Article
Studing The Mechanical Properties Of Ternary Blends Of Hdpe/Pp/Abs

Authors: Zanaib.Y.Shnea --- Nabeela A. Mohammed
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2008 Volume: 26 Issue: 7 Pages: 885-893
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

In this work a type of polymer blend has been prepared from mixing differentpercent (40,50,60, and 70) % of High-density polyethylene, polypropylene and adding 6%weight percent of acrylonitril-butadiene-styrene by using single-screw extruder. Theextrusion process concentrated on the homogeneous mixing manner among materialsthrough a regular selection of machine screw revolution per minute and temperature used inextrusion process. Some of mechanical properties such as impact strength, modulus ofelasticity and shore hardness of polymer blend, were determined at different weight fractionof blend. It was found that the addition (6%wt) of ABS to the binary blends HDPE/PP leadsto increase the modulus of elasticity, the impact strength and shore hardness.On the other hand increasing % HDPE content from 40 to 70wt% in HDPE/PPternary blends leads to increase the modulus of elasticity from 166.35 Mpa to 186.25 Mpa,and impact strength increase from o.o52 to o.o6 J/mm2 while decreases the shore hardnessfrom 89 to 69.

في البحث الحالي تم تحضير خلائط بوليمرية جديدة والتي هي عبارة عن مخلوط بوليمري،40,50 ) من البولي اثلين العالي الكثافة مع البولي , يتكون من مزج نسب وزنية مختلفة%( 60,70بروبلين مع إضافة نسبة وزنية%( 6) من اكريلونتريل-بيوتا دين-ستايرين(وذلك باستخدام جهاز الباثقةالمنفرد).تم استخدام عملية البثق في تحضير المواد المتراكبة وذلك بواسطة استخدام ماكنة البثق أحاديةاللولب حيث ركزت على أسلوب الخلط المتجانس بين المواد من خلال تحديد سرعة دوران اللولب الماكنةودرجات الحرارة المستخدمة في عملية البثق. وبعد ذلك جرت دراسة بعض الخصائص الميكانيكية مث لمقاومه الصدم ،معامل المرونة وصلادة شور ولجميع خلائط بوليميرية المحضرة. والنتائج التي تم الحصولعليها أوضحت عند إضافة%( 6) من اكريلونتريل-بيوتا دين-ستايرين الى خلائط ثنائي( البولي اثلين العاليالكثافة –البولي بروبلين) ادى الى زيادة معامل المرونة ,قوه الصدمة وصلادة شور. من ناحية أخرى وجدبأن زيادة اضافة البولي اثيلين عالي الكثافة من( 40 الى 70 )% إلى خلائط ثلاثية (البولي اثيلين عاليالكثافة-البولي بروبلين - اكريلونتريل-بيوتا دين-ستايرين) تحسنت الكثير من الخواص الميكانيكية حيثادى الى زيادة معامل المرونة م ن( 166,35 )إلى ( 186,25 )ميكاباسكال وقوه الصدمة م ن.( 0,053 الى 0,060 )جول/مليملتر 2 . بينما قلت صلادة شور من ( 89 ) إلى (


Article
Studying the Impact Strength of (Epoxy with TiO2 and MgO) Composite

Authors: Balkees M.Deya’a --- Fawziea M. Hussien --- Intihah Gatia Dway
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2011 Volume: 29 Issue: 10 Pages: 1971-1978
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

This work has been done with using of epoxy resin mixed with polystyrene(90/10) % to compose binary blend. Two types of powder (TiO2, MgO) in two volume fractions of (10, 15) % were used as reinforcement materials to the prepared polymer (B).Hand lay-up technique is used in fabrication of the composite samples. Impact test was carried out for the proper samples in both normal condition and after immersion in water, KOH (0.5 N), HCL (0.5 N) solutions for periods ranging up to 8 weeks. After comparing the results between the polymer blend and their composite, it was found that Impact Strength were greater for the matrix (B) after immersion compared with their values beforeimmersion while the results of the composite before immersion show that(B+10%MgO) has higher impact strength (11.333) KJ/m2


