Studying the Effect of Volume Fraction of Glass Fiberson the Thermal Conductivity of the Polymer Composite Materials
دراسة تأثير الكسرالحجمي لألياف الزجاج على الموصلية الحراريةللمواد المتراكبة البوليمرية

Author: Mohammed Sellab Hamza محمد صلاب حمزة
Journal: Al-Khwarizmi Engineering Journal مجلة الخوارزمي الهندسية ISSN: 18181171 23120789 Year: 2008 Volume: 4 Issue: 3 Pages: 85-97
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

In this study the effect of fiber volume fraction of the glass fiber on the thermal conductivity of the polymer composite material was studied. Different fiber volume fraction of glass fibers were used (3%, 6%, 9%, 12%, and 15%). Specimens were made from polyester which reinforced with glass fibers .The fibers had two arrangements according to the direction of the thermal flow. In the first arrangement the fibers were parallel to the direction of the thermal flow, while the second arrangement was perpendicular; Lee's disk method was used for testing the specimens. The experimental results proved that the values of the thermal conductivity of the specimens was higher when the fibers arranged in parallel direction than that when the fibers arranged in the perpendicular direction. The percentage of increasing of experimental thermal conductivity was 96.91% for parallel arrangement and 13.33% for perpendicular arrangement comparison with its original value before the using of glass fibers.
Also the experimental results indicated that the thermal conductivity increases with the increasing of the fiber volume fraction. Minimum value was (0.172 W/m.C) for perpendicular arrangement at fiber volume fraction 3% and maximum value was (0.327 W/m.C) for parallel arrangement at fiber volume fraction 15%.

تم في هذا البحث دراسة تأثير الكسر الحجمي لالياف الزجاج وبنسب مختلفة (15%, 12%, 9%, 6%, 3% ) على التوصيلة الحرارية للمادة المتراكبة. حيث صنعت العينات من مادة البولي أستر غير المشبع المقواة بالياف الزجاج. العينات صنعت في مجموعتين المجموعة الاولى كانت فيها الياف الزجاج مرتبة بشكل موازي للانسياب الحراري، اما المجموعة الثانية نضمت بترتيب الالياف بشكل عمودي على الانسياب الحراري. استخدمت طريقة قرص لي (Leeś disk ) في فحص العينات. اثبتت النتائج العملية ان الترتيب الموازي للالياف يعطي موصلية حرارية اعلى من الترتيب العمودي وان الموصلية الحرارية للمادة المتراكبة تزداد مع زيادة الكسر الحجمي للالياف. حيث كان مقدار الزيادةفي الموصلية الحرارية بسبب التقوية بالالياف هو 96.91% للترتيب الموازي و 13.33% للترتيب العمودي كذلك اثبت النتائج العملية ان اقل قيمة للموصلية الحرارية كانت (0.172w/m.C) للترتيب العمودي عند الكسر الحجمي (Vf=3%) اما اعلى قيمة كانت (0.327W/m.C) للترتيب الموازي عند كسر حجمي (Vf = 15%).


Article
EFFECT OF JUTE FIBERS ON THE MECHANICAL PROPERTIES OF EPOXY RESIN
تأثير الياف الجوت على الخواص الميكانيكية لراتنج الايبوكسي

Loading...
Loading...
Abstract

Epoxy resins are widely used in industry by virtue of combinations of favorable characteristics including good mechanical and physical properties, ease of processing and low cost. However, these resins suffer from the disadvantage of brittleness, which limits their use in many applications.In this work, polymeric composites were prepared from epoxy resin reinforced Bi-directionally (0o - 90o) by jute and glass fibers singly and in combination as a hybrid.A comparison is made between the elastic modulus, material toughness and fracture toughness of the composites with those of un-reinforced epoxy to find out the effect of reinforcement on the composites at varying temperatures (0, 25, 40, and 60 Co). Volume fraction for each reinforcement fibers (glass or jute) was 30% but for hybrid composite was (15% glass fibers and 15% jute fibers). The results show that the jute- reinforced laminates have much better properties than the resin alone; but the properties are inferior to those of glass reinforced epoxy. The most appropriate role for the jute fibers is, to use them as filler fibers in combination with glass fibers to get moderate and acceptable mechanical properties during applications. The improvements in mechanical properties (elasticity modulus, material toughness, and fracture toughness) are 623%, 565%, and 593% respectively in comparison with un-reinforced epoxy samples.

تستخدم راتنجات الايبوكسي بصورة واسعة في الصناعة وذلك لامتلاكها العديد من المزايا المرغوبة والتي تشمل الخواص الميكانيكية والفيزياوية الجيدة وسهولة التشكيل وقلة الكلفة . لكن إحدى مساوئ هذه الراتنجات هي صفة التقصف التي تحدد من استعمالها في العديد من الاستخدامات.تم في هذا البحث تحضير مواد مركبة بوليمرية من راتنج الايبوكسي مع ألياف تقوية ثنائية الاتجاه(0o -90o ) شملت ألياف الجوت والزجاج منفردة وسوية لتكوين ماده مركبة هجينة.تم مقارنة معامل المرونة ومتانة المادة ومتانة الكسر للمواد المركبة مع راتنج الايبوكسي غير المقوى وذلك لملاحظة تأثير عملية التقوية على خواص المواد المركبة عند درجات حرارية مختلفة هي ( 0, 25, 40, 60) مْ . وقد كانت نسبة الكسر ألحجمي لألياف التقوية للنماذج المقواة بألياف الزجاج والمقواة بألياف الجوت هي( 30%) و( 15% ألياف زجاج مع 15%ألياف جوت) للمواد المركبة الهجينة. أظهرت النتائج إن الخواص الميكانيكية للايبوكسي المقوى بألياف الجوت أعلى بكثير من الايبوكسي غير المقوى . ولكنه في نفس الوقت أقل من الايبوكسي المقوى بألياف الزجاج. إن الدور الأكثر ملائمة لألياف الجوت , استخدامه كألياف مالئة سوية مع ألياف الزجاج لتحقيق خواص ميكانيكية معتدلة ومقبولة عند الاستخدام , حيث كان مقدار التحسن في الخواص الميكانيكية ( معامل المرونة , متانة المادة, ومتانة الكسر هي 623%, 565%, 593% على التوالي مقارنة بنماذج الايبوكسي غير المقواة ).