Article
Reinforcing of Aluminum-Silicon Alloy with Nano Composites

Authors: Ali. M --- Mohsen O.S.
Journal: Iraqi Journal of Applied Physics المجلة العراقية للفيزياء التطبيقية ISSN: 18132065 23091673 Year: 2013 Volume: 9 Issue: 2 Pages: 25-30
Publisher: iraqi society for alternative and renewable energy sources and techniques الجمعية العراقية لمصادر وتقنيات الطاقة البديلة والمستجدة

Loading...
Loading...
Abstract

The microstructures of composites were examined using optical microscopy (OM) and transmission electron microscopy (TEM). Microscopic observations of the microstructures revealed that the dispersion of the particles was uniform. The tensile strength (yield strength and ultimate tensile strength) and the Young's modulus improve with the addition of nano particles although some reduction in ductility is observed. The highest yield strength and UTS was obtained by 3.5 vol. % of SiC nano-particles. A relatively ductile fracture in tensile fractured samples was observed by fractography examination.


Article
The Study of Dielectric and Microstructure Properties for Iraqi Kaolin Under the Effects of Binder and Calcinations.
دراسة الخواص العزلية والتركيبية للكاؤؤلين العراقي تحت تأثيرالمادة الرابطة وعمليات الكلسنة

Authors: F. A. Rasin فاضل عبد رسن --- R. S. Al-Khafaji رغد صبحي الخفاجي
Journal: Iraqi Journal of Science المجلة العراقية للعلوم ISSN: 00672904/23121637 Year: 2013 Volume: 54 Issue: 2 Pages: 333-339
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

The calcination treatments and a binder of poly acrylic acid PAA (1wt%) effects on kaolinite particles were investigated through dielectric properties at 1MHz ,quantitative analysis of X-ray diffraction and microstructure. The calcinated samples at 850°C/3hr and fired at 1350°C/2hr were revealed decrease in broadening (Full Width at half maximum) FWHM and increase of dielectric constant.

ان المعاملة تحت تأثيرعمليات الكلسنة (التحميص) والمادة الرابطة بولي أكرلك أسد ((1wt% على حبيبات الكاؤؤلينيت تمت دراستها من خلال الفحوصات التشخيصية للاشعة السينية والمجهرية والقياسات العزلية وتبين ان العينة المكلسنة عند 850م˚لمدة 3ساعات والملبدة الى 1350 م˚لمدة ساعتين امتازت بنقصان في التعريض عند منتصف الشدة (FWHM) وزيادة في ثابت العزل.


Article
THEORETICAL AND EXPERIMENTAL INVESTIGATION OF FRICTION STION STIR WELDING FOR COPPER ALLOY
دراسة نظرية وعملية للحام الاحتكاكي لسبائك النحاس

Authors: Nabeel Shallal Thamer --- Ahmed Hadi Abood --- Dr. Hani Aziz Ameen
Journal: Al-Qadisiyah Journal for Engineering Sciences مجلة القادسية للعلوم الهندسية ISSN: 19984456 Year: 2013 Volume: 6 Issue: 3 Pages: 332-351
Publisher: Al-Qadisiyah University جامعة القادسية

Loading...
Loading...
Abstract

Friction stir welding (FSW) is a relatively new solid-state joining process. Thisjoining technique is energy efficient. In particular, it can be used to join highstrengthaerospace aluminum alloys and other metallic alloys that are hard to weldby conventional fusion welding. In this paper the investigation is made on frictionstir welding process for joining of copper alloy. Friction stir welding experimentswas performed using different pins (pin with straight boundary and pin with curvedboundary). Welding joints efficiencies were found for each set. Mechanical andmicrostructural analysis has been performed experimentally on the welding zone.Non- linear numerical models was built in ANSYS software to simulate thethermal history of a workpiece undergoing friction stir welding by a movingheating source. An accurate prediction of temperature fields is evident. Exclusiveresult for effect of rotating a friction stir tools with respect to boundary conditionson stress-strain curves is presented. The results shown that the friction stir weldingwith pin of curved boundary is more efficient than that of straight boundary

تعتبر عملية اللحام الاحتكاكي من اكفأ عمليات اللحام والتي تستعمل لربط المعادن مثل الالمينيوم والمعادن)FSW( الاخرى والتي من الصعوبة لحامها بالطرق التقليدية . في هذه الدراسة تم تطبيق الحام الاحتكاكيلسبائك النحاس من خلال تصميم وتصنيع نوعين من الأدوات )الدبوس بحواف مستقيمة والدبوس بحوافمنحنية(. وقد وجد ان كفاءة اللحام جيدة لكلا الحالتين وقد تم إجراء تحاليل ميكانيكية ومجهرية على منطقةاللحام . وقد تم انشاء موديل غير خطي ببرنامج الانسز لمحاكاة التأثيرات الحرارية خلال عملية اللحامباستخدام مصدر حراري متنقل . وقد تم الحصول على نتائج الخواص الميكانيكة منحنى )الاجهاد-الانفعال (لكلا الاوادت التي تم تصنيعها. وقد بينت النتائج ان اللحام باستخدام دبوس بحواف منحنية هو اكثر كفاءة منالحواف المستقيمة .


