Article
Refinement the Microstructure of Al–7Si Alloy by the Addition of Cadmium

Author: Sura Abd Al-Zahrah Muhsion
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2012 Volume: 20 Issue: 1 Pages: 62-66
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

Cadmium (Cd) modified aluminium–silicon cast alloys are well known for their outstanding mechanical properties as they combine excellent strength with good ductility that is due to a modification of brittle Si in the eutectic with traces of Cd (0.2–1.0 wt%). The results showed that the Cd leads to the refinement of eutectic silicon from ~95 to 10µm. The alloys which used in this work were Al-7Si alloy with additions of 0.2, 0.6 and 1 wt% Cd as well as Al-7%Si with out Cd addition. The effect of keeping time also studied and the results indicate that the addition of 1%Cd with keeping time 3min was the best (about 10 µm).

تكون مصبوبات سبائك الألمنيوم-سليكون، المعدلة بنيتها البلورية بإضافة كميات محسوبة من الكادميوم، ذات خواص ميكانيكية عالية. وهذه الخواص ناتجة عن الجمع بين المتانة العالية والمطيلية الجيدة والناتجة عن تعديل البنية البلورية لطور السليكون الايوتكتيكي من شكل رقائق أو صفائح هشة إلى شكل خيطي منتظم وذلك بفعل إضافة الكادميوم لغاية 1% كمعدل للبنية البلورية. تشير نتائج فحص البنية المجهرية لطور السليكون الايوتكتيكي إلى أن المصبوبة المضاف إليها كادميوم بنسبة 1% قد يصل تحول هذا الطور من شكل ابري أو رقائقي ذو طول حوالي 95 مايكرون إلى خيطي بطول حوالي 10 مايكرون . إن السبائك التي تم دراستها في هذا البحث هي ألمنيوم-7%سليكون بإضافة الكادميوم بنسب(0.2، 0.6 و 1.0%) إضافة إلى السبيكة الأصلية بدون إضافات. كذلك تم دراسة تأثير وقت الحفظ عند درجة حراة إضافة الكادميوم وقد أظهرت النتائج إن المصوبة التي أضيف لها الكادميوم بنسبة 1.0% ووقت حفظ 3 دقائق كانت هي الأفضل (طول السليكون الايوتكتيكي الخيطي10 مايكرون).


Article
Refinement the Microstructure of Al–7Si Alloy by the Addition of Cadmium

Author: Sura Abd Al-Zahrah Muhsion
Journal: Journal of University of Babylon مجلة جامعة بابل ISSN: 19920652 23128135 Year: 2012 Volume: 20 Issue: 1 Pages: 62-66
Publisher: Babylon University جامعة بابل

Loading...
Loading...
Abstract

Cadmium (Cd) modified aluminium–silicon cast alloys are well known for their outstanding mechanical properties as they combine excellent strength with good ductility that is due to a modification of brittle Si in the eutectic with traces of Cd (0.2–1.0 wt%). The results showed that the Cd leads to the refinement of eutectic silicon from ~95 to 10µm. The alloys which used in this work were Al-7Si alloy with additions of 0.2, 0.6 and 1 wt% Cd as well as Al-7%Si with out Cd addition. The effect of keeping time also studied and the results indicate that the addition of 1%Cd with keeping time 3min was the best (about 10 µm).

تكون مصبوبات سبائك الألمنيوم-سليكون، المعدلة بنيتها البلورية بإضافة كميات محسوبة من الكادميوم، ذات خواص ميكانيكية عالية. وهذه الخواص ناتجة عن الجمع بين المتانة العالية والمطيلية الجيدة والناتجة عن تعديل البنية البلورية لطور السليكون الايوتكتيكي من شكل رقائق أو صفائح هشة إلى شكل خيطي منتظم وذلك بفعل إضافة الكادميوم لغاية 1% كمعدل للبنية البلورية. تشير نتائج فحص البنية المجهرية لطور السليكون الايوتكتيكي إلى أن المصبوبة المضاف إليها كادميوم بنسبة 1% قد يصل تحول هذا الطور من شكل ابري أو رقائقي ذو طول حوالي 95 مايكرون إلى خيطي بطول حوالي 10 مايكرون . إن السبائك التي تم دراستها في هذا البحث هي ألمنيوم-7%سليكون بإضافة الكادميوم بنسب(0.2، 0.6 و 1.0%) إضافة إلى السبيكة الأصلية بدون إضافات. كذلك تم دراسة تأثير وقت الحفظ عند درجة حراة إضافة الكادميوم وقد أظهرت النتائج إن المصوبة التي أضيف لها الكادميوم بنسبة 1.0% ووقت حفظ 3 دقائق كانت هي الأفضل (طول السليكون الايوتكتيكي الخيطي10 مايكرون).


