DIELECTRIC PROPERTIES AND THERMAL CONDUCTIVITY OF HDPE AND PS
الخواص العزلية و التوصيلية الحرارية للبولي اثيلين عالي الكثافة و البولي ستايرين

Authors: Hameed Majed Ahmed حميد مجيد احمد --- Shakhawan Hassan Ali شاخوان حسن علي
Journal: Iraqi Journal of Science المجلة العراقية للعلوم ISSN: 00672904/23121637 Year: 2012 Volume: 53 Issue: 2 Pages: 330-334
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

Dielectric constant ( ) over the frequency range 1KHz-1MHz and thermal conductivity (k) have been measured for high-density polyethylene (HDPE) and polystyrene (PS) (with thicknesses 1.6 and 1.1 mm respectively and all with diameter 3.2 cm), in the temperature range 30-110°С, It has been found that the dielectric constant is almost frequency independent and slightly temperature dependent, this reveals the fact that these polymers are non-polar. However, there was a significant effect of temperature on the thermal conductivity of the samples, especially at Tg of PS and Tm of HDPE.

تم قياس ثابت العزل الكهربائي ( ) في مدى الترددات 1KHz-1MHz والقابلية التوصيلية الحرارية لكل من البولي أثيلين عالي الكثافة (HDPE) و بولي ستايرين (PS) (بسمك 1.6mm و mm 1.1) و بقطر 3.2cm ، في درجات الحرارة (30-110oC). لقد وجد بان ثابت العزل الكهربائي لهما لا يعتمد على التردد و أعتمادهما على درجات الحرارة ضئيل، وهذا يدل على ان هذين البوليمرين هما غير قطبيان كهربائيا. وهناك تاثير مهم لدرجة الحرارة على التوصيلية الحرارية للنماذج خاصة في درجة حرارة أنتـقال زجاجي (Tg) لبولي استلين(PS) و درجة حرارة الأنصهار البلوري (Tm) لـبولي اثيلين (HDPE).


Article
Study Of Factors Affecting The Thermal Conductivity Of Iraqi Bentonite
دراسة العوامل المؤثرة على الموصلية الحرارية لآطيان البنتونايت العراقية

Author: Qasid Abdul Sattar Saleh قاصد عبد الستار صالح*
Journal: Baghdad Science Journal مجلة بغداد للعلوم ISSN: 20788665 24117986 Year: 2012 Volume: 9 Issue: 3 Pages: 548-553
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

Thermal conductivity of compacted bentonite is one of the most important properties where this type of clay is proposed for use as a buffer material. In this study, Lee's disc method was used to measure the thermal conductivity of compacted bentonite specimens. The experimental results have been analyzed to observe the three major factors affecting the thermal conductivity of bentonite buffer material. While the clay density reaches to a target value, the measurement is taken to evaluate the thermal conductivity. By repeating this procedure, a relationship between clay dry density and thermal conductivity has been established in specimens after adjusting the water contents of the bentonite by placing its specimens in a drying oven for different periods. So relationships of thermal conductivity with each of these major factors (clay density, water content, and sand volume fraction) are established in this study. The relevance of these relationships be analyzed together using experimental data on many compacted bentonites.

تمت دراسة مدى تأثر الموصلية الحرارية لاطيان البنتونايت والتي تستخدم كمادة عازلة للماء والسوائل الاخرى فضلا عن استخاماتها في تبطين جداول السقي وفي الصناعات وبالاخص الطبية بأهم ثلاث عوامل رئيسية هي الكثافة الجافة لمضغوطة البنتونايت , المحتوى المائي فضلا عن النسبة الحجمية لمزيج بنتونايت – رمل والذي غالبا مايتواجدان معا في التربة وبنسب مختلفة من موقع الى آخر، حيث تم في هذا البحث قياس الموصلية الحرارية لهذه الاطيان بأستخدام طريقة قرص ليز.ووفق تحليلنا للنتائج المستحصلة من خلال أيجاد علاقة للموصلية الحرارية مع كل عامل من هذه العوامل الثلاث كل على حدة , حيث أظهرت هذه العلاقات مدى تأثر الموصلية الحرارية لهذا النوع من الاطيان بتلك العوامل الثلاث حيث تزداد قيمة الموصلية للطين بزيادة تلك العوامل الثلاث والتي أكدت عليها الكثير من البحوث والدراسات المنشورة في الدوريات العالمية، مما يمكننا من تطبيق وتأسيس نفس تلك العلاقات على انواع اخرى من الاطيان التي تزخر بها تربة العراق لتكون قيد الدراسة ولتحسين خواصها الحرارية.


