Article
Effect of Water Diffusion on Adhesion Strength
تأثير امتصاص الماء على قوة التلاصق

Authors: A. G. Baker اميرة غريب بكر --- Harith I. Jaffer حارث ابراهيم جعفر
Journal: Baghdad Science Journal مجلة بغداد للعلوم ISSN: 20788665 24117986 Year: 2011 Volume: 8 Issue: 2عدد خاص بمؤتمر الفيزياء Pages: 588-594
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

The adhesion strength between Polyethylene (PE) film and Aluminum surface by using the adhesive material (Cyanoacrylate) has been studied. Aluminum (Al) was used as a substrate, and polyethylene (PE) was used as a film adhered to the Al surface. Standard specimens were prepared to use in the peeling test in dry condition, other specimens were immersed in water for 12 days at room temperature. the results for the specimens in the dry condition had shown that high value in the peel force and the peel energy, the peel force was 0.38*103 N/m and the peel energy was 0.605*103 N/m, peeling the film from Al surface leaves a residual of the adhesive material on both adherend, the failure for this specimen were combination of adhesive and cohesive failure. For the specimens that were immersed in water for 12 days, the results had shown that the effect of water on the specimen (Al /PE), where the water diffusion coefficient on the adhesive joint was 1.09*10-14 m2/s and the peel force was 0.062*103 N/m and the peel energy was 0.124*103 N/m, PE film was peeled from Al surface without any resistance.

تم دراسة قوة التلاصق بين غشاء البولي اثيلين ومعدن الالومنيوم باستخدام مادة اللاصق (سيانواكريليت). وقد استخدم الألمنيوم كقاعدة أساسية , كما استخدم البولي اثيلين كغشاء يلصق على سطح المعدن.هيأت عينات قياسية لاستخدامها في فحص السلخ في الحالة الجافة وعينات اخرى غمرت في الماء لمدة 12 يوما بدرجة حرارة الغرفة. أظهرت النتائج القيمة العالية لقوة وطاقة السلخ للعينات الجافة حيث كـــانت قوة السلخ 0.38*103 N/m وطاقة السلخ 0.605*103 N/m .وعند سلخ غشاء البولي اثيلين من سطح الالومنيوم كانت هناك بقايا من مادة اللاصق على السطحين حيث فشل العينة هو فشل مزدوج ( فشل التلاصق والتماسك). اما بالنسبة للعينات المغمورة بالماء لمدة 12 يوما اظهرت النتائج تأثير الماء على العينات حيث كان معامل انتشار الماء عند منطقة التلاصق 1.09*10-14 m2/sاما قوة السلخ فكانت 0.062*103 N/m وطاقة السلخ كانت 0.124*103 N/m وسلخ الغشاء من سطح المعدن كان بدون أي مقاومة.


Article
Influence of water absorption on fatigue behavior for chopped and woven-glass-fibers-reinforced PMMA denture
تأثير امتصاصية الماء على خصائص الكلل للألياف الزجاجية نوع الحصيرة والعشوائي المسلحة بالبولي مثيل ميثا أكريليت

Authors: Harith .I.Jaafar حارث ابراهيم جعفر --- Zainab.R.Muslem زينب رحيم الشمري
Journal: Iraqi Journal of Physics المجلة العراقية للفيزياء ISSN: 20704003 Year: 2011 Volume: 9 Issue: 16 Pages: 57-60
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

The influence of fiber orientation and water absorption on fatigue crack growth resistance for cold cure acrylic (PMMA) reinforced by chopped and woven -glass-fibers were investigated. A weight of 2 g for chopped fibers and the same weight for woven -glass-fibers (one layer) were used to prepare samples. Some of these samples would storage in dry condition; the others were immersed in water for 15 days. Fatigue test was carried out. The results shows that, for PMMA, the initial bending stress for dry specimen was 3.392 N/cm2 and the number of cycles were 1364, the initial bending stress for wet samples was 4.20 N/cm2, and the number of cycles was 2411. The samples would cut in two pieces because of the cracks would propagated fast during the test. Reinforcement PMMA with different kinds of glass fibers would increase the initial bending stresses for all specimens. The cracks would appear slowly during the test, and the specimens will not separate during the test except the samples which reinforced by Woven-Glass-Fibers.

تم دراسة تأثير اتجاهية الليف وامتصاصية الماء على ممانعة نمو الشق في فحص الكلل لعينات من الاكريليك البارد التقسية والمسلح بالالياف الزجاجية نوع الحصيرة والعشوائي . تم وزن 2 غم من الالياف العشوائية والحصيرة (كطبقة واحدة) ، تم خزن هذه النماذج في الظروف الجافة ثم غمرت في الماء لمدة 15 يوم . اظهرت النتائج ان متانة الانحناء الابتدائي للعينات الجافة كان بحدود 3.392 نيوتن / سم2 وللعينات الرطبة بحدود 4.2 نيوتن / سم2 و ان عدد الدورات بحدود 1364 للعينات الجافة و2411 للعينات الرطبة ، كذلك لوحظ انكسار العينات بسبب انتشار الشقوق داخلها كما ان التسليح يزيد من متانة الانحناء الابتدائي لكل العينات حيث ان انتشار الشقوق يكون ببطئ بالنسبة للعينات المسلحة بنوع الحصيرة.

