Article
Investigation of Flexural Properties and Thermal Conductivity for Wood Dust Filled Epoxy.

Author: Ban M. Al-Shabander
Journal: Al-Nahrain Journal of Science مجلة النهرين للعلوم ISSN: (print)26635453,(online)26635461 Year: 2013 Volume: 16 Issue: 3 Pages: 104-109
Publisher: Al-Nahrain University جامعة النهرين

Loading...
Loading...
Abstract

This paper presents the flexural properties and thermal conductivity of composites made from wood dust filler particles and epoxy resin. The flexural tests of composites, based on wood dust filler particles at different filler contents viz. (0, 1, 3, 5, 7 and 10) Wt%, were carried out using an Instron universal testing machine according to ASTM D790 and their results were presented. Experimental results showed that the flexural strength of the composites decreased with the increase of the filler particle content. Concerning the relation between the Young’s modulus and percentage of filler for flexural tests, it was found to be directly proportional at low concentrations of wood dust, at concentrations of 7 Wt% and 10 Wt% wood dust, the Young’s modules decreases with increasing wood dust, with values of (1.870) and (1.824) GPa respectively.Thermal tests were done using Lee’s disk to determine the coefficient of thermal conductivity. The results obtained showed that the increasing weight percentage of wood dust in the composite leads to decreasing the thermal conductivity.

يعنى هذا البحث بدراسة خواص الالتواء والتوصيلية الحرارية لمتراكبات مكونه من جسيمات غبار الخشب والايبوكسي. وقد قمنا بأختبار متراكبات تحوي نسب مختلفه من جسيمات غبار الخشب و قدرها (0, 1, 3, 5, 7, 10) Wt% وذلك بأجراء اختبارات عالمية طبقا لتوصيف محدد ASTM D 790. وقد اظهرت هذه الاختبارات ان متانة الانحناء تتناقص مع زياده نسبة الجسيمات الممزوجة. اما بخصوص العلاقه بين معامل يونك والنسبة المئوية للمادة الممزوجة فأنها تزداد بزيادة نسبه جسيمات الخشب عند التراكيز الواطئة اما عند التراكيز العالية (7) Wt% و (10) Wt%فأن معامل يونك يتناقص مع زيادة نسبه جسيمات الخشب وتساوي (1.870) و (1.824) GPa على الترتيب. اجريت اختبارات حرارية تضمنت استخدام قرص لي لحساب معامل التوصيل الحراري واظهرت النتائج المستحصلة انخفاض التوصيلية الحرارية مع زيادة نسبة جسيمات الخشب.


Article
Studying The Mechanical And Electrical Properties Of Polyester Resin Reinforced With Silica Particals
دراسة الخواص الميكانيكية والكهربائية لراتنج البولي استر المدعم بدقائق السليكا

Author: Shayma. H. Mohammad شيماء حميد محمد
Journal: Journal of Engineering and Sustainable Development مجلة الهندسة والتنمية المستدامة ISSN: 25200917 Year: 2013 Volume: 17 Issue: 6 Pages: 201-214
Publisher: Al-Mustansyriah University الجامعة المستنصرية

Loading...
Loading...
Abstract

A study has been made on mechanical properties of polyester resin matrix reinforced with weight fraction (10,20, 30&40) % of silica particles. The specimens were subjected to tensile test bending test (three point method), and hardness test .The experimental results indicate that the tensile strength of the matrix material were found to be significantly higher than those of the composite material (36%,36.1%,52%,57.5) while the young modulus of matrix material were found to be less than of composite material (14%,33%,42%, 45%). Test result also indicate that the flexural strength of the matrix material were found to be significantly higher than those of the composite material (6%,27%,29%,51) while the young modulus of matrix material were found to be less than of composite material(41%,50%,57.6%, 63%) . hardness of the composite materials are significantly higher than those of the matrix material (20%,28.6%,34%,43%) the enhancement in these properties are found to be directly proportional to the weight fraction of reinforcement materials. Test results also indicate that the electrical conductivity increased with increasing the silica concentrations.

تم في هذا البحث دراسة الخواص الميكانيكية والكهربائية لراتنج البولي استر المدعم بدقائق السليكا وبنسب وزنيه (10, 20, 30 &40 ). تعرضت العينيات إلى اختبار الشد وجساءة الانحناء (ثلاثي النقاط ) والصلادة حيث أظهرت النتائج إن متانة الشد للمادة الأساس أعلى من المادة المركبة بمقدار (57.5%,52%,36.1%,36%) إما معامل المرونة للمادة الأساس اقل من المادة المركبة بمقدار (14%,33%,42%, 45%) .إما في اختبار الانحناء أظهرت النتائج إن متانة الانحناء للمادة الأساس أعلى من المادة المركبة بمقدار (51%,29%,27%,6%) إما معامل المرونة للمادة الأساس اقل من المادة المركبة بمقدار (41%50%,57.6%, 63%) .إما نتائج اختبارات الصلادة أظهرت إن صلادة المواد المركبة أعلى بكثير من المادة الأساس 43%,34%,28.6%,20% ))وان التحسن في الخواص يتناسب طرديا مع الكسر ألوزني للمواد المدعمة إما بالنسبة لاختبار التوصيل الكهربائي فقد أظهرت النتائج إن خاصية التوصيل الكهربائي للمادة المركبة اعلى من المادة الأساس وتزداد بزيادة النسبة الوزنية لدقائق التدعيم .


Article
MICROMECHANICAL MODELING OF SHORT –FIBER REINFORCED POLYMERIC
النمذجة الميكانيكية الدقيقة لمركب مسلح بألواح البوليمر

Author: Kareem N. Hussien كريم نجم حسين
Journal: Muthanna Journal of Engineering and Technology(MJET) مجلة المثنى للهندسة والتكنولوجيا ISSN: 25720317 25720325 Year: 2013 Volume: 2 Issue: 2 Pages: 73-82
Publisher: Al-Muthanna University جامعة المثنى

Loading...
Loading...
Abstract

This paper presents a method considering the effect of fiber geometry and volume fraction for predicting the tensile strength, shear stress and Von Mises stress. The finite element scheme for the micromechanical modeling of the behavior of fiber reinforced polymeric composites under external load is developed. The model is used to estimate the stress distribution throughout the composite domain and to identify the location where maximum stresses occur. The ratio between fiber modulus and matrix modulus must be high enough to improve the mechanical properties and to reduce the premature interfacial failure. The prediction of the stress distribution by using a simulation tool could be helpful for more understanding the real reasons behind failure of polymer composites.

يقدم هذا البحث طريقة لحساب تأثير أبعاد الألياف ونسبتها الحجمية للتنبؤ بقيم مقاومة الشد, أجهاد القص وأجهاد فون ميسيس. اعتمد هذا البحث على تطوير طريقة العناصر المحدودة لنمذجة التصرف المايكروميكانيكي للبوليمر المقوى بالألياف تحت تأثير الحمل الخارجي. أستخدم النموذح العددي لتقدير توزيع الأجهاد على مدى المادة المركبة بغرض تحديد أماكن الأجهاد الاقصى. تعتبر النسبة العالية بين معامل الليف الى البوليمر أساسا لتحسين الخواص الميكانيكية ولمنع الأنهيار المبكر . أن التنبؤ بتوزيع الأجهاد باستخدام نماذج المحاكاة الدقيقة يساهم في زيادة الفهم لأسباب الأنهيار للمواد البوليمرية المركبة.