Improvement of Physical and Mechanical Properties of Iraqi Gypsum Using Resole Resin

Author: Atheer Alaa Abdulhussein
Journal: journal of kerbala university مجلة جامعة كربلاء ISSN: 18130410 Year: 2012 Volume: 10 Issue: 2 Pages: 211-220
Publisher: Kerbala University جامعة كربلاء

Loading...
Loading...
Abstract

The objective of the present work is to improve physical and mechanical properties of local gypsum reinforced with Resole resin. The water-gypsum ratio was kept at 45% throughout all these experiments. The prepared composites show a clear improvement in impact, compression strength and modulus of elasticity while, the bending strength is reduced when the Resole resin proportion in gypsum was increased from 2.5 to 10%. The other objective of this study was to evaluate the water absorption of Resole –gypsum composite. From the experimental results it may be concluded that swelling % was reduced when the Resole percentage in gypsum- Resole composite was increased.

الهدف من العمل هو بتحسين الخواص الميكانيكية والفيزيائية للجبس المحلي المعزز براتنج الريسول. نسبة الماء الى الجبس ثبتت على نسبة 45% خلال جميع التجارب. النماذج المتراكبة المحضرة من راتنجResole)) مع الجبس حصل فيها تحسين ملحوض في قوة التصادم والانضغاط ومعامل المرونة في حين لوحظ هناك انخفاض في قوة الانحناء عندما تغيرت نسبة الريسول في الجبس من 2.5% الى 10% الهدف الاخر من هذه الدراسة هو تقييم امتصاص الماء من قبل متراكبات الجبس والريسول. من النتائج العملية ظهر بشكل واضح, ان درجة الانتفاخ تقل كلما ازدادت نسبة راتنج الريسول في متراكبات جبس-ريسول.


Article
Mechanical Properties and Dynamic Response of Lightweight Reinforced Concrete Beam
الخصائص المیكانیكیة والاستجابة الدینامیكیة للعتبات الخرسانیة المسلحة خفیفة الوزن

Authors: AzizI brahimAbdulla1 --- Alya’a A. Ali --- Ahmed Adnan Ghanee
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2012 Volume: 30 Issue: 2 Pages: 293-311
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

The study is conducted to perform two goals: The first geal is to produce alightweight concrete using major components which are locally available withsome standard admixtures.Many mixtures are prepared using many ratios ofsuperplasticizer (SP) and silica fume (SF) admixtures to yield a lightweightaggregate concrete, the effects of using different ratios of these admixtures on unitweight, compressive strength and flexural strength are studied individually andaccumulatively. The secondis to study the dynamic specifications of normal andlightweight reinforced concrete beams.The results showed that the increasing in dosage of superplasticizer (SP) for(LWAC) increases the density of (LWAC), and the increasing in dosage of silicafume (SF) decreases the density of (LWAC). The experimental impact tests forR.C. beams shows that the lightweight R.C. beams have a better response underimpact loading with respect to the maximum dynamic deflection (2.955mm fornormal weight beam and 1.58mm for lightweight beam). Also,Impact forcetransferred to supports reactions of lightweight beams is smaller within 45% thanthe impact force transferred to reaction of normal weight concrete under the sameimpact load, and the time to reach 90% damping equal to 1.223 sec and 1.6 sec forlightweight and normalweight R.C. beams respectively. Also, the reinforcedconcrete beams are tested under repeated impact load up to failure. The testsshowed that the no. of blows to cause first crack for lightweight concrete beamsmore than twice of this for normalweight concrete beams.

