Fabrication of Tio2 and V2o5 Thin Films by Powder Coating Technique
تصنیع اغشیة رقیقة من اوكسید التیتانیوم و اوكسید الفنادیوم بتقنیة مساحیق الطلاء

Authors: Mohammed S. Hamza --- Alaa Aladdin --- Shatha Kazem
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2013 Volume: 31 Issue: 16 Part (A) Engineering Pages: 3194-3202
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

Titanium dioxide (TiO2) and vanadium oxide (V2O5) in different mixing percentage(100, 50, 0)% from them powders as thin film on substrate of glass .the coatingthickness was ( 0.37 ±0.03 μm ).Thin films were inspection by microphotographs with scanning electron microscopy(SEM) and x-ray diffraction (XRD).The results showed that thin films was prepared crystalline and also the compound(tio2, v2o5), and the structure was regular and smooth.

Keywords

TiO2 --- V2O5 --- THIN film --- SEM --- XRD


Article
Mechanical and Morphological Properties of HDPE: PP and LDPE: PP Polymer Blend Composites Reinforced with TiO2 particles
الخواصالمیكانیكیة و المجھریة لمتراكبات الخلائط البولیمریة HDPE: PP و LDPE: PP المقواة بدقائق اوكسید التیتانیوم

Authors: Sihama I. Salih --- Abdullkhaliq F.hamood --- Alyaa H. Abdalsalam
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2013 Volume: 31 Issue: 12 Part (A) Engineering Pages: 2211-2227
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

In this research two groups of polymer blends have been prepared First group included (High density polyethylene (HDPE): Polypropylene (PP))While the Second group(included Low density polyethylene (LDPE): Polypropylene (PP)) both groups prepared withpolypropylene of (20% and 80%). From the results of tensile test for the prepared blends it has been showed that the optimum blending ratio was (20%LDPE:80%PP and 20%HDPE:80%PP) which thenreinforced with (2, 5 and 8wt%) oftitanium dioxide (TiO2), particle size (0.421μm). Titaniaparticles weremechanically mixed with the polymers prior tomelt mixing for better dispersion.Polymerblend composites were obtained by using single screw extruder. Results showed that mechanical properties increased as titania content increased except elongation.Furthermore the result recorded highest values ofimpact strength and fracture toughness at2%wt TiO2which is 312 Mpa and 572.8Mparespectively,for the polymer blend (20%HDPE: 80%PP) composite and for the polymer blend (20%LDPE: 80%PP) composites the impact strength and fracture toughness are 262.5Mpa and 468 Mpa respectively.The mechanical properties values of 20%HDPE: 80%PP is higher than 20%LDPE: 80%PP polymer blendcomposites. Scanningelectron microscopy (SEM) imagesshowed that there isbonding developed between TiO2 and polymer blends in some regions.

Keywords

Polymer blend --- TiO2 --- HDPE --- PP --- composite --- Mechanical properties


Article
Annealing Effect on the Growth of Nanostructured TiO2 Thin Films by Pulsed Laser Deposition (PLD)
تأثير التلوين على انماء الاغشية الدقيقة ل((TiO2 ذات التركيب الثانوي بواسطة تركيب الليزر النبضي

Authors: Sarmad S.Kaduory --- Ali A.Yousif --- Adawiya J. Haider --- Khaled Z.Yahya
Journal: Engineering and Technology Journal مجلة الهندسة والتكنولوجيا ISSN: 16816900 24120758 Year: 2013 Volume: 31 Issue: 4 Part (B) Scientific Pages: 460-470
Publisher: University of Technology الجامعة التكنولوجية

Loading...
Loading...
Abstract

In this work, Nanostructured TiO2 thin films were grown by pulsed laser deposition (PLD) technique on glass substrates at 300 °C. TiO2 thin films were then annealed at 400-600 °C in air for a period of 2 hours. Effect of annealing on the structure, morphology and optical properties were studied. The X-ray diffraction (XRD) and Atomic Force Microscopy (AFM) measurements confirmed that the films grown by this technique have good crystalline tetragonal mixed anatase and rutile phase structure and homogeneous surface. The study also reveals that the RMS value of thin films roughness increased with increasing annealing temperature .The optical properties of the films were studied by UV-VIS spectrophotometer. The optical transmission results shows that the transmission over than ~65% which decrease with the increasing of annealing temperatures. The allowed indirect optical band gap of the films was estimated to be in the range from 3.49 to 3.1 eV. The allowed direct band gap was found to decrease from 3.74 to 3.55 eV with the increase of annealing temperature. The refractive index of the films was found from 2.27 -2.98 at 550nm. The extinction coefficient increase with annealing temperature.

