values of compressive strength and surface roughness between the control and sprayed groups at (24 and 48) hours, this could be due to the fact that the sprayed specimens absorbs fewer amounts of disinfectants than the immersed groups.Conclusions: The immersion of the specimens in (70%) ethanol for (10) seconds and (30) minutes decrease the compressive strength and increase the surface roughness.


Article
SOME MECHANICAL PROPERTIES OF CONCRETE REINFORCED WITH REED FIBERS
بعض الخواص الميكانيكية للخرسانة المسلحة بألياف القصب

Author: Ali Hasson Nahhab علي حسون نهاب
Journal: Al-Qadisiyah Journal for Engineering Sciences مجلة القادسية للعلوم الهندسية ISSN: 19984456 Year: 2009 Volume: 2 Issue: 1 Pages: 31-37
Publisher: Al-Qadisiyah University جامعة القادسية

Loading...
Loading...
Abstract

This research produces a new results about using of locally available reed fibers in concrete. The main parameter of this study was the volume fraction of fibers. The reed fibers were added to the mix in percentages of 1, 2, 3, 4,and 6%. The test program included: slump, compressive strength, splitting tensile strength and impact resistance. It was found that the presence of reed fibers leads to reduce workability, compressive, splitting tensile and impact strength. It was also found that, generally, this reduction increases as the volume percentage of fibers is increased.

يقدم هذا البحث نتائج جديدة حول استخدام ألياف القصب المتوفرة محليا في الخرسانة . المتغير الرئيسي في هذه الدراسة هو النسبة الحجمية للألياف حيث أضيفت بنسب 1و 2و 3 و4 و6 % . تضمن برنامج العمل فحوصات الهطول و مقاومة الانضغاط ومقاومة الشد الانشطاري ومقاومة الصدم . أظهرت النتائج إن وجود ألياف القصب في الخلطة يؤدي إلى نقصان كل من قابلية التشغيل و مقاومة الانضغاط ومقاومة الشد الانشطاري ومقاومة الصدم وبصورة عامة يزداد هذا النقصان بزيادة النسبة الحجمية للألياف .


Article
USING OF WASTE GLASS AS FINE AGGREGATE IN CONCRETE
استخدام مخلفات الزجاج كركام ناعم في الخرسانة

Loading...
Loading...
Abstract

The present investigation was carried out to study the possibility of using waste glass of size up to 5mm as a fine aggregate in concrete and mortar. The waste glass was used as a partial weight replacement of sand with percentages of 10, 20, 30 and 40 %. The results have indicated that increasing the fractions of sand replacement by waste glass leads to reduce the compressive and tensile strength for both mortar and concrete. Up to 20 % replacement, the 28 days compressive strength of concrete and mortar is about 92 and 95 percent from the reference strengths, respectively. Also, it was found that the expansion of mortar specimens increase with increasing the waste glass content in the mix. At 20 % of sand replacement by waste glass, the expansion is slightly higher than that for the control specimens.

يهدف هذا البحث إلى دراسة إمكانية استخدام مخلفات الزجاج وبمقاس أقصى مقداره (5 ملم) كركام ناعم في الخرسانة والمونة السمنتية. تم استخدام مخلفات الزجاج كبديل جزئي عن الرمل وبنسب وزنية (10، 20، 30 و40) %. اظهرت النتائج بان زيادة محتوى هذه المخلفات المستبدلة من الرمل يؤدي إلى نقصان في مقاومة الانضغاط والشد لكل من المونة والخرسانة. عندما تصل نسبة الاستبدال إلى 20 % فان مقاومة الانضغاط بعمر 28 يوم تصبح بحدود (92 و95)% من الخلطات المرجعية لكل من الخرسانة والمونة على التوالي. بالإضافة إلى ذلك فقد وجد بان هناك زيادة في مقدار التمدد لنماذج المونة عند زيادة نسبة المخلفات الزجاجية في الخلطة. عند استبدال 20 % من الرمل بهذه المخلفات فان مقدار التمدد للنماذج يصبح أعلى بقليل أذا ما قورن بنماذج الخلطة المرجعية.


