Article
Hard Chromium Electroplating and Improvement the Properties by the Thermo Chemical Treatments (Solid Carburizing) of Low Carbon Steel
الطلاء الكهربائي بالكروم الصلد وتحسين الخواص بالمعاملات الحرارية الكيمياوية (الكربنه الصلبة) لفولاذ منخفض الكاربون

Authors: Ahmed Salloum Abbas أحمد سلوم عباس --- Amin Dway Thamir أمين دواي ثامر --- Muna Khedier Abbas منى خضير عباس
Journal: Al-Khwarizmi Engineering Journal مجلة الخوارزمي الهندسية ISSN: 18181171 23120789 Year: 2009 Volume: 5 Issue: 4 Pages: 99-114
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

In this research the hard chromium electroplating process, which is one of the common methods of overlay coating was used, by using chromium acid as source of chromium and sulphuric acid as catalyst since the ratio between chromic acid and sulphuric acid is (100 : 1) consequently. Plating process was made by applying current of density (40 Amp / dm2) and the range of solution temperature was (50 – 55oC) with different time periods (1-5 hr). A low carbon steel type (Ck15) was used as substrate for hard chromium electroplating. Solid carburization was carried out for hard chromium plating specimen at temperature (925oC) with time duration (2 hr) to be followed with quenching and tempering. The phase analysis was conducted by using X– ray diffraction. The examination results show that the chromium carbides in plating layer were (Cr23C6, Cr7C3). The microhardness of hard chromium plating specimen was measured, and the results show that the high hardness was about (907HV). After solid carburization the hardness values increase and the results show that the higher hardness for chromium plating layer on low carbon steel surface was (1276 HV). Wear apparatus type (Pin on Disc) was used to study dry sliding wear properties of low carbon steel (As received) and hard chromium plating specimens and solid carburized. The effect of applied normal load on wear rate was studied with weighting method using five normal loads (5, 10, 15, 20, 25 N) at constant sliding speed (2.198 m / sec). The results reveal that the wear rate increases with the increasing of applied normal load. A good improvement in wear resistance was noticed for hard chromium plating specimens as compared with substrate specimen. It was also seen that, the improvement in wear resistance was (94%) as compared with substrate metal when carburizing treatment is carried out on hard chromium plating specimens.

في هذا البحث استخدمت طريقة الطلاء الكهربائي بالكروم الصلد، وهي إحدى طرائق الطلاء بتكوين غطاء على السطح، باستخدام حامض الكروميك كمصدر الكروم وكذلك حامض الكبريتيك كعامل محفز اذ أن نسبة حامض الكروميك إلى حامض الكبريتيك كانت (1:100) على التوالي. تمت عملية الطلاء بتسليط كثافة تيار مقدارها (40 Amp / dm2) ودرجة حرارة محلول الطلاء 55 – 50)ºC) ولفترات زمنية مختلفة (1 – 5 hr). استخدم الفولاذ منخفض الكاربون نوع ((CK15 كسبيكة أساس (Substrate) لغرض طلاءها بالكروم الصلد. تم أجراء المعاملة الحرارية الكيمياوية ( الكربنة الصلبة) للعينات المطلية بالكروم الصلد عند درجة حرارة (925ºC) ولفترة زمنية (2hr) للحصول على طبقة من كاربيدات الكروم. إذ تم تحديد الأطوار البلورية المكونة لطبقة الطلاء بعد أجراء الكربنة الصلبة والمتبوعة بالتقسية والمراجعة بجهاز حيود الأشعة السينية فقد تم الحصول على كاربيدات الكروم من نوع (Cr23C6, Cr7C3). وتم قياس الصلادة الدقيقة للعينات المطلية بالكروم اذ تم الحصول عل صلادة عالية تقدر (907HV). أما بعد أجراء الكربنة الصلبة لعينات الطلاء فقد ارتفعت قيم الصلادة وبشكل ملحوظ حيث أظهرت النتائج أن أعلى صلادة كانت لطبقة طلاء الكروم على سطح الفولاذ منخفض الكاربون كانت (1276HV) ويعزى سبب ارتفاع قيم الصلادة إلى وجود كاربيدات الكروم ضمن طبقة الطلاء.استخدم جهازالبلى نوع المسمار – القرص (Pin on Disc) لدراسة خواص البلى الانزلاقي الجاف لعينات الفولاذ منخفض الكاربون (كما استلمت) والعينات المطلية بالكروم الصلد والمكربنة كربنة صلبة. ولقد تم دراسة تأثير الحمل المسلط على معدل البلى بطريقة الفقدان بالوزن باستخدام أحمال عمودية مختلفة هي 25 , 20 , 15 , 10 , 5) N) وسرعة انزلاقية (Sliding speed) (2.198 m / sec). وقد أظهرت النتائج ان معدل البلى يزداد مع زيادة الحمل المسلط للعينات المطلية بالكروم, وأن أعلى مقاومة للبلى تم الحصول عليها بعد أجراء الكربنة الصلبة للعينات المطلية بالكروم حيث لوحظ التحسن الكبير في مقاومة البلى وبما يعادل (%94 ) مقارنة بالفولاذ منخفض الكاربون بحالته المستلمه.