في هذه البحث، تم انماء أغشية اوكسيد التيتانيوم ((TiO2 النانوية بواسطة تقنية ترسيب الليزر النبضي (PLD) على قواعد زجاجية في درجة حرارة 300 مئوية. ومن ثم لدنت أغشية TiO2 الرقيقة من 400 الى 600 درجة مئوية في الهواء لمدة ساعتين . وتم دراسة تأثير التلدين على تركيب وطبوغرافية السطح والخصائص البصرية. من قياسات حيود الأشعة السينية (XRD) ومجهر القوة الذرية ((AFM اثبت بأن الاغشية المنمات بهذه الطريقة لها تبلور جيد وذات تركيب رباعي وخليط من طورين الأناتاس والروتيل وذات سطح متجانس. وتظهر الدراسة بأن قيم RMS للأغشية الرقيقة والخشونة تزداد مع زيادة درجة الحرارة التلدين. وتم دراسة الخصائص البصرية للأغشية في مطياف النفاذية للأشعة المرئية وفوق البنفسجية (قيست بواسطة مطياف(UV-VIS . نتائج النفاذية الضوئية تظهر بأن هنالك نفاذية أكثر من~ 65٪ والتي تقل مع زيادة درجات الحرارة التلدين. فجوة الطاقة البصرية المسموحة الغير مباشرة الأغشية قدرة بحدود من 3.49 الى 3.1 الكترون فولت. ووجد ان فجوة الطاقة البصرية المسموحة المباشرة تقل من 3.74 الى 3.55 إلكترون فولت بزيادة درجة حرارة التلدين. ووجد ان معامل الانكسار للأغشية تتراوح من 2.27 الى 2.98 عند الطول الموجي 550 نانومتر. وان معامل الخمود يزداد بزيادة درجة حرارة التلدين


Article
Study of Annealing Effect on the Some Physical Properties of Nanostructured TiO2 films prepared by PLD
دراسة تأثير التلدين على بعض الخصائص الفيزيائية للأغشية TiO2التركيب النانوي المصنعة بتقنية PLD

Authors: Ali A.Yousif علي احمد يوسف --- Sarmad S. Al-Obaidi سرمد العبيدي
Journal: Journal of College of Education مجلة كلية التربية ISSN: 18120380 Year: 2013 Issue: 3 Pages: 139-160
Publisher: Al-Mustansyriah University الجامعة المستنصرية

Loading...
Loading...
Abstract

Nanostructured Titanium Dioxide (TiO2) thin films were prepared by pulsed laser deposition (PLD) on the glass substrates. The effects of different annealing temperature (400, 500 and 600 °C) towards the some physical properties such as structural, morphological and optical have been studied. From X-ray diffraction result, the crystallinity of TiO2 thin films improved at higher annealing temperature. It also could be observed that the rutile phase start to exist at annealing temperatures of 500 °C and 600 °C. The Full Width at Half Maximum (FWHM) of the (101) peaks of these films decreases from 0.450° to 0.301° with increasing of annealing temperature. AFM measurements confirmed that the films grown by this technique have good crystalline and homogeneous surface. The Root Mean Square (RMS) value of thin films surface roughness increased with increasing of the annealing temperature. From UV-VIS spectrophotometer measurements, the optical transmission results shows that theمجلة كلية التربية ............................................................. العدد الثالث 3102140transmission over than ~65% in the near-infrared region which decrease with the increasing of annealing temperatures. The allowed indirect optical band gap of the films was estimated to be in the range from 3.49 to 3.1 eV. The allowed direct band gap was found to decrease from 3.74 eV to 3.55 eV with the increase of annealing temperature. The refractive index of the films was found from 2.27 -2.98 at 550nm. The extinction coefficient, real and imaginary parts of the dielectric constant increase with annealing temperature.


Article
Quantitative Phase Analysis for Titanium Dioxide From X-Ray Powder Diffraction Data Using The Rietveld Method
تحليلات الطور الكمية لثاني أوكسيد التيتانيوم بطريقة ريتفيلد من بيانات حيود الأشعة السينية

Author: T.A.AL-Dhahir طارق عبد الرضا الظاهر
Journal: Diyala Journal For Pure Science مجلة ديالى للعلوم الصرفة ISSN: 83732222 25189255 Year: 2013 Volume: 9 Issue: 2 Pages: 108-119
Publisher: Diyala University جامعة ديالى

Loading...
Loading...
Abstract

In this study, we report the quantitative phase analysis which is performed by Rietveld X-ray diffraction using “fullprof”( fullprof.2k,Version 5.00 - Jan2011-ILL JRC) program to four different samples of TiO2 . Titanium dioxide is formed of two phases, Anatase and Rutile with different weight percentage. Four samples under study , first is a nanopowder , second is thin a film ,third is the micropowder while the fourth is formed of 50:50 Anatase and Rutile TiO2 which is considered as standard. Retiveld refinement on X-ray data for the samples is performed . The obtained results have a good optimization between the observed x-ray diffraction pattern and that calculated by Retiveld. This optimization is determined according to Rp, Rwp and GOF . The accuracy check was done by examining the fourth sample by X-ray. Then, quantitative phases were calculated by comparing method which needs pure phases mixture. The final result shows that Retiveld refinement is more accurate than comparing method.

