The Effect of the Solution Heat Treatment on the Mechanical Properties of Aluminum-Copper Alloy (2024-T3) Using Rolling Process
تأثير المعاملة الحرارية المحلولية على الخواص الميكانيكية لسبيكةألمنيوم- نحاس (2024-T3) باستعمال عملية الدرفلة

Loading...
Loading...
Abstract

The effect of solution heat treatment on the mechanical properties of Aluminum-Copper alloy. (2024-T3) by the rolling process is investigated. The solution heat treatment was implemented by heating the sheets to 480 C° and quenching them by water; then forming by rolling for many passes. And then natural aging is done for one month. Mechanical properties (tensile strength and hardness) are evaluated and the results are compared with the metal without treatment during the rolling process. ANSYS analysis is used to show the stresses distribution in the sheet during the rolling process. It has been seen that good mechanical properties are evident in the alloy without heat treatment due to the strain hardening and also the mechanical properties are improved after heat treatment and rolling process but with lower forces and stresses when compared with the untreated.

دراسة تأثير المعاملة الحرارية المحلولية على الخواص الميكانيكية لسبيكة ألمنيوم -نحاس 2024-T3 من خلال عملية الدرفلة . حيث تم إجراء معاملة حرارية تضمنت تسخين صفائح من هذه السبيكة إلى درجة حرارة (480°C) ثم التبريد السريع بالماء بعدها تم إجراء عملية التشكيل اللدن (بالدرفلة) على هذه الصفائح المقساة ثم إجراء عملية تعتيق طبيعي لمدة شهر بعدها تم دراسة الخواص الميكانيكية من مقاومة شد وصلادة حيث تم إجراء عملية التشكيل بواسطة عملية الدرفلة من خلال تمرير الصفائح بين درافيل وبنسب تشكيل متعددة ومقارنة النتائج للمعدن بدون تعامل. تم استخدام برنامج ANSYS لدراسة توزيع الاجهادات في عملية الدرفلة . لقد تبين أن الخواص الميكانيكية للسبيكة بدون تعامل حراري افضل بسبب ما يسمى بالاصلاد الانفعالي والخواص الميكانيكية للسبيكة بعد المعاملة الحرارية والدرفلة تحسنت ايضاً ولكن بجهد وقوى اقل مقارنة بتلك التي اجريت بدون معاملة


Article
Effect of Heat Treatments on The Mechanical Properties And Wear Resistance of Al- Alloy Matrix Composite
تأثير المعاملات الحرارية على الخواص الميكانيكية ومقاومة البلى لمادة مركبة ذات أساس المنيوم

Authors: منى خضير عباس --- ايمان خليل أبراهيم --- ايمان صبيح نعيم
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2011 Volume: 29 Issue: 12 Pages: 518-533
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Metal matrix composite (MMCs) of the base alloy (Al-0.978%Mg-1.03%Si) reinforcedwith SiC particles (10 wt %) with particle size (53-106) μm was prepared by stir castingusing vortex technique. Solution heat treatment and aging are carried out at a constanttemperature of 175C° for different aging times. Many inspections and tests such asmicrostructure, Vickers hardness and XRD analysis. Wear test type ( Pin – on – Disc) withvarious applied loads and different exposure times at constant parameters was carried outunder dry sliding conditions.It was found that the addition of SiC particles to base alloy improved the hardness andwear resistance before and after heat treatment (precipitation hardening).In addition, using SiC particles with alloy matrix resulted in a faster aging response i.e thetime of peak hardness decreased from 8hr to 5hr for base alloy and composite respectively.These results indicate that the addition of SiC particles to Al –alloy matrix accelerates theaging kinetic.

(Al – 0.978% Mg – 1.03% Si) تم تحضير مادة مركبة معدنية ذات اساس من سبيكة53 ) بطريقة السباكة – 106) μm وبنسبة (% 10 ) وذوحجم حبيبي (SiC) مقواة بدقائق كاربيد السيلكونبالتحريك باستخدام تقنية الدوامة. واجريت عملية المعاملة الحرارية (المعاملة المحلولية والتعتيق) عند175 ولفترات تعتيق مختلفة. وقد اجريت عدة فحوصات واختبارات منها فحص البنية C◦ درجة حرارةالمجهرية وفحص الصلادة الفيكرزية والفحص بحيود الاشعة السينية .وكذلك أجري أختبار البلى الانزلاقيباستعمال احمال متغيرة وازمان تعرض مختلفة مع ثبوت العوامل (Pin –on- Disc) الجاف نوعالاخرى.الى السبيكة الاساس ادى الى تحسين الصلادة ومقاومة البلى قبل وبعد (SiC) وقد لوحظ ان اضافة دقائقالى أرضية السبيكة (SiC) اجراء المعاملة الحرارية (الاصلاد بالترسيب). وكذلك لوحظ ان اضافة دقائقوتقليل زمن التعتيق اللازم (Mg2Si) ادى الى تعجيل عملية التعتيق وترسيب دقائق الطور الثاني5 بالنسبة للسبيكة الاساس والمادة المركبة على hr 8 الى hr للوصول الى قيمة الصلادة العظمى منالتوالي.