Article
The Effect of PVP Addition on the Mechanical Properties Of [84%LLDPE: 15 %(( 100- X) %PP: X%PVP):1%Basalt Particle] Polymer Blend Composites.
دراسة تأثير أضافة (PVP) على الخواص الميكانيكيه للخليط البوليمري المتراكب: [84%LLDPE:15%((100-X)%PP:X%PVP):1%basalt particle]

Authors: Teeb A. Mohammed --- Akram R. Jabur --- Sihama E. salih
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2014 Volume: 32 Issue: 3 Part (A) Engineering Pages: 573-585
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Polymer blends composites were prepared according to the formula [84%LLDPE:15%((100-X)%PP:X%PVP):1%B.P] with weight ratios selected for X values (0,4,8,12,16 %), as strips by double screw extruder and use press process the strips to prepare the samples according ASTM specification, the mechanical properties were studied for all theprepared samples which are (tensile, flexural, compression, impact, hardness, and creep tests). The results are as following:- results showed increment of mechanical properties as PVP ratio increases except elongation, furthermore the results recorded highest values of fracture strength, young modulus, compressive strength, flexural strength, maximum shear stress, flexural modulus and creep modulus at PVP 8% wt. which are (31.32MPa, 0.14GPa, 27.4MPa,24MPa, 0.6MPa, 1.08GPa and 0.558GPa) respectively.While the highest values of fracture toughness and hardness recorded at 12% wt. (1.4696Pa√m), and at 4% wt. (56.5) respectively.

حضرت المتراكبات ذات أساس الخليط البوليمري الثلاثي, وفق الصيغة [84%LLDPE:15%((100-X)%PP:X%PVP):1%B.P] وبنسب وزنية مختارة لقيم x 16,12 ,8 ,4 ,0) %). وقد تم تحضيرها بشكل شرائط حضرت بعملية البثق بواسطة باثقة ثنائية اللولب واستخدمت عملية كبس الاشرطة لتحضير العينات وفق المواصفة القياسية (ASTM) , درست الفحوصات الميكانيكية للعينات المحضرة والمتمثلة ( فحص الشد والانحناء والانضغاط والصدمة والصلادة والزحف) أظهرت النتائج زيادة في الخصائص الميكانيكية مع زيادة نسبة PVP باستثناء المطيلية وعلاوة على ذلك سجلت النتائج أعلى قيم لمقاومة الشد, معامل الرونة, مقاومة الانضغاط ومقاوة الانحناء واعلى أجهاد قص ومعامل مرونة الانحناء ومعامل الزحف عند نسبة (8% wt) PVPوهي على الترتيب (31.32MPa , 0.14GPa , 0.6MPa , 27.4MPa , ( 0.558GPa , 1.08Gpaفي حين سجلت أعلى قيم لمتانة الصدمة وقيم الصلادة عند نسبةPVP 12% wt.)) (1.696 Pa√m) و 4%wt ((56.5 على الترتيب .


Article
Mechanical and Morphological Properties of HDPE: PP and LDPE: PP Polymer Blend Composites Reinforced with TiO2 particles
الخواصالمیكانیكیة و المجھریة لمتراكبات الخلائط البولیمریة HDPE: PP و LDPE: PP المقواة بدقائق اوكسید التیتانیوم

Authors: Sihama I. Salih --- Abdullkhaliq F.hamood --- Alyaa H. Abdalsalam
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2013 Volume: 31 Issue: 12 Part (A) Engineering Pages: 2211-2227
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

