Article
THE STUDY OF BACTERIAL GROWTH ON LOW-DENSITY POLYETHYLENE- LIGNIN COMPOSITE
دراسة النمو البكتيري على أقراص متراكبات بوليمر الاثيلين الواطئ الكثافة - اللكنين

Author: Nawres N. jaber نورس نوري جابر
Journal: Basrah Journal of Veterinary Research. مجلة البصرة للابحاث البيطرية ISSN: Print:18138497 E; 24108456 Year: 2011 Volume: 10 Issue: 1 Pages: 97-105
Publisher: Basrah University جامعة البصرة

Loading...
Loading...
Abstract

In the present study, Low density polyethylene with various contents of lignin films were investigated for their resistance to bacterial adhesion. The disc diffusion method was employed for this purpose. The results of bacterial growth on low-density polyethylene (LDPE )–lignin composite were reported. lignin was added by 1%,2%,3%,4%,5%,10% and 15% of polyethylene weight. We compared initial adhesion and surface growth of staphylococcus aureus , streptococcus pyogens, pseudomonus aerugenosa, eschrishia coli and klebciala spp. A 5 mm of test polymer composites were inoculated in the 9 cm Petri dish for 1-2 days and zone of inhibition and bacterial growing were observed and recorded. After 24 hours the bacterial growing of S. aureus , S. pyogens and E. coli were distributed all over the control agar with no growth on the polymeric composites films while Both P. aeruginosa and K. spp. have a dense growing. After 48 hours a slight adhesion of S. aureus on polyethylene-lignin discs was found with radius of growing was 3 mm .For P. aeruginosa we have more dense growing . It was found that the lignin contents have no clear inhibition against tested bacteria where this might be due to a limitation of the agar disc diffusion method. The vanishing of inhibition zone was combined with the absence of adherent bacteria on the polyethylene films. More concentration of natural lignin is required to get inhibition effect.

تم في هذا البحث التحقق من مقاومه بوليمر الاثيلين الواطئ الكثافه والمطعم باللكنين النمو البكتيري باستخدام طريقه الانتشار بواسطة القرص الصلب حيث كانت نسبه المضاف الوزنيه من اللكنين الى هذا البوليمر مساوية إلى 1 % و2% و 3% و 4% و5% و10 % واخيرا 15 % من وزن بوليمر الاثيلين باستخدام خمسه أنواع من الجراثيم وهي staphylococcus aureus , streptococcus pyogens, pseudomonus aerugenosa, eschrishia coli and klebciala spp. وتم حقن هذه الاقراص ذات قطر 5 ملم في الإطباق الزجاجية ذات قطر 9 سم لمده تراوحت بين (1-2) يوم ومراقبه وتسجيل منطقه منع النمو البكتيري وبينت النتائج بعد مرور 24 ساعه ان النمو البكتيري لكل من S. aureus , S. pyogens and E. coli مع عدم تسجيل أي نمو على سطح الاقراص البوليمريه في حين كان نمو كل من P. aeruginosa و K. spp. كثيفا في الاطباق . وبعد مرور 48 ساعة لوحظ وجود نمو خفيف على الأقراص البوليميريه وبقطر نمو 3 ملم مصحوبا بنمو كثيف لبكتريا P. aeruginosaووجد أيضا إن اللكنين المضاف ليس له تأثير واضح على البكتريا المستخدمة في هذا البحث وتم تفسير النتائج بالاعتماد على محدوديه طريقه الانتشار بواسطة القرص وان غياب منطقه منع النمو البكتيري كان مصحوبا بغياب النمو البكتيري على هذه سطوح أقراص البولي اثيلين الواطئ الكثافه ولابد من زياده تركيز اللكنين في هذه الاقراص للحصول على فعاليه ضد البكتريا المستخدمة


Article
THE HISTOLOGICAL AND BIOCHEMICAL STUDY OF THE EFFECT OF PURE FLAX SEED LIGNIN ON THE MAMMARY GLAND IN FEMAL RABBITS
دراسة نسجية وكيموحيوية لتأثير اللكنان المنقى من بذور الكتان على الغدد اللبنية لأناث الأرانب

