Effect of Metakaolin on Properties of Lightweight Porcelinate Aggregate Concrete

Authors: Nada M. Fawzi --- Kalil I. Aziz --- Sheelan M. Hama
Journal: Journal of Engineering مجلة الهندسة ISSN: 17264073 25203339 Year: 2013 Volume: 19 Issue: 4 Pages: 439-452
Publisher: Baghdad University جامعة بغداد

Loading...
Loading...
Abstract

Research in Iraq has expanded in the field of material technology involving the properties of the lightweight concrete using natural aggregate. The use of the porcelinate aggregate in the production of structural light concrete has a wide objective and requires a lot of research to become suitable for practical application. In this work metakaolin was used to improve compressive strength of lightweight porcelinate concrete which usually have a low compressive strength about 17 MPa . The effect of metakaolin on compressive, splitting tensile, flexure strengths and modulus of elasticity of lightweight porcelinate concrete have been investigated. Many experiments were carried out by replacing cement with different percentages of metakaolin. The metakaolin was replaced by 5%, 10%, 15% and 20%. A control reference mix without metakaolin was made for comparison purpose. For all mixes, compressive, splitting tensile, flexure strengths and modulus of elasticity were determined at 28-day. The results showed that the using of metakaolin improve the compressive, splitting tensile, flexure strengths and modulus of elasticity of lightweight porcelinate concrete. The higher compressive, splitting tensile, flexure strengths and modulus of elasticity were found for 15% metakaolin.

توسعت البحوث في العراق في حقل تكلنوجيا المواد من ضمنها دراسة خواص الخرسانة خفيفة الوزن باستخدام ركام طبيعي. استخدام البورسلينايت كركام خفيف الوزن في انتاج خرسانة انشائية يتطلب العديد من الدراسات لفهم وتحسين خواصها لتصبح مناسبة للتطبيقات العملية. في هذه الدراسة استخدمت مادة ميتاكاؤلين كنسبة مئوية مِنْ وزنِ سمنت، لتحسين خواص خرسانة البورسلينايت الخفيفة الوزن التي تمتاز عادة بمقاومة انضغاط واطئة حوالي 17 ميكاباسكال. تم دراسة تاثير اضافة ميتاكاؤلين على كل من مقاومة الانضغاط, مقاومة الانفلاق, معامل التصدع, و معامل المرونة للخرسانة البورسلينايت الخفيفة الوزن. وقد استبدل جزء من السمنت بالنسب التالية من ميتاكاؤلين: 5%, 10%, 15%, و 20% من وزن السمنت, بالاضافة الى الخلطة المرجعية بدون اضافات لغرض المقارنة. لكل الخلطات تم قياس كل من مقاومة الانضغاط, مقاومة الانفلاق, معامل التصدع, و معامل المرونة بعمر 28 يوم. وقد وجد بان اسبتدال نسبة 15% من سمنت بميتاكاؤلين تحسن مقاومة الانضغاط, مقاومة الانفلاق, معامل التصدع, و معامل المرونة.


Article
EVALUATION OF TELLOL AL-KIEND CLAY IN MOSUL CITY FOR THE PRODUCTION OF LIGHT WEIGHT AGGREGATES

Authors: Doaa M. Hammed --- Mayada S. Joodi --- Abdul Wahab AR. Al-Ajeel
Journal: Iraqi Bulletin of Geology and Mining مجلة الجيولوجيا والتعدين العراقية ISSN: 18114539 Year: 2013 Volume: 9 Issue: 2 Pages: 151-160
Publisher: Ministry of Industry and Minerals وزارة الصناعة والمعادن

