Evaluation of compressive strength for refractory casts made from different investment materials

Author: Ahmed A Al–Ali
Journal: Al-Rafidain Dental Journal مجلة الرافدين لطب الأسنان ISSN: 18121217 Year: 2007 Volume: 7 Issue: 2 Pages: 166-172
Publisher: Mosul University جامعة الموصل

Loading...
Loading...
Abstract

Aims: To compare the compressive strength of refractory casts made from investments for cobalt–chromium and investment for titanium and to study the effect of mixing fluid on compressive strength.Materials and Methods: Three types of investments were used, one for titanium and two for cobalt–chromium, each one is mixed with three types of mixing fluids; tap water, distilled water and special liquid,to produce refractory casts. Compressive strength test was carried out using compression testing machine.Results: Showed significant differences in compressive strength between the types of investments, withtitanium investment mixed with special liquid showed the highest value. There were significant differencesbetween subgroups of the same type by changing mixing fluid type. Conclusions: Refractory casts madefrom titanium investment showed significantly higher compressive strength than refractory casts madefrom Co–Cr investments, and there was a difference between the two special liquids used, and tap water inwhich it produced casts with higher compressive strength than distilled water in two out of the threeinvestment materials tested.


Article
Effect of Admixture Type on Compressive Strength and Modulus of Elasticity of Rubber- Tire - Waste Concrete
تاثير نوع المضاف على مقاومة الانضغاط ومعامل المرونة لخرسانة الاطارات المطاطية المستهلكة

Author: Khalid Battal Najim خالد بتال نجم
Journal: Anbar Journal of Engineering Sciences مجلة الأنبار للعلوم الهندسية ISSN: 19979428 Year: 2007 Volume: 1 Issue: 1 Pages: 88-103
Publisher: University of Anbar جامعة الانبار

Loading...
Loading...
Abstract

The presented work investigates the effect of addition admixtures (superplasticizer and polymer) to Chopped Worn-Out Tire concrete as a partial replacement of cement weight. Superpasticizer was addition by 4% and polymer (SBR) by 15%. The Chopped Worn-Out Tire (Ch.W.T.) addition to reference concrete with the three proportions as a Partial Replacement Ratio (PRR) of (25,25),(20,30),and (30,20) by volume of (sand and gravel) respectively. Three mixes were selected with above PRR for each type of admixture in additional to three mixes for Ch.W.T. concrete without admixtures and three reference mixes with admixtures without Ch.W.T. Thus, twelve mixes could be used in this investigation. Compressive strength and modulus of elasticity (static and dynamic) were tested. The test results indicated that the use of admixture led to significant improvement in concrete properties in general. Superplasticizer gave best results comparative with polymer, for example at 28 day the compressive strength of superplasticizer Ch.W.T. concrete Csp25,25 was 32.5 MPa, while compressive strength of polymer modified Ch.W.T. concrete CB25,25 was 28 MPa and compressive strength of Ch.W.T. concrete C25,25 was 21.2 MPa.

يدرس هذا البحث تأثير إضافة بعض أنواع المضافات (الملدن المتفوق والبوليمر) إلى خرسانة الإطارات المطاطية المستهلكة. حيث تم إضافة الملدن المتفوق بنسبة 4% والبوليمر بنسبة 15% من وزن الاسمنت. تم إضافة مفروم الإطارات المطاطية المستهلكة إلى الخلطات الخرسانية كجزء مستبدل من حجم الركام الخشن والناعم بثلاث نسب استبدال هي (25, 25), (20, 30) و (30, 20) (ركام خشن وناعم على التوالي). تم اختيار ثلاث خلطات بنسب الاستبدال أعلاه لكل مضاف إضافة إلى ثلاث خلطات بدون مضافات وثلاث خلطات مصدرية مع المضافات وبدون مفروم الإطارات وبذلك يكون مجموع الخلطات اثنا عشر خلطة. تم إجراء فحص مقاومة الانضغاط ومعامل المرونة ( الساكن والديناميكي), وقد أظهرت نتائج الفحص تحسن ملحوظ لخواص الخرسانة عند إضافة المضافات وكانت الأفضلية باستخدام الملدن المتفوق بشكل عام.فعلى سبيل المثال بعمر 28 يوم كانت مقاومة الانضغاط لخرسانة الإطارات الحاوية على الملدن المتفوق Csp25,25 32.5MPa بينما كانت مقاومة الانضغاط لخرسانة الإطارات المطورة بالبوليمر CB25, 25 هي 28 MPa وكانت مقاومة الانضغاط لخرسانة الإطارات بدون مضافات C25, 25 هي 21.2 MPa.