للدراس ةھدفین رئیس یین:- الھ دف الاول ھوانت اج خرس انةخفیفةالوزن باس تخدام مكون ات رئیس یةمحلیةالص نع م ع بع ض الاض افات القیاس یة. ع دةخلطات ت م تحض یرھا باس تخدام نس ب مختلف ة م نأن تأثیراس تخدام تل ك النس ب المختلف ة م ن ھ ذه . (SF) وغی ار الس یلكا (SP) ىالمل دن الف ائقالاضافات على وح دة ال وزن ومقاومةالانض غاط ومقاومةالش د ت م دراس تھ ا بش كل منفص ل وتراكم ي .الھ دف الث اني ھودراسةالخص ائص الدینامیكی ة للعتب ات الخرس انیة الاعتیادی ة والعتب ات الخرس انیةخفیفة الوزن.اظھ رت النت ائج ان الزی ادة ف ي نس بة المل دنالفائق تزی دمن كثاف ة الخرس انة ذات الرك ام خفی ف ال وزنبینماالزی ادة ف ي نسبةغبارالس لیكا تقل ل م ن كثافةالخرس انة ذات الرك ام خفی ف ال وزن. التج ارب العملی ةالتياجری ت لقی اس الخص ائص الدینامیكی ة للعتب ات الخرس انیة ب ین ت ان العتب ات الخرس انیة خفیف ةالوزن تمتل كاستجابة دینامیكیة جیدة تحت احمال الصدمة بالاعتمادعلى الانحناء في منتصف العتبة ( 2.955 ملم للأعت ابالاعتیادی ة و 1.58 مل م للأعت اب خفیف ةالوزن)،ك ذلك ف ان قوةالص دمةالمنقولةالى المس ند (ردالفع ل ) للعتب اتخفیفة الوزن اقل بمقدار 45 % مقارنة بقوة الص دمةالمنقولةالى المس ندفي حال ةالعتبات الاعتیادی ة تح ت نف سحمل الصدمة المسلط.امابالنسبة للزمن اللازم للوصول ال ى اخم اد بمق دار 90 % فان ھ یس اوي 1.233 ثانی ةو1.6 ثانیة للعتبات خفیفة الوزن والعتبات الاعتیادی ةعلى الت والي . كم ا ت م فح ص العتب ات تح ت تأثیرالاحم الالساقطةالمتكررة لحدالفشل. اظھرت نتائج ھذاالفحص ان عددالضربات اللازمة لإحداث الشقال اول للعتب ابخفیفةالوزن اكثربمرتین من عدد الضربات اللازمة لإحداث الشقال اول في العتبات الاعتیادیة.


Article
Mechanical properties of carrot fiber - epoxy composite
الخصائص الميكانيكية لمتراكبات الياف الجزر –ايبوكسي

Authors: Sewench N. Rafiq سه وينج نور الدين رفيق --- Wafaa A. Hussain وفاء عبد الخالق حسين
Journal: Baghdad Science Journal مجلة بغداد للعلوم ISSN: 20788665 24117986 Year: 2012 Volume: 9 Issue: 2 Pages: 335-340
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

Interest has largely centered on the use of plant fibers to reinforce plastics, because these fibers are abundant and cheap. Carrot fibers (Curran) have been extracted from carrot, left over from carrot juice manufacture. The fibers of two sizes fine (50<µm) and coarse (100-150 µm) have been mixed with epoxy in four levels of loading (10, 20, 30, 40 wt %) respectively. Impact test, shore d hardness test and three point bending test of epoxy and carrot fiber-epoxy composites samples have been determined. The impact strength values of samples prepared with fine and coarse fibers increased as compared with pure epoxy sample. Hardness values increased, and the Young’s modulus values decreased with fiber content of both sizes.

هنالك اهتمام كبير باستخدام الياف النباتات لتقوية البلاستك, لان هذه الالياف متوفرة ورخيصة. تم استخراج الياف الجزر من الجزر المتبقي من عملية عصره. خلطت الالياف بحجمين(µm>50) و (µm 150-100) مع الايبوكسي باربعة نسب (10 , 20, 30, 40 نسبة وزنية %) على التوالي. تم قياس اختبار الصدمة واختبار الصلادة واختبار الانحناء الثلاثي النقط لنماذج الايبوكسي ومتراكبات الياف الجزر-ايبوكسي. زادت قيم مقاومة الصدمة للنماذج المحضرة بالالياف الناعمة والخشنة مقارنة مع نمودج الايبوكسي لوحده. هنالك زيادة في قيم الصلادة ونقصان في قيم معامل يونك مع زيادة نسبة الالياف لكلا الحجمين.


