Study the Synergetic Activity of Aluminium Tri Hydroxide with Zinc Oxide as Flame Retardants for Unsaturated Polyester Resin
دراسة الفعل التازري لهيدروكسيد الالمنيوم مع اوكسيد الخارصين كمثبطات للهوبية البولي استر غير المشبع

Authors: Jalil R. Ugal --- Rawnaq B. Jimaa
Journal: journal of kerbala university مجلة جامعة كربلاء ISSN: 18130410 Year: 2012 Volume: 1 Issue: المؤتمر العلمي الاول للتربية للعلوم الصرفة Pages: 43-50
Publisher: Kerbala University جامعة كربلاء

Loading...
Loading...
Abstract

In this work, aluminum tri hydroxide (I), zinc oxide (II) and their mixture (1:1) (III) were used as flame retardants for unsaturated polyester resin in the weight ratios of (0, 2, 4, 7, 10, and 12) %, by preparing films of (130*130*3) mm in dimensions.Three standard test methods used to measure the flame retardation which are: ASTM: D-2863 to measure the limiting oxygen index (LOI), ASTM: D-635 to measure the rate of burning (R.B) & ASTM: D-3014 to measure the maximum height of flame (H). Results obtained from these tests indicated that; ATH, ZnO and their mixture have a good effect as flame retardants for unaturated polyester resin. The synergetic effect was the best.

في هذا البحث تم استخدام هيدروكسيد الالمنيوم (مضاف I), اوكسيد الخارصين(مضاف II) ومزيجهما بنسبة (1:1) مضاف (III) كمثبطات للهوبية البولي استر غير المشبع. بنسب مئوية وزنية (10, 7, 4, 2, 0و 12) % بواسطة تحضير شرائح بابعاد (130*130*3) ملم.استخدمت ثلاث طرق قياسية لاختبار تثبيط اللهوبية وهي: الطريقة القياسية (( LOI ASTM: D-2863 لقياس معامل الاوكسجين المحدد, الطريقة القياسية ASTM: D-635 لقياس سرعة الاحتراقوالطريقة القياسية ASTM: D-3014 لقياس اقصى ارتفاع يصل اليه اللهب(H) اظهرت النتائج المستحصل عليها ان المضافات المستعملة في هذه الدراسة تمتلك تاثير جيدا كمثبطات لهب للبولي استر غير المشبع. وان افضلها كانت عندما كان التاثيرتازريا


Article
Effect of carbon nanotube and Zn particles addition on the some mechanical properties and thermal conductivity of unsaturated polyester resin
تأثير انابيب الكاربون النانوية وجسيمات الخارصين المضافة على بعض الخواص الميكانيكية و معامل التوصيل الحراري لراتنج البولي استر غير المشبع

Authors: N.A.Ali نادية عباس علي --- S.I.Husaen سيناء ابراهيم حسين --- H.I.Jaffer حارث ابراهيم جعفر
Journal: Iraqi Journal of Physics المجلة العراقية للفيزياء ISSN: 20704003 Year: 2012 Volume: 10 Issue: 18 Pages: 98-104
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

In this research work a composite material was prepared contains a matrix which is unsaturated polyester resin (UPE) reinforced with carbon nanotube the percentage weight (0.1, 0.2, 0.4.0.5) %, and Zn particle the percentage weight (0.1, 0.2,0.4,0.5)%.All sample were prepared by hand lay-up, process the mechanical tests contains hardness test, wear rate test, and the coefficient of thermal conductivity. The results showed a significant improvement in the properties of overlapping, Article containing carbon nano-tubes and maicroparticles of zinc because of its articles of this characteristics of high quality properties led to an, an increase in the coefficient of the rmalconductivity, and increase the hardness values with increased percentage weight when the wear rate increase with increased the applied load and percentage weight.

تم في هذا البحث تحضيرمادة متراكبة من راتنج البولي استرغير المشبع مقواة بانابيب الكاربون النانوية وجسيمات الخارصين وبنسب وزنية 0.2)و0.4و0.8و(1%واستخدمت طريقة القولبة اليدوية في تحضير العينات واجريت اختبارات ميكانيكية تضمنت فحص الصلادة وفحص معدل البلى وقياس معامل التوصيل الحراري.اظهرت النتائج تحسنا كبيرا في خواص المادة المتراكبة الحاوية على انابيب الكاربون النانوية وجسيمات الخارصين لما تتمتع به هذه المواد من خصائص عالية الجودة ادت الى زيادة في معامل التوصيل الحراري وزيادة قيم الصلادة بزيادة النسب الوزنية ومعدل البلى كان يزداد بزيادة الحمل المسلط وزيادة النسب الوزنية .


Article
USING OF REINFORCING BY CARBON FIBERS TO IMPROVEMENT MECHANICAL PROPERTIES OF UNSATURATED POLYESTER RESIN
إستخدام التقوية بألياف الكاربون لتحسين الخواص الميكانيكية لراتنج البولي أستر غير المشبع

Author: علي جاهل سلمان
Journal: AL-TAQANI مجلة التقني ISSN: 1818653X Year: 2012 Volume: 25 Issue: 3 Pages: A1-A6
Publisher: Foundation of technical education هيئة التعليم التقني

Loading...
Loading...
Abstract

Studying the effect of reinforcement by carbon fibers as woven roving (°90-°0) with density (1.95 Kgm3) on mechanical properties of unsaturated polyester resin after reinforcing it by different percentage of fibers (20%, 40%,60%) and these properties included : impact strength , tensile strength , compression strength , flexural strength , and hardness . the Mechanical properties were carried out for unsaturated polyester resin before and after reinforcement by fibers, and studied the effect on the above mechanical properties as illustrated in the diagrams between mechanical properties and reinforcing percentage .