Article
Predicting The Relationship Between The Modulus Of Rupture And Compressive Strength Of Cement Mortar
التنبؤ بعلاقة بين معامل الكسر ومقاومة الانضغاط لمونة الاسمنت

Author: Sura A. Majeed سرى عبد الرزاق مجيد
Journal: AL Rafdain Engineering Journal مجلة هندسة الرافدين ISSN: 18130526 Year: 2009 Volume: 17 Issue: 5 Pages: 59-68
Publisher: Mosul University جامعة الموصل

Loading...
Loading...
Abstract

The present paper deals with studying the effect of sand/cement (s/c) ratio and water/cement (w/c) ratio on the mechanical properties of cement mortar and to predict a relationship between modulus of rupture and compressive strength for the cement mortar. In the present work seventy two sample of cubes and prisms were tested for compressive strength and modulus of rupture. All the tests were carried out in accordance to the ASTM specification C109 using twelve different mix proportions of cement/sand ratio and water/cement ratio. From the test results and based on regression analysis a best power relation between modulus of rupture and compressive strength are proposed.Keywords: compressive strength, modulus of rupture, mortar, sand.

الخلاصةيتضمن البحث دراسة تأثير تغير نسبة الرمل الى الاسمنت وتغير نسبة الماء الى الاسمنت في مونة الاسمنت على خواصها الميكانيكية وايجاد علاقة بين معامل الكسر ومقاومة الانضغاط لمونة الاسمنت من خلال اقتراح معادلة تحكم هذه العلاقة. تضمن البحث اجراء الفحص على 72 عينة من مكعبات وموشورات مونة الاسمنت وذلك بفحص مقاومة الانضغاط ومعامل الكسر لهذه العينات. وقد تم اجراء جميع الفحوصات حسب مواصفات الجمعية الأمريكية للفحوصات والمواد ASTM باستخدام 12 مزجة مختلفة بتغيير نسبة الرمل الى الاسمنت وتغير نسبة الماء الى الاسمنت. تم استخدام نتائج الفحص من هذه الدراسة لاشتقاق معادلة تجريبية للعلاقة بين معامل الكسر ومقاومة الانضغاط لمونة الاسمنت.


Article
Physical Properties and Compressive Strength of the Technical Plaster and Local Juss
الصفات الفيزيائية والمقاومة الانضغاطية للبلاستر الفني والجص المحلي

Loading...
Loading...
Abstract

Five physical properties (water/powder ratio, setting time, fineness, porosity and dendsity) and compressive strength were determined and compared for technical plaster and local juss.Data were monitored using a standard dental stone. The relationships between these properties were also studied. It was revealed that local juss has inferior properties compared with technical plaster. It has lower compressive strength; higher water/powder ratio; shorter setting time; larger grain size and higher porosity. There is an inverse relationship between compressive strength and the two properties water/powder ratio and porosity. There is a direct relationship between compressive strength and the two properties particle size and density. There is also a direct relationship between setting time and the two properties particle size and water/powder ratio.

تم دراسة خمس خواص فيزيائية وهى (نسبة الماء إلى المسحوق وزمن التجمد والنعومة والمسامية والكثافة) والمقاومة الانضغاطية لكل من البلاستر الفني والجص المحلي وتم استعمال حجر الأسنان كنموذج قياسي. وتم كذلك دراسة العلاقات بين هذه الصفات ووجد بأن للجص المحلي صفات متدنية مقارنة مع البلاستر الفني، حيث له مقاومة انضغاطية اقل ونسبة الماء الى المسحوق أعلى وزمن تجمد اقصر وحجم حبيبي اكبر ومسامية أعلى من البلاستر الفني. وأوضحت الدراسة وجود علاقة عكسية بين المقاومة الانضغاطية والصفتين نسبة الماء الى المسحوق والمسامية. وعلاقة طردية بين المقاومة الانضغاطية والصفتين الحجم الحبيبي والكثافة. وتبين ايضا وجود علاقة طردية بين زمن التجمد والصفتين الحجم الحبيبي ونسبة الماء الى المسحوق.


Article
Effect of Freezing and Thawing on Stress-Strain Relationships of Polymer Modified Concrete (PMC)
تأثير دورات الانجماد – الذوبان على علاقة الاجهاد – الانفعال

Authors: محمد حمودي صالح --- قصي عبد الحميد جبل --- أمير غايب طالب
Journal: Al-Qadisiyah Journal for Engineering Sciences مجلة القادسية للعلوم الهندسية ISSN: 19984456 Year: 2009 Volume: 2 Issue: 3 Pages: 574-583
Publisher: Al-Qadisiyah University جامعة القادسية

Loading...
Loading...
Abstract

The investigation includes the effect of freezing and thawing cycles on stress-strain relationships of polymer modified concrete (PMC). Cycles of freezing and thawing contains 12 hours at 100°C and 12 hours at -4°C. The process of cycles of freezing and thawing
Simple experimental technique is used to obtain the complete stress-strain curves up to strain of 0.006 (Both ascending and descending portions) sample subjected to freezing and thawing cycles (FTC), then subjected also to stress-strain tests.