Article
Mass Transfer Coefficient During Cathodic Protectionof Low Carbon Steel in Seawater
معامل انتقال المادة خلال الحماية الكاثودية لحديد واطئ الكاربون في مياه البحر

Authors: Ameel Mohammed Rahman أميل محمد رحمن --- Anees Abdullah Khadom أنيس عبد الله كاظم --- Khalid W. Hameed خالد وليد حميد
Journal: Al-Khwarizmi Engineering Journal مجلة الخوارزمي الهندسية ISSN: 18181171 23120789 Year: 2009 Volume: 5 Issue: 1 Pages: 20-32
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

The aim of this research is to calculate mass transfer coefficient, kd, during cathodic protection of low carbon steel in neutral seawater (3.5% W/V NaCl in distilled water with pH = 7). Two types of cathodic protection were used:
First: Sacrificial anode cathodic protection (SACP) were a pipeline of steel carrying seawater using zinc as a sacrificial anode and with variable temperatures ranged (0 – 45oC) and volumetric flow rate ranged (5 – 900 lit/hr). It was found that the kd increases with increasing temperature and volumetric flow rate of seawater, where kd ranged (0.24×10-6 – 41.6×10-6 m/s).
Second: Impressed current cathodic protection (ICCP) technique adopting a rotating vertical steel cylinder in seawater with variable temperatures ranged (0 – 45oC) and rotating velocity ranged (0 – 400 rpm). It was found that the kd increases with increasing temperature and rotating velocity, where kd ranged (7.25×10-6 – 36.82×10-6 m/s).

الهدف من البحث هو حساب معامل انتقال المادة, kd , خلال الحماية الكاثودية لحديد واطئ الكاربون في مياه البحر المتعادل (%3.5 NaCl وزنحجم في الماء المقطر و دالة حامضية = 7). تم استخدام طريقتين من الحماية الكاثودية: الاولى: الحماية الكاثودية بطريقة أنود التضحية لأنبوب الحديد حاملاًً مياه البحر بأستخدام قطب الخارصين كأنود تضحية عند المتغيرات الاتية: درجة الحرارة بمدى (0 – 45 هم) ومعدل جريان حجمي بمدى (5 – 900 لترساعة). لقد وجد أن kd يزداد بزيادة درجة الحرارة وزيادة معدل الجريان الحجمي او رقم رينولد , حيث تراوحت قيمة kd .(0.24×10-6 – 41.6×10-6 m/s)الثانية: الحماية الكاثودية بطريقة التيارالمسلط لأسطوانة حديدية مدورة عمودياً في مياه البحر المتعادل عند المتغيرات الاتية: درجة الحرارة بمدى (0 – 45 هم) وسرعة تدوير بمدى (0 – 400 دورةدقيقة). لقد وجد أن kd يزداد بزيادة درجة الحرارة وزيادة سرعة تدوير الاسطوانة او رقم رينولد, حيث تراوحت قيمة kd .(7.25×10-6 – 36.82×10-6 m/s)


Article
Aِ studing The Effect of Chemical Composition of Workpiece on Built Up Edge Formation And Surface Roughness
دراسة تأثير التركيب الكيميائي للمشغولة على تكون الحد القاطع الناشىء والخشونة السطحية

