Effect of Nanocomposites TiO2 addition on the Dielectric Properties of Epoxy resin
تأثير متراكبات النانو بإضافة TiO2¬ على خواص العزل لراتنج الأيبوكسي

Loading...
Loading...
Abstract

Sheets of Epoxy (EP) resin with addition of TiO2 of grain size (1.5μm, and 50nm) and weight percentage (1%, 3%, and 5%) were prepared. Discs of 20mm diameter and 3mm thickness were cut for dielectric measurements. Dielectric properties (dielectric constant, dispassion factor and electrical conductivity) over the frequency range 102 -106 Hz were measured.Comparison was made between the effect of micro and nano particles of TiO2 on the dielectric properties of EP composites with different weight percentage. Epoxy composites with micro sized particles of TiO2 were observed to have the better values of dielectric properties.

في هذا البحث تم تحضير صفائح راتنج الايبوكسي Ep باضافة ثنائي اوكسيد التيتانيوم TiO2 بمقاس حبيبي ((1.5μm, 50nm وبنسب وزنية مئوية مختلفة (1%, 3%, 5%). تم قطع اقراص بقطر 20mm وسمك 3mm من المادة المحضرة ولذلك لغرض القياسات العزلية. الخواص العزلية (ثابت العزل وعامل الفقد والتوصيلية الكهربائية) اجرت القياسات لمدى من الترددات بين 102 -106 Hz.تم كذلك مقارنة تأثير الجسيمات TiO2 من ابعاد النانومتر والمايكرمتر على الخصائص العزلية من متراكبات الايبوكسي وبنسب وزنية مختلفة. وتبين من النتائج ان الجسيمات TiO2 بابعاد المايكرو متر ذات خصائص عزلية افضل


Article
Study of Some Mechanical Properties for Polymeric Composite Material Reinforced by Fibers
دراسة بعض الخواص الميكانيكية لمادة مركبة بوليميرية مقواة بالألياف

Author: Ali I.Al-Mosawi علي إبراهيم الموسوي
Journal: Al-Qadisiyah Journal for Engineering Sciences مجلة القادسية للعلوم الهندسية ISSN: 19984456 Year: 2009 Volume: 2 Issue: 1 Pages: a14-a24
Publisher: Al-Qadisiyah University جامعة القادسية

Loading...
Loading...
Abstract

The objective of this research is to study the effect of changing the reinforcement percentage by fibers on Mechanical properties, for composite material consists of conbextra epoxy (EP-10) resin reinforced by biaxial woven roving kevlar fibers (°45-°0) with density (340 g/cm3) which included impact strength , tensile strength , flexural strength and hardness Where the Mechanical properties were extracted for phenol formaldehyde resin before reinforcement by fibers, then we reinforced the resin by different weight percentage from Kevlar fibers(20%,40%,60%) and studied the effect on the above mechanical properties as illustrated in the diagrams .

إن الهدف من هذا البحث هو دراسة تأثير تغيير نسبة التقوية بالألياف على الخواص الميكانيكية للمادة المركبة المكونة من راتنج الإيبوكسي نوع كونبكسترا (EP-10) المقوى بألياف كيفلار بشكل ظفائر محاكة ثنائية الإتجاه (°45-°0) ذات كثافة سطحية (340 g/cm3) وقد شملت هذه الخواص كل من مقاومة الصدمة ، مقاومة الشد ، مقاومة الإنثناء ، والصلادة حيث تم في البداية إستخراج الخواص الميكانيكية لراتنج الفينول فورمالدهيد قبل التقوية بالألياف بعدها تم تدعيم الراتنج بنسب وزنية مختلفة من ألياف كيفلار (%60, %40, %20) و دراسة تأثير ذلك على الخواص المذكورة وكما موضح في المخططات البيانية