In this research two groups of polymer blends have been prepared First group included (High density polyethylene (HDPE): Polypropylene (PP))While the Second group(included Low density polyethylene (LDPE): Polypropylene (PP)) both groups prepared withpolypropylene of (20% and 80%). From the results of tensile test for the prepared blends it has been showed that the optimum blending ratio was (20%LDPE:80%PP and 20%HDPE:80%PP) which thenreinforced with (2, 5 and 8wt%) oftitanium dioxide (TiO2), particle size (0.421μm). Titaniaparticles weremechanically mixed with the polymers prior tomelt mixing for better dispersion.Polymerblend composites were obtained by using single screw extruder. Results showed that mechanical properties increased as titania content increased except elongation.Furthermore the result recorded highest values ofimpact strength and fracture toughness at2%wt TiO2which is 312 Mpa and 572.8Mparespectively,for the polymer blend (20%HDPE: 80%PP) composite and for the polymer blend (20%LDPE: 80%PP) composites the impact strength and fracture toughness are 262.5Mpa and 468 Mpa respectively.The mechanical properties values of 20%HDPE: 80%PP is higher than 20%LDPE: 80%PP polymer blendcomposites. Scanningelectron microscopy (SEM) imagesshowed that there isbonding developed between TiO2 and polymer blends in some regions.

Keywords

Polymer blend --- TiO2 --- HDPE --- PP --- composite --- Mechanical properties


Article
Mechanism of Hybrid Reinforcement and its Effect on some Properties of Binary Polymer Blend
ألية التسليح الهجين وتأثيرها على بعض الخواص لخليط بوليمري ثنائي

Authors: Awham M. Hameed --- Entihaa G. Daway
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2014 Volume: 32 Issue: 2 Part (B) Scientific Pages: 287-301
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

The aim of current study is carrying out some modifying in properties of resin material (Unsaturated polyester, UPE) by adding thermoplastic material (polystyrene, PS) with different weight ratios included (0%, 5%, 10%, 15% and 20%) of (PS) to prepare binary polymer blend. The optimum ratio was selected in terms of the homogeneity case between the two polymers and studying the nature of the surfaces of the prepared materials using the optical microscope. Some mechanical tests were performed to determine the values of impact strength (I.S), ultimate tensile strength (UTS) for all prepared specimens. The ratio (80/20, weight/weight)% of (UPE/PS) blend was selected and reinforced with fibers volume fraction Фf = 10% using three types of fibers included(glass fibers (G.F), Carbon fibers (C.F) and hybrid from the two types (5% G.F and 5% C.F). All the above tests were repeated after the reinforcement for comparing the results and studying the behavior of materials under work. The results exhibited that the values of (I.S) increase with increasing of the blending ratio of (PS) while the values of (UTS) decrease at blending ratios (10, 15) % of (PS) and return to increase at the ratio 20% . After the reinforcement, it was found that the composite reinforced with carbon fibers records the highest values of impact strength for un notch specimens while the hybrid composite has the highest value of the ultimate tensile strength comparing with E-glass and carbon fibers composites.

الهدف من الدراسة الحالية هو اجراء بعض التحوير في خواص مادة راتنجية ( البولي استر غير المشبع , UPE) بأضافة مادة ثرموبلاستيكية (البولي ستايرين ,PS) وبنسب وزنية مختلفة شملت0,5 10, 15, 20) )% من البولي ستايرين لتحضيرخليط بوليمري ثنائي.وقد تم اختيارالنسبة المثلى بدلالة حالة التجانس بين البوليمرين ودراسة طبيعة السطوح للموادالمحضرة بأ ستخدام المجهر الضوئي. أجريت بعض الاختبارات الميكانيكية لتحديد قيم مقاومة الصدمة (I.S) , مقاومة الشد القصوى (UTS) لجميع النماذج المحضرة. تم اختيارالنسبة الوزنية (80/20)% من خليط البولي استر غير المشبع/ البولي ستايرين وسلحت بالالياف وبكسرحجمي (Фf = 10%) باستخدام ثلاثة انواع من الالياف شملت (الياف الزجاج (G.F), الياف الكاربون ((C.F وهجين من نوعي الالياف (5% G.F) و(5% C.F). تم تكرار جميع الاختبارات اعلاه بعد التسليح لغرض مقارنة النتائج ودراسة سلوك المواد قيد البحث. أظهرت النتائج بأن قيم (I.S) تزداد مع زيادة نسبة الخلط للبولي ستايرين في حين قيم (UTS) تنخفض عند نسبتي الخلط (10, 15)% من البولي ستايرين وتعود لتزداد عند النسبة 20%. وبعد التسليح اظهرت النتائج بأن المتراكب المسلح بألياف الكاربون يسجل القيم الاعلى لمقاومة الصدمة لنماذج غير محزوزة في حين المتراكب الهجين يمتلك القيمة الاعلى لمقاومة الشد القصوى مقارنة مع متراكبات الياف الزجاج والكاربون.


