Article
Microstructural Modification of Al-base Composite by Friction Stir Processing
تعديل التركيب الحجري للمواد المتراكبة باستخدام المعالجة بالخط الاحتكاكي

Author: Nawal Ezzat
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2010 Volume: 28 Issue: 6 Pages: 1094-1105
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

A novel surface modifying technique, Friction Stir Processing, is used toenhance mechanical properties of Al-Si / Al2O3 composite, through microstructural refinement and homogenization. The effect of processing parameters onresultant microstructure and wear rate is investigated in this work.The Friction Stir Processing resulted in significant breakup of the coarse Siand Al-dendrites and uniform distribution of Si and Al2O3 in the matrix withsignificant micro structural refinement. These microstructures changes lead tosignificant improvement in wear resistance of composite

استخدمت تقنيه جديده لتعديل بنيه السطوح هي المعالجه بالخلط الاحتكاكي وذلك لتحسبنالخواص الميكانيكيه للمواد المتراكبه المنتجه من سبيكه الالمنيوم –سليكون,المقواه بدقائق منالالومينا, من خلال تنعيم ومجانسه الينيه المجهريه . في هذا البحث تم دراسه تاثير متغيراتالعمليه على البنيه المجهريه ومعدل البلى. اظهرت النتائج ان اسنخدام تقنيه الخلط الاحتكاكيادت الى تكسير دقائق السليكون وطور الالمنيوم الشجيري اضافه الى التوزيع المتجانسللسليكون ودقائق الالومينا في السبيكه الاساس مع حدوث تنعيم في البنيه المجهريه .ان هذهالتغيرات في البنيه المجهريه ادت الى تحسين واضح في مقاومه البلى للماده المتراكبه


Article
Influence of Ausforming Treatment of 0.4wt%C Steel Modified With Nb On The Microstructure And Hardness Properties
تأثير المعاملة (Ausforming) على التركيب ألمجهري والصلادة لصلب wtC 0.4% مضافاً إليه عنصر النيوبيوم

Author: Hiam Razzak kadhum
Journal: Tikrit Journal of Engineering Sciences مجلة تكريت للعلوم الهندسية ISSN: 1813162X 23127589 Year: 2012 Volume: 19 Issue: 3 Pages: 19-25
Publisher: Tikrit University جامعة تكريت

Loading...
Loading...
Abstract

In the present work the relationship between the microstructure and the hardness of the Steel both with and without an addition of niobium was studied. Investigation by direct observation using optical microscopy was carried out.The purpose of this work was to analyze the effects of the low thermomechanical treatment of ausforming on the final microstructure and hardness of steel and of the same steel modified with niobium.It was found that the deformation during low thermomechamical treatment of ausforming introduces changes in the microstructure, such as carbide precipitation, which affect the hardness of the steel.The results show that the mechanical properties of the ausformed Steel depend on the deformation temperature, amount of deformation. The addition of niobium lead to change in the hardness of the Steels investigated.


Article
MICROSTRUCTURE EVOLUTION OF HYPOEUTECTIC AL – SI ALLOY USING DIRECTIONAL SOLIDIFICATION IN CERAMIC MOLD
تحديد البنية الدقيقة لسبائك ألألمنيوم – سليكون تحت اليوتكتيك باستعمال التجمد ألاتجاهي في قالب سيراميكي

Author: Dr. Ayad M. Takhakh Ammar I. Saleh
Journal: Iraqi journal of mechanical and material engineering المجلة العراقية للهندسة الميكانيكية وهندسة المواد ISSN: 20761819 Year: 2010 Volume: 10 Issue: 2 Pages: 251-261
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

Ex perimental and numerical study has been achieved on a hypoeutectic Al - Si alloy under the effect of directional solidification in ceramic mold chilled with copper. From the coupling between experimental (microstructure evaluation) and numerical (solidification simulation) study, a model is obtained. This model can be used to predict the microstructural features of a hypoeutectic Al – Si alloys.