Keywords

water absorption --- Fatigue --- Denture


Article
Effect of Water Absorption on Hardness Property for Epoxy Reinforced by Glass Fibers
تاثیر امتصاصیة الماء على خاصیة الصلادة للأیبوكسي المدعم بالألیاف الزجاجیة

Authors: Faik H. Anter فائق حماد عنتر --- Hind Salah Hasan هند صلاح حسن
Journal: Journal of university of Anbar for Pure science مجلة جامعة الانبار للعلوم الصرفة ISSN: ISSN: 19918941 Year: 2011 Volume: 5 Issue: 3 Pages: 23-28
Publisher: University of Anbar جامعة الانبار

Loading...
Loading...
Abstract

This research includes studying the effect of water absorption on hardness properties for Epoxy reinforced withglass fibers .Composite materials prepared from the Epoxy resin as matrix reinforced by E-glass fibers [0 - 90oWoven Roving and Random ] with volume fraction 25%.The shore D hardness of all samples investigatedbefore and after immersion in water at room temperature . Results of the work show that the value of hardnesswhich done at room temperature decreases with increasing the time of immersion in water . The weight ofabsorbed water increases with increasing the time of immersion in water specially in the first week .The quantityof absorbed water decreases or increases also according to kind and number of reinforcing layers of glass fiber

یتضمن البحث د ا رسة تأثیر امتصاصیة الماء على خاصیة الصلادة للأیبوكسي المدعم بالألیاف الزجاجیة . إن المادة المت ا ركبة تم تحضی رها من0) و العشوائیة و بكسر حجمي – 90o) كمادة أساس و تمت تقویته و تسلیحه بالألیاف الزجاجیة بنوعیها المتعامد [EP- ا رتنج الأیبوكسي [ 10قدره % 25 . تم قیاس خاصیة الصلادة لجمیع النماذج قبل و بعد الغمر بالماء و بدرجة ح ا ررة الغرفة و بینت نتائج الد ا رسة بأن قیم الصلادة تقلمع زیادة زمن الغمر بالماء ، و أن وزن الماء الممتص یزداد بزیادة أیام الغمر و خصوصا في الأسبوع الأول . إن كمیة الماء الممتص تقل أوتزداد حسب نوع و عدد طبقات التقویة من ألیاف الزجاج .


Article
Water absorption and mechanical properties of high – density polyethylene/ egg shell composite
دراسة الخواص الميكانيكية وامتصاصية الماء لمتراكب البولي اثيلين عالي الكثافة/ قشور البيض

Author: Abdullah A. Hussein, Rusel D. Salim and Abdulwahab A. Sultan
Journal: Journal of Basrah Researches (Sciences) مجلة ابحاث البصرة ( العلميات) ISSN: 18172695 Year: 2011 Volume: 37 Issue: 3A Pages: 36-42
Publisher: Basrah University جامعة البصرة

Loading...
Loading...
Abstract

In this research, the water absorption and mechanical properties of (high-density polyethylene /egg shell) composites as a function of egg shell powder weight content in the grain size (75,125 μm) were investigated. Polymer composite was fabricated by mixing (HDPE) with (5, 10, 15, 20, 25) wt.% of egg shell powder to obtain desirable properties. The parameters such as tensile strength, tensile modulus, elongation at break and impact test were carried out on the prepared samples. It was found that the addition of egg shell powder to the polymer leads to decrease the tensile strength, modulus of elasticity, shore-D hardness on other hand it increases the % elongation at break, and for the impact strength. Water absorption of the composites behaviours as function of days has also been investigated, and it increases by increasing exposure time for the same filler content, while the absorbed amount of water increases, by increasing the wt.% of egg shell constant exposure time.

تم في هذا البحث دراسة الخواص الميكانيكية وامتصاصية الماء للبولي أثيلين عالي الكثافة كدالة للنسبة الوزنيه لقشور البيض عند الحجم دقائقي (75,125 μm). تم تحضير المتراكبات بمزج البوليمر مع نسب وزنية مختلفة (5%,10%,15%,20%,25%) من قشور البيض للحصول على أفضل الخصائص. تمت دراسة السلوك الميكانيكي لهذا الخليط من خلال دراسة الفحوصات الاتلافية (فحص الشد و معامل المرونة و الاستطالة عند الكسرو فحص الصدم). أظهرت النتائج العملية بان إضافة قشور البيض تعمل على تقليل قوة الإجهاد ومعامل يونك و الإجهاد عند الوهن. كما وجد أن مقدار الاستطالة عند الكسر وفحص الصدم يقل بزيادة تركيز المضاف. كما تم دراسة سلوك امتصاصية الماء كدالة للزمن للمتراكبات المحضرة. وتبين بان كمية الماء الممتصة تزداد بزيادة فترة التعرض إلى الماء عند ثبوت نسبة قشور البيض ، كما إنها (تزداد ،تقل) بازدياد نسبة قشور البيض عند ثبوت زمن التعرض.

Listing 1 - 4 of 4
Sort by
Narrow your search

Resource type

article (4)


Language

English (4)


Year
From To Submit

2011 (4)