تم في هذه الدراسة إجراء التحليلات الكمية بطريقة ريتفيلد بإستخدام برنامج “fullprof” لأربع عينات مختلفة من TiO2 المتكون من طوري الأنتيز والروتايل وبنسب وزنية مختلفة ،الأولى مسحوق نانوي والثانية غشاء رقيق والثالثة والرابعة مسحوق مايكروي .أجريت تصفية ريتفيلد على البيانات المأخوذة من حيود الأشعة السينية, حيث دلت النتائج على الموائمة الجيدة بين مخطط الحيود الملاحظ المأخوذ مباشرة من حيود الأشعة السينية ومخطط الحيود المحسوب بطريقة ريتفيلد على نجاح عملية التصفية حيث تم ذلك من خلال عوامل الموثوقية GOF, Rwp , Rp .للتحقق من دقة نتائج التحليل الكمي بهذه الطريقة تم إعتبار العينة الرابعة كمقياس لذلك حيث تم تحضيرها بخلط طوري الأنتيز والروتايل بنسبة وزنية متساوية 50:50 لكل منهما, ثم فحصت العينة بالأشعة السينية .ولإجراء المقارنة تم إجراء التحليل الكمي بطريقة المقارنة المباشرة حيث تحتاج هذه الطريقة الى الأطوار النقية من العينة التي يجرى التحليل الكمي لها ,على خلاف طريقة ريتفيلد , وقد كان التحليل الكمي بطريقة ريتفيلد أكثر دقة من طريقة المقارنة المباشرة .


Article
Effect of Sputtering pressure and partial pressure on Structural Properties of TiO2thin Films
تاثير ضغط الترذيذ والضغط الجزيئي على الخصائص التركيبية لأغشية ثنائي اوكسيد التيتانيوم المحضرة باستخدام الترذيذ بالتيار المستمر

Authors: Mahdya A.Yeser مهدية احمد يسر --- Raaed S.Atea رائد ستار عطية
Journal: Journal of Kufa - physics مجلة الكوفة للفيزياء ISSN: 20775830 Year: 2013 Volume: 5 Issue: 2 Pages: 15-20
Publisher: University of Kufa جامعة الكوفة

Loading...
Loading...
Abstract

Effect of sputtering pressure and partial pressure on structural properties of TiO2 films prepared using DC-sputtering to glass substrate was investigated. sputtering pressures are changed (1.8,2.8,3.8,4.3 pa) at constant O2 /Ar Ratio(5%). Measurements reveal that the TiO2 films at the sputtering pressure 1.8 pa is amorphous , while at increasing pressure to 2.8 pa becomes crystalline with Rutile phase (110) and when we increase the pressure to 4.3 pa get crystalline structure with anatas phase ( 101) .Grain size is calculated per crystalline structure of the anatas and rutile (15.7) nm and(14.2) nm respectively. For constant sputtering pressure (2.8pa) and changedO2/Ar Ratio(10% ,15% ,20% ,25% ,30% , 35%),TiO2 thin films are a amorphous, except percentage (25%) is crystalline with anatas phase (101) and with grain size (15.7 nm).

تم في هذا البحث دراسة تاثير كل من ضغط الترذيذ والضغط الجزيئي على الخصائص التركيبة لاغشية ثنائياوكسيد االتيتانيوم المحضرة باستخدام منظومة الترذيذ بالتيار المستمر على ارضيات زجاجية . الخطوة الاولىفي البحث تم تثبيت الضغط بتثبيت الضغط الجزيئي للاوكسجين عند النسبة 5%) ( وتغير ضغط غاز الترذيذ( 1.8,2.8,3.8,4.3pa ( وثانيا تم تثبيت ضغط الترذيذ عند الضغط ) 2.8 pa ( وتغير الضغط الجزيئيللاوكسجين (10%,15%,20%,25%,30%,35% ) . من قياسات حيود الاشعة السينية تبين ان الاشعة عندالضغط ) 1.8 pa ( عشوائية التركيب ولكن عند الضغط ) 2.8 pa ( تصبح بلورية التركيب وبطور الروتيلوبزيادة الضغط اكثر تصبح الاغشية وبالتحديد الضغط ) 4.3 pa ( بلورية التركيب وبطور الاناتاس وبتوجيهية( 101 ) , بينما عند تثبيت النسبة وزيادة الضغط سوف نحصل على تركيب بلوري وبطور الاناتاس وبتوجيهة( 101 ( عند النسبة .25%قمنا بحساب الحجم الحبيبي للاغشية المحضرة كدالة لكل من ضغط الترذيذ مرة والضغط الجزيئي مرة اخرى

Listing 1 - 6 of 6
Sort by
Narrow your search

Resource type

article (6)


Language

English (6)


Year
From To Submit

2013 (6)