Article
Studying the effect of a new polyamide as adhesive for wood-wood surfaces

Authors: Mohammad N. AL-Baiati --- Laith B. AL-Asady --- Hawraa H. AL-Zubadi --- Saja A. Abd-Alkareem
Journal: journal of kerbala university مجلة جامعة كربلاء ISSN: 18130410 Year: 2012 Volume: 1 Issue: المؤتمر العلمي الاول للتربية للعلوم الصرفة Pages: 15-21
Publisher: Kerbala University جامعة كربلاء

Loading...
Loading...
Abstract

In this research, a new copolyamid was prepared from reaction Aceglutamide with Formaldehyde by esterfication process, and used this copolymer as adhesive between wood – wood surface. Five different weight ( 0.2, 0.4 , 0.6, 0.8 & 1.0 gm ) from the prepared copolymer respectively, were used as adhesive to prepared the specimens of wood / adhesive . Four standard test methods were used to measured the adhesion properties which are; ASTM: D-790, ASTM: D- 695, ISO – 179 &ASTM: D-638 .The results obtained from these tests indicated that, the specimens of wood / adhesive containing 1.0 gm from the prepared copolymer have high values in all standard tests; Impact strength was 45 MPa, Compressive strength was 40 MPa, Flexural strength was 250 MPa and Tensile strength was 8150.41 MPa ; compared with the other specimens which contain on less weight from the prepared copolymer.


Article
Polymerization and Synthesis of New Modified Methacrylic acid and Studying Some of their Properties
بلمرة وتخليق تحويرات جديدة لحامض الميثاأكريلك ودراسة بعض خواصه

Authors: Emad Taha Baker --- Ayad Sady Hameed --- Haitham Dalol Hanoon
Journal: journal of kerbala university مجلة جامعة كربلاء ISSN: 18130410 Year: 2012 Volume: 1 Issue: المؤتمر العلمي الاول للتربية للعلوم الصرفة Pages: 174-185
Publisher: Kerbala University جامعة كربلاء

Loading...
Loading...
Abstract

During this research, some chemical modifications have been done on linear polymethacrylic acid.Obviously, chemically modified polymers [6, 7, 8, 9, 10] have new different chemical and physical properties, with expected new industrial application. This research describes the synthesis of new modified polymers. Through the condensation of methacrylic polymer with appropriate acid hydrazide in the presence of phosphorus oxychloride. Where prepared many modified polymers in this method.The structures of these new modified polymers have been established on the basis of physical and spectral data (FT-IR and UV). Acid number, viscosity, molecular weight and swelling of the polymers were also determined.

خلال هذا البحث تم إجراء بعض التحويرات الكيميائية على بوليمرات الميثاكريلك، لغرض الحصول على بوليمرات محورة [6، 7، 8، 9، 10] والتي من المتوقع ان يكون لها خواص كيميائية وفيزيائية وكذلك تطبيقات صناعية جديدة تختلف عن البوليمر الأصلي، تم تحضيرالبوليمرات المحورة من خلال تفاعل التكاثف لبوليمرات الميثاكريلك مع هيدزيدات الحوامض المناسبة بوجود اوكسي كلوريد الفسفوريل، حيث تم تحضير عدد من البوليمرات باستخدام هذه الطريقة.تم التأكد من صحة التراكيب المقترحة للبوليمرات بواسطة استخدام الطرق الطيفية (طيف الأشعة تحت الحمراء وطيف الأشعة فوق البنفسجية) والقياسات الفيزيائية. كذلك تم تعين العدد الحامضي، اللزوجه، الوزن الجزيئي والأنتفاخ للبوليمر [10].


