Article
Experimental And Theoretical Investigation Of Composit Materials As Thermal Insulation For Resident Building
دراسة نظرية وعملية لمواد مركبة كعازل حراري لبناية سكنية

Loading...
Loading...
Abstract

This work involves a theoretical and experimental investigation of three types of composite laminated materials as thermal insulations for roofs. The composite consist of three types fiberglass with polyester resin. The first is of; random fiberglass type-1, (density of 659.3 kg/m3).The second is random fiberglass type-2, (density of 731.8 kg/m3) and the last is matt fiberglass,( density 1010.5 kg/m3). The theoretical investigation involved a study of the solar radiation received by the walls and roof, heat gain reduction of roof for the three types of composite materials at different variables; these involved the (insulation thickness, number of layers of composite insulation, volume fraction, and the air gap between roof and the insulation. The experimental investigation is divided into two parts: the first part included measurement of thermal conductivity of composite materials using Lee's disc method with different volume fraction. The second part included manufacturing of two rigs (reference rig and test rig) with dimension (1m x 1m x 1m height). Theoretical results proovs that the heat gain for the roof is more than that of the walls. Also the heat gain is decreased with different percentages depending on the type of insulation. Obviously the heat gain is decreased with using air gap. The thermal conductivity is increased with volume fraction theoretically and experimentally. Experimental result proofs that using random fiberglass type-1 is best in the present work. Also the air gap increases the efficiency of thermal insulation.

تمت دراسة نظرية وعملية لاختبار ثلاثة انواع من المواد الركبة كعوازل حرارية للسقوف. تتكون هذه المواد من الالياف الزجاجية وراتنج البولستر. انواع الالياف المستخدمة هي الياف زجاجية عشوائية نوع-1 وتبلغ كثافتها 659.3kg/m3 , الياف زجاجية عشوائية نوع-2 وتبلغ كثافتها 731.8 kg/m3, والياف زجاجية (حصيرة) ذات كثافة kg/m3 1010.5.تضمن الجزء النظري حساب كمية الاشعاع الشمسي المستلم عبر الجدران والسقف , وتحديد نسبة تخفيض الكسب الحراري للسقف عند استخدام العوازل الثلاثة لعدة متغيرات هي (سمك العازل,عدد طبقات الالياف في العازل, الكسر الحجمي, وجود فجوة هوائية بين العازل والسقف). يتضمن الجزء العملي قسمين: يتضمن القسم الاول قياس الموصلية الحرارية للمواد المركبة لعدة كسور حجمية باستخدام تقنية ( اقراص – لي). في القسم الثاني تم بناء هيكلين ابعاد كل منهما (1مx1مx1م ) , الهيكل الاول يعتبر مصدر اساس لدرجات الحرارة المقاسة اما الهيكل الثاني فيستخدم لاختبار العوازل الحرارية. اثبتت النتائج النظرية ان الحرارة المكتسبة عبر السقف مقارنة بالجدران هي الاكبر. كما ان الكسب الحراري عند استخدام العوازل الحرارية الثلاثة يقل بنسب متفاوتة وحسب نوع العازل. كما يقل الكسب الحراري بشكل ملحوض عند استخدام فجوه هوائية بين العازل والسقف. لوحظ ان الموصلية الحرارية للمواد المركبة تزداد بزيادة الكسر الحجمي لهذه المواد نظريا وعمليا. برهنت النتائج العملية ان استخدام الالياف الزجاجية


Article
Study the Effect of Antimony Tetroxide Addition on Thermal Conductivity for Araldite Resin Reinforced by Biaxial Glass Fibers
دراسة تأثير إضافة أُوكسيد الأنتيمون الرباعي على الموصلية الحرارية لراتنج الإرلدايت المقوى بألياف الزجاج ثنائية الإتجاه

Author: علي إبراهيم الموسوي
Journal: AL-TAQANI مجلة التقني ISSN: 1818653X Year: 2010 Volume: 23 Issue: 4 Pages: A28-A37
Publisher: Foundation of technical education هيئة التعليم التقني

Loading...
Loading...
Abstract

This research studied the effect of flame retardant material addition which is antimony Tetroxide on thermal conductivity for composite material consist of araldite resin reinforced by biaxial woven roving E–type glass fibers (°90-°0) with density (300 g/m2) where we added a different percentage from antimony Tetroxide (10%, 20%,30%) and study the effect on thermal conductivity , and we used Fourier equation to calculate the thermal conductivity coefficient (k) for this composite material before and after addition of flame retardant material illustrated in diagrams which represent the relation between thermal conductivity coefficient (k) with temperature.