Loading...
Loading...
Abstract

In this research a representative sample from Tellol Al-Kiend clay deposit (Injana Formation), Naenava Governorate, Iraq, was evaluated for lightweight aggregates preparation. Two methods of heat treatment were carried out. Iso-thermal treatment conducted at (1180 – 1200) °C range, for aggregates made from clay only, using different socking time. Whiles, rapid (or flush) firing, were carried out at 1200 °C, for aggregates made from clay with different types and amounts of additives (dolomite, waste engine oil, and straw). The iso-thermal tests reveal that bloating can occurs at 1180 °C only for 45 minutes holding time. The aggregates obtained, have a specific gravity of about 1.38 and 0.8% water absorption. In rapid firing, it was found that, the bloating of the clay can be significantly improved by the addition of dolomite. The results obtained indicated that aggregates having 1.35 specific gravity with about 1% water absorption value could be produced from aggregates made of clay and 5 wt.% dolomite. The firing time has been about 5 minutes. Thereupon, it can be suggested that, Tellol Al-Kiend clay can be used for the production of lightweight aggregates by rapid firing. Concrete made from these lightweight aggregates shows a compressive strength (28 days) of about 173 kg/cm2, which can be designated as structural and insulating concrete.

جرى في هذا البحث تقييم نموذج ممثل لترسبات أطيان تلول الكند (تكوين إنجانة) في محافظة نينوى لإنتاج الركام الخفيف، وجربت طريقتان للمعالجة الحرارية. جرى في الطريقة ألأولى معالجة الركام المحضر من الطين فقط في درجات حرارة تتراوح مابين (1180 ـ 1200) °م وزمن استبقاء مختلف. أما الركام المحضر من الطين مع كميات وأنواع مختلفة من المواد المضافة (دولومايت، مخلفات زيت المحركات والقش) فقد تم معالجتها بالحرق السريع (أو المفاجئ) عند درجة حرارة 1200 °م مع زمن استبقاء 2 أو 3 دقائق. بينت نتائج حرق الركام المحضر من الأطيان فقط بأن الانتفاخ يمكن أن يحصل فقط عند حرارة 1180 °م وبزمن استبقاء 45 دقيقة، وإن الركام الناتج من هذه العملية أعطى كثافة نوعية بحدود 1.38 ونسبة امتصاص للماء 0.8%. ولكن وجد أنه باستخدام الحرق المفاجئ فإن انتفاخ ركام الطين يتحسن بشكل ملحوظ عند إضافة الدولومايت وبينت النتائج المستحصلة من هذه العملية إمكانية إنتاج ركام يمتلك كثافة نوعية بحدود 1.35 ونسبة امتصاص للماء 1% عند إضافة 5% وزناً من الدولومايت للطين وإن الزمن اللازم للحرق هو بحدود 5 دقائق. وعليه يمكن استخدام أطيان تلول الكند في إنتاج الركام الخفيف بإتباع الحرق السريع. كما بينت نتائج فحص الكونكريت المحضر من الركام الخفيف بأن مقاومة الانضغاط بعد 28 يوم بحدود 173 كغم/ سم2 والذي يمكن أن يستخدم في تحضير الخرسانة الإنشائية العازلة.


Article
Effect of Plastic Fibers on Properties of Foamed Concrete
تأثير الألياف البلاستيكية على خواص الخرسانة الرغوية و الخفيفة الوزن

Authors: Hisham K. Ahmed --- Waleed A. Abbas --- DohaM. Abdul-Razzaq
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2013 Volume: 31 Issue: 7 Part (A) Engineering Pages: 1313-1330
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

The main objective of this work is to study the effect of adding plastic fibers on Lightweight Aggregate Foamed Concrete (LWAFC) using mix proportion of 1:2.6:0.4 by volume (cement: fine Porcelanite: coarse Porcelanite) with 2% foaming agent by weight of water, and using sand as a partial and total replacement of local Porcelanite aggregate in that mix. The properties of lightweight aggregate foamed concrete reinforced with different percentages of plastic fiber (0.5, 0.75, and 1% by volume) were studied. Compressive strength, splitting tensile strength, flexural strength, dry density, initial surface absorption, water absorption, ultrasonic pulse velocity, acoustic impedance, and impact resistance tests were conducted on mixes at ages of 7, 28, and 60 days. The results showed a significant increasing in impact resistance, splitting tensile strength, and water absorption 34.55%, 4.2%, 326%, and 27.3% respectively. While the results indicated that the compressive strength, ultrasonic pulse velocity, dry density and acoustic impedance of the composites were reduced when the crimped plastic fiber volume fraction increases. The percentage of reduction of these properties was 15%, 11.1%, 6.23%, and 12.55% respectively.