Article
Studying the Effect of Corrosive Liquids on Pipes Properties of Unplastizied Polyvinyl Chloride (UPVC) Which is Used in Sewage Purpose
دراسة تأثير المحاليل الآكالة على خصائص أنابيب البولي كلورايد الفاينيل الجسيء (UPVC) المستخدمة في الصرف الصحي

Author: Ahmad Star Ali احمد ستار عيل
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2012 Volume: 30 Issue: 15 Pages: 329-340
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

The current study concerns with studying some mechanical and physical properties of different samples taken from Unplasticized Polyvinyl Chloride (UPVC) pipes used in sewage purpose. Impact strength, compressive strength, shore-D hardness, and diffusion coefficient also were calculated for the samples immersed in different solutions (Wastewater, HCl-0.5N, and Tape water) for four months. Results showed that the mechanical properties of samples were affected by solutions and reduced by (3 – 5)% for impact strength and (10%) for compressive strength. Values for diffusion coefficient (D) were calculated, itwas found that (HCl-0.5N) had a higher value, followed by wastewater then tape water. No cracks were observed, and there were no changes in sample’s dimensions after immersion in solutions.

تم في هذا البحث دراسة بعض الخصائص الميكانيكية و الفيزيائية لنماذج مختلفة من المحاليل على نماذج مقطعة من انابيب الماء و الصرف الصحي المصنعة من البولي كلوريد الفاينيل الجسيء (UPVC). اذ تم حساب متانة الصدمة والصلادة و كذلك متانة الانضغاط للنماذج قبل و بعد غمرها في محاليل من ماء المجاريو ماء الحنفية و المحلول الحامضي (0.5 N). كذلك تم حساب معامل الانتشار بعد غمرها في المحاليل السابقة و لمدة أربعة اشهر. وقد أظهرت النتائج تأثر الخصائص الميكانيكية بعد غمرها في المحاليل و بنسب قليلة بعد انتهاء فترة اربعة اشهر حيث انخفضت بنسبة (3 – 5)% بالنسبة لمتانة الصدمة و كذلك (10)% بالنسبة لمتانة الانضغاط. اما معامل الانتشار فكانت نسبة التغير فيه واضحة.


Article
PHYSICALAND THERMAL PROPERTIES OF FIBER(S-TYPE)-REINFORCED COMPOSITEARALDITE RESIN (GY 260)

Author: Mahmoud A. Hassan
Journal: Al-Qadisiyah Journal for Engineering Sciences مجلة القادسية للعلوم الهندسية ISSN: 19984456 Year: 2012 Volume: 5 Issue: 4 Pages: 341-346
Publisher: Al-Qadisiyah University جامعة القادسية

Loading...
Loading...
Abstract

This study aims to investigate: first, study the effect of changing the reinforcement percentage by fibers on mechanical properties (Impact, tensile, and compressive strength) for composite material consist of Araldite resin reinforced by chopped glass fibers with density (2.6g/cm3) .glass fibers was mixed with araldite resin in different weight reinforcement percentage (20%, 40%, 60%) . the best results was obtained with large reinforcement percentage (60%). Second, study the effect ofthe same above reinforcement percentage on thermal conducting of composite material, where the result show increased thermal conducting with increasing percentage of reinforcement. Fourier equation was used to calculate the changing in thermal conductivity coefficient (k) for composite material.


Article
Study the Effect of Volume Fraction of Mica With Different Particle Size on the Mechanical and Electrical Properties for Unsaturated Polyester Composites
دراسة تأثیر الكسر الحجمي للمایكا باحجام حبیبیة مختلفة على الخصائص المیكانیكیة والكھربائیة للمادة المتراكبة للبولي استر غیر المشبع

Author: Rafah A.Nasif
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2012 Volume: 30 Issue: 20 Pages: 3573-3580
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

This study was carried out to investigate the effect of adding mica (5, 10, 15, 20, 25% vf) with variable particle size (35, 57, 70μm) on the mechanical and electricalproperties of the unsaturated polyester composites. Some mechanical tests were carriedout like (impact strength, flexural strength) and dielectric strength. Flexural strengthand dielectric strength were found to increase with filler concentrations whereas impactstrength was found to decrease at higher concentrations for all particle size.