Article
Mechanical, Electrical and Thermal Properties of Polypropylene and Polycarbonate Blend Filled with Carbon Black
دراسه الخواص الميكانيكية و الحراريه والكهربائيه للخلائط البولي البروبلين والبولي كاربونيت المدعم بمسحوق الكاربون

Author: Fadhil Abbas Hummdai
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2012 Volume: 30 Issue: 12 Pages: 2076-2086
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

In this work a composite materials were prepared containing matrix of polymer blend (polypropylene 80% + polycarbonate 20%) reinforced by (carbon black) with different of weight fraction %. The specimen sheet, were obtained by hotcompression from extruded material, using single extruder operated at a temperature between (190-200)Co. The extrusion processes give homogeneous mixer through a regular selection of machine screw revolution per minute and temperature used in extrusion process. The weight fraction of the carbon blacks ranged from 0.0 up to 20 wt % with the polypropylene and polycarbonate blend. All samples related to, mechanical, thermal and electrical tests were prepared by single –extruder. By discharging a high voltage through the composite it was found that the resistivity of the composite decreased from (1.00E+09)-(1.00E+028). Carbon black–polypropylene and polycarbonate composites show significant differences from the neat blends measured in the frequency range. The study of physical test show that the thermal conductivity decreases with the increase of weight fractionfrom (0.157-0.23).

في البحث الحالي تم تحضير مواد مركبة جديدة التي هي عبارة عن مخلوط بوليمري، يتكون 80 ) مع اضافة نسب وزنية / من مزج بولي بروبلين مع بولي كاربونيت بنسبة وزنية ثابتة ( 20 مختلفة من مسحوق اسود الكاربون وذلك باستخدام جهاز الباثقة المنفرد حيث ركزت على أسلوب الخلط المتجانس بين المواد من خلال تحديد سرعة دوران اللولب الماكنة ودرجات الحرارة 200 ) درجة - المستخدمة في عملية البثق. حيث تم تشغيلها عند درجات حرارة تتراوح بين ( 190 مئوية.في هذا البحث تم دراسه الخواص الميكانيكيه و التوصيل الحراري والكهربائي للخلائط البولي البروبلين والبولي كاربونيت المدعم باسود الكاربون بنسب مئويه وزنيه تتراوح من 0 الى % 20 .وجد عند امرار فولتيه عاليه خلال النماذج المدعمة حدوث انخفاض واضح في المقاومه النوعيه مقارنه بنماذج البولي بروبلين مع بولي كاربونيت غير المدعمه باسود الكاربون.ووجد.زياده في خواص التوصيل الحراري لمتراكبات البولي بروبلين مع بولي كاربونيت المدعم باسود الكاربون مقارنه بالخليط غير المدعم .


Article
Effect of carbon nanotube and Zn particles addition on the some mechanical properties and thermal conductivity of unsaturated polyester resin
تأثير انابيب الكاربون النانوية وجسيمات الخارصين المضافة على بعض الخواص الميكانيكية و معامل التوصيل الحراري لراتنج البولي استر غير المشبع

Authors: N.A.Ali نادية عباس علي --- S.I.Husaen سيناء ابراهيم حسين --- H.I.Jaffer حارث ابراهيم جعفر
Journal: Iraqi Journal of Physics المجلة العراقية للفيزياء ISSN: 20704003 Year: 2012 Volume: 10 Issue: 18 Pages: 98-104
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