إن الهدف الرئيسي لهذا البحث هو دراسة تأثير إضافة الالياف البلاستيكية على الخرسانة الرغوية الخفيفة الوزن باستعمال نسب خلط حجمية 1 ، 2.6 ، 0.4 (سمنت : بورسيلانايت ناعم : بورسيلانايت خشن) وباضافة 2% من المادة الرغوية كنسبة وزنية من الماء وباحلال الرمل كبديل جزئي أو كلي من ركام البورسيلانايت المحلي في الخلطة. تمت دراسة استعمال الالياف البلاستيكية بنسب حجمية مختلفة ( 0.5 ، 0.75 ، 1.0% ) لتسليح الخرسانة الرغوية الخفيفة الوزن. تم إجراءفحوصات مقاومة الانضغاط و مقاومة الشد و فحص الانثناء و مقاومة الصدم والكثافة الجافة و الامتصاص السطحي الاولي و الامتصاص الكلي وسرعة الذبذبات الفوق الصوتية والمعاوقة الصوتية للخلطات بأعمار 60،28،7 يوماً. بينت النتائج زيادة ملحوظة في مقاومة الصدم و مقاومة شد الانفلاق و امتصاص الماء و التي بلغت 34.55% , 4.2%, 27.3% على التوالي مع زيادة محتوى الالياف على الرغم من تسجيل انخفاض في مقاومة الانضغاط و الذبذبات فوق الصوتية و الكثافة الجافة و المعاوقة الصوتية مع زيادة محتوى الالياف. وقد بلغ مقدار الأنخفاض في هذه الخصائص 15%, 11.1%, 6.23%, 12.55% على التوالي.


Article
High performance lightweight concrete reinforced with glass fibers
الخرسانة الخفیفة الوزن العالیة الاداء المسلحة بالألیاف الزجاجیة

Authors: Eethar Thanon Dawood ایثار ذنون داؤد --- Ali Jihad Hamad علي جھاد حمد
Journal: AL-MANSOUR JOURNAL مجلة المنصور ISSN: 18196489 Year: 2013 Issue: 20 Pages: 73-87
Publisher: Private Mansour college كلية المنصور الاهلية

Loading...
Loading...
Abstract

This paper demonstrates the effect of glass fibers on mechanical properties of highperformance lightweight concrete which are: compressive strength, flexural strength,workability (flow), and density. Foam agent was used to produce lightweight concreteusing different mix proportion to obtain good workability and compressive strengthwith least fresh density. Superplasticizer used in some mixes about 1% by weight ofcement. Glass fibers were added in different volume fraction 0.06, 0.2, 0.4, and 0.6%for foam concrete and foam concrete with superplasticizer. The results of foamedconcrete mixes indicate that the increase of glass fibers content can produce highperformance lightweight concrete and improve the mechanical properties of suchconcrete. The compressive and flexural strength increased with the increase of glassfibers with acceptable range of workability, addition 0.6% of glass fibers increase33.7% and 16.1% of compressive and flexural strength respectively but the flowreduced about 38% compare without glass fibers.