تم في هذا البحث دراسة تأثير إضافة مادة معيقة للّهب وهي أُوكسيد الأنتيمون الرباعي على الموصلية الحرارية لمادة مركبة مكونة من راتنج الإرلدايت المقوى بألياف الزجاج بشكل ظفائر محاكة ثنائية الإتجاه (90º- 0º) نوع (E-Glass) ذات كثافة سطحية (300gm3) حيث تم إضافة الأُوكسيد بنسب مختلفـة (30%, 20%,10%) ودراسة مدى تأثر الموصلية الحرارية بهذه الإضافات حيث إستُخدامت معادلة فورير لحساب التغير في قيمة معامل التوصيل الحراري (k) لهذه المادة المركبة قبل وبعد إضافة المادة المعيقة للّهب وكما موضح في المخططات البيانية التي تمثل العلاقة بين معامل التوصيل الحراري (k) ودرجة حرارة الإختبار .الكلمات الدالة : مادة معيقة للّهب ، الموصلية الحرارية ، مادة مركبة .


Article
دراسة عملية لحساب الموصلية الحرارية لنشارة الخشب

Author: هيثم كامل داود
Journal: Journal of Engineering and Sustainable Development مجلة الهندسة والتنمية المستدامة ISSN: 25200917 Year: 2010 Volume: 14 Issue: 1 Pages: 9-20
Publisher: Al-Mustansyriah University الجامعة المستنصرية

Loading...
Loading...
Abstract

The thermal performance of saw dust was studied experimentally to investigate its validity of usage as thermal insulator. The sawdust has low thermal conductivity and cheap in price since it is carpentry waste material. The thermal conductivity is a function of temperature differences, between specimen sides, and its increases as the temperature difference increases. The results showed that the insulation value increases as the density of the samples decreases; this is due to the increase of the volume of air voids and hence increasing of thermal insulation material because of low thermal conductivity of air which resist the flow of the heat through the void. The effect of binders was studied and it showed that the thermal conductivity increases as the binding material increases for the same density, the lowest value of thermal conductivity was 0.18W/moC at lowest density 100kg/m3 without using binder and the highest value of thermal conductivity was 0.285W/moC at highest value of density 250kg/m3 with 40% of binding material.

نظرا للاهتمام المتزايد في ترشيد استهلاك الطاقة داخل الأبنية اتجه بعض الباحثين إلى دراسة الخصائص الحرارية للمواد العازلة، تم دراسة الأداء الحراري لنشارة الخشب بصورة عملية للتعرف على إمكانية استخدامها كمادة عازلة.بينت الدراسة أن مادة نشارة الخشب يمكن استخدامها كعازل حراري في الأبنية وذلك لانخفاض موصليتها الحرارية كما أنها مادة رخيصة الثمن لكونها ناتج عرضي في صناعة الخشب. لوحظ في هذه الدراسة زيادة الموصلية الحرارية بزيادة فرق درجات الحرارة عبر جانبي العينات.بينت النتائج أن قيمة العزل الحراري تزداد كلما قلت كثافة العينة حيث يؤدي نقصان الكثافة إلى زيادة حجم الفجوات الهوائية (التي تؤدي إلى إعاقة سريان الحرارة عبر هذه الفجوات) وبالتالي إلى زيادة قيمة العزل الحراري. كذلك تم دراسة تأثير إضافة المادة الرابطة إلى عينات الدراسة وتبين أن الموصلية الحرارية تزداد عند إضافة المادة الرابطة لنفس الكثافة، حيث كانت أوطأ موصلية حرارية 0.18W/moC عند أوطأ كثافة 100kg/m3 في حالة عدم وجود مادة رابطة، فيما كانت أعلى موصلية 0.285W/moC عند أعلى كثافة 250kg/m3 مع وجود مادة رابطة بنسبة 40%.


