Effect of Heat Treatment on Fatigue Life of Aluminum Alloys 2024 And 7075
تأثير المعاملة الحرارية على عمر الكلال في سبائك الالمنيوم 2024 و 7075

Author: Ahmed. N. Al-Khazraji
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2010 Volume: 28 Issue: 22 Pages: 6469-6481
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

This research studies the effect of heat treatment (precipitation hardening) on fatigue life of two aluminum alloys (2024) and (7075). The alloy (2024) is hardening by natural aging, while the artificial aging is used to hardening the alloy (7075). Mechanical tests are performed to determine the mechanical properties such as yield stress, ultimate tensile strength, hardness and endurance limit of thealloys. The specimens which used in the tests are divided into eight groups according to the type of alloy, type of heat treatment, and shape. Notched and un-notched specimens are used to perform the tests. The fatigue tests are performed for different type of specimens.The equations of fatigue life estimation are determined according to data which is obtained from the fatigue tests and endurance limit is calculated by using these equations for each type of specimens.

يدرس البحث تأثير المعاملة الحرارية ( التصليد بالترسيب ) على عمر الكلال لسبيكتين من الالمنيوم هما ( 2024 ) و ( 7075 ). السبيكة ( 2024 ) صلدت بالتعتيق الطبيعي بينما استخدم التعتيق الصناعي لتصليد السبيكة ( 7075 ). اجريت الفحوصات الميكانيكية لتحديد الخواص الميكانيكية مثل اجهاد الخضوع ، مقاومة الشد القصوى، الصلادة وحد التحمل للسبائك المستخدمة. قسمت العينات الى ثمانية مجاميع اعتمادا حسب نوع السبيكة ونوع المعاملة الحرارية والشكل. استخدمت عينات محززة وغير محززة لاجراء الفحوصات. اختبارات الكلالاجريت للانواع المختلفة من العينات. تم تحديد معادلات تخمين عمر الكلال اعتمادا على النتائج المستخرجة من الاختبارات. من هذه المعادلات تم حساب عمر الكلال للعينات وتحديد مقدار التحسن في عمر الكلال والخواص الميكانيكية بعد اجراء المعاملة الحرارية.


Article
Effect of Heat Treatment on Notch Sensitivity Factor for Aluminum Alloys
تأثير المعاملة الحرارية على معامل حساسية الحز لسبائك الألمنيوم

Authors: Ahmed. N. Al-Khazraji --- Emad Abdul Hussein Al-mudhafar
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2010 Volume: 28 Issue: 3 Pages: 509-519
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

This study is concerned with the effect of heat treatment (precipitationhardening) on notch sensitivity factor for aluminum alloy (7075). Tests wereconducted on four configurations of specimens, three of them which had externalcircumferential notches with notch radii of 0.5 mm, 0.7 mm, and 1 mm. Thefourth configuration is un-notched specimens. The alloy samples which were usedin fatigue test were subjected to cold working before heat treatment. Dimensionsand roughness of the specimens were measured. The fatigue tests were performedfor different types of specimens. The (S-N) equation was derived for each group toestimate the fatigue life under any applied stress amplitude. In addition, thestrength reduction factor (kf )and notch sensitivity factor (q) were calculated.The results showed that the fatigue strength reduction factor wereincreased after heat treatment and with decreasing notch radius. Also the notchsensitivity factor increased with increasing notch radius and after heat treatment.The enhancement percentage in notch sensitivity factor after the heat treatment for1 mm radius notch was (22.616%).

يتناول البحث تأثير المعاملة الحرارية ( التصليد بالترسيب ) على معامل حساسية الحزلسبيكة الألمنيوم ( 7075 ). الاختبارات أجريت على اربعة أشكال من العينات ثلاث منهاتحتوي على حز محيطي خارجي بنصف قطر 0.5 ملم، 0.7 ملم، و 1 ملم, والرابعة بدون حز.العينات التي استخدمت في اختبارات الكلل معرضة إلى تشكيل بارد قبل إجراء المعاملةالحرارية عليها. تم قياس أبعاد العينات وكذلك فحص الخشونة. اجريت اختبارات الكلل للأنواعالمختلفة من العينات. وتم تحديد معادلات تخمين عمر الكلل اعتمادا على النتائج المستخرجةمنها. وكذلك إيجاد معامل تقليل مقاومة الكلل ومعامل حساسية الحز.يزداد بعد المعاملة الحرارية ويزداد أيضا (kf) لوحظ من النتائج بان معامل تقليل مقاومة الكلليزداد بزيادة نصف قطر الحز وبعد (q) كلما قل نصف قطر الحز. وان معامل حساسية الحزالمعاملة الحرارية.ان نسبة التحسن في مقدار معامل حساسية الحز بعد المعاملة الحرارية للحز.( بنصف القطر 1 ملم كانت (% 22.616