ھذا البحث یتناول استخدام الالیاف الزجاجیة وتاثیرھا على الخصائص المیكانیكیة للخرسانة الخفیفةالوزن عالیة الاداء. تم دراسة الخصائص المیكانیكیة وھي مقاومة الانضغاط ومقاومة الانحناء وقابلیةالتشغیل (الانسیابیة) والكثافة. الخرسانة الرغویة استخدمت لانتاج خرسانة خفیفة الوزن بنسب مختلفةللحصول على مقاومة انضغاط وقابلیة تشغیل مناسبة مع تقلیل الكثافة. الملدن المتفوق استخدم بنسبة%1 من وزن السمنت. الالیاف الزجاجیة استخدمت كنسب حجمیة وكانت كالاتي : 0.4 0.2 0.06 و%0.6 . النتائج اوضحت بان الخرسانة الرغویة تحسنت بشكل واضح باستخدام الالیاف الزجاجیةوخاصة مقاومة الانضغاط ومقاومة الانحناء ,حیث ان اضافة 0.6 % من الالیاف الزجاجیة سوف یحسن% من مقاومة الانضغاط بنسبة زیادة 33.7 % وكذلك تحسن في مقاومة الانحناء بنسبة زیادة 16.1مقارنة مع الخرسانة التي لاتحتوي على الالیاف الزجاجیة ولكن من جھة اخرى سوف تقل قابلیة التشغیل.% بنسبة 3


Article
Pretreatment of Sawdust for Producing Sawdust Concrete
المعالجة المسبقة للنشارة في انتاج خرسانة نشارة الخشب

Author: Haitham H. Saeed
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2013 Volume: 31 Issue: 3 Part (A) Engineering Pages: 541-549
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Sawdust concrete has some shortcomings due to the harmful effects of some organic soluble components existing in the sawdust which affects setting and strength of sawdust concrete. Also, volume changes of sawdust as an aggregate due to variation of moisture content, cause large volume changes in the sawdust concrete. In this work, sawdust was treated before using as an aggregate for making sawdust concrete. The treatment included boiling the sawdust in water containing hydrated lime in order to dissolve all soluble organic components. To reduce water absorption of sawdust, it was dried and treated with waterproofing material. Two types of waterproofing materials were used (cutback asphalt and classic varnish). The properties of sawdust concrete were highly improved using pretreated sawdust. The increase of compressive strength was up to 50% for moderate sawdust ratios. Flexural strength is also increased, water absorption and thermal conductivity were highly reduced, while the basic advantages of sawdust concrete such as lightness of weight, sawability and nailability were not affected.

خرسانة نشارة الخشب لها بعض السلبيات بسبب احتواء النشارة على بعض المواد الضارة ذات الطبيعة العضوية و القابلة للذوبان في الماء والتي تؤثر على تصلب و مقاومة خرسانة نشارة الخشب. كما ان التغيرات الحجمية للنشارة الناجمة عن تغير محتوى الرطوبة فيها تسبب تغيرات حجمية في الخرسانة التي تحتوي على هذه النشارة. في هذا البحث تمت معالجة نشارة الخشب قبل استخدامها كركام في الخرسانة. تضمنت عملية المعالجة غلي النشارة في ماء يحتوي على الجير المطفأ لغرض اذابة و التخلص من كل المواد الضارة الموجودة في النشارة. ولغرض تقليل امتصاص النشارة للماء, تمت معالجة النشارة بعد تجفيفها بمواد مانعة للرطوبة. تم استخدام نوعين من المواد المانعة للرطوبة وهما الزفت القيري و الورنيش التقليدي. و من خلال البحث وجد ان خواص خرسانة نشارة الخشب تحسنت بشكل كبير باستخدام نشارة معالجة حيث ارتفعت مقاومة الانضغاط بحدود 50% بخلط نسب متوسطة من النشارة. كذلك فان نسبة امتصاص الماء والتغيرات الحجمية قلت بشكل ملحوظ, بينما لم تتأثر الايجابيات و الميزات الاساسية لخرسانة نشارة الخشب - كخفة الوزن و امكانية قصها بالمنشار و دق المسامير فيها- بالمعالجة.

Keywords

pretreatment --- sawdust --- concrete --- lightweight --- lime --- cutback --- asphalt --- varnish.