Author: Sinaa Jaboori Al-Bazii Wefak Jaboori Al-Bazii سيناء جبوري البازي وفاق جبوري البازي
Journal: Basrah Journal of Veterinary Research. مجلة البصرة للابحاث البيطرية ISSN: Print:18138497 E; 24108456 Year: 2014 Volume: 13 Issue: 1 Pages: 198-210
Publisher: Basrah University جامعة البصرة

Loading...
Loading...
Abstract

This study was carried out to investigate the effect that result from taking 40 mg /kg BW of purified lignan from the seed of flax Linum usitatissimum L. in the growth and development of mammary glands during virgin , pregnancy and lactating stages for 14 days. Thirty (30) rabbits were used in this experiment divided into six groups, two groups at maturity (virgin) stage, two groups at pregnancy stages and two groups at lactating stages (5 rabbitseach group). The following studies were decided: histological, histochemical, biochemical and hormonal studies for each group. Microscopic examination of mammary gland in the virgin rabbits that treated with pure flax lignan showed more growth in the size of lobules and alveoli. In pregnant, the treated groups showed more branching of alveoli with more flattened epithelium. In lactating treated group showed the lobules were expanded and contained more branching alveoli with discontinuous flattened epithelium. The PAS staining reaction of histological sections of mammary gland from treated groups and control were showed positive reactions in all groups. The biochemical studies showed a significant increase (p<0.05) in the serum reduced glutathione concentration with decrease in the malondialdehyde concentration in the three stages that treated with pure flax lignan compared with control. The hormonal study indicated a noticeable increase in prolactin hormones with significant decreased in estrogen in all groups of treated animals for the three physiological stages (virgin, pregnant and lactating) compared with their controls.

أجريت هذه الدراسة بهدف تسليط الضوء على التأثيرات التي يمكن أن يؤديها تناول40 ملغم / كغم من وزن الحيوان من اللكنان المنقى المستخلص (Lignan) من بذور نبات الكتان ( ( Linum usitatissimum L.في زيادة ونمو وتطور الغدد اللبنية أثناء مراحل (البلوغ "العذارى" والحمل والرضاعة) لمدة 14 يوم. استخدم (30) ارنب في هذه التجربة قسمت إلى ست مجاميع ،مجموعتين في مرحلة البلوغ ومجموعتين في مرحلة الحمل بالإضافة إلى مجموعتين في مرحلة الرضاعة(5 ارانب لكل مجموعة) , ثم أجريت عليها دراسات نسجية وكيميانسجية كيموحيوية بالإضافة إلى القياسات النسجية لكل مجموعة. بينت النتائج المعطيات التالية :أظهرت المقاطع النسجية إن الحيوانات العذارى المجرعة باللكنان المنقى زيادة في حجم وعدد الفصيصات.أما في مرحلة الحوامل فقد لوحظ وجود تفرعات في الأسناخ مع تسطح في البطانة الطلائية بالاضافة الى توسع في النبيبات الفصيصية .أما عند معاملة مجاميع المرضعات فان الفصيصات أظهرت توسعا اكثر مع تفرع واضح في الاسناخ. من ناحية اخرى، بينت المقاطع النسجية المصبوغة بصبغة الـ PAS لمجاميع الحيوانات المعاملة باللكنان المنقى لجميع و مجاميع السيطرة إفراز موجب للصبغة الـ PAS . اما الدراسات الكيموحيوية فأظهرت أن المجاميع المعاملة بالكنان ارتفاعا معنويا (p<0.05) في مستوى الكلوتاثيون مع انخفاض معنوي في مستوى المالون داي الديهايد في مصل الأرانب للمجاميع المعاملة الثلاث مقارنة بالسيطرة. أوضحت نتائج الدراسات الهرمونية زيادة معنوية (p<0.05) في مستوى هرمون البرولاكتين مع انخفاض معنوي في مستوى هرمون الاستروجين للمجاميع المعاملة مقارنة مع مجاميع السيطرة .

Keywords

Lignin --- Mammary Glands.


