Influence of substrate temperature on structural and optical properties of SnO2 films
تأثير درجة حرارة الأرضية على الخواص التركيبية والبصرية لأغشية SnO2الرقيقة

Loading...
Loading...
Abstract

Tin Oxide (SnO2) films have been deposited by spray pyrolysis technique at different substrate temperatures. The effects of substrate temperature on the structural, optical and electrical properties of SnO2 films have been investigated. The XRD result shows a polycrystalline structure for SnO2 films at substrate temperature of 673K. The thickness of the deposited film was of the order of 200 nm measured by Toulansky method. The energy gap increases from 2.58eV to 3.59 eV when substrate temperature increases from 473K to 673K .Electrical conductivity is 4.8*10-7(.cm)-1 for sample deposited at 473K while it increases to 8.7*10-3 when the film is deposited at 673K

تم ترسيب اغشية (SnO2) بطريقة الرش الكيميائي عند درجات حرارة ارضية مختلفة وقد تمت دراسة تاثير تغيير تلك الدرجات الحرارية على تركيب الاغشية وخصائصها البصرية والكهربائية. أظهرت نتائج حيود الاشعة السينية ان الاغشية المحضرة عند درجة حرارة ارضية (673K) كانت ذات تركيب متعدد البلورات. كان سمك الاغشية المحضرة بحدود (200nm) وقد تم قياسها بطريقة تولانسكي(Toulansky). ازدادت فجوة الطاقة البصرية من 2.58 الى 3.59 الكترون-فولت .كما ان التوصيلية الكهربائية ازدادت من 4.8*10-7(ohm.cm)-1 الى 8.7*10-3 (ohm.cm)-1 عند زيادة درجة حرارة الارضية من 473K الى 673K.

Listing 1 - 1 of 1
Sort by
Narrow your search

Resource type

article (1)


Language

English (1)


Year
From To Submit

2012 (1)