Article
The Influence of Microstructure on the Corrosion Rate of Carbon Steels
تأثير البنية المجهرية على معدلات تأكل الفولاذ الكربوني

Authors: Sami I. Al-rubaiey --- Eman A. Anoon --- Mahdi M. Hanoon
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2013 Volume: 31 Issue: 10 Part (A) Engineering Pages: 1825-1836
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

This paper presents the influence of carbon steel microstructure on the corrosion rates. Four types of microstructures have obtained by quenching and tempering and iso-thermal annealing. These microstructures are: banded ferrite/pearlite microstructure, fine ferrite/pearlite microstructure, coarse ferrite/pearlite microstructure and tempered martensite microstructure. General corrosion and localized corrosion (penetration rates) were determined via mass loss and optical microscopy. The different microstructures of steels investigated in this paper revealed corrosion rate variations of 0.8– 3.2 mm y-1 and 3.3–6.4 - mm y-1 for the general and localized forms, respectively. The corrosion stability of the various microstructures may arise from variations of phases within the steel. A banded ferrite/pearlite microstructures have worse general corrosion properties, while tempered martensite worse microstructures have localized pitting corrosion properties. Coarse ferrite/pearlite microstructures have better localized pitting corrosion resistances compared to others investigated microstructures This paper has demonstrated that, microstructure is an important consideration when selecting carbon steel for an industrial corrosion resistance application.

يهدف البحث الحالي إلى دراسة تأثير بنية الفولاذ الكربوني على معدلات التآكل . تمت دراسة بنى مجهرية مختلفة, قسمت إلى أربعة مجاميع هي :حزم من الفرايت / البيرلايت ,المجموعة الثانية : الفرايت / البيرلايت الناعم, الفرايت / البيرلايت الخشن , المارتنزايت المراجع. تم كشف التآكل وحساب معدلاته بواسطة الفقدان بالوزن والمجهر الضوئي . بينت النتائج ان اختلاف البنى المجهرية يؤدي إلى تغير في معدلات التآكل من 0.8- 3.2 مم / سنة ومن 3.2 – 6.4 مم / سنة لكل من التآكل العام والتآكل الموضعي على التوالي. إن استقرارية التآكل تأتي من اختلاف البنى المجهرية . تمتلك حزم الفرايت / بيرلايت على مقاومة تأكل عام قليلة , بينما تمتلك بنية المارتنزايت المراجع مقاومة تأكل موضعي قليلة قيما تمتلك بنية الفرايت / البيرلايت الخشن على أفضل مقاومة تأكل موضعي مقارنة بالبني المجهرية المفحوصة الأخرى. أكدت نتائج البحث إن البنية المجهرية عامل مهم في اختيار الفولاذ الكربوني في التطبيقات الصناعية التي تتطلب مقاومة تأكل عالية .


Article
The Effect of Tool Path Strategy on Mechanical Properties of Brass (65-35) in Single Point Incremental Sheet Metal Forming (SPIF)
تأثير مسار العدة على الخواص الميكانيكية في التشكيل النقطي التزايدي لسبيكة البراص35-65

Authors: Qasim Mohammed Doos Al-Attaby قاسم محمد دوس --- Tahseen Fadhel Abaas تحسين فاضل عباس --- Aqeel Sabree Bedan عقيل صبري بدن
Journal: Journal of Engineering مجلة الهندسة ISSN: 17264073 25203339 Year: 2013 Volume: 19 Issue: 5 Pages: 629-636
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

In this paper, three tool paths strategies; iso-planar, helical and adaptive have been implemented to investigates their effect on the mechanical properties of Brass 65-35 formed by single point incremental sheet metal forming process. To response this task, a fully digital integrated system from CAD modeling to finished part (CAD/CAM) for SPIF process has been developed in this paper.The photo-micrographs shows an identical grain formation due to the plastic deformation of the incremental forming process, change in the grain shape and size was observed. It's found that the adaptive tool path play a significant role to increase the hardness of the formed specimen from (48 to 90 HV) and the grain texture of the formed specimen found as round shape, while the hardness is increased in little amount from (48 to 74 HV) in the specimen formed using helical and it’s grain texture was found as needle shape

تم في هذا البحث اعتماد ثلاثة طرق لمسار العدة في دراسة تاثيرها على الخواص الميكانيكية لسبيكة البراص (65-35) عند تشكيلها بطريقة التشكيل النقطي التزايدي وباستخدام نظام تصميم وتصنيع متكامل تم تطويره لانجاز هذا البحث, تبين من خلال الفحص المجهري للعينات المنجزة بان البنية المجهرية قد تغيرت من ناحية الشكل والحجم نتيجة التشكيل اللدن من جراء التشكيل واستنتج بان مسارات العدة لها اثر كبير في تغير الخواص من ناحية الصلادة والبنية المجهرية حيث تبين بان مسار العدة المحسن (Adaptive) رفع من صلادة النماذج المشكلة (48-90) وحافظ على الشكل الدائري للبنية المجهرية للبراص في حين ان مساري العدة (Isoplaner and Helical) قد رفعا الصلادة بمقدار اقل من الاول(48-74) بينما تغيرت البنية المجهرية للنماذج المشكلة حيث تم الحصول على بنية مجهرية طولية الشكل.

Listing 1 - 5 of 5
Sort by
Narrow your search

Resource type

article (5)


Language

English (5)


Year
From To Submit

2013 (5)