Article
An Evaluation of Some Mechanical Properties of Autopolymerizing Acrylic Resin with the Modified One after Changing the Curing Environment: (In vitro Study)

Author: Intisar J. Ismail
Journal: Journal of baghdad college of dentistry مجلة كلية طب الاسنان بغداد ISSN: 16800087 Year: 2015 Volume: 27 Issue: 4 Pages: 62-71
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

Background: Studying and investigating the transverse strength(Ts), impact strength(Is), hardness (Hr) and surfaceroughness(Ra) of conventional and modified autopolymerizing acrylic resin with different weight percentages ofbiopolymer kraftlignin, after curing in different water temperatures; 40°C and 80°C.Material and Methods: Standard acrylic specimens were fabricated according to ADA specification No.12 fortransverse strength, ISO 179 was used for impact testing, Shore D for hardness and profilometerfor surface roughness.The material lignin first dispersed in the monomer, then the powder PMMA is immediately added. Lignin added indifferent weight percentages. Then cured using pressure pot (Ivomet) in two temperatures;40°C and 80°C under 2bar pressure, for 30 minutes.Atotal of 144samples were prepared for this study. Ts, Is, Ra, and Hr were tested, by usingInstron universal testing machine, charpy impact tester, shore D tester, and profilometer respectively.Results: The transverse strength increased in both the conventional and modified onewhen compared with thatcured in air. The addition of 0.5wt% lignin gave the higher effect (78.0017MPa) with highly significant difference foundbetween groups at 40°C polymerizing temperature. While the impact strength in both temperatures in the modifiedresin revealed increased results than conventional one, 1.25wt% of kraft lignin gave the highest value (12.7355KJ/m2)with highly significant differences found between groups at 80°C polymerizing temperature. Hardness and surfaceroughness showed also highly significant differences found between groups at 40°C polymerizing temperature, allthe groups had increased Hr. than the control one (78.95), while the Ra. decreased for 1.0% ,1.25,1.50 and 1.75 wt%lignin content to (0.26,0.10,0.063, 0.12μm) respectively in 40°C polymerizing temperature, the lowest value present in1.75 wt% lignin (0.05 μm) at 80°Cpolymerizing temperature.Conclusions: It seems that increasing the polymerizing temperature to 40°C had a positive effect on the mechanicalproperties of autopolymerizing acrylic resin and the one enforced by kraft lignin biopolymer in low percentages.Increasing the polymerizing temperature to 80°C will doesn’t have much positive effect but it doesn’t deteriorate themechanical properties. However, when submitted to increasing the temperature to 80°C, specimens showed asignificantincrease in impact strength


Article
Effect of the addition of bio-polymer lignin on the Transverse and Impact strength of the autopolymerizing acrylic resin.

Authors: Basima M.A. Hussein باسمة محمد --- Thikra I. Hamad ذكرى حمد --- Intisar J. Ismail انتصار جاسم
Journal: Journal of the Faculty of Medicine مجلة كلية الطب ISSN: 00419419 Year: 2010 Volume: 52 Issue: 3 Pages: 359-363
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

Background: Acrylic resin dentures are susceptible to fracture; it is unresolved problem in prosthodontics. The repair procedure should be simple, strong, and accurate. This study evaluated the transverse and impact strength of autopolymerizing acrylic resin, the repair material was modified with kraft lignin as a new enforcement material and compared with the commercially available self cured acrylic resin. Materials and Methods: The addition of kraft lignin to the acrylic resin were done in percentages of 0.25%, 0.5%, 0.75%, 1.0%, 1.25%, and 1.5% (wt%). Seventy specimens were made according to the ADA specification No 12 for transverse strength using three point bending test and Impact strength test was conducted following the procedure given by the ISO 179 with Charpy Type Impact testing instrument.Results: Mean transverse strength of experimental specimens where increased only in 0.25wt% addition of lignin (61.3400 Mpa) then results tend to decrease, and no statistical differences found between the control and any one of the modified groups. The impact strength increased more than the control in the groups 0.25, 0.50, 0.75,and 1.0wt%,13.9700, 15.5900, 35.2100, 33.6900 Kj/m2 respectively, then has been decreased at 1.50wt% until reach value of the control (9.2525 Kj/m2).Highly significant difference was found at 0.5, 0.75 and 1.0wt% (p<0.05).Conclusions: The autopolymerizing acrylic resin exhibited significantly higher impact strength as a result of addition the biopolymer lignin. The transverse strength of the modified specimens was decreased after increasing the weight percent addition of lignin.Key words: Autopolymerizing acrylic resin, KL (kraft lignin), transverse strength, impact strength


