STUDY OF THE EFFECT OF NH4F CONCENTRATION ON THE STRUCTURE OF ELECTROCHEMICALLY PREPARED TiO2 NANOTUBES
دراسة تاثير تركيز NH4F على تركيب الانابيب النانوية لـ (TiO2) المحضرة الكتروكيميائياً

Loading...
Loading...
Abstract

In this study Titania nanotube arrays were prepared at room temperature (~25 ºC) via electrochemical anodization process of pure titanium foil in glycerol base electrolyte, different concentrations of ammonium fluoride salt (0.5 and 1.5wt.%) were added to the electrolyte as a tube enhancing agent. When anodizing Ti in 0.5 wt. % NH4F, nanotubes are formed with 54 ± 10 nm tube diameter, 20 ± 3 nm wall thickness and 1.76 µm tube length. When anodizing Ti in 1.5 wt. % NH4F, nanotubes are formed with 69 ± 10 nm tube diameter, 29 ± 3 nm wall thickness and 2.71 µm tube length. The morphology and structure of the Titania films were studied by scanning electron microscopy (SEM), X-ray diffraction (XRD), and atomic force microscopy (AFM). PACS numbers: 81.65.Mg, 82.45. +z, 81.10.-h.

في هذه الدراسة صفوف التيتانيا نانوتيوب حضرت في درجة حرارة الغرفة ~25 ºC بطريقة الانودة الكهروكيمائية لصفائح التيتانيوم النقي في محلول كهربائي اساسه جليسيرول (glycerol)، تراكيز مختلفة من ملح فلوريد الامونيوم 0.5 and 1.5wt.% اضيفت الى المحلول كعامل محسن للانبوب. عندما يؤكسد التيتانيوم في 0.5 wt%.NH4F ، كان قطر الانابيب النانوية المشكلة 10nm± 54 ، سمك الجدار nm 3± 20 و µm 1.76 طول الانبوب. عندما يؤكسد التيتانيوم في 1.5 wt%.NH4F ، كان قطر الانابيب النانوية المشكلة 10nm± 69 ، سمك الجدار nm 3± 29 و µm 2.71 طول الانبوب. تمت دراسة مورفلوجية وتركيب افلام التيتانيا بواسطة المجهر الالكتروني الماسح، مجهر القوة الذرية و حيود الاشعة السينية.


Article
Study the effect of adding TiO2 nano-powder on some surface properties of TiO2 thin film prepared on stainless steel substrate
دراسة تأثير إضافة مسحوق نانو TiO2 على بعض الخصائص السطحية لغشاء رقيق TiO2 مرسب على قواعد من الفولاذ المقاوم للصدأ

Authors: Alaa A. Abdul-Hamead الاء علاء الدين عبد الحميد --- Ali H. Ataiwi علي عطاوي
Journal: Iraqi Journal of Physics المجلة العراقية للفيزياء ISSN: 20704003 Year: 2012 Volume: 10 Issue: 18 Pages: 29-34
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

In this research TiO2 nano-powder was prepared by a spray pyrolysis technique and then adds to the TiO2 powder with particle size (0.523 μm) in ratio (0, 5, 10, 15 at %) atomic percentage, and then deposition of the mixture on the stainless steel 316 L substrate in order to use in medical and industrial applications.Structure properties including x-ray diffraction (XRD) and scanning electron microscope (SEM0, also some of mechanical properties and the effect of thermal annealing in different temperature have been studied. The results show that the particle size of a prepared nano-powder was 50 up to 75 nm from SEM, and the crystal structure of the powders (original and nano powder) was rutile with tetragonal cell. An improvement in all the properties after the addition of TiO2 nano –powder was take place.

في هذا البحث تم تحضير مسحوقَ نانوي من أوكسيد التيتانيوم TiO2 بطريقة الرش الكيمياوي الحراري spray pyrolysis بعد ذلك تم خلط المسحوق النانو ي المحضر مع مسحوق جاهز من TiO2 أيضا و بحجمِ حبيبي ِ بلغ (0.523µ m) و بنسبِ خلط بلغت(0 , 5 , 10 , 15 atom %) ، وبعد ذلك ترسيب الخَلِيْطِ على قواعد من الفولاذ المقاوم للصدأِ 316L و المَستعملَة في التطبيقاتِ الطبيةِ والصناعيةِ بشكل واسع. درست الخواص التركيبية باستخدام (XRD,SEM)، أيضا بعض الخواص ميكانيكية، وِتأثير التَلْدين الحراريِ أيضاً في درجةِ الحرارة المختلفةِ. بينت النَتائِجَ بأنّ حجمَ جسيمات المسحوقَ النانو المحضر كَانَ بحدود50 nm إلى حوالي 75 nm مِنْ فحص SEM ، و تحسن قد حصل في كُلّ الخواص بعد إضافةِ مسحوقَ اوكسيد التيتانيوم النانوي.