تم في هذا البحث إجراء دراسة عملية ونظريه على سبائك ألألمنيوم – سليكون تحت اليوتكتيكية بتأثير التجمد ألاتجاهي في قالب سيراميكي بوجود مصقع من النحاس. من خلال التعشيق بين الدراسة العملية (حساب البنية الدقيقة) والنظرية (محاكاة التجمد) تم الحصول على نموذج رياضي. ممكن استخدام هذا الموديل للتنبؤ بالبنية الدقيقة لسبائك ألألمنيوم – سليكون تحت اليوتكتيك.


Article
Low Loss in a Gas Filled Hollow Core Photonic crystal fiber
خسائر قليلة في الليف البلوري الفوتوني ذي قلب المجوف المملوء بالغاز

Author: Hanan J. Taher حنان جعفر طاهر
Journal: Baghdad Science Journal مجلة بغداد للعلوم ISSN: 20788665 24117986 Year: 2010 Volume: 7 Issue: عدد خاص بمؤتمر العلمي النسوي 1 Pages: 129-138
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

The work in this paper focuses on the experimental confirming of the losses in photonic crystal fibers (PCF) on the transmission of Q-switched Nd:YAG laser. First HC-PCF was evacuated to 0.1 mbar then the microstructure fiber (PCF) was filled with He gas & gas. Second the input power and output power of Q-switched Nd:YAG laser was measured in hollow core photonic bandgap fiber (HCPCF). In this work loss was calculated in the hollow core photonic crystal fiber (HCPCF) filled with air then N2, and He gases respectively. It has bean observed that the minimum loss obtained in case of filling (HC-PCF) with He gas and its equal to 15.070 dB/km at operating wavelength (1040-1090) nm.

يركز العمل على أثبات وبطريقة عملية الخسائر في الألياف البلورية الفوتونية لنقل ليزر الندميوم-ياك ذو عامل النوعية Q.أولاً الليف البلوري الفوتوني ذي القلب المجوف يفرغ من الهواء الى 0.1 ملي بار ثم يملئ بغاز الهليوم وبعدها بغاز النايتروجين الليف الصغير التركيب (PCF). ثانياً تم قياس القدرة الداخلة والقدرة الخارجة لليزر الندميوم-ياك ذو عامل النوعية Q خلال الليف البلوري الفوتوني ذي القلب المجوف, في هذا العمل الخسائر حسبت في الليف البلوري الفوتوني ذي القلب المجوف(HCPCF) المملؤ بالهواء وبعدها بغاز الهليوم ثم بغاز النايتروجين تم ملاحظة أقل خسائر مستحصلة في حالة مليء الليف البلوري الفوتوني ذي القلب المجوف بغاز الهليوم وتساوي dB/km 15.070 عند الطول الموجي (1040-1090) نانومتر.


Article
Study of the Mechanical and Metallurgical Properties of Dissimilar Welds

Authors: Sami A. Nawi --- Kasim A. Khalaf --- Muna K. Abbas
Journal: Journal of Engineering مجلة الهندسة ISSN: 17264073 25203339 Year: 2007 Volume: 13 Issue: 1 Pages: 1283-1294
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

In this research dissimilar welds were made of low carbon steel (A516) and austenitic stainless steel (316L) by shielded metal arc welding (SMAW) and with different electrodes (E7018) , (E6013) , (E309L) and (E308L). The sheet thickness (6 mm), welding current (120 A), voltage (78V), polarity (DCRP) and electrode diameter (3.25 mm) were remained constant. Many tests were carried out, mechanical tests included tensile test, bending and microhardness also made , and metallurgical inspections included microstructure, delta- ferrite phase and x- ray diffraction analysis. It was found from tensile and bending tests results that the electrode (E309L) was the most convenient for dissimilar welds of base metal (C.St. A516) and (St. St. 316L). Hardness tests showed that the highest hardness value appears in (HAZ) and there are two peaks of maximum hardness, each peak value in each (HAZ) for both dissimilar metals, the peak values are not equal and the higher value appears in the zone, where the electrode differ from the base metal, i. e. when the electrode is used (E6013) the higher value appeared in the (HAZ) which is near the stainless steel (316L), and when the electrode (E309L) is used, the higher value appeared in (HAZ) near the low carbon steel (A516) .The tests demonstrated that the delta ferrite phase was about 3-10% near stainless steel and for all used electrodes.