5,10,15,20,25 ) باحج ام حبیبی ة مختلف ة % vf) تم اجراء ھذه الدراسة لبحث تاثیر الكسر الحجم ي للمایك ا35 ) على الخصائص المیكانیكیة والكھربائیة للمادة المتراكبة للبولي استر غیر المش بع . اجری ت , 57, 70 μm)بعض الاختبارات المیكانیكیة مثل (مقاومة الصدمة ومقاومة الانحناء)ومقاومة العزل الكھربائي واوضحت النتائجزیادة قیم مقاومة الانحناء ومقاومة العزل الكھربائي عند زیادة الكسر الحجمي للمایكا بینما لوحظ نقصان مقاوم ةالصدمة عند زیادة الكسر الحجمي لكل الاحجام الحبیبیة.


Article
Effect of Water Proof Admixture on Hardened Concrete
تأثير المضاف المانع للرطوبة على الخرسانة المتصلبة

Authors: Asmaa Mahdi Ali --- Gheed Basil Hameed
Journal: journal of the college of basic education مجلة كلية التربية الاساسية ISSN: 18157467(print) 27068536(online) Year: 2012 Volume: 18 Issue: 73 Pages: 49-67
Publisher: Al-Mustansyriah University الجامعة المستنصرية

Loading...
Loading...
Abstract

Admixtures improve the compressive strength of concrete. This study shows the using of water proof admixture on hardened concrete (40MPa) when the samples Water curing condition is used and the age at testing are 7, 28 and 90 days to evaluate the mechanical properties such as compressive strength, splitting tensile strength and flexure strength and 28 days and are exposed to temperature (100°C and 500°C) at samples in 28 days. In this study the compressive strength decreases by about (33.03 %) and increases by about (29.95%) at (7 and 90) days respectively. They study shows that the compressive strength decreases by about (0.96% and 19.12 %) at 100°C and 500°C respectively while the tensile strength decreases by about (2.06% and 19.38%) at 100°C and 500°C respectively, and the flexural strength decreases by about (3.01% and 21.07%) at 100°C and 500°C respectively. All the above results are compared with cubes tested at room temperature (25 °C).

تستخدم المضافات لتقليل كمية الماء المضافة و زيادة مقاومة الانضغاط، حيث تم استخدام مضافات "Water reducing" للخرسانة ذات مقاومة انضغاط مقدارها (40 نت/مم2). تم صب50 نماذج مكعبة بأبعاد (150X150)مم لفحص مقاومة الانضغاط بعمر (7، 28و 90) يوم لكل عمر وقد تم تعريض هذه النماذج بعمر 28 يوم الى درجات حرارة (100 م° و 500م°)، ثم مقارنتها مع النماذج التي تم فحصها بدرجة حرارة الغرفة (25 م°) وكذلك صب 50 نماذج اسطوانية بأبعاد (150X300) مم لفحص مقاومة الشد الانشطاري وصب 50 نماذج موشورية بأبعاد (100X100X500) مم لفحص مقاومة الانحناء بعمر 28 يوم و تعريضها إلى درجات حرارة (100م° و 500م°)، ثم مقارنتها مع النماذج التي تم فحصها بدرجة حرارة الغرفة (25 م°) ، لوحظ أن مقاومة الانضغاط تقل بمقدار ( 33,03 % ) بعمر 7 ايام و تزداد بمقدار (29,95 %) بعمر 90يوم عند مقارنتها مع النماذج بعمر 28 يوم. عند تعرض النماذج الى درجة حرارة (100 م° و 400م° ) لوحظ أن مقاومة الانضغاط تقل بمقدار(0,96% و 19,12% ) على التوالي بينما تقل مقاومة الشد الانشطاري بمقدار ( 2,06% و19,38 %) و مقاومة الانحناء تقل بمقدار (3,01 % و 21,07%) عند التعرض الى درجة حرارة (100 م° و 400م° ) على التوالي