Article
Electrochemical Investigation of Lignin Resin Doped with Different Ratios Rhodamine B
دراسة السلوك الكهروكيميائي لراتنج اللكنين المشوب بنسب مختلفة بصبغة الرودامين ب

Author: Samah Hussein Kadhim سماح حسين كاظم
Journal: Univesity of Thi-Qar Journal مجلة جامعة ذي قار العلمية ISSN: 66291818 Year: 2018 Volume: 13 Issue: 1 Pages: 25-42
Publisher: Thi-Qar University جامعة ذي قار

Loading...
Loading...
Abstract

The electrochemical behavior was investigated of Lignin Resin by using the cyclic voltammetry technique. Such investigation mainly focuses on the expected properties of the doped resin with different doping ratios of Rhodamine B (0.01, 0.5, 0.1, 0.15, 0.2) %wt. This is indicated by the electron transfer between the dopant and resin, which clearly shows the appearance of oxidation – reduction peaks accompanied log increase in electrical current Ip as applied potential changes. The heights of Ip oscillate due to the change in scan rate . The results of linear of relationships between Ip with 1/2 indicated that the electron transfer was a process of one electron transfer

تضمن البحث دراسة السلوك الكهروكيميائي لراتنج اللكنين بوساطة تقنية المسح الجهدي الحلقي، وتم التركيز على خواصه المتوقعة بعد التشويب بصبغة الرودامين ب بنسب (0.01, 0.5, 0.1, 0.15, 0.2) %wt وذلك وفقا لما يسببه الانتقال الالكتروني بين الصبغة المشوبة وراتنج اللكنين حيث انعكس ايجابيا على ظهور واضح لقمم التأكسد والأختزال رافق ذلك زيادة في قيم التيار الكهربائي (Ip) لمدى تغيير الجهد الكهربائي المسلط اذ تفاوتت وفقا لاختلاف سرع المسح الجهدي المطبقة والمتوقعة أصلا في هذه الحالات. ان نتائج العلاقة الخطية المستنبطة بين Ip والجذر التربيعي لسرعة المسح الجهدي 1/2 دلت على أن الانتقال الالكتروني هو عملية أنتقال الكترون واحد.


Article
Effect of Temperature and Doping Ratios on Electrical Conductivity of Lignin Resin with Rhodamine B

Authors: Samah Hussein Kadhim --- Athraa Hameed Mekky
Journal: Journal of Education for Pure Science مجلة التربية للعلوم الصرفة ISSN: 20736592 Year: 2018 Volume: 8 Issue: 1 Pages: 237-246
Publisher: Thi-Qar University جامعة ذي قار

Loading...
Loading...
Abstract

AbstractElectrical conductivity of lignin resin films doped with different ratios of Rhodamine B (0.01, 0.04,0.06,0.08,0.1)%wt, were studied. The composite films prepared using casting method. The resultshowed that the conductivity increased with increasing temperature and doping ratios. The values ofactivation energy decreased with increasing temperature and doping ratios of dyes.

الخلاصة(0.01, 0.04, 0.06, 0.08, تضمنت الدراسة تحضیر راتنج اللكنین المشوب بنسب وزنیة مختلفة بصبغة الرودامین ب %( 0.1، استخدمت طریقة الصب لتحضیر اغشیة رقیقة في دراسة الخواص الكھربائیة للراتنج المشوب.اظھرت النتائج المستحصل علیھازیادة التوصیلیة الكھربائیة بزیادة كلا من درجة الحرارة ونسب التشویب، كما وان قیم طاقة التنشیط تناقصت بزیادة الحرارة ونسبالتشویب، مما یدل على ان الراتنج المشوب یمتلك خصائص اشباه موصلات.


Article
Poly aromatic hydrocarbons degradation by lignin peroxidase produced from local isolate Aspergillus terreus SG777

Authors: Sahar Ghazi Imran --- Nada S. Razuqi --- Ghazi M.Aziz
Journal: Journal of Petroleum Research & Studies مجلة البحوث والدراسات النفطية ISSN: 22205381 Year: 2018 Issue: 19 Pages: E144-E154
Publisher: Ministry of Oil وزارة النفط

Listing 1 - 7 of 7
Sort by
Narrow your search

Resource type

article (7)


Language

English (7)


Year
From To Submit

2018 (3)

2015 (1)

2014 (1)

2011 (1)

2010 (1)