Article
Characterization of Sherardized Low Carbon Steel Used in Oil Pipelines Coated with Polymer Blends Layers
خصائص الفولاذ المننخفض الكاربون المطلي بالخارصين والمستخدم في خطوط انابيب النفط وطلائها بطبقات من الخلائط البوليمرية

Authors: Ali H. Ataiwi --- Sihama I. Al-Shalchy --- Gufran Abdul Mahdi
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2015 Volume: 33 Issue: 4 Part (A) Engineering Pages: 855-867
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Oil pipelines of low carbon steel were coated by sherardizing process at 400oC for different treatment times (15, 30, 60, 120, 240) min and then the sherardizing samples coated by polymer blend unsaturation polyester resin with butadiene rubber (UP: BR) and unsaturation polyester resin with nitrile butadiene rubber (UP: NBR) with different percentage weight ratio of BR and NBR (0, 5, 10 and 15 %) in the blends. The thickness of sherardizing coated, hardness, surface roughness and adhesive strength were studied. The results of this research showed that the thickness of sherardizing coated and hardness values increase with increasing time treatment. The adhesive strength of sherardizing surface coated with polymer blends layer increases with increasing surface roughness of sherardizing coated with two mixed group of polymers blends [(UP:BR) and (UP:NBR)] samples, as well as the adhesive strength decreases with increasing percentages weight of BR or NBR in the blend. The higher values of adhesion force reach to (2.761KN) and (0.848KN) for polymer blends (95%UP: 5%NBR) and (95%UP:5%BR) respectively. Whereas coating sherardizing surface by unsaturated polyester only has the high value of the adhesion force (2.921 KN) at surface roughness (2.29µm). As well as the results show the sherardizing surface coated by mixed polymers blend (UP: NBR) having higher values of adhesion force compared with other samples coated by mixed (UP: BR) polymer blend.

في هذا البحث أجريت عملية الطلاء بالخارصين لأنابيب النفط الصلب منخفض الكربوني في درجة حرارة 400 درجة مئوية لأزمان مختلفة (15، 30، 60، 120، 240) دقيقة ثم طلاء هذه العينات بالخليط البوليمري المتمثل براتنج البوليسر الغير مشبع مع مطاط البيوتاتين والخليط الاخر متمثل المتمثل براتنج البوليسر الغير مشبع مع مطاط نترال البيوتاتين وبنسب مختلفة من المطاط (0،5،10 و 15٪) في الخليط البوليمري. وتم قياس سمك العينات المطلية باخارصين,الصلادة, خشونة السطح وقوة الالتصاق. وتناظرت النتائج بأن سمك الطلاء والصلادة تزداد مع زيادة وقت المعاملة . إضافة إلى ان الصلادة تزداد مع زيادة سمك العينات المطلية بالخارصين . تتزداد قوة التصاق السطح المطلي بالخارصين وطبقة طلاء الخليط البوليمري تزداد مع زيادة خشونة السطح للعينات المطلية بالخارصين ولكلا نوعين الخلائط الوليمرية , إضافة إلى ان قوة الالتصاق تتناقص مع زيادة النسب الوزنية للمطاط في الخليط واعلى قيم تصل اليها هي 2.761كيلو نيوتين لل(95%بوليستلر:5% مطاط نترال بيوتايتين) و0.848كيلو نيوتين لل(95% بوليستلر:5% مطاط بيوتايتين) للخلائط البوليمرية على التوالي. في حين سطح المعدن المطلي بالخارصين ثم طلاءه بالبوليستر الغير مشبع فأن له اعلى قوة التصاق تصل الى 2.921 كيلو نيوتين للعينات التي لها خشونة 2.29مايكرون . كما يمكن ان نلاحظ نتائج سطح المطلي بالخارصين مع الخليط البوليمري( بوليستر :مطاط نترال بيوتايتين) له قيم التصاق اعلى مقارنة مع الخليط البوليمري (بوليستر :مطاط بيوتايتين).


