Preparing and Studying Some Mechanical Properties of Aluminum Matrix Composite Materials Reinforced by Al2O3 particles

Authors: Ali Hubi Haleem --- Newfal Zuheir --- Newal Muhammad Dawood
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2012 Volume: 20 Issue: 1 Pages: 30-38
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

The aim of this work is preparing and studying some of mechanical properties [Brinell hardness (BHN) and compression strength] of aluminum matrix composite material that reinforced by (3, 6 , 9 , and 12 wt.% ) Al2O3 particles. Powder technology technique is used in samples preparing. Samples were compacted by using single action pressing then followed directly by sintering process at 500°C under the effect of inert gas conditionsResults were showed an advancing in the Brinell hardness (BHN) and compression strength especially at 12 wt.% α- Al2O3. The development in the Brinell hardness (BHN) and compression strength were found to reach 89% and 54% respectively from the initial properties of unreinforced aluminum samples.

يهدف البحث الحالي إلى تحضير ودراسة بعض الخواص الميكانيكية ( صلادة برينل ومقاومة الانضغاط) لمادة مركبة ذات أساس من الألمنيوم مقوى بدقائق الألومينا وبنسب وزنيه .(3, 6, 9, 12wt.%) استخدمت تكنولوجيا المساحيق في تحضير النماذج حيث تم كبس النماذج بأسلوب أحادي الاتجاه و تلى ذلك تلبيدها بدرجة حرارة 500°Cفي جو خامل. أظهرت النتائج إن تقوية الألمنيوم بدقائق الألومينا يظهر تحسنا في صلادة برينل ومقاومة الانضغاط وخاصة عند نسبة تقوية .12 wt.% حيث بلغ مقدار التحسن في صلادة برينل ومقاومة الانضغاط للمادة المركبة 89% و 54% على التوالي بالمقارنة مع الألمنيوم غير المقوى.


Article
Preparing and Studying Some Mechanical Properties of Aluminum Matrix Composite Materials Reinforced by Al2O3 particles

Authors: Ali Hubi Haleem --- Newfal Zuheir --- Newal Muhammad Dawood
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2012 Volume: 20 Issue: 1 Pages: 30-38
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

The aim of this work is preparing and studying some of mechanical properties [Brinell hardness (BHN) and compression strength] of aluminum matrix composite material that reinforced by (3, 6 , 9 , and 12 wt.% ) Al2O3 particles. Powder technology technique is used in samples preparing. Samples were compacted by using single action pressing then followed directly by sintering process at 500°C under the effect of inert gas conditionsResults were showed an advancing in the Brinell hardness (BHN) and compression strength especially at 12 wt.% α- Al2O3. The development in the Brinell hardness (BHN) and compression strength were found to reach 89% and 54% respectively from the initial properties of unreinforced aluminum samples.

يهدف البحث الحالي إلى تحضير ودراسة بعض الخواص الميكانيكية ( صلادة برينل ومقاومة الانضغاط) لمادة مركبة ذات أساس من الألمنيوم مقوى بدقائق الألومينا وبنسب وزنيه .(3, 6, 9, 12wt.%) استخدمت تكنولوجيا المساحيق في تحضير النماذج حيث تم كبس النماذج بأسلوب أحادي الاتجاه و تلى ذلك تلبيدها بدرجة حرارة 500°Cفي جو خامل. أظهرت النتائج إن تقوية الألمنيوم بدقائق الألومينا يظهر تحسنا في صلادة برينل ومقاومة الانضغاط وخاصة عند نسبة تقوية .12 wt.% حيث بلغ مقدار التحسن في صلادة برينل ومقاومة الانضغاط للمادة المركبة 89% و 54% على التوالي بالمقارنة مع الألمنيوم غير المقوى.