البحث يتضمن تأثير دورات الانجماد والذوبان على منحني الإجهاد–الانفعال للخرسانة المطورة بالبوليمر.دورات الانجماد والذوبان تتكون من 12 ساعة بدرجة حرارة (100) درجة مئوية و12 ساعة بدرجة حرارة (-4) درجة مئوية. دورات الانجماد والذوبان تستمر لمدة (30) يوم لجميع النماذج، تم استخدام موديل عملي للحصول على علاقة الاجهاد – الانفعال الكاملة (الجزء الصاعد والنازل). النماذج أُخضعت لدورات الانجماد والذوبان ثم فحص الاجهاد – الانفعال.


Article
TENSILE STRENGTH OF HIGH STRENGTH POLYMER MODIFIED CONCRETE
مقاومة الشد للخرسانة المطورة بالبوليمر والعالية المقاومة

Author: Qusay A. Jabal قصي عبد الحميد جبل العطيه
Journal: Al-Qadisiyah Journal for Engineering Sciences مجلة القادسية للعلوم الهندسية ISSN: 19984456 Year: 2009 Volume: 2 Issue: 1 Pages: 22-30
Publisher: Al-Qadisiyah University جامعة القادسية

Loading...
Loading...
Abstract

High strength concrete is widely used especially during the last century. High
Strength concrete means concrete with max. Compressive strength ( )more than 50 N/mm2 (Shetty, 1988). Polymer modified concrete was) used since 1970s by adding polymer monomers such as styrene Butadiene rubber (SBR) to ordinary concrete during casting as a percentage of weight of cement in order to improve the mechanical properties of concrete.
This research includes the study of the effect of styrene Butadiene Rubber on Tensile Strength of Polymer modified concrete PMC, also include the effect of the polymer on compressive strength and relationship between tensile and compressive strength (as a mathematical model). A different types of mixes (1: 1.5: 2, 1:1.5:3 and 1:2:4) were used in this research.

إن الخرسانة المطورة بالبوليمرات أصبحت من المواد الشائعة الاستخدام في الصناعة الإنشائية والتي بدأت في السبعينات من القرن الماضي في اليابان والولايات المتحدة ثم شاعت الاستخدام على مستوى العالم. الخرسانة العالية المقاومة مثل الخرسانة المطورة بالبوليمر أيضا استخدمت بصورة شائعة في القرن الماضي والخرسانة العالية المقاومة تعني الخرسانة التي مقاومة انضغاطها العظمى أكثر من (50) ميكا باسكال واستخدم هذا النوع من الخرسانة في بداية السبعينات عن طريق إضافة مستحلبات البوليمرات مثل مستحلب الستايرين بيوتادين للخرسانة الاعتيادية أثناء صب الخرسانة وإنتاجها كنسبة مئوية من وزن الاسمنت لتحسين الخواص الميكانيكية للخرسانة الاعتيادية .,ويتضمن هذا البحث تأثير هذا المستحلب على مقاومة الشد للخرسانة المطورة بالبوليمر ويتضمن أيضا تأثير إضافة نسب مختلفة من ( الستايرين بيوتادين ) على مقاومة الانضغاط واستخراج موديلات رياضية لهذه العلاقات إضافة إلى استنباط موديل رياضي يربط مقاومة الانضغاط بمقاومة الشد وتم استخدام نسب خلط مختلفة من ( الاسمنت : الركام الناعم: الركام الخشن) في هذا البحث.


Article
Using Citric Acid As An Admixture and It's Influence on Some Properties of Concrete
استعمال حامض ألستريك كمضاف ودراسة تأثيره على بعض خواص الخرسانة

Author: Wasan I. Khalil
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2009 Volume: 27 Issue: 1 Pages: 32-41
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

The objective of this investigation is to find the effectiveness of the citric acid asretarding admixture. The experimental results indicate that the optimum dosage of citricacid is 0.02% by weight of cement. This dosage causes a delay in initial and final settingtime of 1:42 and 3:18 hour: minute, respectively; and a reduction in water-cement ratioof 13% relative to reference concrete mix. So, citric acid can be classified according toASTM-C494 as water-reducing and retarding chemical admixture type D.The investigation also extends to evaluate the effect of using citric acid onproperties of concrete such as, compressive strength, splitting tensile strength, modulusof rupture and dynamic modulus of elasticity at normal conditions and after exposure tosalt solutions. Generally the results indicate that using citric acid in concrete enhance it'sproperties at normal conditions, the percentage increase in compressive strength,splitting tensile strength, modulus of rupture and dynamic modulus of elasticity at age180 days was about 56%, 13%, 24% and 8% respectively relative to reference concrete.Also it was observed that concrete containing citric acid has good performance after 180days exposure to salt solution in comparison with reference concrete.