Article
Comparative Study of Some Properties of Two Groups’ Binary Polymer Blends Prepared By a Twin-Screw Extruder
دراسة مقارنة لبعض الخصائص لمجموعتين من الخلائط البوليمرية الثنائية المحضرة بواسطة باثقة ثنائية اللولب

Authors: Sihama I. Al-Shalchy --- Kadhum M. Shabeeb --- Rula F. Hasan
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2015 Volume: 33 Issue: 8 Part (A) Engineering Pages: 1971-1985
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

In this paper, the preparation and compare of some mechanical and physical properties of two groups of polymer blends consisting of polyvinyl chloride with polypropylene (PP-PVC) and poly-vinyl chloride with high-density polyethylene (HDPE-PVC). Using a twin-screw extruder, three weight percentages of PP and HDPE (5, 10 and 15%) were used to prepare the polymer blends. Experimental investigation was carried out for analyzing the mechanical properties liketensile strength, flexural strength, compression, impact, and hardnessand physical properties (thermal characteristics and melt flow index) for the polymer blend samples. The results show that the polymer blend (HDPE-PVC) get higher values than polymer blend (PP-PVC) in fracture strength, young´s modulus, elongation, flexural strength, creep resistantand maximum shear stress and thermal characteristics, whereas the polymer blends (PP-PVC) get higher values in impact strength, fracture toughness, hardnessand compression and melt flow index. Besides, the increment in PP or HDPE content weak the properties of the polymer blends and the samples with (5%PP:95%PVC) and (5%HDPE:95%PVC)were the best among the other polymer blends samples.

تم في هذا البحثتحضير ومقارنة بعض الخواص الميكانيكيةوالفيزيائية لمجموعتين من الخلائط بوليمرية المتكون من البولي فاينيل كلورايد مع البولي بروبلين(PP-PVC) والبولي فاينيل كلورايد مع البولي اثيلين عالي الكثافة(HDPE-PVC). وباستخدام الباثقة ثنائية اللولب , حضرتالخلائط بوليمرية باستخدام ثلاثة نسب وزنية لكل من البولي بروبلين و البولي اثيلين عالي الكثافة ( 5 و 10 و 15). وقد تم اجراء التحري التجريبيلتحليل الخواص الميكانيكية مثل مقاومة الشد ومقاومة الانحناء والانضغاط والصدمة والصلادةوالخواص الفيزيائيةلنماذج الخلائط البوليمرية. وقد بينت النتائج ان الخليط البوليميري (HDPE-PVC)حصل على اعلى النتائج في مقاومة الكسر، معامل يونك،الاستطالة، متانة الالتواء, مقاومة الزحف واقصى إجهاد للقص و الخصائص الحراريه مقارنةمع الخليط البوليميري (PP-PVC) . بينما الخليط البوليميري (PP-PVC) حصل على اعلى النتائج في مقاومة الصدمة، متانة الكسر، الصلادة، والانضغاط ومؤشر التدفق. وقد بينت النتائج ايضا ان زيادة محتوى PP او HDPE في الخليط البوليميري تؤدي الى اضعاف الخصائص الميكانيكيه للخليط وان نسبة (5%PP:95%PVC) و (5%PVC:95%PVC) كانت الافضل بين العينات الاخرى للخليط البوليميري.