Article
Preparation a Composite Material (UP/Cann F) with Evaluation Its Toughness Under the Influence of Temperature and Humidity.
تحضير مادة مركبة من (راتنج البولي إستر المدعم بألياف القنب) ودراسة متانتها تحت تأثير درجات الحرارة والرطوبة

Author: Nasser A.M. Habib ناصر عبد الله محمد حبيب
Journal: Anbar Journal of Engineering Sciences مجلة الأنبار للعلوم الهندسية ISSN: 19979428 Year: 2012 Volume: 5 Issue: 2 Pages: 198-208
Publisher: University of Anbar جامعة الانبار

Loading...
Loading...
Abstract

In this research we have prepared a composite material by using Vegetative Cellulose Fibers of Cannabis (Cann F) to reinforced a matrix of Unsaturated Polyester (UP) resin. This kind of fibers is distinguished by good properties such as high tensile strength, low elongation, thermal resistance and low cost. The impact strength was tested by using Charpy method for three materials (UP resin), composite (UP / Cann F) and composite (UP/Glass F). The results indicated that the fracture energy (Uc) decreased as the notch depth (a) increased on the sample from (0.7 mm) up to (4.9 mm). However, the fracture energy increased as the temperature of the composite increased for different temperatures of (0, 35, 50 and 75) oC. It was noticed that the Material toughness (Gc) has been improved significantly, where in case of the composite (UP /Cann F), the improvement of (Gc) was from (2.45 kJ/m2 ) to (14.5 kJ/m2 ) and it was (17 kJ/m2 ) for composite (UP/GF) has been measured at (35) oC. When those composite materials (UP/Cann F) exposed to humidity for a period of (72 hrs) without immersion, their properties did not change, hence the effects are not of chemical but of physical nature. The conclusion, the difference between the toughness of the material (Gc) for the reinforced composites by Cannabis and E-glass fibers for all temperatures is not large, so this encourage the development of Cannabis fiber reinforced composites in the future to abundance, and low cost for industrial investment

مع زيادة الحاجة الى المواد المركبة Composite Materials في التطبيقات الصناعية الحديثة أصبح توفير المواد البديلة في تحضيرها أمر في غاية الأهمية لتقليل الكلفة والاحتفاظ بنفس المواصفات الهندسية العالية التي تتمتع بها تلك المواد في مقاومة ظروف الخدمة (الصدمة , الحرارة والرطوبة) . في البحث الحالي تم استخدام الياف نباتية من نوع القنب Cannabis في تقوية نوع من الراتنجات المصلدة حراريآResin Thermosetting هوالبولي استرغير المشبع(UP) Unsaturated Polyester , حيث تمتاز تلك الالياف بالمتانة العالية ومقاومتها للشد وقلة استطالتها وتحملها لدرجات الحرارة العالية بالاضافة الى وفرتها وكلفتها القليلة (وهو سبب اختيارها لمادة البحث). تم اختبار مقاومة الصدمة Impact Strength لثلاث أنواع من المواد (راتنج , راتنج مدعم بالياف القنب وراتنج مدعم بالياف زجاجية ) بطريقة Charpy وقياس طاقة الكسر Fracture Energy لها لحزوز Notches مختلفة العمق تراوحت بين (4.9-0.7)ملم ولدرجات حرارية مختلفة (75,50,35,0)مْ ، فقد لوحظ بأن الطاقة اللازمة للكسر لعينات من الراتنج (غير المدعم ) تزداد بنقصان عمق الحز وبزيادة درجة الحرارة وتبعآ لذلك تزداد متانة المادة (Gc)Fracture Toughness . أما في حالة تدعيم الراتنج بالياف القنب فأن الطاقة اللازمة للكسر ازدادت وبمقدار اكبر مما هو علية في عينات الراتنج غير المدعم حيث امتصت الالياف الجزء الاكبر من طاقة موجة الصدمة لذا زادت متانتها بمقدار كبير ولجميع درجات الحرارة ففي درجة حرارة المختبر (35)مْ زادت المتانة من 2.45 الى 14.5 كيلوجول/م2 عند تدعيمه بألياف القنب , ولغرض المقارنة كانت متانة الراتنج المدعم بالالياف الزجاجية أكبر من متانة الراتنج المدعم بالياف القنب بمقدار قليل حيث بلغت (17.1 كيلوجول/م2) لنفس درجة الحرارة نظرأ للمرونة والكثافة العاليتين التي تمتلكها الالياف الزجاجية لكنها مادة مكلفة وغير متوفرة . أما عند تعريض المادة المركبة للرطوبة ولفترات قصيرة (مامجموعه 72 ساعة رش بالماء دون غمرها) وجد أنها لاتتأثر لأن الرطوبة لاتدخل مع الراتنجات بعلاقة كيميائية بل تحدث تأثيرا قليلآ (غير سلبي ) على خواصها الفيزيائية .

Listing 1 - 4 of 4
Sort by
Narrow your search

Resource type

article (4)


Language

English (2)

Arabic (1)

Arabic and English (1)


Year
From To Submit

2012 (4)