Article
Effect of Normalizing Process on Mechanical Properties of Submerged-arc Weldment

Author: Abbas Sheyaa Alwan
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2011 Volume: 29 Issue: 8 Pages: 1554-1562
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Submerged arc welding is carried out and efficient metal- joining process widelyused in great importance in many industrial applications, structures of ships, storagetanks and agriculture equipments. Low alloy steel used under welding conditionswhich are, (560 Amp) welding current, (42cm/min) welding speed, (3.25mm) wirediameter, direct current straight polarity (DCSP) with the joint geometry of single -Vbuttjoint and weld one pass are used for plate of thickness 16mm. After welding, thecomponents have be submitted to a normalization heat treatment in order to recoverthe original mechanical properties of the welds. In this work two different filer metalsboth in the as welded condition and after normalizing heat treatment have been studied.Optical microscopy was used to observe the weld microstructure. Tensile and CharpyV toughness testing and microhardness measurements were used to evaluate themechanical properties of joint. Results show that normalizing reduces the originalcolumnar structure in the as welded condition to an equiaxial structure. It was observeda high decrease in the tensile properties specially the yield strength after normalizing.In respect of toughness, the normalizing heat treatment was observed to increase theCharpy V energy.


Article
The effect of SiC – particles – reinforced MgO composites
تأثير دقائق كاربيد السليكون المدعمة لمتراكب اوكسيد المغنيسيوم

Loading...
Loading...
Abstract

The influence of SiC particles on the physical and mechanical properties for MgO/SiC composites was investigated. MgO matrix was reinforced with (2 wt%,4 wt%,6 wt% and 8 wt% ) of SiC particles which synthesized using powder technology technique. Five samples of each patch have been prepared and supplied to physical properties (green density (G.D) and bulk density (B.D)) and mechanical properties (hardness and compressive strength) were measured. It was observed that the green density of all samples were decreases with increasing SiC particles content. This due to the lower density of SiC than MgO particles. Prepared samples were sintered at different temperatures (800 ˚C, 1100 ˚C, and 1450 ˚C). The bulk density reviled the unaffecting property for samples sintered at 800C and 1100˚C, but it was observed a significant increasing in B.D for samples sintered at higher temperature (1450˚C). It has been found that Vickers hardness, compressive strength and diametrical strength values increases with increasing sintering temperature and decreasing with SiC particles content. The purpose of this study was to confirm the influence of SiC addition on some physical and mechanical properties of MgO matrix.

تم دراسة تأثير إضافة دقائق كاربيد السليكون على الخواص الفيزيائية والميكانيكية لمتراكب اوكسيد المغنيسيوم/كاربيد السليكون وبنسب مئوية مضافة من كاربيد السليكون هي 2%،4%،6%،8% والتي تم تصنيعها بطريقة تكنولوجيا المساحيق. تم تحضير العينات وقياس الخصائص الفيزيائية (الكثافة قبل الحرق والكثافة الحجمية) والخصائص الميكانيكية( الصلادة ومتانة الانضغاط). لقد تم ملاحظة أن الكثافة الطرية لكل العينات تقل بازدياد دقائق كاربيد السليكون المضافة وهذا نتيجة انخفاض كثافة كاربيد السليكون مقرنة باوكسيد المغنيسيوم. أظهرت الكثافة الحجمية عدم تأثرها بالعينات الملبدة بدرجات الحرارة 800م، 1000م وتأثرها الواضح بدرجة التلبيد1450م. لوحظ أيضا آن صلادة فيكرز ومتانة الانضغاط والمتانة القطرية تزداد بازدياد درجة حرارة التلبيد وتقل بازدياد كمية الدقائق المضافة.الغرض من البحث هو لتوضيح تأثير إضافة دقائق كاربيد السليكون على الخواص الفيزيائية والميكانيكية لقالب اوكسيد المغنيسيوم.