تناول البحث انتاج وصلات لملحومات غير متشابهة من الفولاذ منخفض الكاربون (A516) مع الفولاذ مقاوم الصدأ الاوستنايتي (316L) بطريقة لحام القوس الكهربائي المعدني المغلف بالصهيرة (SMAW) باختيار اقطاب لحام مختلفة هي (E308 L, E309L, E6013, E7018) مع ثبات سمك الصحفيحة (6 mm) وتيار اللحام (120 Amp) والفولتية (78 volt) والقطبية (DCRP) وقطر قطب اللحام (3.25mm) .تم اجراء فحوصات ميتالورجية مختلفة شملت البنية المجهرية وفحص طور دلتا فبرايت والفحص بحيود الاشعة السينية وكذلك اجريت الاختبارات الميكانيكية ومنها اختبار الشد والحني والصلادة الدقيقة . أظهرت نتائج أختبارات الشد والحني ان القطب (E309L) هو الاكثر ملائمة في لحام الوصلات للملحومات غير المتشابهة من حيث المعدن الاساس (فولاذ منخفض الكاربون (A516) مع فولاذ مقاوم للصدأ (316L)) . اظهرت نتائج الصلادة ان أعلى صلادة هي في المنطقة المتأثرة بالحرارة (HAZ) وقد وصلت الصلادة الى قيم أعلى من منطقة اللحام (W.M) وهذا يعني ظهور قمتين للصلادة العظمى (قمة في كل منطقة HAZ) لكلا المعدنين غير المتشابهين وهاتين القمتين غير متساويتين وتكون الصلادة أعلى في الجانب الذي يكون فيه القطب مختلفا عن نوعية المعدن الاساس أي انه عند اللحام بقطب (E6013) اظهرت القمة العليا في (HAZ) القريب من الفولاذ مقاوم للصدأ (316 L) ، أما عند اللحام بقطب (E309 L) ظهرت القمة العليا في منطقة (HAZ) القريب من الفولاذ منخفض الكاربون في حالة الملحومات غير المتشابهة . أوضحت نتائج الفحص لطور الدلتا فيرايت ان قيمة هذا الطور تتراوح من (10-3) % من جانب الفولاذ مقاوم الصدأ ولجميع الاقطاب المستعملة .


Article
The Effect of Disinfectant on the Microstructure of Dental Stone at Different Time Intervals

Author: Dr. Shorouq Majid Abass B.D.S., M.Sc.* د. شروق ماجد
Journal: MUSTANSIRIA DENTAL JOURNAL مجلة المستنصرية لطب الاسنان ISSN: 18138500 Year: 2007 Volume: 4 Issue: 2 Pages: 199-205
Publisher: Al-Mustansyriah University الجامعة المستنصرية

Loading...
Loading...
Abstract

Gypsum products have been considered to be among the most widely used model and die materials. Modifications of these materials by adding chemicals or salts result in a change in their structure. This study was designed to evaluate the effect of the addition of Calcium Hypochlorite disinfectant on the microstructure of dental stone.Calcium Hypochlorite disinfectant in aqueous solution in different concentrations (0.5, 1.0, 1.5 and 2.0%) was added to type III dental stone. The microstructure of the dental stone samples was examined under the microscope and then photo scoped, pictures were taken at different time intervals (immediately, after 10, 30 min., 1and 2 hours) for all the test groups.The results of this study showed that at different time intervals, from the beginning of mixing of dental stone with Calcium Hypochlorite disinfectant solution, deformation in the microstructure was produced (calcium sulfate dihydrate crystals).Microscopically appearance of dental stone samples mixed with Calcium Hypochlorite disinfectant solution revealed a deformation in size and shape of the calcium sulfate dihydrate crystals when compared with the control group.