Author: Saad kariem shather
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2009 Volume: 27 Issue: 10 Pages: 2061-2071
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

the phenomena built-up edge was the unwanted rough edge on cutting tool that is created by workpiece material welding onto the tool during cutting , occurs at the chip/tool interface when multiple materials are machined at low cutting speeds under high compressive stresses, this study involve relation between the chemical composition of workpiece and the built-up edge ( B.U.E ) formation which is generated on cutting tool during machining at dfferent types of low carbon steelusing turning machine , experments prove that increasing percentage of carbon on workpiece causes reduction in weight of cutting tool from ( 14.532g to 13.823g ) at cutting speed 40 m/min and 0.10% and 014% carbon also to 12.672g at 0.20% carbon because built – up edge was disappear and surface roughness was improving from the value ( 5.43μm ) at 0.10% carbon and to ( 3.362 μm ) at 0.14% carbon and to (3.543μm) at 0.20% carbon .

أن ظاهرة الحد الناشىء التي تؤدي الى خشونة غير مرغوب فيها للعدة القاطعة والتي تنتج من التصاق أو التحام معدن المشغولة أثناء القطع وتحدث عند التصاق النحاتة بالعدة أثناء تشغيل معادن مختلفة بأستخدام سرع قطع واطئة وتحت أجهادات ضغطية عالية . لقد تضمنت هذه الدراسة علاقة مابين التركيب الكيميائي للمشغولة والحد الناشىء الذي ينمو على سطح العدة القاطعة من خلال التشغيل بأستخدام ماكينة الخراطة مع عدة قطع وتشغيل أنواع مختلفة من الفولاذ الواطىء الكاربون ذات التركيز الكاربوني المختلف , التجارب أثبتت أن زيادة نسبة الكاربون في المشغولة تؤدي الى نقصان في الوزن للعدة القاطعة من ( 14.532 غم ) الى( 13.823 غم ) عند سرعة قطع 40 م/ دقيقة ) ونسبة كاربون ( 0.10 % وكذلك 0.14 % ) بسبب أختفاء الحد القاطع )الناشىء والذي يؤدي الى تحسن خشونة السطح من ( 5.43 مايكرون ) عند نسبةكاربون الى 0.10 % الى 3.362 مايكرون عند % 0.14 والى( 3.543 مايكرون )عند % 0.20 كاربون


Article
Corrosion Inhibition of Carbon steel on Hydrochloric acid Using Zizyphus Spina – Chritisi Extract
دراسة الفعل التثبيطي لمستخلص أوراق السدر على الفولاذ الكاربوني في حامض الهيدروكلوريك

Loading...
Loading...
Abstract

Naturally occurring substances are increasingly being tried to used as corrosion inhibitors of metals in acid cleaning processes to replace some toxic and expensive chemicals currently in use. The corrosion inhibition of carbon steel in hydrochloric acid by Zizyphus Spina – Chritis leaves extract was studied using weight loss techniques. Maximum inhibition efficiency and surface coverage were obtained at an optimum concentration. However, an increase in temperature lead to decreased in the inhibition efficiency at the temperature studied. Optimum inhibition efficiency for carbon steel in the presence of Zizyphus Spina – Chritis leaves extract was 99.5%, 75% and 66% at 1%,1%and 2% concentration of the inhibitor at 25oC, 35oC and 45oC respectively. The phenomenon of physical adsorption has been proposed from the activation energy values (55.66KJmol-1). The surface coverage (θ) data augment the above observation and the inhibition is attributed to the physical adsorption of the chemical components of the additive on the surface of the carbon steel. Inexpensive environmentally safe inhibitor formulations indicate have been obtained.