Article
Thermal conductivity and diffusion coefficient of polymer blend 80%EP/20%UPE reinforced with sand particles
دراسة التوصيلية الحرارية ومعامل الانتشار لخليط بوليمري من 80%EP/20%UPE مدعم بدقائق الرمل

Authors: R. H. Khalaf رافد حماد خلف --- A. H. Sarraf عبد الحميد الصراف --- F. H. Anter فائق حماد عنتر
Journal: Iraqi Journal of Physics المجلة العراقية للفيزياء ISSN: 20704003 Year: 2018 Volume: 16 Issue: 38 Pages: 17-25
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

New polymer blend with enhanced properties was prepared from (80 %) epoxy resin (Ep), (20%) unsaturated polyester resin (UPE) as a matrix material. The as-obtained polymer blend was further reinforced by adding Sand particles of particle size (53 µm) with various weight fraction (5, 10, 15, 20 %). Thermal conductivity and sorption measurements are performed in order to determine diffusion coefficient in different chemical solutions (NaOH, HCl) with concentration (0.3N) after immersion for specific period of time (30 days). The obtained results demonstrate that the addition of sand powder to (80%EP/20%UPE) blend leads to an increase of thermal conductivity, with an optimum/minimum diffusion coefficient in (HCl)/(NaOH), respectively.

تم في هذا البحث تحضير خليط بوليمري مكون من رتنج الايبوكسي و البولي استر الغير مشبع بوصفة مادة اساس بنسبة (80%) من الايبوكسي و (20%) من البولي استر الغير مشبع, وتم تقوية الخليط بإضافة دقائق من الرمل بحجم (53 µm). وتمت دراسة الفحوصات الفزيائية التي تضمنت حساب معامل التوصيل الحراري، وكما تم اجراء اختبار الامتصاصية لحساب معامل الانتشار لجميع النماذج وذلك بعد غمرها في الوقت نفسه ولفترة زمنية معينة بحدود (30 يوم) في محاليل كيميائية مختلفةNaOH, HCl) ) وبعارية لمحاليل (N 0.3), حيث وجد ان اضافة مسحوق الرمل (53 µm) الى الخليط البوليمري(EP/UPE) تؤدي الي زيادة التوصيلية الحرارية, كما وجد ان أعلى واقل قيمة لمعامل الانتشار ظهرت في محلول (NaOH)/(HCl) على التوالي.


Article
Preparation, Characterization and Prophylactic Study of New Microsphere Containing Doxycycline against Diseases of Shrimp
تحضير وتشخيص و دراسة وقائية للمايكروسفير المحمل بالدوكسيسايكلين لامراض الروبيان

Loading...
Loading...
Abstract

Therapeutically and prophylactically using Microspheres containing doxycycline isolated from shell of shrimp. Low molecule weight poly lactic acid was prepared. In this study, Poly lactic acid (PLA)/ poly vinyl alcohol (PVA)/poly ethyleneglycol(PEG) loading doxycycline blend solutions was prepared. Also Poly lactic acid (PLA)-Tannin blend via solvent evaporation method was prepared. Microspheres of chitosan/gelatin microsphere loading doxycycline was prepared by emulsion crosslinking technique. Both microsphere and blends were characterized by Fourier transform infrared (FTIR) spectrophotometer. The FTIR spectra were shown distinguish bands. The in vitro release of doxcycline from its matrix at pH 7 was studied. The prophylactic against white spot (Ich) disease of shrimp (Macrobrachium nipponense) was studied. The results were shown increase of percentage of survival of shrimp in both microsphere and blend compared with control. The highly percentage of survival was shown in the microsphere compare with blends.

يستخدم قشور الروبيان في تصنيع المايكروسفير المحمل بالدوكسيسايكلين للاغراض الوقائية والعلاجية , لذلك حضر بوزن جزيئي واطىء بولي حامض اللاكتيك. في هذه الدراسة أستخدم طريقة تبخير المذيب لتحضير مخاليط بوليمرية من بولي حامض اللاكتيك مع بولي فنيل الكحول مع بولي اثيلين كلايكول المحمل بالدوكسيسايكلين وكذلك حضر بولي حامض اللاكتيك مع المواد التانينية . وأستخدمت طريقة المستحلب المتشابك في تحضير المايكروسفير من الكيتوسان والجيلاتين والمحمل بالدوكسيسايكلين . شخصت المخاليط البوليمرية والمايكروسفير بواسطة طيف الاشعة تحت الحمراء ليعطي الحزم المميزة لهذه المركبات . درس تحلل الدواء من المنظومة البوليمرية في محلول منظم بدالة حامضية 7 . وكذلك درس الخاصية الوقائية لمرض البقعة البيضاء المسببة لهلاكات الروبيان وقد اظهرت النتائج زيادة نسبة البقاء على قيد الحياة من الروبيان في كل من المايكروسفير والمخاليط البوليمرية مقارنة مع الكنترول وكانت نسبة البقاء الاعلى هي للروبيان المعامل بالمايكروسفير .