Article
Some properties of accelerated cured no fine Lightweight concrete
بعضخصائصالخرسانة خفیفة الوزن الخالیھ من الركام الناعم المعجلة الانضاج

Author: Zena K.A.Al Anbori زینة خضیر عباس
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2013 Volume: 31 Issue: 13 Part (A) Engineering Pages: 213-224
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Thermal insulation is one of the main problems facing the engineers working inbuilding and housing sector spatially for the high summer temperature in the mostArab Gulf and spatially in Iraq, so the study of lightweight aggregate thermalinsulation (No fine concrete) is important. The experimental work consist of concretemixes (cement: porcelinite aggregate) ratios (1:4), (1:5) and (1:6) and for each mixescement content changes (200, 300 and 400) Kg/m3. Dependence on mixing (1:5) andcement content (300Kg/m3) change the water to cement ratio (0.4, 0.45 and 0.5) byweight. The research presents the tests of density, absorption, porosity, ultrasonicpulse velocity, accelerated compressive strength according to British standard (BS1881: Part 112: 1983), normal compressive strength at 7, 28 and 90-day. Light weightconcrete was obtained of density ranging from (721-770) kg/m3 and thermalconductivity ranging from (0.17- 0.24) W/ (m.K). The good correlation betweenaccelerated compressive strength at one day with normal compressive strength at 28-day is approximately (0.245 ±0.005) for water bath at 55°C and (0.335±0.05) forwater bath at 82°C.


Article
Effect of glass fibers on mechanical properties of structural lightweight foamed concrete(SLFC)
تأثير اضافة الالياف الزجاجية على الخصائص الميكانيكية للخرسانة الرغوية الخفيفة الوزن الانشائية

Authors: Eethar Thanon Dawood --- Ali Jehad Hamad
Journal: University of Thi-Qar Journal for Engineering Sciences مجلة جامعة ذي قار للعلوم الهندسية ISSN: 26645564/26645572 Year: 2013 Volume: 4 Issue: 3 Pages: 110-128
Publisher: Thi-Qar University جامعة ذي قار

Loading...
Loading...
Abstract

Lightweight foamed concrete exhibits many advantages and excellent features comprising more efficient strength-to-weight ratio in structural elements, high strength, reduced dead load, decrease foundation loads, energy saving, waste consuming, temperature conservation, and noise insulation. This work was prepared to investigate the effect of glass fibers on mechanical properties of structural lightweight foamed concrete (SLFC), Foam agent (organic material) was used to produce SLFC using different mix proportions to obtain structural compressive strength and high workability with slightest fresh density. Five mixes of SLFC with Superplasticizer is experimentally studied, also five mixes without Superplasticizer were tested. The compressive strength, flexural strength, ultrasonic pulse velocity (UPV), workability (flowability) and density were measured. Superplasticizer used in some mixes was 1% by weight of cement. Glass fibers were added in different volume fraction for SLFC and SLFC with superplasticizer. The volume fractions of the glass fibers used are: 0.06, 0.2, 0.4, and 0.6 % total volume. The results of SLFC mixes showed that the increase of glass fibers content can produce foam concrete with enhanced mechanical properties. For all percentages of glass fibers in the mixes it increases in compressive strength and flexural strength. But the increase in compressive strength was 51% for 0.6% glass fibers. Also the flexural strength increased 19.2% for 0.6% glass fibers. The compressive and flexural strength increased with the increase of glass fibers with acceptable range of workability.

