Effect of Wax Burn-Out Heating Temperature on The Compressive Strength of Casting Dental Alloy Investment

Author: Lamia T Rejab
Journal: Al-Rafidain Dental Journal مجلة الرافدين لطب الأسنان ISSN: 18121217 Year: 2008 Volume: 8 Issue: 2 Pages: 197-204
Publisher: Mosul University جامعة الموصل

Loading...
Loading...
Abstract

Aims: To evaluate the effect of the burn-out heating on the compressive strength of investment materials.Materials and Methods: Three commercial investment materials were used in this study. Seventy two cylindrical shape specimens were prepared to evaluate the compressive strength of the investment materials at room temperature (cold strength) and at two different burn-out heating temperatures : 700 oC and 1000 oC (hot strength). Three groups were prepared according to tested investment materials, The specimens were then subdivided into three subgroups according to burn-out heating temperatures,eight specimens for each subgroup. The compressive strength (kg /cm2) was evaluated by using Instron testing machine. Mean values were compared statistically with one way analysis of variance (ANOVA),Duncan , s multiple range test and t-test to determine the significant difference among the tested groups at (p<0.05) level of significance .Results: The results showed that there is a significant difference of the means value of the compressive strength among the three tested investment materials. The compressivestrength value significantly decreased with increasing burn-out heating temperature. Conclusion:The result of this study showed that the increase of burn-out heating had a significant decrease the compressive strength of the investment materials, and cold compressive strength gives an indicationof the hot strength .


Article
Using of Waste Materials for Production of High Performance Concrete

Authors: Mohammed Abdulla Baker --- Nadia Salim Ismael
Journal: AL-TAQANI مجلة التقني ISSN: 1818653X Year: 2008 Volume: 21 Issue: 4 Pages: 182-188
Publisher: Foundation of technical education هيئة التعليم التقني

Loading...
Loading...
Abstract

High performance concrete with compressive strength (40 – 120) MPa and other perfect properties is a new type of cementitious materials. The research deals with the use of industrial by-product waste material as partial replacement of sand to produce high performance concrete with compressive strength higher than 40 MPa. The result indicate that partial replacement of sand by industrial waste material (Brass) in addition of use of admixtures (Superplasticizer) and powder of pure silica gives high strength in comparative with reference mix.

الخرسانة عالية الاداء التي لها مقاومة انضغاط بين (40-120) ميكاباسكال بالاضافة الى خصائص اخرى تعتبر احد انواع الخرسانة الحديثة.يتضمن البحث استخدام بعض المخلفات الصناعية كاستبدال جزئي للركام الناعم ( الرمل) لانتاج خرسانة عالية الاداء ذات مقاومة انضغاط اكثر من (40) ميكاباسكال . النتائج المختبرية توضح ان الاستبدال الجزئي للرمل بمادة البراص (Brass) الذي يعتبر احد الفضلات الصناعية والتي تتخلف بكميات كبيرة بالاضافة الى استخدام عامل مقلل للماء (Superplasticizer) والسليكا النقية تعطي مقاومة انضغاط عالية مقارنة بالخلط المرجعية .


Article
EFFECT OF MAGNETIZED WATER ON THE PROPERTIES OF CEMENT MORTARS AT THE EARLIER AGES
تأثير الماء الممغنط على خواص المونة السمنتية في الأعمار المبكرة

Author: Adnan Flayih Hassan
Journal: Al-Qadisiyah Journal for Engineering Sciences مجلة القادسية للعلوم الهندسية ISSN: 19984456 Year: 2008 Volume: 1 Issue: 1 Pages: 95-108
Publisher: Al-Qadisiyah University جامعة القادسية

Loading...
Loading...
Abstract

This study had been conducted to investigate the influence of magnetized water on the properties of cement mortars such as initial and final setting time, consistency and compressive strength with various water/cement ratios at the ages of 1 and 7 day. Results of (50) specimens with different shapes had been adopted, which represented mortars specimens having compressive strength ranging from (5.5) to (32.5) MPa, initial setting time ranging from (4) to ( 32) minutes and final setting time ranging from (303) to (546) minutes, by using two types of mixing water , first one is tap water , and the other is magnetized water.The results showed that the use of magnetized water in producing cement mortars lead to increase in the compressive strength and decreasing in the initial and final setting time with compare to use of tap water. Results also showed that the optimum water/cement ratio give best compressive strength under the conditions of this study was (0.45).