Article
The Effect of Polymer Blend on the Third Order Nonlinearity of Oxazine Dye Doped Films by Using Z-Scan Techniques

Author: Amal F. Jaffar
Journal: Al-Nahrain Journal of Science مجلة النهرين للعلوم ISSN: (print)26635453,(online)26635461 Year: 2015 Volume: 18 Issue: 3 Pages: 80-88
Publisher: Al-Nahrain University جامعة النهرين

Loading...
Loading...
Abstract

The nonlinear optical properties of the laser dye Oxazine doped with polystyrene (OX /PS), Ox/poly methylmethacrylate (PMMA) and Ox/PS-PMMA blend films have been studded. The films deposited by free-casting technique and characterized by Z- scan technique .Z-scan experiment was performed using continuous wave (CW) diode laser at 650 nm at in two parts. The first part was done using a closed-aperture placed in front of the detector to measure the nonlinear refractive index ,with the second part; the aperture in front the detector was removed (open aperture) to measure the nonlinear absorption coefficient. The open-aperture curve exhibits a normalized transmittance (valley), indicating the presence of induced absorption. The observed nonlinearity is found to be of the third order, as it fits to two photon absorption process (TPA). The closed-aperture curve exhibits a peak to valley shape, indicating a negative value of the nonlinear refractive index n2. The effective values of the nonlinear refractive index n2, the nonlinear absorption coefficient β2, real and imaginary parts of the third-order optical nonlinearity, χ(3) for Ox/PMMA-PS films comparatively with that of Ox/PMMA and Ox/PS has much lower transmittance value obtained shows that these films can be used as efficient optical limiters.

لقد تمت دراسة الصفات البصرية اللاخطية لاغشية الصبغة الليزرية الاوكسازين المطعمة مع بوليمير البولسترين PS و بوليمير اللبوليمثيل اكريليت PMMA و مزيج كل من البوليمرينPS و PMMA تم ترسيب هذه الاغشية بتقنية الطرح الحر و ميزت بتقنية المسح على البعد الثالث. تجربة المسح على البعد الثالث نفذت باستخدام ليزر الدايود ذو الموجات المستمرة وبطول موجي 650 نانومتر و بجزأين. في الجزء الأول تم وضع فتحة أمام الكاشف لغرض دراسة معامل الانكسار اللاخطي. في الجزء الثاني أزيلت الفتحة من أمام الكاشف (open aperture) لغرض قياس معامل الامتصاص اللاخطي. اظهر الرسم البياني لازالة الفتحة نفاذية طبيعية (قعر) مشيرة الى وجود امتصاص محتث. وجد أن اللاخطية الملاحظة هي من المرتبة الثالثة،لانها تتطابق مع عملية إمتصاص فوتونين. أظهر منحني الفتحة المغلقة شكل قمة الى قعر مشيرا الى معامل انكسار لاخطي ذو قيمة سالبة .القيم الفعالة لمعامل الانكسار اللاخطي، ومعامل الامتصاص اللاخطي والاجزاء الحقيقية والخيالية للصفات اللاخطية من المرتبة الثالثة لاغشية OX/PMMA-PS مقارنة مع اغشية Ox/PMMA واغشية Ox/PS مع القيمة الواطئة جداً للنفاذية التي تم الحصول عليها اوضحت بإمكانية استخدم هذه الاغشية كمحددات بصرية فعالة.

Listing 1 - 10 of 12 << page
of 2
>>
Sort by
Narrow your search

Resource type

article (12)


Language

English (12)


Year
From To Submit

2018 (1)

2017 (2)

2015 (4)

2014 (2)

2013 (1)

More...