Evaluations of Some Physical Properties of Cement with PVA/Polyol as Binder Material to produce insulating board
دراسة الخواص الفيزيائية لمزيج البوليمر البولي فاينيل اسيتيت/البولي اول المخلوط مع الاسمنت

Loading...
Loading...
Abstract

The composition of polymer blend (PVA/Polyol) by percentage 3:1, which is mixed with different a percentage (10%-90%) with different percentages of cement (10%-90%), where investigated. The optimal percentage of polymer blend and cement is 10% and 90% respectively. Physical properties of the mixture such as density, water absorption and compressive strength were determined; mixture of 10% cement was used as a binder to study the physical properties with different percentages of polymer blend and sand. This will prove a resistance to water absorption and can be used in ready construction panels.

تكوين مزيج من خلط البولي فينيل اسيتيت/البولي اول بنسبة 3:1الذي تم دراسته بنسب مختلفة (10-90)% مع نسب مختلفة من الاسمنت (10-90)%. كانت النسبة المثلى من خلط مزيج البوليمر و الاسمنت 10% و90% على التوالي. تم تعيين الخواص الفيزيائية للخليط، مثل الكثافة, امتصاص الماء و مقاومية الانضغاطية. كذلك دراسة الخواص الفيزيائية بأستخدام خليط بنسبة 10% اسمنت كرابط مع نسب مختلفة من مزيج البوليمر والرمل. هذا الخليط سوف يبرهن على مقاوميته لأمتصاص الماء وأمكانية أستخدامه في ألواح البناء الجاهز.


Article
THE EFFECT OF NANO METAKAOLIN MATERIAL ON SOME PROPERTIES OF CONCRETE
تأثیر المواد البوزولانیة النانویة على بعض خواص الخرسانیة

Loading...
Loading...
Abstract

ABSTRACT:- This investigation aimed to study the effect of nano metakaolin ( NMK ) onsome properties (compressive strength ,splitting tensile strength & water absorption ) ofconcrete. The nano metakaolin (NMK) was prepared by thermal activation of kaolin clay for 2hours at 750 Ċ. The cement used in this investigation consists of ordinary Portland cement(OPC). The OPC was partially substituted by NMK of ( 3, 5 & 10%) by weight of cement.The C45 concrete was prepared , using water/cement ratio ( W/c) of (0.53) .The Waterabsorption was tested at 28 days while the tests (compressive strength ,splitting tensilestrength) were tested at ages of (7, 28, 60,& 90) days . The compressive strength andsplitting tensile strength of concrete with NMK were higher than that of reference concretewith the same W/c ratio.The improvement in the compressive strength when using NMK was(42.2, 55.8 , 63.1% ) at age 28 days for ( 3%, 5%, &10% ) replacement of NMK respectivelywhereas the improvement in the splitting tensile strength was (0% , 36% & 46.8 %) at age of28 days when using (3%, 5%, &10% ) NMK respectively. The improvement in the waterabsorption was (16.6%, 21.79%, &25.6 ) when using (3, 5, &10% )NMK.

الخلاصةهذا البحث یهدف الى دراسة تأثیر مادة النانو میتاكائولین على بعض خواص الخرسانة (مقاومة الانضغاط، مقاومةالشد الانفلاقي، وامتصاص الماء) .تم تهیئة مادة النانو میتاكائولین بواسطة التفعیل الحراري لاطیان الكاؤولین لمدة ساعتینو عند درجة حرارة ٧٥٠ درجة مئویة .الاسمنت المستخدم بهذه الدراسة هو اسمنت بورتلاندي اعتیادي .تم استبدال٥%،و ١٠ %) من وزن الاسمنت .الخرسانة المستخدمة بهذا ،% الاسمنت جزئیا بمادة ثانویة هي المیتاكاؤولین بنسب ( ٣المستخدمة = 0.53 .تم فحص امتصاص الماء عند عمر ٢٨ یوم W/C ونسبة C البحث كانت ذات مقاومة انضغاط 45اما بقیة الفحوصات فیتم فحصها بالاعمار ( ٦٠,٢٨,٧ ،و ٩٠ ) یوم .اظهرت النتائج زیادة في لمقاومة الانضغاط للخرسانة٥٥.٨ ،و ٦٣.١ % ) عند ، الحاویة النانو میتاكاؤولین مقارنة مع الخلطة المرجعیة عند نفس نسبة الاسمنت بمقدار ( ٤٢.٢٥%و ١٠ %) على التوالي بینما كانت نسبة التحسین لمقاومة الشد ،% استخدام مادة النانو المیتاكاؤولین بنسب استبدال ( ٣٥%، و ١٠ %) على ،% ٣٦ %، و ٤٦.٨ %) عند استخدام نسب استبدال لمادة النانو المیتاكاؤولین ( ٣ ،% الانفلاقي هي ( ٠،%٥ ،% ٢١.٧٩ %، و ٢٥.٦ %) عند استخدام ( ٣ ،% التوالي .نسبة التحسین الحاصل في فحص امتصاص الماء ( ١٦.٦و ١٠ %) نانو میتاكاؤولین على التوالي.