Article
Dielectric behavior and Ac conductivity measurements of bulk (TiO2, ZnO/Epoxy) composites
دراسة السلوك العازل الكهربائي والتوصيلية الكهربائية المتناوبة لتمراكبات (راتنج الايبوكسي ـ اوكسيد التيتانيوم) و(راتنج الايبوكسي ـ اوكسيد الزنك)

Authors: Abdullah A. Hussein --- Abdulwahab. A.Sultan --- Tahseen A. Saki
Journal: journal of kerbala university مجلة جامعة كربلاء ISSN: 18130410 Year: 2012 Volume: 10 Issue: 3 Pages: 348-356
Publisher: Kerbala University جامعة كربلاء

Loading...
Loading...
Abstract

Dielectric behavior and ac conductivity measurements on epoxy resin filled with (5, 10, 15, 20, 25 wt.%.) micro sized particles of TiO2 and ZnO have been studied.. The measurements were carried out in the frequency range (120Hz - 2MHz) and over a wide temperature 30 ◦C and 110◦C. Different dielectric behavior was observed depending on filler type, filler contact, frequency and temperature. Results show that dielectric permittivity (ε') and dielectric loss(ε") increases with the addition of epoxy resin, which has been attributed to interfacial polarization. The value of (ε') increased with increasing temperature, due to the greater freedom for movement of the dipole molecular chains within the epoxy at high temperature. The value of (ε') decreases with increasing frequency, which indicates that the major contribution to the polarization comes from orientation polarization. Interfacial relaxation is found to be strongly dependent on the presence of micro-filler particles. The Alternating Current (AC) conductivity increases as the temperature and frequency, because of the segmental mobility and electrical conduction.

تمت دراسة السلوك العازل الكهربائي والتوصيلية الكهربائية المتناوبة لراتنج الايبوكسي المضاف إليه حشوات اوكسيد التيتانيوم و اوكسيد الزنك بنسب وزنيه(5, 10, 15, 20, 25 wt.%.). أجريت القياسات العملية لسلوك العزل الكهربائي عند مدى الترددات (120Hz - 2MHz) ودرجة حرارة(30 – 110) oC . ان اختلاف السلوك العازل للمتراكبات المحضرة يعتمد على نوع ومحتوى الحشوة والتردد ودرجة الحرارة. أظهرت النتائج المختبرية بان سماحية العزل و فقد العازل تزداد بزيادة محتوى الحشوة والذي قد تعزى إلى ظهور الاستقطاب البيني، كذلك تزداد السماحية بزيادة درجة الحرارة نتيجة لزيادة حرية الحركة للسلاسل الجزيئية لثنائيات الأقطاب داخل الايبوكسي عند درجة حرارة عالية، وتقل السماحية بزيادة التردد بسبب الاستقطاب ألاتجاهي. كذلك تم الاستنتاج على إن الاسترخاء البيني يعتمد على الحجم ألدقائقي للحشوة. التوصيلية الكهربائية المتناوبة تزداد بزيادة درجة الحرارة والتردد بسبب حركة الشحنات الحرة و تيار التوصيل.


Article
Optical properties of TiO2 thin films prepared by reactive d.c. magnetron sputtering
الخصائص البصرية لاغشية TiO2المرسب بطريقة الترذيذ المغناطيسي

Loading...
Loading...
Abstract

TiO2 thin films were deposited by reactive d.c magnetron sputtering method on a glass substrate with various ratio of gas flow (Oxygen /Argon) (50/50, 100/50 and 150/50) at substrate temperature 573K. It can be observe that the optical energy gap of TiO2 thin films dependent on the ratio of gas flow (oxygen/argon), it varies between (3.45eV-3.57eV) also it is seen that the optical constants (α, n, K, εr and εi ) has been varied with the change of the ratio of gas flow (Oxygen /Argon).

رسبت اغشية Tio2بأستخدام طريقة الترذيذ المغناطيسي على ركائز من الزجاجية بنسبة مختلفة من تدفق غازات كل من (الاكسجين / الارجون) (50/150 و 50/100 و50/50) وفي نفس درجة حرارة الركيزة 573K. درست الخصائص البصرية لاغشية TiO2وتم تحليلها ووجد ان فجوة الطاقة الضوئية لاغشية ال TiO2 تعتمد على نسبة تدفق الغاز ( الاكسجين / الارجون ) ، حيث تتغاير ما بين (3.45eV-3.57eV) وكذلك وجد ان الخصائص البصرية (α , εi, εr, K , n) تتغير مع تغير نسبة تدفق الغازات ( الاكسجين / الارجون ).


Article
Synthesis and photocatalytic activity of TiO2 Nanoparticles

Authors: MAJEED A. SHAHEED --- FALAH H. HUSSEIN *
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2012 Volume: 22 Issue: 1 Pages: 423-433
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

Titanium dioxide (TiO2) nanoparticles have been synthesized by sol gel method. The synthesized nanoparticles followed by calcinations at different temperatures in the range 200-800°C for 2 hours. Both the evolution of the crystal size and nature of the phases were studied as a function of annealing temperatures. These materials display a good thermal stability up to 400°C, in term of crystal size, and up to 600°C, regarding the crystalline phase. The phase purity and crystallite size of as grown TiO2 particles were characterized via X-ray diffraction (XRD). The characterized results indicated that the synthesized TiO2 powders had a pure two phases anatase and rutile structures and the average particle sizes were about 5-53 nm.The synthesized TiO2 nanoparticles exhibited 1.0053% time higher photocatalytic activity for Bismarck Brown R than that of commercial Hombikate (UV100) .


Article
Effect substrate temperatures on the structural, morphology and optical properties of nanocrystalline TiO2 thin films prepared by PLD

Loading...
Loading...
Abstract

Titanium dioxide is a wide band semiconductor which exists in three crystallographic phases: rutile , anatase and brookite. The first two polymorphs have a tetragonal symmetry and due to their strong photocatalytic properties and stability have become materials of high scientific interest. TiO2 nanostructures , as they significantly reinforce the photocatalytic properties of titanium , are commonly used in optical devices, self-cleaning protective coatings

Listing 1 - 6 of 6
Sort by
Narrow your search

Resource type

article (6)


Language

English (6)


Year
From To Submit

2012 (6)