In this research work a composite material was prepared contains a matrix which is unsaturated polyester resin (UPE) reinforced with carbon nanotube the percentage weight (0.1, 0.2, 0.4.0.5) %, and Zn particle the percentage weight (0.1, 0.2,0.4,0.5)%.All sample were prepared by hand lay-up, process the mechanical tests contains hardness test, wear rate test, and the coefficient of thermal conductivity. The results showed a significant improvement in the properties of overlapping, Article containing carbon nano-tubes and maicroparticles of zinc because of its articles of this characteristics of high quality properties led to an, an increase in the coefficient of the rmalconductivity, and increase the hardness values with increased percentage weight when the wear rate increase with increased the applied load and percentage weight.

تم في هذا البحث تحضيرمادة متراكبة من راتنج البولي استرغير المشبع مقواة بانابيب الكاربون النانوية وجسيمات الخارصين وبنسب وزنية 0.2)و0.4و0.8و(1%واستخدمت طريقة القولبة اليدوية في تحضير العينات واجريت اختبارات ميكانيكية تضمنت فحص الصلادة وفحص معدل البلى وقياس معامل التوصيل الحراري.اظهرت النتائج تحسنا كبيرا في خواص المادة المتراكبة الحاوية على انابيب الكاربون النانوية وجسيمات الخارصين لما تتمتع به هذه المواد من خصائص عالية الجودة ادت الى زيادة في معامل التوصيل الحراري وزيادة قيم الصلادة بزيادة النسب الوزنية ومعدل البلى كان يزداد بزيادة الحمل المسلط وزيادة النسب الوزنية .


Article
Study the effect of the proportion of coal and the size of the added grains on the thermal conductivity of the ceramic
دراسة تأثير نسبة الفحم المضاف وحجم حبيباته على التوصيلية الحرارية للسيراميك

Author: tagreed muslim alsaady تغريد مسلم الساعدي
Journal: Diyala Journal For Pure Science مجلة ديالى للعلوم الصرفة ISSN: 83732222 25189255 Year: 2012 Volume: 8 Issue: 1 Pages: 86-95
Publisher: Diyala University جامعة ديالى

Loading...
Loading...
Abstract

Studied in this research the impact of the proportion of added coal and the size of its grains on the thermal conductivity of the samples of ceramic used soil as a basis and added to its coal percentages by weight are: (20, 10, 5.1, 0.5, 0.2, 0.1)% and four volumes of granulomas, and then compressed samples in tablets of 25mm diameter and burned much 1100оC. Calculated the thermal conductivity using a CD-I Lee's disk) (and then calculated the porosity and absorbency of water and the density of each sample. Found that there is a close relationship between thermal conductivity and the proportion of added coal and the size of its grians, with increasing thermal conductivity of the ratios weighted low-lying (0.2 - 0.1)% and then starts decreasing with increasing the proportion of coal in the sample, on the other hand decreasing thermal conductivity increase size granular added coal, recorded samples with ratios weighted high of 20% and size granular coarse (600-1180) μm lower values for the conduction heat. wecan take advantage of the low thermal conductivity of the work of thermal insulation ceramic used for lining furnaces, cooking and drying can also be employed in the manufacture of brick construction to increase the thermal isolation.