Article
MECHANICAL PROPERTIES OF ARALDITE MATRIX COMPOSITES REINFORCED WITH HYBRID CARBON - KEVLAR FIBERS
الخواص الميكانيكية لمادة مركبة ذات أساس من الإرلدايت مقواة بألياف الكاربون وألياف كيفلار الهجينة

Loading...
Loading...
Abstract

The mechanical properties of araldite matrix composites incorporated with hybrid carbon - kevlar fibers were evaluated . There are indications that the incorporation of both fibers into a single matrix which is araldite resin will stabilize mechanical properties and lowering manufacturing costs . In this research the impact strength , tensile strength ,flexural strength ,and hardness were studied for composite material reinforced with hybrid fibers as a woven roving (°90-°0) with density (225g/cm3) and (285g/cm3) for carbon and kevlar fibers respectively . These fibers were mixed with araldite resin in different reinforcement percentage (20%,40%,60%) and the effect on the above mechanical properties were studied , where we see Improves in these mechanical properties after reinforcement by fibers The value of mechanical properties will increase with increasing percentage of reinforcement .

تم في هذه الدراسة حساب قيم الخواص الميكانيكية للمادة المركبة ذات أساس من الإرلدايت المدمج مع ألياف الكاربون وألياف كيفلار الهجينة . حيث هنالك مؤشرات على إن دمج هذين النوعين من الألياف في أرضية واحدة يحافظ على الخواص الميكانيكية ويخفض تكاليف التصنيع . في هذا البحث تم دراسة مقاومة الصدمة ، مقاومة الشد ، مقاومة الإنثناء ، والصلادة للمادة المركبة المقواة بألياف هجينة بشكل حصيرة ثنائية (°0-°90) من ألياف الكاربون وألياف كيفلار بكثافة (225g/cm3) و(285g/cm3) على التوالي . حيث تم مزج هذه الألياف في أرضية من راتنج الإرلدايت وبنسب تقوية مختلفة (60%,40%,20%) ودراسة أثر ذلك على الخواص الميكانيكية ، حيث تم تحسين هذه الخواص بعد التقوية بالألياف إضافة إلى زيادة قيمة هذه الخواص مع زيادة نسبة التقوية بالألياف .


Article
STATE STRAIN AND DEFORMATION FOR POLYMER COMPOSITE MATERIAL BY USING NUMERICAL SOLUTION
تحديد الانفعال والتشوه لمادة مركبة ذات أساس بوليمري باستخدام الحلول الرقمية

Author: Ahmed Falh Hasan احمد فالح حسن
Journal: DIYALA JOURNAL OF ENGINEERING SCIENCES مجلة ديالى للعلوم الهندسية ISSN: 19998716/26166909 Year: 2010 Volume: Engineering Sc. Conference Issue: First Pages: 12-25
Publisher: Diyala University جامعة ديالى

Loading...
Loading...
Abstract

ABSTRACT:-This study deal with composite materials made of E-glass , carbon fiber with epoxy matrix at volume fraction 0.6 , by using mat lab 2008 a was used to state the deformation and strain in both x,y direction . 40*40 mm element was subjected to tensile stress in x direction with value 200,300,400 and 500 MPa with two angle θ=0 and θ=45 degree, the von miss stress distribution has been stated by using solid work at 400,500 MPa. The results was showed when θ=0 glass fiber have value of strain more than carbon fibers, when θ=45 carbon fiber have value of strain more than glass fibers .the change in right angle gave us zero indicating when θ=0 ,and θ=45 the change in right angle gave us negative indication .the von miss stress at 500 MPa was low factor of safety .Keywords:- composite material, mat lab, epoxy, strain, deformation.

الخلاصة تهدف الدراسة الحالية الى تحديد قيم التشوه والانفعال بالمحورين x,y لمادة متراكبة ذات ارضية من الايبوكسي ومدعمة بالياف تقوية من الياف الكاربون و الياف الزجاج وباستخدام برنامج mat lab -2008a حيث تم تحضير عينة بابعاد 40*40 ملم وتسليط اجهاد شد على المحور السيني ومتعامدة على الالياف وبقيم زاوية 0 و45 درجة عند قيم اجهاد (200-300-400-و 500) ميكا باسكال. وكذلك تناولت الدراسة تحديد قيم توزيع الاجهاد لهذه المادة المتراكبة باستخام برنامج solid work 2003 عند قيم اجهاد 500و400 ميكا باسكال . من النتائج تبين ان عند زاوية صفر الانفعال والتشوه باتجاه المحور السيني الياف الزجاج ذات قيم اعلى من الياف الكاربون وعند الزاوية 45 درجة تعكس الحالة وان عند اجهاد 500 ميكا باسكال كان نتائج توزيع الاجهاد عالية للنوعين وذات معامل امان وطى. كلمات الدالة:مادة مركبة –الانفعال و التشوه –ايبوكسي –برنامج مات لاب.