Article
THE EFFECT OF HEAT TREATMENT TEMPERATURES (ANNEALING, AGING AND DOUBLE AGING) ON HARDNESS OF 16%NI CAST MARAGING STEELS
دراسة تاثير تغير درجات الحرارة للمعاملة الحرارية (التلدين -التعتيق) على صلادة الفولاذ المراجيني الحاوي على نيكل بنسبة16%

Author: MUNTHIR MOHAMMED RADHY منذر محمد راضي
Journal: Iraqi journal of mechanical and material engineering المجلة العراقية للهندسة الميكانيكية وهندسة المواد ISSN: 20761819 Year: 2011 Volume: 11 Issue: 2 Pages: 333-343
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

AbstractThe primary purpose of the present work was to study the effect of different annealing and aging temperature on the mechanical properties of 16%Ni cast Maraging steels. In addition subsidiary studies were made of the hardening mechanism responsible for high strength. It was found the annealing temperature must be done above approximate 750C◦ but not exceed 1250C◦ to give the good hardness during aging.. Marked hardening occurred within several minutes during from 485oC to545 oC but only after several hours in the range between 325 to 375 oC Heat treatment of 3 hour at 485 oC of cast alloys was most satisfactory. While the aging at 485 oC for long time decrease this hardening caused softening due to the reversion of the body centered cubic matrix to austenite. The aging kinetics mechanism refer to that lattice defect were influencing the reaction rate. X-ray diffraction evident indicated the formation of any bcc structure of matrix as martensite and the appeared that hardness was due to coherent precipitate having concentration in matrix that formed as Fe2CoNi,Ni3Ti and Ni3Mo phases. The double aging of cast alloys in different temperature given normal hardening result.

ملخص البحثان الغرض الاساسي من هذا البحث هو دراسة تاثير تغير عدة درجات حرارية للمعاملة الحرارية(التلدين و التعتيق ) على صلادة مسبوكة الفولاذ المراجين ي (المارتنسايت المعتق ) الذي يحتوي على16% ). اضافة الى دراسات ثانوية تخص مبكانيكية استجابة السبائك المصلدة الى المتانة العالي ة . لقد وجد Ni)1250 )لاعطاء oC) 750 ) وان لاتتجاوز oC) ان درجات حرارة التلدين يجب ان تنجز فوق درجة حرارةصلادة جيدة ومقبولة خلال التعتيق كذلك وجد بداية ظهور الصلادة بعد عدة دقائق خلال التعتيق في(375oC) 545 ) بينما هذاالظهور يبدا بعد عدة ساعات في مدى درجات حرارة( 325 ) الى oC) 485 ) الى oC)485 ) للسبائك المسبوكة يكون مقنع في اعطاء قيم صلادة oC) 3) عند hr) . المعاملة الحرارية التعتيق لمدةجيدة ولكن التعتيق لفترة طويلة عند هذه الدرجة الحرارية ربما يسبب في انخفاض في قيمة الصلادة ناتجهالى اوستنايت . انة ميكانيكية الحركية (bcc) من تلين التركيب بسبب ظهور انعكاس تحول المارتنسايت(X) للتعتيق تشير الى ان العيوب الشبكية متاثرة بمعدل التفاعل خلال التعتيق حيث ان فحص حيود اشعةبشكل مارتنسايت اضافة الى ان ظهور زيادة في الصلادة ناتج (bcc) يوضح مؤشرا تشكيل تركيب قوام ذو.(Fe3CoNi,Ni3Ti and Ni3Mo) من تمركز رواسب التصاقية في القوام والتي تشكل بصيغة اطوار مثلالتعتيق المزدوج للسبائك المزدوج للسبائك المسبوكة عند عدة درجات حرارية مختلفة تعطي نتائج تصليداعتيادية .


Article
Corrosion Resistance of Aluminum Alloy 7020-T6 in Sea Water

Author: Mustafa Khaleel Ismael
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2011 Volume: 29 Issue: 8 Pages: 1482-1490
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

The present work is aimed to investigate the effect of heat treatment on corrosion resistance of Al-alloy 7020-T6 in sea water, the specimens which manufactured by (1.5*1.5*0.2) cm, according to ASTM (G31-72) [1] The heat treatment was carried out at 480°C and water quench after that artificial aging are implemented at temperature 150°C for (1, 4) hours. Microstructure and phase properties after heat treatment and corrosion test were investigated by optical microscope; X-ray diffraction andcomputer potentiodynamic polarization technique have been used to study corrosion behavior in 3.5% NaCl. The results of corrosion resistance 7020-T6 decrease by solution heat treatment and, increase the holding time from 1- 4 hour would increase the corrosion rate, Intermetallics compounds containing zinc represent as the sacrificial anode and control pitting corrosion in 7020-T6 alloy also, the artificialageing time increase the precipitation of zinc and decrease pitting corrosion at 1 hour.