دُرس في هذا البحث تأثير نسبة الفحم المضاف وحجم حبيباته على التوصيلية الحرارية لعينات سيراميكية أستخدمت التربة Soil كمادة أساس وأضيف لها الفحم Coal بنسب وزنية هي : (20 , 10 , 5 , 1 , 0.5 , 0.2 , 0.1 )% ولأربعة حجوم حبيبية , ثم كُبست العينات بشكل أقراص قطر كل منها 25mm وحُرقت بدرجة 1100оC. حُسبت التوصيلية الحرارية بإستخدام قرص لي Lee’s disk) (ثم حُسبت المسامية وإمتصاصية الماء وكثافة كل عينة. وجد أن هناك علاقة وثيقة بين التوصيلية الحرارية ونسبة الفحم المضاف وحجم حبيباته , حيث تتزايد التوصيلية الحرارية للنسب الوزنية الواطئة (0.2 - 0.1 )% ثم تبدأ تتناقص مع تزايد نسبة الفحم في العينة , ومن جهة أخرى تتناقص التوصيلية الحرارية بزيادة الحجم الحبيبي للفحم المضاف حيث سجلت العينات ذات النسب الوزنية العالية 20% والحجم الحبيبي الخشن (600-1180) µm أقل قيم للتوصيلية الحرارية. يمكن الإستفادة من إنخفاض التوصيلية الحرارية لعمل عوازل حرارية سيراميكية تستخدم لتبطين أفران الطبخ والتجفيف كما يمكن توظيفها في صناعة طابوق البناء لزيادة عزله الحراري .


Article
MECHANICAL AND PHYSICAL PROPERTIES OF HIGH DENSITY POLYETHYLENE FILLED WITH CARBON BLACK AND TITANIUM DIOXIDE
الصفات المیكانیكیة و الفیزیاویة لمزیج البولي اثلین العالي الكثافة مع ثاني اوكسید التیتانیوم – اسود الكاربون

Author: Zanaib.Y.Shnean زینب یوسف شنین
Journal: DIYALA JOURNAL OF ENGINEERING SCIENCES مجلة ديالى للعلوم الهندسية ISSN: 19998716/26166909 Year: 2012 Volume: 5 Issue: 1 Pages: 147-159
Publisher: Diyala University جامعة ديالى

Loading...
Loading...
Abstract

ABSTRACT:- In this work composite material composed of high density polyethylene and inorganic pigment (carbon black and titanium dioxide) was prepared. Different amounts of carbon black and titanium dioxide (2– 15) wt% were added as filler. The preparation of filled and unfilled (High density polyethylene /Carbon black and titanium dioxide) composite was carried out using a single – screw extruder operated at a temperature of (170 – 190)oC.The incorporation was performed in a single screw extruder and sheets specimens were obtained by hot compression from extruded materials. Many mechanical and physical tests were used to determine the properties of the prepared composite material which involved compression strength, impact strength and modulus of elasticity for all the preparation composite. An untreated HDPE sheet is used for the purpose of comparison. In this study, the influence of addition of Carbon black and titanium dioxide, on the mechanical ,electrical and thermal a properties test of high-density polyethylene (HDPE). The results show that the use of pigments, carbon black and TiO2 in appropriate concentration ratios give a reliable improvement in the mechanical properties. The weight fraction of the carbon blacks and titanium dioxide ranged from 0.0 up to 15 wt % with the high density polyethylene. By discharging a high voltage through the composite it was found that the resistivity of the composite decreased. Carbon black and titanium dioxide –highdensity polyethylene composites show significant differences from the neat high-densitypolyethylene measured in the frequency range. It was found that the carbon black and titanium dioxide/ high-density polyethylenecomposites have better thermal properties than the neat high-density polyethylene.Keyword: high density polyethylene. Titanium dioxide, Carbon black, Electrical properties, Thermal conductivity, Mechanical properties