Article
USING OF HYBRID FLAME RETARDANTS TO INCREASE THERMAL EROSION RESISTANCE FOR ADVANCED COMPOSITE MATERIALS
إستخدام المثبطات الهجينة للّهب لزيادة مقاومة التعرية الحرارية للمواد المتراكبة المتقدم

Author: Ali Ibrahim علي إبراهيم الموسوي
Journal: DIYALA JOURNAL OF ENGINEERING SCIENCES مجلة ديالى للعلوم الهندسية ISSN: 19998716/26166909 Year: 2010 Volume: Engineering Sc. Conference Issue: First Pages: 148-156
Publisher: Diyala University جامعة ديالى

Loading...
Loading...
Abstract

ABSTRACT:- This research aims to attainment two essential purposes : first, using of inorganic flame retardant which represent zinc borate to increase the flame retardancy for advanced composite material consist of araldite resin (CY223) reinforced by hybrid fibers from carbon and Kevlar fibers as a woven roving (º 45 - º 0), by using a surface layer from zinc borate as a coating layer of (4mm) thickness .Then, this system was exposed to a direct flame generated from gas flame (2000ºC) with different flame exposure distances (10 mm, 20mm), and study the range of resistance of retardant material layer to the flames and protected the substrate . Second, forming a hybrid flame retardant by added antimony trioxide to zinc borate with various amount(10%,20%,30%) to enhance the retardant action of this material to flame and exposure this hybrid material to same flame temperature and exposure distances and time periods (5-60 sec) and (5-95 sec). Method of measuring the surface temperature opposite to the flame was used to determined the heat transferred to composite material . The best results was obtained with large exposed distance and large percentage from protective layer which is zinc borate with (30%) antimony trioxide.Keywords:- Hybrid Flame Retardant, Composite Material, , Inorganic Retardants .

الخلاصة يسعى هذا البحث إلى تحقيق غرضين أساسيين: الأول،هو إستخدام مثبط لهب لاعضوي متمثل ببورات الزنك لزيادة تثبيط اللهب لمادة متراكبة متقدمة مكونة من راتنج الإرلدايت (CY223) الذي تم تقويته بألياف الكاربون وألياف كيفلار الهجينة بشكل حصيرة (º 0 - º 45) حيث تم إستخدام طبقة سطحية من بورات الزنك كطبقة طلاء سمكها (4mm) . بعدها تم تعريض هذا النظام للهب مباشر متولد من شعلة غازية درجة حرارتها (2000ºC) وبمسافات تعرض مختلفة للّهب (20mm,10mm) ودراسة مدى مقاومة طبقة المادة المثبطة للهب ومدى حمايتها للطبقة التي تحتها . الهدف الثاني ، تكوين مثبط لّهب هجين بإضافة ثالث أُوكسيد الأنتيمون إلى بورات الزنك بكميات متنوعة (30%,20%,10%) لتحسين فعل تثبيط اللهب لهذه المادة وتعريض هذه المادة الهجينة لنفس درجة حرارة الّلهب ومسافات التعرض ولفترات زمنية ( 5-60 ثانية ) و( 5-95 ثانية ) . تم إستخدام طريقة السطح المعاكس للشعلة لقياس الحرارة المنتقلة للمادة المتراكبة . أفضل النتائج المستحصل عليها كانت مع أكبر مسافة تعرض ونسبة من الطبقة الحامية الهجينة والتي هي بورات الزنك مع (30%) ثالث أُوكسيد الأنتيمون .الكلمات الدالة : مثبط لّهب هجين ، مادة متراكبة ، المثبطات اللاعضوية.

Listing 1 - 6 of 6
Sort by
Narrow your search

Resource type

article (6)


Language

English (3)

Arabic (2)

Arabic and English (1)


Year
From To Submit

2010 (6)