الخرسانة الرغوية الخفيفة الوزن لها العديد من الايجابيات والخصائص والتي تتضمن: مقاومة عالية مقارنة بوزن العنصر الانشائي و تقلل من الحمل الميت و تقليل الاحمال على الاسس و استخدام المخلفات و هي عازلة للحرارة والصوت. ان هذا البحث يهدف الى دراسة تأثير الالياف الزجاجية على الخصائص الميكانيكية للخرسانة الرغوية الخفيفة الوزن الانشائية. استعمل العامل الرغوي للحصول على خرسانة رغوية الخفيفة الوزن الانشائية, حيث تم عمل عدة نسب خلط للوصول او الحصول على مقاومة انضغاط انشائية مع قابلية تشغيل عالية وبأقل كثافة. خمس نسب خلط للخرسانة الرغوية الخفيفة الوزن الانشائية مع الملدن المتفوق وخمس نسب خلط اخرى للخرسانة الرغوية الخفيفة الوزن الانشائية بدون الملدن المتفوق , كل هذه الخلطات اجريت عليها فحص مقاومة الانضغاط وفحص مقاومة الانحناء و فحص سرعة الموجات فوق الصوتية وقياس قابلية التشغيل والكثافة. استخدم الملدن الفائق بنسبة 1% من وزن السمنت. كانت نسبة الالياف الزجاجية المضافة للخرسانة الرغوية الخفيفة الوزن الانشائية مع الملدن الفائق و الخرسانة الرغوية الخفيفة الوزن الانشائية بدون الملدن الفائق هي 0.06 و 0.2 و 0.4 و 0.6% من الحجم الكلي للخرسانة. النتائج اوضحت ان اضافة الالياف الزجاجية للخرسانة الرغوية الخفيفة الوزن الانشائية يحسن من مقاومة الانضغاط بنسبة 51% بنسبة الياف زجاجية 0.6% مقارنة مع الخلطة التي بدون الياف زجاجية. كذلك بالنسبة لمقاومة الانحناء تحسنت بنسبة 19.2% عند اضافة 0.6% من الالياف الزجاجية. وكذلك بالنسبة لباقي نسب الخلط حيث ان مقاومة الانضغاط والانحناء لكل النسب ازدادت بزيادة نسبة الالياف الزجاجية اي ان اضافة الالياف الزجاجية الى الخرسانة الرغوية الخفيفة الوزن الانشائية سوف يحسن من مقاومة الانضغاط ومقاومة الانحناء مع الحفاظ على قابلية التشغيل.


Article
Using the Fly Ash to Reduce the Steel Corrosion in Lightweight Concrete
أستعمال ( الرماد الطائر) لتقليل تأكل حديد التسليح في الخرسانة الخفيفة الوزن

Author: Wasan Q. Fayyadh وسن قاسم فياض
Journal: Univesity of Thi-Qar Journal مجلة جامعة ذي قار العلمية ISSN: 66291818 Year: 2013 Volume: 8 Issue: 3 Pages: 165-177
Publisher: Thi-Qar University جامعة ذي قار

Loading...
Loading...
Abstract

The aim goal of this research was to study the effect of using the fly ash to reduce the steel corrosion in lightweight concrete. The test which adopted was compressive strength test, Rapid chloride permeability test and electrochemical parameters test. In the compressive strength test found that adding the fly ash to concrete with change the water-cement ratio to product the same value of workability this addition lead to reduce the compressive strength test with increased the fly ash ratio, the compressive strength value was (31MPa to 44 MPa) and this value is above the (30 MPA) which recommended to use it in construction. In the Rapid chloride permeability test found with increasing the fly ash ratio the permeability became lower. In the electrochemical parameters test found that increasing the fly ash ratio lead to increase the parameters which increased the steel protection from the corrosion in lightweight concrete.