Article
Effect of Thermal and Wet Chemical Treatments on The Electrical Conductivity of Active Carbon
تاثير المعالجة الحرارية والكيميائية الرطبة على توصيلية الكاربون المنشط

Loading...
Loading...
Abstract

Abstract Activated carbon is a weak conductor 18x10-3 Sm-1 , it's electrical conductivity could be enhanced either by heating the specimen in an open oven to a temperature of 100 to 600 oC ,or by different wet chemical treatments including: acids, organic solvents, reducing agents, oxidizing agents, and finally consecutive chemical treatments .The electrical conductivities were increased compared to the untreated specimens as follow: Acids( HCl 60.3% , Nitric 55.2%. Sulfuric 48.7%,Phosphoric 41%. Acetic 15.4% ). Organic solvents( Chloroform 45.9%,Acetone 34.5%,Diethyl ether 3.1%.Cyclohexane26.3%).Reducing agents (Sodium borohydride 57.5%, Zinc chloride/ HCl 40.9%).Hummer's Reagent 42.2% . Bromine 27.2% . Consecutive treatments a)Solvent – Oxidizing agent –Reducing agent 70.9%.b) Solvent –Reducing agent –Oxidizing agent 69.2 %.Heat / Air (100 oC: 9%,250 oC : 18.1%, 350 oC: 26.1%, 450 oC 36.3% , 600 oC: 45.4%Sample treated with sodium borohydride shows a highest pore area 222.87 g m-2 compared to untreated specimen 153.76 g m-2 and that treated with hydrochloric acid 171.27 g m-2. XRD, ATR, FT-IR and TGA techniques were implemented to monitor structural changes induced by above mentioned treatments.

الخلاصة الكاربون المنشط موصل ضعيف 1.8×10–3 Sm–1غير ان توصيليته الكهربائية يمكن تحسينها اما بتسخين النموذج في فرن مفتوح بدرجة حرارة بين 100 الى600 درجة مئوية , او بواسطة المعالجات الكيميائية الرطبة والمتضمنة : الحوامض والمذيبات العضوية والعوامل المختزلة والعوامل المؤكسدة او سلسلة من المعالجات المتعاقبة . ازدادت التوصيلية الكهربائية مقارنة بالعينات غير المعالجة بالحوامض كما ياتي ( حامض الهيدروكلوريك 60.3%،والنتريك 55.2% , والكبريتيك 48.7% , والفسفوريك 41% ، والخليك 15.4 % ) وفي المذيبات العضوية كما ياتي ( الكلروفورم 45.9 % ، والاسيتون 34.5 % ، والاثيل ايثر 3.1 % ، والسايكلوهكسان 26.3 % ) وبالعوامل المختزلة كما ياتي ( هايدروبورات الصوديوم 57.5 % ، وكلوريد الزنك / حامض الهيدروكلوريك 40.9 % ، وكاشف همر 42.2 % ، والبروم 27.2 % ، والمعالجات المتعاقبة با لكواشف (ا) مذيب ، مؤكسد ، مختزل 70.9 % و(ب) مذيب مختزل مؤكسد 69.2 % . اما المعالجة بالهواء/ حرارة فكانت 100 م: 9 % ، 250 م : 18.1 % ، 350 م : 26.1 % ، 450 م : 36.3 % 600 م : 45.5 % .اظهرت النماذج المعالجة ببوروهيدريد الصوديوم اعلى مساحة للمسامات (222.87 غم / م2 ) مقارنة بالغير معالجة ( 153.76 غم / م2 ( وبذلك المعالج بحامض الهيدروكلوريك 171.27 غم / م2 .تم توضيف حيود الاشعة السينية ، مطيافية الاشعة تحت الحمراء ، التحليل الحراري التفاضلي لمسح التغيرات التركيبية المحتثة بالمعالجات المذكورة.

Listing 1 - 5 of 5
Sort by
Narrow your search

Resource type

article (5)


Language

English (5)


Year
From To Submit

2012 (5)