Article
EXPERIMENTAL EVALUATION OF BUTT WELDED SPECIMENS OF AA2024-T3 ALLOY WELDED BY FRICTION STIR WELDING WITH TWO CONSEQUENT PASSES
تقييم تجريبي لوصلات اللحام التناكبي للالومنيوم AA2024-T3 الملحومة بطريقة اللحام الاحتكاكي بالخلط وبتمريرتي لحام متعاقبتين

Author: Hatim Mohammed . Mahmood
Journal: AL-TAQANI مجلة التقني ISSN: 1818653X Year: 2012 Volume: 25 Issue: 1 Pages: E 11-E 23
Publisher: Foundation of technical education هيئة التعليم التقني

Loading...
Loading...
Abstract

The aim of the present work is to investigate the mechanical properties and macrostructure of butt joints friction stir welded (FSW) specimens welded with two subsequent passes (one from each side).The material used is AA2024-T3 aluminum alloy 5 mm thick .Pin rotational speed of 900 rpm and 25 mm/min feed is used in this work . The two passes either interferes each other by 0.5 mm or a gap of 0.5 mm between them is existed. The welded specimens have been tensile tested at room temperature in order to analyze the mechanical properties with respect to the parent metal. The macrostructure of the welded specimens has been studied by employing optical microscopy. Micro-hardness examination is also performed on the welded specimens. The two passes FSW specimens with 0.5 mm clearance showed higher yield stress and less percentage elongation than the others ,while specimens with 0.5 mm interference showed higher ultimate tensile stress and higher percentage elongation.

الهدف من البحث هو تقييم الخواص الميكانيكية والتركيب الماكروي للوصلات التناكبية الملحومة بطريقة اللحام الاحتكاكي بالخلط و بتمريرتي لحام متعاقبتين (واحد من كل جهة).المعدن المستخدم هو صفائح اللحام ( AA2024-T3 ) وبسمك 5 ملم .سرعة اداة اللحام الدورانية 900 دورة بالدقيقة وبتغذية خطية 25 ملم /دقيقة.في التمريرتين كانت اداة اللحام اما متداخلتين مع بعضهما بمقدار 0,5 ملم او بينهما خلوص مقداره 0,5 ملم .العينات الملحومة فحصت بجهاز الشد في درجة حرارة الغرفة وذلك لتحليل الخواص الميكانيكية ومقارنتها بالمعدن الاساس. التركيب الماكروي للعينات الملحومة تمت دراسته ايضا.كذلك تم قياس الصلادة المايكروية لمنطقة اللحام في العينات الملحومة.اضهرت النتائج ان العينات الملحومة بخلوص مقداره 0.5 ملم بين اداة اللحام في التمريرتين تمتلك اجهاد خضوع اعلى من العينات الاخرى ولكن نسبة الاستطالة المئوية لهذه العينات اقل من العينات الاخرى ,في حين ان العينات التي تداخلت فيها اداة اللحام اضهرت اجهاد اقصى اعلى ونسبة استطالة مئوية اعلى من العينات الاخرى


Article
The Effect of Ceramic Particale Oxides addition on Wear Resistance of Composite Material for Aluminum Base Alloy
تأثير اضافة دقائق أوكسيدية سيراميكية على مقاومة البلى لمادة متراكبة ذات أساس من سبيكةألالمنيوم

Authors: Israa Abdulkader --- Maryam Abduladhem
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2012 Volume: 30 Issue: 7 Pages: 1249-1264
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

To The aim of this research is to study the effect of 5 wt % Al2O3addition Al- base alloy on sliding wear resistance under dry slidingconditions using pin- on- disc machine . Wear test was conductedafter squeeze casting under different pressure ( 30 , 60 , 90) Mpa.The results show that wear rate for Al- base alloy compositesincreases with increasing applied load but decreases with increasingsliding speed conditions . The composites which casting at 90 Mpapressure represents lower wear rate than those which cast at 30, 60 Mpapressure and the base alloy . The results also observed that thecoefficient of friction increasing with increasing sliding time but reaches to the steady state after 200 sec. The microhardness and ultimate tensile strength increases with increasing squeeze casting pressure.