الهدف من هذا البحث هو دراسة أضافة الرماد الطائر الى الخرسانة الخفيف الوزن لتقليل التآكل في حديد التسليح حيث أظهرت نتائج الأختبارات التي أجريت وهي فحص مقاومة الأنضغاط وفحص النفاذية السريعة للكلورايد وفحص العوامل الكهروكيميائية للخرسانة الخفيف الوزن. حيث أظهر فحص مقاومة الأنضغاط أن أضافة الرماد الطائر ألى الخرسانة مع تغيير نسبة الماء إلى السمنت لجعل قابلية التشغيل ذات قيم متقاربة للخلطات بجميع النسب، أن هناك أنخفاض في مقاومة الأنضغاط كلما زادت نسبة الرماد الطائر ولكن القيم بقيت ضمن الحدود المطلوبة في المنشأت وهي أعلى أو تساوي (30MPA ) حيث كانت القيم تتراوح بين (31MPa إلى 44MPa). في فحص النفاذية السريعة للكلورايد أظهرت التجارب أنه كلما أزدادت نسبة الرماد الطائر المضاف إلى الخرسانة قلت النفاذية. من فحص العوامل الكهروكيميائية وجد ان أضافة الرماد الطائر يزيد من معدل العوامل التي تزيد من حماية الحديد الموجود في الخرسانة ضد التآكل.


Article
Compressive Strength of Lightweight Porcelanite Aggregate Concrete -New Formulas
مقاومة إنضغاط خرسانة البورسيلانايت خفيفة الوزن – معادلات جديدة

Authors: Nabeel A-M. Al-Bayati --- Kaiss F. Sarsam --- Ihsan A. S. Al-Shaarbaf
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2013 Volume: 31 Issue: 10 Part (A) Engineering Pages: 1897-1913
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

From the various kinds of concrete, lightweight concrete (LWC) is one of the most interesting subjects for researchers because of its advantages such as the savings in concrete member size, reinforcement, formwork and scaffolding , foundation costs as well as the savings derived from the reduced cost of transport and erection. The reduction of dead load due to a lower density of concrete allows for smaller and lighterweight structural members. Reductions in the dimensions of columns and beams result in more available space, and reductions in their selfweight can improve the seismic resistance capacity of building structures. Furthermore, better fire resistance, heat insulation, sound absorption, frost resistance, and increased damping are other advantages of lightweight concrete. Lightweight aggregate concrete (LWAC) is not new in concrete technology; it has been used since ancient times. The fact that some of these structures are still in good condition validates the durability of concrete. The paper presents the results of testing 30 specimens (15 cylinders and 15 cubes) according to ASTM for determining the mechanical properties of sand lightweight aggregate concrete (SLWAC)made from Porcelanite (as a natural local material). The paper further presents new empirical predicted formulas for cylinder compressive strength, cube compressive strength; and relationship between them.

من بين ألانواع المختلفه من الخرسانه تعتبرالخرسانه خفيفة الوزن(LWC) من أكثر المهمة المواضيع إثاره للاهتمام للباحثين بسبب مزاياها مثل التوفير في كمية خرسانة الصب، حديد التسليح, قالب الصب، وتكاليف الأساس، فضلا عن التوفير المستمد من انخفاض تكلفة النقل والإنشاء. التقليل من الحمل الميت نتيجة لانخفاض كثافة الخرسانه تسمح بتقليل أبعاد مقاطع الأعضاء الهيكليه. نتيجة إجراء هذه التخفيضات في أبعاد الأعمده والعتبات سوف يوفر المزيد من الحيز المتاح، وتحسين قدرة مقاومة الزلازل لهياكل المنشأ. وعلاوه على ذلك، تحسين مقاومة الحريق، العزل الحراري، وامتصاص الصوت، ومقاومة الصقيع، وكذلك زيادة التخميد التي تعتبر من المزايا الأخرى للخرسانة خفيفة الوزن. والخرسانة خفيفة الوزن (LWAC) ليست جديده في مجال تكنولوجيا الخرسانه، إلا أنها استخدمت منذ القدم. من المعلوم أن بعض هذه الهياكل الخرسانيه لا تزال في حاله جيده من سلامة وقوة التحمل مع مرور الزمن. يقدم البحث نتائج اختبار 30 عينه خرسانيه تتضمن (15 اسطوانه و 15 مكعب) وفقا للمواصفات الاميركيه لفحص المواد ASTM لتحديد الخواص الميكانيكية للخرسانه خفيفة الوزن (SLWAC) مصنوعه من البورسيلانايت (صخور طبيعية محلية). كذلك يعرض البحث الصيغ الجديده التجريبيه لتوقع مقاومة انضغاط, عينة الاسطوانة, مقاومة انضغاط عينة المكعب والعلاقة بينهما.