جرت محاولات عديدة لأستخدم المواد المستخلصة من المواد الطبيعية كمانعات تآكل للعديد من المعادن في عمليات التنظيف بالحامض وذلك لاستبدال بعض المواد الكيماوية الغالية والسامة والتي تستخدم لهذا الغرض. لذا تم في هذا البحث دراسة استخدام مستخلص أوراق السدر في تثبيط تآكل الفولاذ الكاربوني في محلول 0.5M من حامض الهيدروكلوريك وباستخدام طريقة الفقدان بالوزن.تم تحديد أقصى كفاءة تثبيط واكبر جزء من المعدن مغطى بالمثبط حيث بلغت أقصى كفاءة تثبيط 99.5% و 75% و 66% وذلك عند تراكيز من المثبط 1% و 1% و 2% وعند درجات حرارة 25م و 35م و 45م على التوالي. حيث بينت النتائج بأن هذا المستخلص قادر على إيقاف ذوبان الفولاذ الكاربوني وبمدى واسع يعتمد على تركيز المضاف وكذلك زمن التعرض للحامض.. كما أكدت حسابات مساحة السطح المغطى (θ) الاستنتاج السابق. وقد بينت النتائج المستحصلة بأن عملية التثبيط تتم من خلال الأمتزاز الفيزيائي للمكونات الكيميائية للمضاف على سطح الفولاذ الكاربوني.


Article
An Investigation of the Inhibition of the Oxygen Reduction Reaction at a Rotating Cylinder Electrode under Isothermal and Controlled Conditions of Heat and Mass Transfer
دراسة تثبيط تفاعل اختزال الاوكسجين على سطح القطب الاسطواني الدوار عند ظروف انتقال الحرارة والكتلة

Authors: Shatha. A. Sameh --- Sadiq. H. Alwash
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2009 Volume: 27 Issue: 5 Pages: 930-941
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

The inhibition of the oxygen reduction reaction on a carbon steel rotatingcylinder electrode in naturally aerated 600 ppm Cl- solution was studied using anoptimum inhibitor blend, i.e., Sodium Nitrite (SN): Sodium Hexametaphosphate(SHMP) = 500:100 obtained via a weight loss technique. Potentiostatic technique, then,was applied at different bulk temperatures and various flow rates using un-inhibited andinhibited solutions under isothermal and controlled conditions of heat transfer.In an un-inhibited solution and under isothermal conditions, with limiting conditions ofconcentration polarization, the limiting current density of oxygen reduction reaction isflow and temperature dependent. The charge transfer of the oxygen reduction reaction isa 4 electron process in the range of bulk temperature employed from 303 to 323 K.Under heat transfer conditions, the charge transfer is still 4 electron process up to 336 Kinterfacial temperature, above which the contribution of the 2 electron process appeared.Moreover, the limiting current density values of the oxygen reduction reaction ininhibited solutions is much lower than those under identical conditions in un-inhibitedsolutions. This confirms the inhibition of the cathodic reaction, i.e., the oxygenreduction reaction under isothermal and heat transfer conditions, due to SHMP.

تم دراسة الحد من تفاعل اختزال الاوكسجين لقطب اسطواني دوار من الفولاذ الكاربوني في ماء ملحي متعادل يحتوي على 600 جزء بالمليون من ايونات الكلوريد، بأستخدام تركيز (SHMP) و فوس فات الصوديوم السداسية (SN) امثل لخليط مثبط التآكل من نتريت الصوديوم 100:500 تم التوصل اليها بطريقة فقدان الوزن. =SHMP: SN بنسبة اجريت تجارب الاستقطاب بالمجهاد الساكن في ظروف ثبات درجة الحرارة بأستخدام محلول خال من خليط مثبط التآكل في درجات حرارة مختلفة للمحلول و معدلات جريان اضطرابي مختلفة لك ل درجة حرار ة. ثم اجريت تجارب مماثلة تحت ظروف انتقال حرارة مسيطر عليه من سطح المعدن الى المحلول . علاوة على ذلك، اجريت تجارب مماثلة لاعلاه بوجود مثبط التآكل موضوع البحث.اظهرت النتائج، عند ثبوت درجة حرارة المحلول الخال من مثبط التاكل و تحت ظروف الاستقطاب ال تركيزي، زيادة كثافة التيار المحدد لتفاعل اختزال الاوكسجين مع زيادة درجة حرارة المحلول و كذلك مع زيادة معدل الجريان . ان تفاعل اختزال الاوكسجين في مدى درجات حرارة بين 303 و 323 كلفن هو عملية استهلاك 4 الكترونات . اما تحت ظروف انتقال الحرارة، فان تفاعل اختزال الاوكسجين هو عملية استهلاك 4 الكترونات و لحد درجة حرارة سطح المعدن 336 كلفن اما في درجات حرارة اعلى من 336 كلفن لسطح المعدن فتظهر مشاركة عملية استهلاك 2 الكترون مع عملية استهلاك 4 الكترونات.كما بينت النتائج ان اقيام كثافة التيار المحدد لتفاعل اختزال الاوك سجين بوجود مثبط التأكل هي اقل بكثير من نظيراتها في محلول خال من مثبط التاكل، و هذا يؤكد الحد من التفاعل الكاثودي، اي تفاعل اختزال الاوكسجين تحت ظروف ثبات درجة الحرارة و كذلك ظروف انتقال الحرارة، بسبب تأثير فوسفات الصوديوم السداسية.