يهدف هذا البحث الى دراسة تأثير أضافة دقائق أوكسيد ألالمنيوم بنسبة مئوية وزنية 5 % لسبيكة ذات اساس المنيوم على مقاومة البلى الانزلاقي تحت ظروف الانزلاق الجاف باستخدام جهاز ذو ترتيبة المسمار على القرص . لقد تم اجراء اختبار البلى بعد اجراء السباكة . ( 90 . 60 ، 30 ) Mpa بالعصر تحت ضغوط عصر مختلفة تبين من النتائج ان معدل البلى للسبيكة الاساس والمادة المتراكبة يزداد مع ازدياد الحمل المسلط لكنه يقل مع ازدياد سرعة الانزلاق . كما تبين ان المادة المتراكبة الناتجة بعد اجراء 90 اظهرت معدل بليان منخفض مقارنة مع المادة Mpa سباكة العصر تحت ضغط 60 و 30 ) والسبيكة الاساس . كما اظهرت النتائج ان ) Mpa المتراكبة المسبوكة تحت ضغط معامل الاحتكاك يزداد مع ازدياد زمن الانزلاق ثم يصل الى حالة الاستقرار بعد مرور 200ثانية من الاختبار . أما بالنسبة لقيم الصلادة الدقيقة ومقاومة الشد القصوى فانها تزداد مع ازدياد ضغط السباكة بالعصر.


Article
Mechanical, Electrical and Thermal Properties of Polypropylene and Polycarbonate Blend Filled with Carbon Black
دراسه الخواص الميكانيكية و الحراريه والكهربائيه للخلائط البولي البروبلين والبولي كاربونيت المدعم بمسحوق الكاربون

Author: Fadhil Abbas Hummdai
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2012 Volume: 30 Issue: 12 Pages: 2076-2086
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

In this work a composite materials were prepared containing matrix of polymer blend (polypropylene 80% + polycarbonate 20%) reinforced by (carbon black) with different of weight fraction %. The specimen sheet, were obtained by hotcompression from extruded material, using single extruder operated at a temperature between (190-200)Co. The extrusion processes give homogeneous mixer through a regular selection of machine screw revolution per minute and temperature used in extrusion process. The weight fraction of the carbon blacks ranged from 0.0 up to 20 wt % with the polypropylene and polycarbonate blend. All samples related to, mechanical, thermal and electrical tests were prepared by single –extruder. By discharging a high voltage through the composite it was found that the resistivity of the composite decreased from (1.00E+09)-(1.00E+028). Carbon black–polypropylene and polycarbonate composites show significant differences from the neat blends measured in the frequency range. The study of physical test show that the thermal conductivity decreases with the increase of weight fractionfrom (0.157-0.23).

في البحث الحالي تم تحضير مواد مركبة جديدة التي هي عبارة عن مخلوط بوليمري، يتكون 80 ) مع اضافة نسب وزنية / من مزج بولي بروبلين مع بولي كاربونيت بنسبة وزنية ثابتة ( 20 مختلفة من مسحوق اسود الكاربون وذلك باستخدام جهاز الباثقة المنفرد حيث ركزت على أسلوب الخلط المتجانس بين المواد من خلال تحديد سرعة دوران اللولب الماكنة ودرجات الحرارة 200 ) درجة - المستخدمة في عملية البثق. حيث تم تشغيلها عند درجات حرارة تتراوح بين ( 190 مئوية.في هذا البحث تم دراسه الخواص الميكانيكيه و التوصيل الحراري والكهربائي للخلائط البولي البروبلين والبولي كاربونيت المدعم باسود الكاربون بنسب مئويه وزنيه تتراوح من 0 الى % 20 .وجد عند امرار فولتيه عاليه خلال النماذج المدعمة حدوث انخفاض واضح في المقاومه النوعيه مقارنه بنماذج البولي بروبلين مع بولي كاربونيت غير المدعمه باسود الكاربون.ووجد.زياده في خواص التوصيل الحراري لمتراكبات البولي بروبلين مع بولي كاربونيت المدعم باسود الكاربون مقارنه بالخليط غير المدعم .

Listing 1 - 10 of 36 << page
of 4
>>
Sort by
Narrow your search

Resource type

article (36)


Language

English (26)

Arabic (7)

Arabic and English (3)


Year
From To Submit

2012 (36)