Article
Acidic Attack Resistance of Lightweight Concrete with SF
مقاومة الخرسانة خفيفة الوزن والحاوية على ابخرة السليكا للحوامض

Author: Aziz Ibrahim Abdulla عزيز ابراهيم عبدالله
Journal: Journal of Engineering and Sustainable Development مجلة الهندسة والتنمية المستدامة ISSN: 25200917 Year: 2013 Volume: 17 Issue: 2 Pages: 1-21
Publisher: Al-Mustansyriah University الجامعة المستنصرية

Loading...
Loading...
Abstract

Present research includes studying the effect of hydrochloric acid, sulfuric acid, and hydrochloric + sulfuric acid solutions on the lightweight concrete. The lightweight concrete produced in two ways first by the use of lightweight aggregate and the second using foam. Also studied the effect of the use of silica fume with or without a supeplasticizer in the ultra-lightweight concrete on the resistance to acids solution. The author proposed to use a new method to measure the effect of acid on the concrete in addition to the traditional way, as has been proposed the introduction of hammer test to measure the resistance of hardened concrete. The study has produced important conclusions about the effect of acid on the light-weight concrete with or without additives. Although the use of silica fume increases the resistance of concrete, it's not working always to increase its resistance to acids, but on the contrary may reduce resistance to acids, especially when mixed with superplasticizer.The averages percentage decreasing in compressive strength are 43.6%, 27.74, and 49.8 for lightweight concrete, and 41.22, 42.15, and 41.09 for foam concrete and 50%, 40%, and 58.07% for normal concrete under the effect of HCL, H2SO4, and HCl+H2SO4 solutions respectively. The study proved the efficiency of hammer method to estimate the resistance of concrete to acidic solution.

تم في هذا البحث دراسة تاثير محاليل حامضي الهيدروكلوريك والكبريتيك ومزيجهما على نوعين من الخرسانة خفيفة الوزن الاولى منتجة بواسطة استخدام ركام خفيف الوزن والثانية باستخدام مادة رغوية. و تم دراسة تأثير استخدام ابخرة السليكا مع او بدون الملدن الفائق في الخرسانة خفيفة الوزن على مقاومتها للحوامض. تم استخدام طريقة جديدة مقترحة في قياس تأثير الحوامض على الخرسانة اضافة الى الطريقة التقليدية، كما تم اقتراح ادخال فحص المطرقة لقياس مقاومة الخرسانة المتصلدة في قياس مدى تأثر الخرسانة بالحوامض. جميع النماذج تم غمرها لمدة 60 يوما في المحاليل الحامضية . افرزت الدراسة استنتاجات مهمة حول تاثير الحوامض على الخرسانة خفيفة الوزن مع او بدون المضافات. فبالرغم من ان استخدام ابخرة السليكا تزيد من مقاومة الخرسانة الا انها لاتعمل دائما على زيادة مقاومتها للحوامض بل على العكس قد تقلل من مقاومتها للحوامض وخصوصا عند مزجها مع الملدن الفائق. كان معدل النسبة المئوية للنقصان بمقاومة الانضغاط للخرسانة خفيفة الوزن 43.6% و 27.74% و 49.8% بينما كانت النسب للخرسانة الرغوية 41.22% و 42.15% و 41.09% وللخرسانة الاعتيادية 50% و 40% و 58.07% تحت تاثير محاليل HCL, H2SO4, and HCl+H2SO4 . كما اثبتت الدراسة كفاءة طريقة المطرقة لتخمين مدى تاثر الخرسانة بالحوامض.

Listing 1 - 10 of 10
Sort by
Narrow your search

Resource type

article (10)


Language

English (6)

Arabic and English (2)

Arabic (1)


Year
From To Submit

2013 (10)