Article
Duplex Inhibition of CO2 Corrosion in Iraqi Oilfield

Author: Sami I.J. Al-rubaiey
Journal: University of Thi-Qar Journal for Engineering Sciences مجلة جامعة ذي قار للعلوم الهندسية ISSN: 26645564/26645572 Year: 2011 Volume: 2 Issue: 3 Pages: 74-94
Publisher: Thi-Qar University جامعة ذي قار

Loading...
Loading...
Abstract

New method for inhibition CO2 corrosion in Iraqi oilfield was used in this work. This new method included using combination of heat treatment of steel and added Aromatic (Tetrahydronaphthalene) compounds as corrosion inhibitor in different concentration (0.05%,0.1%, 0.2%, 0.5% and 1%). The results referred that the weight loss was reduced as inhibitor concentration increased for all conditions of specimens whether, there were heat treated or not. The combination of annealing heat treatment of samples and using Aromatic compoundsinhibitor offered a better corrosion resistance than the combination of quenching + tempering (Q+T) samples. The presence of inhibitor improves the corrosion resistance for annealed samples. For fully annealing, the weight loss was 5 times lesser than that for (Q+T) samples,while the weight loss of steel (as received condition) was 3 times lesser than that for (Q+T)samples.


Article
The Effect of SiC Particles on the Physical Properties of MgO Ceramic Matrix Composites
تأثير دقائق كاربيد السليكون على الخصائص الفيزيائية لمتراكب ذات الأساس السيراميكي لأوكسيد المغنيسيوم

Loading...
Loading...
Abstract

ABSTRACT The influence of SiC particles on the physical and mechanical properties for MgO/SiC composites was investigated. MgO matrix was reinforced with (2 wt%,4 wt%,6 wt% and 8 wt% ) of SiC particles which synthesized using powder technology technique. Five samples of each patch have been prepared and supplied to physical properties (green density (G.D) and bulk density (B.D)) and mechanical properties (hardness and compressive strength) were measured. It was observed that the green density of all samples were decreases with increasing SiC particles content. This due to the lower density of SiC than MgO particles. Prepared samples were sintered at different temperatures (800 ˚C, 1100 ˚C, and 1450 ˚C). The bulk density reviled the unaffecting property for samples sintered at 800C and 1100˚C, but it was observed a significant increasing in B.D for samples sintered at higher temperature (1450˚C). It has been found that Vickers hardness, compressive strength and diametrical strength values increases with increasing sintering temperature and decreasing with SiC particles content. The purpose of this study was to confirm the influence of SiC addition on some physical and mechanical properties of MgO matrix.

الخلاصةتم دراسة تأثير إضافة دقائق كاربيد السليكون على الخواص الفيزيائية والميكانيكية لمتراكب اوكسيد المغنيسيوم/كاربيد السليكون وبنسب مئوية مضافة من كاربيد السليكون هي 2%،4%،6%،8% والتي تم تصنيعها بطريقة تكنولوجيا المساحيق. تم تحضير العينات وقياس الخصائص الفيزيائية (الكثافة قبل الحرق والكثافة الحجمية) والخصائص الميكانيكية( الصلادة ومتانة الانضغاط). لقد تم ملاحظة أن الكثافة الطرية لكل العينات تقل بازدياد دقائق كاربيد السليكون المضافة وهذا نتيجة انخفاض كثافة كاربيد السليكون مقرنة باوكسيد المغنيسيوم. أظهرت الكثافة الحجمية عدم تأثرها بالعينات الملبدة بدرجات الحرارة 800م، 1000م وتأثرها الواضح بدرجة التلبيد1450م. لوحظ أيضا آن صلادة فيكرز ومتانة الانضغاط والمتانة القطرية تزداد بازدياد درجة حرارة التلبيد وتقل بازدياد كمية الدقائق المضافة.الغرض من البحث هو لتوضيح تأثير إضافة دقائق كاربيد السليكون على الخواص الفيزيائية والميكانيكية لقالب اوكسيد المغنيسيوم.

Listing 1 - 8 of 8
Sort by
Narrow your search

Resource type

article (8)


Language

English (6)

Arabic (1)

Arabic and English (1)


Year
From To Submit

2011 (8)