Article
Reinforced Microwave - Cured Acrylic Resin Denture Base Material with Glass Fibers

Authors: Mohammed A Abdulla --- Radhwan H. Hasan
Journal: Al-Rafidain Dental Journal مجلة الرافدين لطب الأسنان ISSN: 18121217 Year: 2010 Volume: 10 Issue: 20 Pages: 314-321
Publisher: Mosul University جامعة الموصل

Loading...
Loading...
Abstract

AIMS: To evaluation the Effect of adding glass fibers on the transverse strength and the levels of the residual monomer of specially formulated acrylic resin to be cured by microwave and heat cured acryl-ic resin denture base materials. MATERIALS AND METHODS: The materials were used in this study heat cured acrylic resin and microwave cured acrylic resin which is formulated to be cured by microwave energy( Acronacrylic resin). Thirty two samples were prepared for transverse strength test and divided into the following groups Control group (I) heat cured alone, group (II) microwave cured alone, the group (III) heat cured+fibers, group (IV) microwave cured+fibers the transverse strength was evaluated by using an Instron testing machine . Thirty two samples were prepared for residual mono-mer test and divided into four groups water bath and microwave cured with and without glass fibers, the residual monomer was evaluated by using ultraviolet visible spectrophotometer for seven days. RESULTS: Transverse strength test: Statistical Analysis of Variance(ANOVA) shows that there is significant differences at (p>0.0001)among the four groups and Duncan's multiple range test showed that microwave cured + fibers significantly higher transverse strength followed by heat cured +fibers, microwave alone, while heat alone shows significantly lowest transverse strength. Residual monomer test: Analysis of variance(ANOVA) for the four groups from the first day of immersion in water until 7th day shows that there are significant differences between the four groups in the all six days except the 7th day shows that there are no significant differences among the four groups for the level of the residual monomer. CONCLUSIONS: Microwave cured acrylic resin with glass fibers have signifi-cantly higher transverse strength than that of acrylic resin cured by water bath, also microwave cured acrylic resin have significantly lower residual monomer content from the 1st day of immersion when compared to that of water bath which show the same level of residual monomer at the 7th day of im-mersion


Article
Studying Mechanical Properties For Polymer Matrix Composite Material Reinforced By Fibers And Particles
دراسة الخواص الميكانيكية لمواد متراكبة ذات اساس بوليمري مقواة بالالياف والدقائق

Authors: سهامة عيسى صالح --- كاظم مطر شبيب --- قحطان عدنان حمد
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2010 Volume: 28 Issue: 4 Pages: 81-93
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

The work focuses on the preparation of hybrid polymer matrix compositematerials prepared from the unsaturated polyester resin as matrix reinforced by wovenglass fiber kind ( E-glass ) and graphite particles as first group of samples and the secondgroup of samples reinforced with woven Kevlar fiber kind (49) instead of glass fiber.This work includes studying the effect of selected volume fractions ( 0% , 5% , 10% ,15% , 20% ) of graphite particles with mixture of different particle Size of ( 25 μm – 106μm ) on the properties of the prepared composite materials, Number of mechanical testswere done,they include (Tensile, Compression, Impact, Flexural Strength, Shear Stressand Hardness), which done at room temperature Result of the work shows that thevalues of (Tensile stress, Tensile elastic modulus, Fracture Toughness, Hardness)increase with the increase of graphite particle volume fraction for both groups samples.As well as the values of the (Compression elastic modulus, Flexural strength, Shearstress) increase with the increase of low values of graphite particles volume fraction forboth groups of samples. Where as the values of Impact strength of the preparedcomposite material decreased with the increases of volume fraction of graphite particlesfor both group samples. As well the result shows that the values (Tensile stress, Tensileelastic modulus, impact strength, Fracture toughness) for hybrid composite materialsreinforced by Kevlar fiber are higher than values reinforced by glass fiber instead ofKevlar fiber, While the values of (Compression stress, Flexural Strength, Shear stress,Hardness) for hybrid composite materials reinforced by glass fiber are higher than valuesreinforced by Kevlar fiber instead of glass fiber.

تم في هذا البحث تم تحضير مواد متراكبة هجينية ذات اساس بوليميري بطريقة الصبوقد حضرت المواد المتراكبة من راتنج البولي استر غير المشبع كمادة (Hand lay-up) اليدوي( ذات كسر حجمي ثابت (% 10 (E-GLASS) اساس مدعمة بالياف الزجاج الحصيرية نوعودقائق الكرافيت كمجموعة اولى من العينات ومجموعة ثانية من العينات مدعمه بألياف الكفلرالحصيرية 49 بدلاً من الياف الزجاج. تضمن البحث دراسة تأثيرالكسرالحجمي المختار20%،15%،10%،5%،0% ) لدقائق الكرافيت ذات مزيج من احجام جزيئية مختلفة تتراوح )106 ) على خصائص المواد المتراكبة المحضرة، وقد اجريت مجموعة من μm -25μm) منالاختبارات الميكاينكية عند درجة حرارة الغرفة شملت (اختبار الشد والانضغاط والصدمةومتانة الانحناء واجهاد القص والصلادة ) وقد اظهرت نتائج البحث ان قيمة (اجهاد الشد ،اجهاد الانضغاط ، ومعامل مرونة الشد ، ومتانة الكسر ، والصلادة) تزداد مع زيادة الكسرالحجمي لدقائق الكرافيت كما ان قيم (معامل مرونة الانضغاط ، متانة الانحناء ، اجهاد القص )تزداد عند الكسور الحجمية المنخفضة لدقائق الكرافيت ولكلا عينات المجموعتين بينما تقل قيممقاومة الصدمة مع زيادة الكسر الحجمي لدقائق الكرافيت ولكلا عينات المجموعتين كما وبينتالنتائج ان قيم (اجهاد الشد، معامل مرونة الشد، معامل مرونة الانضغاط، مقاومة الصدمة، متانةالكسر) هي اعلى للمواد المتراكبة الهجينية المدعمة بدقائق الكرافيت والياف الكفلر عن قيمنظيراتها المدعمة بالياف الزجاج بدلاً من الياف الكفلر في حين لوحظ ان قيم (مقاومةالانضغاط، الصلادة، متانة الانحناء، اجهاد القص) هي اعلى للمواد المتراكبة الهجينية المدعمةبالياف الزجاج ودقائق الكرافيت عن قيم نظيراتها المدعمة بالياف الكفلر بدلاً من الياف الزجاج.