الخلاصةفي البحث الحالي تم تحضیرالمواد المتراكبة بواسطة مزج البولي اثلین العالي الكثافة مع نسب وزنیة مختلفة من (2– 15)) كحشوة. باستخدام جهاز الباثقة الاحادیة wt% ( الاصباغ لاعضویة(ثنائي اوكسید التیتانیوم-اسود الكاربونفي هدا البحث تم دراسة تاثیر اضافة ثنائي اوكسید التیتانیوم , اسود الكاربون (190 - o 170 ) م - بدرجة حرارة تتراوح بین ( على الخصائص المیكانیكیة لبولي اثلین العالي الكثافة . تم أجراء العدید من الاختبارات المیكانیكیة والفیزیائیة لغرض تحدید خواص المادة المتراكبة المحضرة، حیث تضمنت تلك الاختبارات: مثل مقاومة الانضقاطیة ومقاومة الصدم ومعامل المرونة، ولجمیع المتراكبات المحضرة وقورنت النتائج المستحصلة مع تلك التي تعود لمادة الأساس بمفردة . من النتائج التي تم الحصول علیها تبین ان استخدام الاصباغ لاعضویة (ثنائي اوكسید التیتانیوم،اسود الكربون) أعطى تحسن في الخصائص المیكانیكیة . في هذا البحث تم دراسه خواص التوصیل الحراري والكهربائي لبولي الاثلین العالي الكثافه المدعم باسود الكاربون واوكسید التیتانیوم بنسب مئویه وزنیه تتراوح من ٠ الى ١٥ % .وجد عند امرار فولتیه عالیه خلال النماذج المدعمة حدوث انخفاض واضح في المقاومه النوعیه مقارنه بنماذج البولي الاثلین العالي الكثافه غیر المدعمه باسود الكاربون واوكسید التیتانیوم .. وو جد تحسن في خواص التوصیل الحراري لمتراكبات البولي الاثلین العالي الكثافه المدعم باسود الكاربون واوكسید التیتانیوم مقارنه باالبولي الاثلین العالي الكثافه غیر المدعم .


Article
Improvement of The Mechanical and Thermal Properties of Clay Bricks by Using Local Materials in Iraq
حتسین المواصفات المیكانیكیة والحراریة للطابوق الطیني باستعمال مواد محلیة في العراق

Author: Haqi Ismael Qatta
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2012 Volume: 30 Issue: 19 Pages: 3308-3327
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

This research studies the effect of adding industrial wastes materials withdifferent percentages on the thermal and mechanical properties of claybricks . Different types of admixtures were used in this work, includingrubber cuttings, wood saw dust and barley reeds ash with ( 5%,10% 15%,20% ) by weight of each one respectively. Thermal conductivity, specific heatcapacity, compressive strength, flexural tensile strength, porosity and variationof density have been examined for each samples at all percent of additionand comparing with the reference clay bricks samples . Test results show thatthe admixtures effect on the properties of clay bricks, when used barley reedsash which the best additives because take good properties, the density of claybricks is reduced 33%,thermal conductivity reduced 46% and the compressivestrength increased 20% comparing with the standard bricks. The experimentalwork carried in the industrial factory of clay bricks in the Nahrawon city inBaghdad.

یھدف البحث الى دراس ة ن وع جدی د م ن الط ابوق الطین ي المتس امي, تن اول البح ثدراسة تاثیر اضافة المخلفات الصناعیة بنسب مختلفة على الخواص الحراریة والمیكانیكیةللطابوق الطیني, ت م اختی ار مف روم الاط ارات ونش ارة الخش ب و مطح ون قص ب الش عیر20 % ) لكل منھا على التوالي, , %15 , %10, % واضافتھا وزنیا كل عاى حده بنسب ( 5تم تقیم مقدار (التوصیل الحرارى, الس عة الحراری ة النوعی ة , مقاوم ة الانض غاط, الكثاف ةوالمسامیة ) ولكل ةبسن من النسب اعلاه ومقارنتھا مع الطابوق القیاسي (بدون اضافة).تم استنتاج ان اس تخدام ھ ذه المض افات ی وثر عل ى خ واص الط ابوق الطین ي وا ن ا س تعمالمطحون قصب الشعیر ھو افضل المضا فات وذل ك لمواص فا ت ھ الجی دة حی ث قل ت الكث ا ف ة بنس بة%33 والتو صیل الحراري ةبسنب 46 % وزادت مقا وم ة الا نض غا ط بنس بة 20 % مق ا رن ةم ع الط ابوق القیاس ي. ت م اج راء النم اذج عملی ا ف ي معم ل تص نیع الط ابوق ف ي مدین ةالنھروان في بغداد.

Listing 1 - 7 of 7
Sort by
Narrow your search

Resource type

article (7)


Language

English (6)

Arabic and English (1)


Year
From To Submit

2012 (7)