Article
Preparation Of Al-12si Foam Using Liquid Technique
تحضير رغوة الالمنيوم –سيليكون 12 بلستخدام تقنية الحالة السائلة

Authors: Adel Mohammad Jaber --- Nawal E. Abdullatef
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2009 Volume: 27 Issue: 12 Pages: 2479-2493
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

This research aims at foaming an Al-12Si alloy by using CaCO3 powderas a foaming agent added to the agitated melt in different weight percents.The foaming process was carried out at different foaming temperatures of700C˚, 750 C˚ and 800C˚ for 5, 10 and 15 minutes using different foamingagent percents (0.5, 1, and 1.5) wt%. The metallic foam had beencharacterized by microstructure examinations, density and porosity andcompression tests.It was found from the results that there is an ability to produce metallicfoams based on Al –Si alloy by using CaCO3 as a foaming agent without theneed for adding ceramic stabilizing materials which are always added in ahigh percent. The mach inability problems caused by the presence of thesematerials can therefore be avoided.It was also pointed out that the porosity of metallic foams fabricated inthis work increased as the foaming agent percent increases within the rangeused (0.5% - 1.5 %) and the preferred amount is 1%, where the optimumfoaming time is 10 minutes at a foaming temperature of 750 C˚.

يهدف البحث انتاج رغوة معدنية من سبيكة الالمنيوم – 12 سليكون وذلك باضافة كاربوناتالكالسيوم كعامل ترغية الى المعدن المنصهر اثناء عملية الخلط وبنسب وزنية مختلفة. ثم اجراء( وبازمان ترغية هي ( 15، 5،10 ˚ عملية الترغية عند درجات حرارية هي ( 750،700،800 )مدقيقة وباضافة نسب مختلفة من عامل الترغية هي ( 0.5،1.5،1 )% . تم توصيف الرغوة المعدنيةالناتجة باستخدام الفحوصات المحهرية وفحوصات الانضغاط ، كما تم حساب الكثافة والمسامية.من نتائج التجارب وجد ان هنالك امكانية لانتاج رغوة معدنية من سبيكة الالمنيوم- 12 سليكونباستخدام كاربونات الكالسيوم كعامل ترغية بدون الحاجة الى اضافة دقائق سيراميكية مثل كاربيدالسليكون والتي تضاف بنسب عاليةلغرض استقرار الرغوة المعدنية. وبذلك يمكن تقليل المشاكللوحظ من النتائج ان نسبة المسامية Sic الناجمة عن صعوبة تشغيل الرغوه الحاوية على نسب منللرغوة المعدنية المنتجة تزداد مع زيادة نسبة اضافة عامل الترغية. وان افضل نسبة مسامية تمالحصول عليها عند اضافة 1% كاربونات الكالسيوم وزمن ترغية 10 دقائق وبدرجة حرارة.˚ 750


Article
Studying The Bonding Mechanismand Microstructure for Arc Welding of Dissimiler Steel to Copper
البنیة المجھریة وآلیة الربط لملحومات القوس الكھربائي غیر المتماثلة فولاذ الى النحاس

Author: عبد الله عذيب مشاري
Journal: Thi-Qar University Journal for Engineering Sciences مجلة جامعة ذي قار للعلوم الهندسية ISSN: 20759746 Year: 2011 Volume: 2 Issue: 1 Pages: 1-15
Publisher: Thi-Qar University جامعة ذي قار

Loading...
Loading...
Abstract

The aim of this work is to study thebonding mechanism and the microstructure of copper to steel welded by shielded metal arc welding (SMAW). The electrodes that used are ECuSi and ECuSn8thenthe examination of microstructure by optical microscopic, it is clearlyobserved that the copper side are completely interfering with epitaxial growth when using ECuSn8 but the side of steel reveal interaction waves at the interface with nonepitaxial growth. Some of fine cracks observed at the interface with ECuSi. The use of ECuSn8 explaininterfering fine blockes from the steel inside the fusion zone.


Article
Refinement the Microstructure of Al–7Si Alloy by the Addition of Cadmium

Author: Sura Abd Al-Zahrah Muhsion
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2012 Volume: 20 Issue: 1 Pages: 62-66
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

Cadmium (Cd) modified aluminium–silicon cast alloys are well known for their outstanding mechanical properties as they combine excellent strength with good ductility that is due to a modification of brittle Si in the eutectic with traces of Cd (0.2–1.0 wt%). The results showed that the Cd leads to the refinement of eutectic silicon from ~95 to 10µm. The alloys which used in this work were Al-7Si alloy with additions of 0.2, 0.6 and 1 wt% Cd as well as Al-7%Si with out Cd addition. The effect of keeping time also studied and the results indicate that the addition of 1%Cd with keeping time 3min was the best (about 10 µm).