الغرض من هذا البحث هو لمعرفة تأثير حام ض ألستريك كأحد المضياف ات المبطئة المؤ ثرة.٠ ٪ من وزن الاسمنت, وإن ‚ تشير النتائج العملية إلى إن الرزمة المثالية من حامض ألستريك هي ٠٢٣ دقيقة : ساعة : ١ و ١٨ : هذه الرزمة سببت تأخير في وقت التجمد الابتدائي والنهائي بمقدار ٤٢على التوالي ونقصان في نسبة الماء - الاسم نت بمقدار ٪ ١٣ بالمقارنة مع خلط ة الخرسانة المرجعية ,كمضاف ASTM-C وبذلك فأن حامض ألستريك يمكن تصنيفه حسب المواصفة الأمريكية 494.(D) كيميائي مقلل للماء ومؤخر للتجمد نوع دشمل البحث أيضا تقييم تأثير استخدام حامض ألستريك على خواص الخرسانة , مقاومة الانضغاط ,مقاومة الشد الانشطاري , معاير الك سر ومعام ل المرونة الديناميكي في الظروف الاعتيادية وبعدالتعرض لمحاليل الأملاح . أظهرت بصورة عامة النتائج بأن استخدام حامض ألستريك في الخرسانةيحسن من خواصها في الظروف الاعتيادية , حيث كانت نسبة الزيادة في مقاومة الانضغاط , مقاومة الشد٢٤ ٪ و ٨ ٪على , ٪١٣ , ٪ الانشطاري, معاير الكسر و معامل المرونة الديناميكي بعمر ١٨٠ يوم ٥٦التوالي مقارنة بالخرسانة المرجعية . كذلك يكون الأداء جيدا بعد التعرض لمحلول الأملاح لفترة ١٨٠يوم بالمقارنة مع الخرسانة المرجعية


Article
“Effect of Magnetic Water on Engineering Properties of Concrete”
“تأثير الماء الممغنط على الخواص الهندسية للخرسانة”

Author: Saddam M. Ahmed صدام محمد احمد السيد
Journal: AL Rafdain Engineering Journal مجلة هندسة الرافدين ISSN: 18130526 Year: 2009 Volume: 17 Issue: 1 Pages: 71-82
Publisher: Mosul University جامعة الموصل

Loading...
Loading...
Abstract

This research investigates the influence of magnetic water on compressive strength and workability (consistence) of concrete. Results show that the compressive strength of concrete samples prepared with magnetic water increases 10-20% more than that of the tap water samples. In the present study, increasing in compressive strength of concrete is achieved when the magnetic strength of water is 1.2 T, and velocity of water current that passes through magnetic field is of 0.71 m/s. It is also found that magnetic water improves the workability (consistency) of fresh concrete.Key words: magnetic water, workability, compressive strength, concrete, Ampere’s Role“

الخلاصة في البحث تم دراسة مقاومة الانضغاط وقابلية التشغيل للخرسانة الممزوجة بالماء الممغنط ومقارنته مع تلك الممزوجة بالماء الاعتيادي (ماء الصنبور). نتائج البحث كشفت أن مقاومة الانضغاط للخرسانة الممزوجة بالماء الممغنط تزداد بنسبة تتراوح بين (10-20%) بالمقارنة مع النماذج المعمولة بالماء الاعتيادي, وبصورة خاصة وجد أن أفضل زيادة مقاومة انضغاط للخرسانة تحقق عندما تكون المقاومة المغناطيسية للماء بحدود (T1.2), وسرعة جريان تيار الماء خلال المجال المغناطيسي بحدود m/s)0.71), ووجد أيضا أن الماء الممغنط يحسن قابلية التشغيل (القوام) للخرسانة الطرية.

Listing 1 - 10 of 12 << page
of 2
>>
Sort by
Narrow your search

Resource type

article (12)


Language

English (12)


Year
From To Submit

2009 (12)