Article
Effect Of Mixing Speed And Solution Temperature On Cathodic Protection Current Density Of Carbon Steel Using Magnesium As Sacrificial Anode
تأثيرسرعة الخلط ودرجة حرارة المحلول على قيمة كثافة تيار الحماية الكاثودية لحديد الفولاذ بأستخدام المغنيسيوم كأنود مضحي

Author: K. T. Rashid
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2009 Volume: 27 Issue: 8 Pages: 1640-1653
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

In present work, The corrosion behavior of carbon steel in sodium chloride (NaCl)solution with different concentrations was studied .Effects of mixing speed (0 to 2220) r.p.mand the solution temperature (25, 35, 45, 55, 65)0c on cathodic protection current density werestudied, that would provide a full cathodic protection for tube metal specimen of carbon steelimmersed in 3.5% NaCl solution by sacrificial anode method using magnesium (Mg) assacrificial anode.The results show that the concentration of sodium chloride in the electrolyte is animportant factor in determining corrosion rate, 3.5 % concentration of sodium chloride givesmaximum rate of corrosion. In addition, it has been found that the cathodic protection currentdensity showed sharp increasing with mixing speed. The results have showed also that thecathodic protection current density increased with increasing the solution temperature andshifts the protection potential to high negative value.

يتضمن البحث دراسة سلوكية تاكل حديد الفولاذ في وسط ملحي بتراكيز مختلفة لكلوريد الصوديوم .أاثبتت النتائج أن معدل التاكل يزداد بازد ياد تركيز الملح(كلوريد الصوديوم) الى أن يصل الى حالة الأشباعوذلك عند تركيز يساوي تقريبا ( 3.5 % ) ثم يبدأ بالتناقص وذلك بسبب تضاؤل كمية الأوكسجين المذاب فيالمحلول ومن ثم دراسة تأثيرسرعة الخلط (صفر- 2220 )دورة/دقيقة و درجة حرار ة0م ، ع لى قيمة كثافة تيار الحماية الكاثودية (بطريقةالأنودالمضحي ) الذي ( المحلول( 25 و 35 و 45 و 55 و 65يعطي حماية كاثودية كاملة لعينة انبوب معدني من حديد الفولاذ مغمور بمحلول كلوريد الصوديوم بتركيز%3.5 وذلك باستخدام المغنيسيوم كأنود مضحي , ,أوضحت النتائج أن كثافة تيار الحماية يزداد زيادة حاد ةعند الانتقال من الحالة الساكنة الى حالة الخلط ويستمر بالزيادة عند الاستمرار بزيادة سرعة الخلط(المزج),وتبين زيادة تيار الحماية الكاثودية عند زيادة درجة الحرارة ومن الواضح ان تاثير سرعة المزج كاناوضح من تاثير درجة الحرارة ,وتمت دراسة تاثير درجة الحرارة على الفولتية المجهزة من قبل انودالمغنيسيوم,حيث تبين ان زيادة درجة الحرارة تؤدي الى زيادة الفولتية المجهزة من قبل انود المغنيسيومبالاتجاه السالب.

Listing 1 - 6 of 6
Sort by
Narrow your search

Resource type

article (6)


Language

English (4)

Arabic and English (2)


Year
From To Submit

2009 (6)