تكون مصبوبات سبائك الألمنيوم-سليكون، المعدلة بنيتها البلورية بإضافة كميات محسوبة من الكادميوم، ذات خواص ميكانيكية عالية. وهذه الخواص ناتجة عن الجمع بين المتانة العالية والمطيلية الجيدة والناتجة عن تعديل البنية البلورية لطور السليكون الايوتكتيكي من شكل رقائق أو صفائح هشة إلى شكل خيطي منتظم وذلك بفعل إضافة الكادميوم لغاية 1% كمعدل للبنية البلورية. تشير نتائج فحص البنية المجهرية لطور السليكون الايوتكتيكي إلى أن المصبوبة المضاف إليها كادميوم بنسبة 1% قد يصل تحول هذا الطور من شكل ابري أو رقائقي ذو طول حوالي 95 مايكرون إلى خيطي بطول حوالي 10 مايكرون . إن السبائك التي تم دراستها في هذا البحث هي ألمنيوم-7%سليكون بإضافة الكادميوم بنسب(0.2، 0.6 و 1.0%) إضافة إلى السبيكة الأصلية بدون إضافات. كذلك تم دراسة تأثير وقت الحفظ عند درجة حراة إضافة الكادميوم وقد أظهرت النتائج إن المصوبة التي أضيف لها الكادميوم بنسبة 1.0% ووقت حفظ 3 دقائق كانت هي الأفضل (طول السليكون الايوتكتيكي الخيطي10 مايكرون).


Article
EFFECT OF THERMOMECHANICAL TREATMENTS ON AGING BEHAVIOR AND FRACTURE TOUGHNESS OF AL-CU-MG ALLOY PLATES USED IN AIRCRAFT STRUCTURE

Author: Dr. Alaa A. Ateia,
Journal: Iraqi journal of mechanical and material engineering المجلة العراقية للهندسة الميكانيكية وهندسة المواد ISSN: 20761819 Year: 2009 Volume: 9 Issue: 1 Pages: 53-67
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

The effects of variations in the thermomechanical treatments parameters on the microstructure and mechanical properties of Al-Cu-Mg alloy plates used in aircraft structure subjected to a post heat treatments have been conducted. It was confirmed that a large gain in fracture toughness combined with a good mechanical properties could be achieved by choice of the correct initial condition, amount and temperature of deformation, and the time temperature of the final age hardening sequence. In general, it was found that the material should be age hardened to the peak hardness conditions before deformation at an elevated temperature (warm rolling at 200°C) in order to prompt homogeneous slip. Room temperature deformation resulted in planar slip at the peak hardness conditions non uniform response on subsequent aging and give lower fracture toughness.

تم في هذا ألبحث دراسة ألتأثيرات ألناجمة من تغيير بعض معاملات ألتعامل ألحراري-ألميكانيكي على استجابة سبيكة ألألمنيوم-نحاس-مغنيسيوم ألمستخدمة في هياكل ألطائرات للتقادم ألاصطناعي أللاحق ومتانة ألكسر. وقد ثبت بأن من ألممكن ألحصول على استجابة جيدة ومتانة كسر عالية عن طريق ألاختيار ألصحيح للظروف ألابتدائية كدرجة حرارة وزمن ألتقادم ألأولي،نسبة ودرجة حرارة ألتشويه بالدرفلة وكذلك درجة حرارة وزمن ألتقادم أللاحق. وبصورة عامة فقد وجد بأن ألواح هذه ألسبيكة يجب أن تصلد حتى ألوصول ألىأعلى صلادة ممكنة قبل أن تدرفل بدرجة حرارة (٢٠٠°م) وذلك لتشجيع حصول عملية انزلاق منتظمة لكل ألبنية ألمجهرية. و ثبت أيضا بأن ألعينات ألمدرفلة بدرجة حرارة ألغرفة في ظروف قمة ألصلادة لاتستجيب جيدا لعملية ألتقادم أللاحق وتعطي متانة كسر منخفضة.

Listing 1 - 10 of 57 << page
of 6
>>
Sort by
Narrow your search

Resource type

article (57)


Language

English (57)


Year
From To Submit

2019 (2)

2018 (7)

2017 (5)

2016 (6)

2015 (6)

More...