أجريت هذه الدراسة للتحري عن تأثير استخدام الماء الممغنط على خواص المونة السمنتية, كزمن التجمد الابتدائي و النهائي و القوام و مقاومة الانضغاط باستخدام نسب ( ماء/ سمنت ) مختلفة , مقاومة الانضغاط تم فحصها بعمر 1 و 7 يوم . تم اعتماد نتائج 50 نموذج ذات مقاومة انضغاط تـــــراوحت بين ( 5.5) و ( 32.5) MPa , زمن تجمد ابتدائي تراوح بين (4) و ( 32) دقيقة و زمن تجمد نهائي تـراوح بين ( 303) و (546) دقيقة وباستخدام نوعين من ماء الخلط , الأول هو ماء الحنفية و الثاني هو الماء الممغنط. النتائج بينت إن استخدام الماء الممغنط في إنتاج المونة السمنتية يؤدي إلى زيادة مقاومة الانضغاط و نقصان في زمن التجمد الابتدائي و النهائي بالمقارنة مع استخدام ماء الحنفية . أما أفضل نسبة ( ماء/ سمنت ) أعطت أعلى مقاومة انضغاط في ظل ظروف هذه الدراسة كانت (0.45).


Article
Effect of Coarse Aggregate Characteristics on Drying Shrinkage of Concrete

Author: Tareq Salih Al-Attar
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2008 Volume: 26 Issue: 2 Pages: 146-153
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Concrete is a composite material, consisting, mainly, of three phases: coarseaggregate, cement mortar, and the interface zone between them. The characteristicsof the interface zone largely govern the bond between cement paste or mortar andaggregate. The restraining effect of aggregate to drying shrinkage strain dependsmuch on the bond between aggregate and cement paste.In this paper, it is aimed to investigate the effect of coarse aggregatecharacteristics, that affect bond strength, such as; type, shape, surface texture, andmoisture content, on drying shrinkage. Four types of coarse aggregate were used.Three of them were normal-weight, while the fourth was a light-weight one. Eachtype of coarse aggregate was used in two moisture conditions, dry and saturated.The testing program extended to 150-days age and comprised; length change,modulus of elasticity, compressive and splitting tensile strength of concrete.It is concluded that using saturated coarse aggregate always yields highershrinkage strain than dry aggregate. The percentage increase seems to be affectedby the aggregate water absorption. At early ages, After 28 days, there is largedifferences in relative shrinkage for different mixes. Later than 28 days, thevariation in ratios settled to approximately fixed values

الخرسانة مادة مركبة ومكونة بشكل رئيسي من ثلاثة أطوار: الركام الخشن ومونة الاسمنتومنطقة السطوح البينية. ان خواص منطقة السطوح البينية تتحكم بشكل كبير في قوى الارتباطبين عجينة الاسمنت (أو المونة) وبين الركام. كما أن الدور المقيد الذي يقوم به الركام تجاهانفعالات انكماش الجفاف للخرسانة يعتمد كثيرأً على قوى الارتباط التي تتطور في منطقةالسطوح البينية.في هذا البحث تم التحري عن تأثير خواص الركام الخشن (مثل:النوع والشكل ونسجة السطحومحتوى الرطوبة)على معدل ومقدار الانكماش للخرسانة عند الجفاف. تم اختيار هذه الخواص لما لها من علاقة قوية بقوى الارتباط بين العجينة والركام. تضمن البحث دراسة تاثير ثلاثةانواع من الركام الطبيعي الوزن ونوعاً رابعاً كان خفيف الوزن. الفحوصات التي اجريت علىالخرسانة كانت: التغير الطولي، معامل المرونة، مقاومة الانضغاط ومقاومة الشد بالانشطاروامتد البرنامج العملي الى عمر ١٥٠ يوم.الخلطات الخرسانية المنتجة بالركام المشبع أظهرت دائماً انكماشاً اكبر من خلطات الركام الجافوهذه الزيادة في الانكماش ارتبطت بقابلية الركام لامتصاص الماء. وعند اعتبار الانكماش النسبيللخلطات تبين أنه في الاعمار المبكرة يتغاير هذا الانكماش كثيراً في حين يستقر عند نسب ثابتةفي الاعمار المتأخرة.